• Journal of the Korean Society for Precision Engineering
• /
• v.16 no.5 s.98
• /
• pp.98-103
• /
• 1999

The application field of porous mold is more and more expended. A mixture of alumina and cast iron is used for making porous mold using slip and vacuum casting method in this study. Slip casting is a process that slurry is poured into silicon rubber mold, dried in vacuum oven, debinded and sintered in furnace, In this procedure, slurry is composed of powder, binder, dispersion agent, and water. Vacuum casting is a technique for removing air bubbles existed in the slurry under vacuum condition. Since ceramics has a tendency of over-shrinkage after sintering, cast iron is used to compensate dimensional change. The results shows that sintering temperature has a great effect on characteristics of alumina-cast iron composite sintered parts. Finally ceramic-metal composite sintered mold can be used for aluminum alloy casting of shoe mold using this process.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.8
• /
• pp.1371-1379
• /
• 2003

RP&M (Rapid Prototyping and Manufacturing) is the most appropriate technology for the small-lot production system, because the production cycle is getting shorter owing to various needs of the consumer. In this paper, rapid tooling technology is applied to the casting process. The casting process has the ability to reflect complicated shapes in one process. But it has not been widely used to make a die and mold because of the poor surface quality caused by air bubbles on the surface of the casting product. In this study, the porous casting mold is fabricated from a mixture of plaster and water-soluble binder. The porous casting mold can improve the characteristics of casting products with the help of the vacuum sealed casting process. The vacuum sealed casting process is an advanced technology that removes the air bubbles between the porous casting mould and the liquid metal, thus making the surface of the casting product finer. The purpose of this paper is to develop a high quality shoe mold using porous casting mold and to apply the RP&M technology to the shoe industry.

• Journal of the Korean Society for Precision Engineering
• /
• v.16 no.11
• /
• pp.62-67
• /
• 1999

The RP&M(Rapid Prototyping and Manufacturing) is the most appropriate technology for the small-lot production system, in which the production cycle is getting shorter owing to various needs from consumers. Recently RP products which are made of plastics, wax, and paper are used to verify the design of samples. But these products cannot be applied to the real mold because the strength enough to be a mold cannot be given by soft materials such as plastics. So RP products are copied to AFR(Al powder Filled Resin) molds or metal molds, which is called the RP&M. In this paper, RP&M is applied to a casting process. A porous casting mold, which is made from ceramic powder and binder, is used for rapid tooling of aluminum shoes molds.

• Journal of Technologic Dentistry
• /
• v.32 no.4
• /
• pp.297-305
• /
• 2010

Purpose: The purpose of this study was to observe the change of metal-mold reaction and surface roughness in titanium casting specimens for phosphate-silica alumina bonded investment with mold temperatures. Methods: The metal-phosphate silica alumina bonded mold interface reaction and surface roughness of titanium casting specimens according to mold temperatures were investigated. The Specimens were analysed by scanning electron microscopy and surface roughness tester. Results: The oxidation behavior indicated by the growth of oxide thickness. The titanium-oxide layer were consisted two layer of a porous external and a dense internal one. The reaction layer and surface roughness increased with increasing investment material temperature. Conclusion: In this work, The most suitable mold temperature in casting of pure titanium was $200^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.36 no.1
• /
• pp.89-96
• /
• 1999

Manufacturing conditions of the porous alumina mold were established to overcome various limits of the gypsum mold. For the preparations of the porous alumina mold, an activated charcoal was added to the Al2O3 with the wt% variation and then mixed. The binary slurry was study dispersed based on the examination of the ESA and rheological behaviro. The cylinder type alumina mold was cast in the gyspum mold and characterized by the shrinkage rate at the variable sintering temperature and the resistance against wear. It was proper to make a sintering of the Al2O3 by the surface diffusion which was non-shrinkage sintering mechansim, and intergranular neck growed stronger while sintering was being made. We studied a sintering by three categories; 1) thermodynamic method below 1,000$^{\circ}C$, 2) kinetic method above 1,000$^{\circ}C$ and 3) combined method. In the results of the respective works, combined method was superiro to the others. The prepared Al2O3 mold had relatively high strength, low drying rate, the resistance against the acid or base and good casting behavior.

• Journal of Korea Foundry Society
• /
• v.20 no.4
• /
• pp.277-282
• /
• 2000

The RP&M (Rapid prototyping and Manufacturing) is the most appropriate technology for the small-lot production system, in which the production cycle is getting shorter owing to various needs from consumers. In this paper, RP&M is applied to a casting process. A casting process has a merit of being able to reflect complicated shapes at one time. But it has not been applied to the precision industry because of bad quality on surface. So we will improve characteristics of aluminum casting process using vacuum sealed casting process and porous ceramic mold which is made by slurry casting process.

• Journal of the Korean Ceramic Society
• /
• v.34 no.1
• /
• pp.70-78
• /
• 1997

3Y-TZP/SUS316 Functionally Graded Material (FGM) was fabricated by slip casting method. Alumina mold was used to overcome problems of gypsum mold in slip casting process, and the optimal dispersion con-ditions of 3Y-TZP/SUS316 binary slurries was determined using electrokinetic sonic amplitude and a viscometer, and observing sedimentation behavior. The properties of the specimens casted by gypsum mold and alumina mold were compared in terms of changes in shrinkage rate, drying and sintering conditions, and microstructure. It was found that the specimens obtaine from the alumina mold showed a clean surface, easier thickness control of each layer, and higher productivity. Especially, no degradation was observed in the SUS316 prepared using alumina mold. Thus it is desirable to use porous alumina mold rather than gyp-sum mold for the slip casting of 3Y-TZP/SUS316-FGM.

• Journal of Korea Foundry Society
• /
• v.19 no.6
• /
• pp.493-500
• /
• 1999

Squeeze casting was used for fabricating a light metal base composite having high strength and wearresistance. Reactive sintering was used to prepare the preform of Squeeze casting. To utilize Fe-Al intermetallic compounds and SiC particle as a reinforcement, there needs to prepare Fe-Al mixed powder at 50, 60, 70at.%Al, and add SiC powder to the above mixture at 4, 7, 16, 24wt.%. The prepared mixture with SiC was reactive sintered in a tube furnace at $660^{\circ}C$ to get a porous hybrid preform of intermetallic compound and SiC. The preform prepared above was placed in a metal mold, preheated at $660^{\circ}C$ AC4C matrix was injected into the mold with the temperature of the melt at $610^{\circ}C$ After these processes, 66MPa was applied to the mold for 5 minute to finish the whole procedure. The maximum reaction temperature was increased with the increased Al amount, but decreased with the increased SiC amount. The density of the preform was decreased with SiC amount increase in the compacts due to swelling of the preform. An optical microscope was applied to observe the micro structure and the dispersion of the reinforcements. To analyze phases, We utilized XRD, EDS. Hardness test were chosen to get the information of mechanical properties. There were no significant changes in micro structure between the composite and preform. However, it was shown that uniform dispersion of the reinforcers and complete infiltration of the melt into the preform were achieved through the procedure of the squeeze casting. It was observed that the hardness of the composite is decreased with increased SiC amount, resulting from the volumetric expansion of the preform.