• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2012.05a
• /
• pp.295-298
• /
• 2012

Repair and strengthening is necessary to extend the service life of existing buildings. Polymer-modified cement mortar (PCM) has been extensively used as a high performance material particularly for finishing and repairing works in concrete building because of itsexcellent adhesion, waterproofing, resistance to chemical attack, and workability. As PCM contains organic polymer, it is necessary to clarify its properties at high temperature under fire, on which sufficient data are not available. This paper evaluated the burn-up characteristics of polymer-modified cement mortar with cone calorimeter test, non-combustibility test and flammability test with experimental parameters such as the types of polymer, unit-polymer content, polymer-cement ratio and thickness of the specimen.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.06a
• /
• pp.96-97
• /
• 2020

Polymer modified cement mortar (PCM) is commonly used as a repair material. However, in high-temperature environments such as fire, it is more likely to explode than cement mortar. The polymer is thermally decomposed at a high temperature to form a gas, and the gas remaining inside the structure increases the internal pressure to generate a burst. When an spalling occurs, the coating is peeled off and dropped, and high temperature is transmitted to the inside of the structure. In severe cases, even the reinforcing bar is exposed, which can lead to the collapse of the structural member due to severe loss of strength. In this study, in order to reduce spalling of PCM, a fiber mixing method was selected from the refractory method to find an appropriate blending ratio of fibers and polymers.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2008.11a
• /
• pp.63-66
• /
• 2008

Not only mechanical properties, bonding properties, electro chemical properties, etc. but also fire safety is required in patch repair materials such as polymer modified cement mortar (PCM) which are used to deteriorated reinforced concrete structure. Unfortunately, it is very difficult to choice the appropriate repair materials because there are not enough information about fire safety properties of PCM. In this study, The combustion characters of PCM were evaluated through the heat release rate test and non-combustibility test. The pyrogenicity test uses the cone calorimeter based on the oxygen consumption method. The non-combustibility test is from the temperature change inside the furnace during the test. The effect of the types of polymer and polymer content were evaluated from the series of test. The results are like followings. 1) The higher the W/C of PCM, the lower the gross calorific value and heat generation rate in the heat release rate test. The amount of heat generation of PCM is like the order of VVA, EVA, and SBR in this study. 2) Some materials such as E45-100, E50-100, E60-100, S50-50, and S50-100 were estimated as not appropriate building materials in the non combustibility test.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.4
• /
• pp.305-311
• /
• 2020

Polymer modified cement mortar (PCM) can improve the performance of adhesion strength, flexural strength, chemical resistance, etc., compared with cement mortar, and is widely used when repairing RC structures. However, PCM causes a burst in an environment with high temperature and fire rate, which causes problems in the stability of the structure. In this study, for the purpose of developing explosive reduction PCM, the polymer mixing ratio is 2%, 4%, 6%, the fiber length is 6mm, 12mm, 6+12mm, and the PP fiber mixing rate is 0.05 Vol% and 0.1 Vol%. Furnace heating experiment (600℃, 800℃) was carried out. As a result of comparative analysis of the explosive properties, it was confirmed that the explosive reduction effect due to the fiber incorporation was insufficient when the polymer mixing amount was 6% or more.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.5
• /
• pp.128-135
• /
• 2010

Polymer-modified cement mortar(PCM) has been widely used for strengthening of the concrete structures due to its excellent physical properties such as high strength and durability. Adhesive strength or behavior, on the other hands, between PCM and concrete is very important in strengthening the concrete member using PCM. Therefore the adhesive failure mechanism between PCM and concrete should be fully verified and understood. This study was performed to evaluate adhesive strength of PCM to the concrete by the direct pull-out test. In the direct pull-out tests, the adhesive strength under the various pre-treatment conditions such as immersion, thunder shower, freezing and thawing are evaluated. Also, the field direct pull-out test are performed to investigate the adhesive strength of mock-up test specimens. In the results of the test, the adhesive strength value by field test are lower than those of the standard curing condition. From these comparison and investigation, field test result was similar with the thunder shower test result. The results of the test was used to evaluate the korean industrial standard of polymer modified cement mortars for maintenance in concrete.

• Proceedings of the Korea Institute of Fire Science and Engineering Conference
• /
• 2013.04a
• /
• pp.29-30
• /
• 2013

폴리머 시멘트 모르타르(Polymer-Modified Cement Mortar, 이하, PCM으로 칭함)는 일반 시멘트 모르타르와 비교해서 접착성, 치밀성, 내약품성, 시공성등이 우수한 재료로, 콘크리트 구조물의 보수 보강에 필수불가결한 재료로 인식되고 있다. 그러나, 혼입된 폴리머는 유기물 재료로, 화재와 같은 고온을 받는 경우에는 무기계 재료인 일반 모르타르 및 콘크리트와는 또 다른 고온역에서의 성상을 보일 것으로 예상된다. 이로 인해, PCM으로 보수 보강된 건축물에 화재가 발생할 경우, 고온에서의 안전성 및 화재 후의 보수 보강 필요성에 대한 평가를 행할 필요가 있다. 이에 본 논문에서는 평가시 기본적인 데이터로 활용될 수 있는 PCM의 고온노출시의 역학적 특성에 대한 검토방안으로, 기존의 실험조건 및 실험방법을 응용한 새로운 실험방법을 적용, 비교검토를 행하고, 고온영역에서의 PCM의 역학적 특성에 대해 고찰했다.