Most investigators recommended that porcelain surface should be roughened with abrasives and/or be etched with acid in repairing the fractured porcelain with composite resin. This study was designed to evaluate the effect of porcelain surface treatments on the bond strength between porcelain and composite resin by measuring the shear bond strength and observing the porcelain surface with SEM. 48 porcelain disc were fabricated with Vintage porcelain and embedded in epoxy resin with the test surface exposed. The specimens were divided four groups at random and the test surfaces of the four groups were prepared as follows : Group 1 : Porcelain surface was roughened with a fine diamond and treated with 32% phosphoric acid gel for 10 seconds. Group 2 : Porcelain surface was roughened with a fine diamond and etched with 8% hydrofluoric acid gel for 5 minutes. Group 3 : Porcelain surface was roughened with a coarse diamond and treated with 32% phosphoric acid gel for 10 seconds. Group 4 : Porcelain surface was roughened with a coarse diamond and etched with 8% hydrofluoric acid gel for 5 minutes. All specimens were washed for 30 seconds. A representative specimen of each group was selected and the porcelain surface was observed with SEM at 1000 magnification. Remaining specimens were silanated, bonded with composite resin, thermocycled, and shear-tested on specially designed zig connected to Instron machine. The results were as follows : 1. The shear bond strength of the group etched with hydrofluoric acid was significantly higher than that of group treated with phosphoric acid(p<0.01). 2. The shear bond strength of the group roughened with a fine diamond was not significantly different from that of the group roughened with a coarse diamond(p>0.01). 3. SEM examination of prepared porcelain surfaces revealed that the surface etched with hydrofluoric acid showed numerous microporosities, undercut, and rougher surface than the surface treated with phosphoric acid. 4. All specimens etched with hydrofluoric acid showed cohesive failure within porcelain, but specimens treated with phosphoric acid mainly showed adhesive failure between porcelain and composite resin.

• 대한치과보철학회지
• /
• 제18권1호
• /
• pp.49-57
• /
• 1980

The adhesive mechanisms on the metal-ceramic restorations have been reported to be mechanical interlocking, chemical bonding, compressive force, and Van der Waal's force, etc. Of these, the mechanical interlocking and chemical bonding forces are thought to affect the adhesive force between Ni-Cr alloy and porcelain. This study investigates the adhesion of Ni-Cr alloy to porcelain according to surface treatment. For this purpose, the following experiments were made; The compositions of Ni-Cr alloy as cast by emission spectrograph, and the oxides produced on Ni-Cr alloy during degassing at $1850^{\circ}F$ for 30 minutes in air and in vacuum were analyzed by X-ray diffractograph. The metal phases of Ni-Cr alloy were observed according to porcelain-baking cyclic heat treatment by photo microscope and the distribution and the shift of elements of Ni-Cr alloy and porcelain and the failure phases between Ni-Cr alloy and porcelain by scanning electron microscope. The adhesive force between Ni-Cr alloy and porcelain was measured according to surface treatment with oxidization and roughening by Instron Universal Testing Machine. Results were as follows; 1. The metal phases of Ni-Cr alloy as cast and degassing state showed the enlarged and fused core, but when subjected to porcelain-baking cyclic heat treatment, showed a dendrite growing. 2. The kinds of metal oxides produced on Ni-Cr alloy during degassing were found to be NiO and $Cr_2O_3$. 3. The distribution of elements at the interface of Ni-Cr alloy and porcelain in degassing state showed demarcation line, but in roughening state, showed mechanical interlocking phase. 4. The shift of elements at the interface occurred in both states, but the shift amount was found to be larger in roughening than in degassing. 5. The adhesive force between Ni-Cr alloy and porcelain was found to be $3.45{\pm}0.93kg/mm^2$, in degassing and $3.82{\pm}0.99kg/mm^2$, in roughening. 6. The failure phase between Ni-Cr alloy and porcelain showed the mixed type failure.

• 대한치과기공학회지
• /
• 제21권1호
• /
• pp.15-26
• /
• 1999

This study was carried out by observing to composition of oxide on the surface of dental porcelain low gold alloy with various Indium additions according to the degassing and analysing the change composition of additional elements In on diffusion behaviors of Porcelain-matal surface. The specimens used were Au-Pd-Ag alloys by small indium addition. These specimens were treated for 10min at $1000^{\circ}C$ in vacuum condition. To investigate the microsturcture of oxidized alloy surface, SEM and EDAX were used, and EPMA were used to investigate the diffusion behaviors of porcelain-metal surface. X-ray diffraction were used to observe the morphological changes in the oxidation zone. The results of this study were obtained as follows ; 1) The hardness of alloy increased with increasing amount of In addition. 2) The formation of oxidation increased with increasing In content after heat treatment. 3) Diffusion of indium elements increased with increasing In content in metal-porcelain surface after firing. 4) The oxidations of alloy surface were mainly $In_2O_3$.

