• Journal of Powder Materials
• /
• v.12 no.3
• /
• pp.174-178
• /
• 2005

This paper deals with the fabrication of titanium carbide using fine titanium hydride. The ratio of $TiH_2$ and C (Activated carbon) was 1:1 (mol) and milled in a planetary ball mill at a ball-to-powder weight ratio of 20:1. Thereafter, TGA was performed at $1400^{\circ}C$ to observe change of weight with milling time. Titanium carbide was obtained by using tempering the milled powders at $1100-1500^{\circ}C$. The microstructures of titanium carbide as well as the change of the lattice parameters and particle size have been studied by X-ray diffraction (XRD) and scanning electron microscopy (SEM).

• Korean Journal of Materials Research
• /
• v.5 no.8
• /
• pp.997-1004
• /
• 1995

Intermetallic compound NbAl₃and amorphous phases were synthesized by mechanical alloying of elemental powder mixtures of niobium and aluminum. The composition of the powder mixtures was Nb-45wt%Al(75at%Al). The mechanical alloying was performed with a high energy SPEX 8000 mixer/mill up to 72 hrs. The resulting powders were analyzed by XRD, DTA, SEM and TEM. The mechanically alloyed powders exhibited lamellar structures in the early stage. And the elements of Nb and Al were homogeneously distributed over the Powder when a steady state was reached. An intermetallic compound, NbAl₃, was formed by mechanical alloying for 4 hrs. The mechanically alloyed powders exhibited a large exotherm around 600℃, corresponding to formation of stable NbAl₃and stress relief.

• Journal of Powder Materials
• /
• v.25 no.2
• /
• pp.126-131
• /
• 2018

In the present study, we investigate the effects of milling time and the addition of a process control agent (PCA) on the austenite stability of a nanocrystalline Fe-7%Mn alloy by XRD analysis and micrograph observation. Nanocrystalline Fe-7%Mn alloys samples are successfully fabricated by spark plasma sintering. The crystallite size of ball-milled powder and the volume fraction of austenite in the sintered sample are calculated using XRD analysis. Changes in the shape and structure of alloyed powder according to milling conditions are observed through FE-SEM. It is found that the crystallite size is reduced with increasing milling time and amount of PCA addition due to the variation in the balance between the cold-welding and fracturing processes. As a result, the austenite stability increased, resulting in an exceptionally high volume fraction of austenite retained at room temperature.

• Korean Journal of Materials Research
• /
• v.21 no.7
• /
• pp.396-402
• /
• 2011

In this study, by using tin chloride solution as a raw material, a nano-sized tin oxide powder with an average particle size below 50 nm is generated by a spray pyrolysis process. The properties of the generated tin oxide powder depending on the inflow speed of the raw material solution are examined. When the inflow speed of the raw material solution is 2 ml/min, the majority of generated particles appear in the shape of independent polygons with average size above 80-100 nm, while droplet-shaped particles show an average size of approximately 30 nm. When the inflow speed is increased to 5 ml/min, the ratio of independent particles decreases, and the average particle size is approximately 80-100 nm. When the inflow speed is increased to 20 ml/min, the ratio of droplet-shaped particles increases, whereas the ratio of independent particles with average size of 80-100 nm decreases. When the inflow speed is increased to 100 ml/min, the average size of the generated particles is around 30-40 nm, and most of them maintain a droplet shape. With a rise of inflow speed from 2 ml/min to 5 ml/min, a slight increase of the XRD peak intensity and a minor decrease of specific surface area are observed. When the inflow speed is increased to 20 ml/min, the XRD peak intensity falls dramatically, although a significant rise of specific surface area is observed. When the inflow speed is increased to 100 ml/min, the XRD peak intensity further decreases, while the specific surface area increases.

