Two component polyurethane (PU) flame retardant coatings were prepared by blending trichloro modified polyesters (TCMPs) and isophorone diisocyanate isocyanurate. TCMPs were synthesized by polycondensation of trichlorobenzoic acid (TCBA), a flame retardant component, with adipic acid, 1,4 butanediol, and trimethylolpropane. The content of TCBA was varied in 10, 20, and 30 wt% for the reaction. Theses new flame retardant coatings showed various properties comparable to other non flame retardant coatings. Moreover, we carried out the combustion test and the flammability test for our flame retardant coatings. The results of vertical burning test for the coatings containing more than 20 wt% of TCBA were determined as no burn. The results of flammability test for the coatings with 20 wt% and 30 wt% of TCBA contents indicated the limiting oxygen index (LOI) values of 26% and 29% respectively, which implied relatively good flame retardancy.

• 한국응용과학기술학회지
• /
• 제34권4호
• /
• pp.851-856
• /
• 2017

스테인레스 스틸에 대한 도료수지의 기계적 특성은 SEM, FT-IR, 인장특성, 그리고 [NCO]/[OH]의 mole %, 입도분석에 의해 측정하였다. 친환경적인 도료에 관한 관심이 고조됨에 따라 스테인레스 스틸 등의 금속에 코팅하는 무용제 도료를 합성하였다. 폴리올, MDI, 충진제, 실리콘 계면활성제, 촉매 등이 함유된 기존 도료수지보다 식물성 오일이 함유된 폴리올, MDI, 충진제, 실리콘 계면활성제, 촉매로 이루어진 합성 도료 수지의 코팅이 내구력과 강도가 양호하였다. 견고한 도료 수지의 기계적 특성은 식물성 오일이 함유된 폴리올로 합성된 폴리우레탄 코팅의 접촉각이 더 컸으며, [NCO]/[OH]의 mole%가 증가함에 따라 강도가 증가하였다. 결론적으로 식물성 오일이 함유된 친환경 도료가 스테인레스 스틸 같은 금속물질의 부식방지용 코팅에 좋은 물질이다.

• 한국응용과학기술학회지
• /
• 제34권4호
• /
• pp.778-786
• /
• 2017

In this study, analyzed the changes occurred after adding casein emulsions to water - dispersed polyurethane using polypropylene glycol (PPG). For this purpose, anionic water - dispersed polyurethane containing PPG, IPDI and DMPA and casein emulsion prepared by dissolving casein in distilled water using ammonia water were prepared. As a result of measuring the alkali resistance by using the prepared resin, there was no change in the physical properties. The tensile strength of the sample having a high casein content was measured to be $2.227kgf/mm^2$. Elongation was measured at 474% for samples containing less casein and The abrasion resistance was measured as 46.090 mg.loss of sample containing much casein as a result of the surface roughness measurement.

• 한국섬유공학회:학술대회논문집
• /
• 한국섬유공학회 2001년도 가을 학술발표회 논문집
• /
• pp.21-24
• /
• 2001

Polyurethane are used for a wide range of commercial applications such as adhesives or coatings for various substrates including textile fabric, plastic, wood, glass fiber, and metals. The types of polyurethane ionomers have been reported according to the ionic charges on the polymer main chain, i.e. anionomer, cationomer, and zwitterconomers. (omitted)

• 한국응용과학기술학회지
• /
• 제23권3호
• /
• pp.264-271
• /
• 2006

PU type flame-retardant coatings (TBAO/L-75, TBAOL ; TBAO/N-100, TBAON) were prepared by blending bromine-containing modified polyester (TBAO) which was synthesized in our earlier work. with two kinds of isocyanate curing agents, Desmodur L-75 and Desmodur N-100. Physical properties of the prepared flame-retardant coatings were tested. TBAOL shows better hardness than TBAON, while TBAON shows better viscosity, accelerated weathering resistance, yellowness index and lightness index difference than TBAOL. There were no remarkable differences in fineness of grind, $60^{\circ}$ specular gloss, cross-hatch adhesion, and abrasion resistance of TBAOL and TBAON. There was no discernable difference in flame-retardancy between the two flame-retardant coatings, TBAOL and TBAON. When the content of tribromo acetic acid, which is flame-retarding component, was 30wt% the LOI value was in a range of $29{\sim}30%$, which indicates that the two coatings are good flame-retardant coatings.