• 대한치과보철학회지
• /
• 제45권5호
• /
• pp.589-600
• /
• 2007

Statement of Problem: Titanium has many advantages of high biocompatibility, physical porperties, low-weight, low price and radiolucency, but it is incompatible with conventional dental porcelain due to titanium's oxidative nature. Many previous studies have shown that they used the method of sandblast surface treatment prior to porcelain application, the researchs are processing about the method of acid etching or surface coating. Purpose: The purpose of this research is to study the effect on bond strength between titanium and porcelain when using macro-surface treatment and micro-surface treatment and macro and micro surface treatment. Material and method: In this study, we evaluated the bond strength by using 3-point bending test based on ISO 9693 after classified 7 groups-group P : polished with #1200 grit SiC paper, group SS : sandblasted with $50{\mu}m$ aluminum oxides, group LS : sandblasted with $250{\mu}m$ alumium oxides, group HC : treated with 10% hydrochloric acid, group NF : treated with 17% solution of fluoric acid and nitric acid, group SHC : treated with 10% hydrochloric aicd after sandblsting with $50{\mu}m$ alumium oxides, group SNF treated with 17% solution of fluoric acid and nitric acid. Results : Within the confines of our research, the following results can be deduced. 1. Group SS which was sandblasted with $50{\mu}m$ aluminum oxides showed the highest bond strength of 61.74 MPa and significant differences(P<0.05). The bond strengths with porcelain in groups treated acid etching after sandblasting decreased more preferable than the group treated with sandblasting only. It gives significant differences(P<0.05). 2. After surface treatments, the group treated with sandblasting showed irregular aspect formed many undercuts, in the SEM photographs. The group treated with hydrochloric acid had the sharp serrated surfaces, the group treated with the solution of fluoric acid and nitric acid had the smooth surfaces, the group with sandblasting and hydrochloric acid had irrigular and porous structure, the group with sandblasting and the solution of fluoric acid and nitric acid had crater-like surfaces. But all of the groups treated with acid etching was not found and undercut. Conclusion: In above results, average surface roughness increase, bond strength also increase, but surface topographs influences more greatly on bond strengths.

• 대한치과기공학회지
• /
• 제19권1호
• /
• pp.13-19
• /
• 1997

The purpose of this study was carried out by oberserving to composition of an oxide on the surface of Dental porcelain alloy according to the conditions of its heat treatment and analysing the change composition on its surface. Morphological change of the heat treated dental porcelain alloy have been investigated with SEM and EDX. The result of this study is summarized ad follows. The surface indium concentration of specimens increased as the heat treatment temperature and the oxygen partial pressure increased.

• 대한치과보철학회지
• /
• 제30권1호
• /
• pp.85-91
• /
• 1992

The purpose of this study was to evaluate the bonding strength between porcelain laminate and Ni-Cr alloy in the various surface treatments of the bonding faces. For this study the metal surface of specimens were treated : 1) etching only, 2) sandblasting only, and 3) sandblasting and etching. The porcelain laminate were made and bonded to the metal specimens with light curing composite resin cement. Instron testing machine was used to measure their bonding strength : and the result was obtained as follows : 1. The bonding strength of the double treatment of the sandblasting and etching group was higher than that of the single treatment of sandblasting or the etching group. 2. The bonding strength of the sand blasting group was higher than that of the etching group. 3. The debonding were mainly occurred between the Ni-Cr alloy and the composite resin cement.

