• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.11a
• /
• pp.71-72
• /
• 2022

In this paper, the performance evaluation of the vibration damping ratio according to the polymer mixing ratio of the polymer modified mortar used as the floor finishing material of the apartment building structure was evaluated. To compare the vibration damping rate, ordinary potland cement (OPC) mortar and polymer modified mortar (PMM) were prepared. In addition, the mixed polymer was mixed with Styrene Butadiene Rubber (SBR) liquid polymer with a solid content of about 49%. Accordingly, the W/C of the test specimen was adjusted and compounded, and the experiment was conducted by mixing 5 types of the test specimen: OPC-60, PMM-5%, PMM-10%, PMM-15%, and PMM-20%. In addition, in order to adjust the W/C of the specimen, the fluidity of each specimen was set as 210 (±5) mm. The specimens measured density and flow in fresh mortar and after curing for 28 days, flexural strength, compressive strength and ultrasonic pulse were measured. The attenuation rate was shown. The experimental results showed that the density increased according to the mixing of the polymer, the flexural strength increased as the mixing rate of the polymer increased, and the compressive strength was decreased. In addition, it was shown that the vibration damping rate increases with the increase in the amount of polymer incorporated.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.571-574
• /
• 2005

This study investigated the strength of concrete to improve construction material with polymer cement mortar. Some mixtures composed of Styrene-Butadiene Rubber(SBR) and Ethylene Vinyl Acetate(EVA) Poly Vinyl Alcohol(PVA) were studied. The three mixtures carried out the physical, mechanical test to determine its properties which a include : compressive, flexural, bond strength test. The test results show that the compressive strength was increased at long-term age when compared to early ages for increasing polymer contents. It was found that flexural strength and bond strength became larger as polymer to cement ratio became higher.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.9 no.2
• /
• pp.81-86
• /
• 2011

Polymer-modified cement is the composite material made by partially replacing and strengthening the cement hydrate binders of conventional mortar with polymeric modifiers such as polymer latexes and redispersible polymeric modifiers. It is known that the addition of polymer to cement mortar leads to improved quality, which would be expected to have a high chemical resistance. Therefore, the purpose of this study is to identify the improved chemical resistance, such as low permeability and low ion diffusivity, of the polymer-modified cement as a solidification agent for the radwaste. First, polymer-modified cement specimens by latex modification were prepared according to the polymer content from 0% to 30% to select the optimized polymer content. At those specimens, the water-to-cement (W/C) ratio was maintained to 33% and 50% respectively. After the much curing time, the structural integrity of specimens was evaluated through the compressive strength test and the porosity evaluation by the water immersion method. From the results, 10% of the polymer content at 33% of the W/C ratio was shown to have the most improved quality. Finally, the leaching test referredfrom ANS 16.1 for the specimens having the most improved quality was conducted. Dedicated specimens for the leaching test were then mixed with radioisotopes of $^{60}Co$ and $^{137}Cs$ at the specimen preparation.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2012.11a
• /
• pp.255-257
• /
• 2012

Epoxy resin without any hardener can harden in the presence of hydroxide ions in cement mortars and concretes at ambient temperature. The purpose of present study is to examine the hardening properties of hardener-free epoxy-modified mortars by curing conditions. The hardener-free epoxy-modified mortars using diglycidyl ether of A epoxy resin are prepared with various polymer-cement ratios, and subjected to initial moist/dry curing, initial steam(90℃) curing, initial steam/heat(80℃, 100℃) curing.As a result, degree of hardening of epoxy resin in initial moist/dry cured, initial steam cured and initial steam/heat(80℃) cured hardener-free epoxy-modified mortars is decreased with increasing polymer-cement ratio. However, it is markedly improved with additional dry-curing periods. On the other hand, regardless of the polymer-cement ratio and dry curing periods, degree of hardening of hardener-free epoxy-modified mortars with initial steam/heat(100℃) cure is over 95%.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.4
• /
• pp.305-311
• /
• 2020

Polymer modified cement mortar (PCM) can improve the performance of adhesion strength, flexural strength, chemical resistance, etc., compared with cement mortar, and is widely used when repairing RC structures. However, PCM causes a burst in an environment with high temperature and fire rate, which causes problems in the stability of the structure. In this study, for the purpose of developing explosive reduction PCM, the polymer mixing ratio is 2%, 4%, 6%, the fiber length is 6mm, 12mm, 6+12mm, and the PP fiber mixing rate is 0.05 Vol% and 0.1 Vol%. Furnace heating experiment (600℃, 800℃) was carried out. As a result of comparative analysis of the explosive properties, it was confirmed that the explosive reduction effect due to the fiber incorporation was insufficient when the polymer mixing amount was 6% or more.