• 한국자동차공학회논문집
• /
• 제22권5호
• /
• pp.5-12
• /
• 2014

Weatherstrip coatings of urethane and silicon type which are fit to EPDM and thermoplastic materials are used in sealing systems for automotive applications for noise reduction and high slip characteristics for external applications, respectively. Polyurethane binder was successfully synthesized from poly(butyladiphate)diol (PBAD), poly(tetramethylene)glycol (PTMG) and isocyanate as starting materials. Then, polyurethane coating agents were prepared by using various additives. To investigate effects of segment types on the abrasion resistance of polyurethane coating agents, thin films based on polyurethane coating materials were fabricated. With increasing the amount of hard segment in the coating agent, abrasion resistance, modulus and tensile strength of the coating films were improved, but the elongation of the coating films was decreased.

• 한국응용과학기술학회지
• /
• 제30권3호
• /
• pp.567-574
• /
• 2013

For this research, prepared water soluble milk casein resin and waterborne polyurethane-acrylic resin. Use these resin, this article has been analyzed about change of mechanical properties by increasing amount of casein resin in polyurethane-acrylic resin on coated leather. According to measure data for solvent resistance, WPA(waterborne polyurethane-acrylic resin) resin and WPA-C1, C2, C3(samples of polyurethane-acrylic resin with milk casein resin) had good property. As known in the results, increase of casein constant did not influence to big change of hybrid resin properties. As test of tensile strength, WPA had lowest tensile characteristic(1.598 $kg_f/mm^2$) and WPA-C3 had highest tensile characteristic(1.718 $kg_f/mm^2$). Also best properties of abrasion was WPA-C3(06.021 mg.loss). In elongation case, WPA had best properties(754 %) in this experiment.

• 한국응용과학기술학회지
• /
• 제18권3호
• /
• pp.241-247
• /
• 2001

Aqueous urethane dispersion resin begins to assume commercial importance due to increasing environmental awareness of VOC in coating industry. Moreover there have been strong industrial needs for the development of reactive-type polyurethane flame retardant coatings. In this study, chlorinated polyester polyols were synthesized by two step polycondensation reaction using mono chloroacetic acid, adipic acid, trimethylol propane, and 1,4-butanediol. In the next step polyurethane dispersion was prepared using these chlorinated polyester polyols and isophorone diisocyanate with dimethylol propionic acid(DMPA) and trimethylamine. The structure of chlorinated polyol was characterized by GPC, FT-IR and NMR. Particle size and its distribution were examined in terms of various dispersion parameters including molecular weight and composition of polyol, amount of DMPA, and NCO/OH ratio, etc. The effect of chlorinated polyols on flammability was also evaluated.

• International Journal of Concrete Structures and Materials
• /
• 제8권3호
• /
• pp.201-212
• /
• 2014

Sixteen reinforced concrete laboratory specimens were used to evaluate a number of corrosion prevention methods under an accelerated (6 months) testing program. The use of galvanic thermal sprayed zinc, galvanic embedded anodes, a tri-silane sealer, an acrylic coating, and an epoxy/polyurethane coating was evaluated. The specimens received various treatments prior to exposure to accelerated corrosion. The performance of the treatments was evaluated with respect to corrosion currents, chloride ingress, extent of cracking, severity of rust staining, and visual inspection of the reinforcing steel after the conclusion of testing and dissection. Results indicated that the tri-silane sealer, the conjoint use of galvanic thermal sprayed zinc and epoxy/polyurethane coating, the epoxy/polyurethane coating, and acrylic coating performed better than the other methods tested. Higher chloride concentrations were measured in the vicinity of embedded zinc anodes.

• 폴리머
• /
• 제35권5호
• /
• pp.409-418
• /
• 2011

A novel silicone (Si) containing vinylic monomer, N-(3-(triethoxysilyl)propyl) methacrylamide (TESPMA), based on 3-aminopropyltriethoxysilane (APTES) and methacryloyl chloride (MCl) has been synthesized for formulation of waterborne polyurethane (WPU). Two types of vinyl group containing Si, methacryloxypropyltriethoxysilane (MPTES) and triethoxyvinylsilane (TEVS), have been used as coupling reagents for comparison of the effects of Si kinds with TESPMA on the WPU. A series of new siliconized WPU, vinyl acetate/vinyl ester of versatic acid (VAc-Veova), TESPMA, MPTES and TEVS hybrid latexes have been successfully prepared by emulsion polymerization in the presence of WPU dispersion.