• 대한치과교정학회지
• /
• 제28권5호
• /
• pp.803-812
• /
• 1998

도재의 표면처리가 세라믹 브라켓의 전단 접착강도에 미치는 영향과 브라켓 탈락 양상을 알아보기 위해 60개의 ceradent 도재 시편을 glazing 후 군당 10개씩 여섯 군으로 다음과 같이 분류하였다: 1군(silane), 2군(etching+silane), 3군(stone+silane), 4군(sandblasting+silane), 5군(stone+etching+silane), 6군(sandblasting+etching+silane) 통상적인 방법으로 세라믹 브라켓을 접착한 후 전단 접착강도를 측정하고 탈락양상을 육안 및 주사전자현미경으로 관찰하여 다음과 같주 결론을 얻었다. 1. 표면처리 후 silane을 도포한 2군부터 6군은 silane만을 도포한 1군에 비해 유의성 있는 전단 접착강도의 증가를 보였다(P<0.05). 2. 한 가지 방법 이상으로 표면처리한 3군부터 6군은 서로 유의한 차이를 보이지 않았다(P>0.05). 3. etching 표면 처리한 2군은 sandblasting 표면 처리한 4군과 복합 표면 처리한 5,6 군에 비해 전단 접착 강도가 낮았다. (p<0.05) 4. sandblasting 표면 처리한 4군은 주사 전자 현미경 소견상 복합 처리한 5,6군보다 감소된 요철 정도를 보였으나 전단접착 강도 측정 결과 유의한 차이를 보이지 않았다. (p>0.05) 이상의 결론을 종합해볼 때 도재에 세라믹 브라켓을 접착하기 위해서는 한가지 이상의 방법에 의한 도재의 표면처리 후 silane을 도포해야 임상적으로 적절한 접착강도를 얻을 수 있으며, 술식의 간편성을 고려할 때 sandblasting 후 silane 처리를 하는 것이 효율적일 것으로 사료된다.

• The Journal of Advanced Prosthodontics
• /
• 제3권4호
• /
• pp.221-228
• /
• 2011

PURPOSE. Veneering porcelain might be delaminated from underlying zirconia-based ceramics. The aim of this study was the evaluation of the effect of different surface treatments and type of zirconia (white or colored) on shear bond strength (SBS) of zirconia core and its veneering porcelain. MATERIALS AND METHODS. Eighty zirconia disks (40 white and 40 colored; 10 mm in diameter and 4 mm thick) were treated with three different mechanical surface conditioning methods (Sandblasting with $110{\mu}m$ $Al_2O_3$ particle, grinding, sandblasting and liner application). One group had received no treatment. These disks were veneered with 3 mm thick and 5 mm diameter Cercon Ceram Kiss porcelain and SBS test was conducted (cross-head speed = 1 mm/min). Two and one way ANOVA, Tukey's HSD Past hoc, and T- test were selected to analyzed the data (${\alpha}=0.05$). RESULTS. In this study, the factor of different types of zirconia ceramics (P=.462) had no significant effect on SBS, but the factors of different surface modification techniques (P=.005) and interaction effect (P=.018) had a significant effect on SBS. Within colored zirconia group, there were no significant differences in mean SBS among the four surface treatment subgroups (P=0.183). Within white zirconia group, "Ground group" exhibited a significantly lower SBS value than "as milled" or control (P=0.001) and liner (P=.05) groups. CONCLUSION. Type of zirconia did not have any effect on bond strength between zirconia core and veneer ceramic. Surface treatment had different effects on the SBS of the different zirconia types and grinding dramatically decreased the SBS of white zirconia- porcelain.

• 대한치과보철학회지
• /
• 제38권3호
• /
• pp.328-335
• /
• 2000

Statement of the problem. Recently an innovative method of fabricating indirect restorations by gold electroforming has been developed. But the bond quality and strength of the gold coping to the porcelain is uncertain. Purpose of study. The purpose of this study is to analyze and evaluate the electroformed gold surface for mechanical bonding between the gold and the ceramic veneering. Methods/material. Electroformed disks were made using electroforming technique. And the surface of the electroformed coping was analyzed after sandblasting, heat-treatment, bonding agent application, opaque porcelain firing with scanning electron microscopy and energy dispersive x-ray analysis. Results. In the analysis with SEM, Sandblasting made the sharp edges and undercuts on the electroformed surface, and after bonding agent application, net-like structure were created on the electroformed surface. In the energy dispersive x-ray analysis it is confirmed that electroformed surface contains some impurities. Conclusion. With the use of sandblasting and bonding agent, electroformed surface seems to be enough to bond with veneering porcelain.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 춘계학술발표회 논문집
• /
• pp.332-332
• /
• 2012

All-ceramic prostheses are widely used to fulfill the high esthetic demand. However, bonding failure between zirconia and porcelain is one of the all-ceramic prostheses failures. In order to improve clinical sucess of all-ceramic prostheses, laboratory or in-office surface conditioning techniques on zirconia have been studied.