• Journal of Powder Materials
• /
• v.28 no.3
• /
• pp.221-226
• /
• 2021

We fabricate the non-equiatomic high-entropy alloy (NE-HEA) Fe_49.5Mn₃₀Co₁₀Cr₁₀C_0.5 (at.%) using spark plasma sintering under various sintering conditions. Each elemental pure powder is milled by high-energy ball milling to prepare NE-HEA powder. The microstructure and mechanical properties of the sintered samples are investigated using various methods. We use the X-ray diffraction (XRD) method to investigate the microstructural characteristics. Quantitative phase analysis is performed by direct comparison of the XRD results. A tensile test is used to compare the mechanical properties of small samples. Next, electron backscatter diffraction analysis is performed to analyze the phase fraction, and the results are compared to those of XRD analysis. By combining different sintering durations and temperature conditions, we attempt to identify suitable spark plasma sintering conditions that yield mechanical properties comparable with previously reported values. The samples sintered at 900 and 1000℃ with no holding time have a tensile strength of over 1000 MPa.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.10a
• /
• pp.85-88
• /
• 1999

We tested the limestone powder as a filler powder for the effective use of slag cement. Hydration process were investigated by measuring the thermal differential analysis(DTA), compressive strength, XRD patterns, calorimeter of slag cement-limestone powder paste prepared by mixing limestone powder-slag cement. The results obtained in this study, there were no significant difference between the cases of adding up to 5% limestone powder, but the reaction time was accelerated. Also the compressive strength was increased for adding up to 5% limestone powder. The min hydrated paste products were Ca(OH)2 and calcium silicate hydrates. In the case of mixed limestone powder peak appear tricalcium carboaluminate hydrate in the sample of 7 days hydration.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.722-723
• /
• 2006

A new method has been developed to fabricate microcomponents by a combination of photolithography and sintering of metallic powder mixtures, without the need for compression and the addition of Mg. This involves (1) the fabrication of a micromould, (2) mould filling of the powder/binder mixture, (3) debinding and (3) sintering. The starting powdered materials consisted of a mixture of aluminium powder(average size of 2.5 um) and alloying elemental powder of Cu and Sn(less than 70nm), at appropriate proportions to achieve nominal compositions of Al-6wt%Cu, Al-6wt%Cu-3wt%Sn. This paper presents detailed investigation of debinding behaviour and microstructural development.

• Journal of Powder Materials
• /
• v.15 no.6
• /
• pp.477-481
• /
• 2008

Formation and characteristics of spraying powder for BSCCO High-Tc superconductor prepared by plasma spray coating were investigated. The addition of 3% of binder gives the best flowability of the powder. Ball milling for 30h and 35h gives the best flowability of powder in the case of 2001 and 0212, respectively. The withdraw ratio increases upon binder addition from 12 to 27% in the case of 2001 and from 18 to 31% in the case of 0212 for sieving powder of $30-90{\mu}m$ in size. The built-up efficiency for $100{\mu}m$ thickness of spray coating is increased more than 30% by binder addition. The microstructure of the spray coated layers was investigated by XRD and EDS analysis.

• Journal of Powder Materials
• /
• v.6 no.1
• /
• pp.75-80
• /
• 1999

The formation of $n-TiO_2$ powder by oxidation of Ti-ethoxied vapor in a flat flame burner reactor maintained under 20 torr has been studied. The produced powder were characterized in terms of crystal structure, chemical composition by XRD and TEM. The results showed that the powder consisted of loose agglomerated anatase and rutile particles and their size were about 10 nm and 20 nm, respectively. In the course of synthesis, changes of the flame color were happened to each condition during heating up the bubbler. The flame color transition phenomena reveled that a critical precursor delivery rate was needed for the powder formation (obtainable powder yield). The critical precursor delivery rate was estimated by a simple function of the bubbler temperature and the carrier gas flow rate. The critical precursor delivery rate was reviewed as an important variable of the nanopowder synthesis.

• Journal of Industrial Technology
• /
• v.41 no.1
• /
• pp.25-30
• /
• 2021

Hydride-dehydride process for efficient recycling of tantalum (Ta) is used for manufacturer of Ta powder. In case of metal powder, Impurities as like nitride, oxygen, hydrogen is decreased of physical properties. For manufacture of Ta powder, control of theses impurities is important. In this study, to decreased of impurities on Ta powder using HDH process optimize dehydride condition. Dehydration behavior of Ta is depended on temperature, time, and atmosphere. Phase transition of Ta hydride is analyzed by X-ray diffraction (XRD). Concentration of hydrogen is decreased with temperature increased. At high temperature, concentration of hydrogen in Ta is similar according to time increased. Size and morphology of powder is not observed after dehydride. Ta powder, which is less than 20 um, concentration of hydrogen under 800 ppm is obtain.