• Journal of the Korean Ceramic Society
• /
• v.47 no.5
• /
• pp.373-380
• /
• 2010

In this study, we studied on the durability of restorative cement mortar for deteriorated concrete at complex deteriorated conditions as variation of temperature and of humidities. We made a comparison between restorative materials with insulation function and restorative materials without insulation function in items of compressive and bending strength and permeability of water, durability for carbonation, salt damage, diffusion coefficient of salt at complex deterioration conditions like change of temperature, change of humidity, For insulation, we used close-pore type Alumino-Silicate lightweight aggregate and substituted 12 wt% and 15 wt% out of original restorative cement mortar without insulation function. As a result, it was found that original restorative cement mortar without insulation function fail to meet Korean Standard on polymer modified cement mortar for maintenance in concrete structure, but restorative cement mortar with insulation function is in contentment Korean Standard to meet excellent than restorative materials without insulation function for durability at complex deteriorated conditions.

• Journal of the Korea Concrete Institute
• /
• v.17 no.3 s.87
• /
• pp.467-472
• /
• 2005

Asphalt emulsion is manufactured by the emulsification of asphalt, and is considered as an energy-saving, ecologically safe material because it does not need any heating processes with gas emission and fire hazard in its use. This study is concerned with evaluating the feasibility of the use of an asphalt emulsion as a poly-meric admixture. Asphalt-modified mortars using an experimentally manufactured asphalt emulsion were prepared with various polymer-cement ratios, and tested far the mechanical properties such as strengths and adhesion and the properties related to durability such as water absorption, permeation, carbonation and chloride ion penetration. As a result, the waterproofness, carbonation resistance and chloride ion penetration resistance of the asphalt-modified mortars were markedly improved with an increase in the polymer-cement ratio, but their compressive strength and adhesion to mortar substrates were reduced with increasing polymer-cement ratio. Therefore, it is recommended to control their polymer-cement ratio to be $10\%$ or lower in their practical applications. Further study to improve their compressive strength and adhesion is needed.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.533-536
• /
• 2005

Drying shrinkage and strength of the redispersible SBR and PAE powder-modified mortars were experimentally investigated. Results of the study that the drying shrinkage rapidly increased until 7 days of age and it was then saturated to the value of about $1\~2\times10^{4}$ after 14 days. It turned out that the polymer-cement ratio exerted more influence on the drying shrinkage than the content of powder shrinkage-reducing agent did. Flexural (compressive) strength of the mortar increased (decreased) as the polymer-cement ratio increased and it was 7$\~$11 (23$\~$39) MPa at 7 days of age. The average (maximum) increasing (decreasing) rate turned out to be about 10 (30) $\%$. As in the drying shrinkage case, the polymer-cement ratio exerted more influence on both flexural and compressive strengths than the content of powder shrinkage agent did.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.537-540
• /
• 2005

Durability of the polymer-modified mortars using the redispersible SBR and PAE powder-modified mortars were experimentally investigated. Results of a previous study were used to determine the mix proportion that optimized the strength, and the freezing-thawing resistence, the carbonation depth and the chloride intrusion depth of the mortar for various polymer-cement ratios were studied. After 300 freezing-thawing cycles, the rate of weight reduction decreased from 7 to below 2 $\%$ as the polymer-cement ratios increased from 0 to 15 $\%$, and, on the 150 cycle basis, durability index increased from 60 to 98. Carbonation depth decreased from initial value of 5.5 to about 2.5 mm and chloride intrusion depth did from 3.5 to 1.5 mm

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2011.11a
• /
• pp.107-108
• /
• 2011

The purpose of present study is to examine the application of effective curing to hardener-free epoxy-modified mortars. The epoxy-modified mortars are prepared with polymer-cement ratios, subjected to two types of curing conditions, and tested for compressive, flexural and tensile strengths. As a result, hardener-free epoxy-modified mortars with steam curing is markedly improved with increasing air-dry curing period. High strength development of the epoxy-modified mortars may be achieved by the dense microstructure by cement and the hardener of the epoxy resin in the mortars.