• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.161-161
• /
• 1999

In the field of material science, the interests and efforts to modify the surface of materials in agreement with the need of usage have been extensively increasing. he modification to improve the wettability of surface is very important is terms of adhesion, printing, etc. It is very difficult to modify metal surface into hydrophilic one. therefore, surfactant coating has been generally used in many cases. However, surfactant has disadvantages such as environmental problem, soluble in water. in this study, hydrophilic polymer films as alternative of surfactant were deposited on metal substrate by DC plasma polymerization. Hydrophilic polymer films deposited by DC plasma show many merits such as good wettability, stone adhesion to substrate, high resistance to most chemicals. Monomer gas and reactive gas were used as source plasma polymerization. Plasma polymerized films were fabricated with process parameters of deposition time, ratio of gas mixture, current, pressure, etc. Effects of these variables on wettability of plasma polymer films will be discussed. With XPS and FT-IR analyses of plasma polymeric films, the relation between wettability and chemical state of polymer films by DC plasma was investigated.

• Macromolecular Research
• /
• v.14 no.3
• /
• pp.267-271
• /
• 2006

Polyelectrolyte complex films were prepared with two compounds, chitosan and poly(ethylene glycol)-monosuccinate, using a casting in order to synthesize a polyelectrolyte complex film with various mole ratios of chitosan and poly(ethylene glycol)-monosuccinate. The solution properties of isolated PEC were investigated for the effects of FTIR, pH value, Brookfield viscosity and cell viability assay using MTT staining. The PEC films were evaluated for mechanical properties by typical stress-strain curve, far thermal properties by DSC and TGA and for surface morphology Properties by SEM. Furthermore, the surface resistance, moisture regain and water content of the films were characterized. The solution properties were affected by several factors including the chitosan content in the PEC, the mixing ratio of PEG and chitosan, and pH. Several PEC in acidic conditions exhibited film formation under appropriate conditions of mixing ratio and chitosan concentration in the mixing process. These PEC films were found to have sufficiently flexible and stable properties due to their hydrophilic structure, which was farmed by the oppositely charged interaction between PEG-MS and chitosan matrix. The results showed the potential applicability of chitosan and poly(ethylene glycol)-monosuccinate films as a biocompatible polymer.

• Journal of Integrative Natural Science
• /
• v.4 no.4
• /
• pp.294-297
• /
• 2011

Quality of PEDOT electrode thin film vapor phase-polymerized on 3-aminopropyltriethoxysilane (APS) self-assembled monolayer (SAM) is very crucial for making an ohmic contact between electrode and semiconductor layer of an organic transistor. In order to improve the quality of PEDOT film, the quality of APS-SAM laying underneath the film must be in the best condition. In this study, in order to improve the quality of APS-SAM, the monolayer was self-assembled on $SiO_2$ surface by a dip-coating method under strictly controlled relative humidity (< 18%RH). The quality of APS-SAM and PEDOT thin film were investigated with a contact angle analyzer, AFM, FE-SEM, and four-point probe. The investigation showed that a PEDOT film grown on the humidity-controlled SAM is very smooth and compact (sheet resistivity = 20.2 Ohm/sq) while a film grown under the uncontrolled condition is nearly amorphous and contains quite many pores (sheet resistivity = 200 Ohm/sq). Therefore, this study clearly proves that a highly improved quality of APSSAM can offer a highly conductive PEDOT electrode thin film on it.

• Journal of Sensor Science and Technology
• /
• v.22 no.6
• /
• pp.400-403
• /
• 2013

The piezoelectric composite film of ferroelectric PZT ceramic ($PbZr_xTi_{1-x}O_3$) and polymer (PDMS, Polydimethylsiloxane) was prepared to improve the flexibility of piezoelectric material. The bar coating method was applied to fabricate flexible nanocomposite film with large surface area by low cost process. In the case of using metal electrode on the composite film, although there is no problem by bending process, the electrode is usually broken away from the film by stretching process. However, the well-attached, flexible CNT electrode on PZT/PDMS film improved flexibility, especially stretchability. PZT particles was usually settled down into polymer matrix due to gravity of the weighty particle, so to improve the dispersion of PZT powder in polymer matrix, small amount of additives (CNT powder, Carbon nanotube powder) was physically mixed with the matrix. By stretching the film, an output voltage of PZT(70 wt%)/PDMS with CNT (0.5 wt%) was measured.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.10
• /
• pp.966-970
• /
• 2006

We reported on characteristics of the piezoelectric ceramic-polymer composite for the application of the thick-film speaker. The PVDF-PZT composites were fabricated to incorporate the advantages of both ceramic and polymer with various mixing ratios by 3-roll mill mixer. The composite solutions were coated by the conventional screen-printing method on ITO electrode coated PET (Polyethylene terephthalate) polymer film. After depositing the top-electrode of silver-paste, 4 kV/mm of DC field was applied at $120^{\circ}C$ for 30 min to poling the composite films. The value of $d_{33}$ (piezoelectric charge constant) was increased when the PZT weight percent was increased. The maximum value of the $d_{33}$ was 24 pC/N at 70 wt% PZT. But the $g{33}$ (piezoelectric voltage constant) showed the maximum value of $32mV{\cdot}m/N$ at 65 wt% of PZT powder. The SPL (sound pressure level) of the speaker fabricated with the 65:35 composite film was about 68 dB at 1 kHz.

• Journal of the Korean Applied Science and Technology
• /
• v.12 no.2
• /
• pp.29-39
• /
• 1995

The phase separated structure and the electro-optical properties of the (polymer/liquid) crystal : LC) composite film strongly depended on the weight fraction of LC in it. The continuous LC phase was formed in a three-dimensional polymer network when the LC weight fraction was above 40wt%. The aggregation structure of the composite film could be controlled by controlling the solvent evaporation velocity during the film preparation process. The smaller LC domains or channels were formed in the case of the faster solvent evaporation velocity. The composite film exhibited reversible light scattering-light transmission switching upon electric field -OFF and -ON states, respectiverly. The light scattering properties of the composite film strongly depended on the spatial distortion of the nematic directors as well as the mismatch in refractive indices between matrix polymer and LC.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.1
• /
• pp.20-25
• /
• 2016

Femtosecond laser ablation of ultrathin polymer films on quartz glass using laser pulses of 100 fs and centered at ${\lambda}=400nm$ wavelength has been investigated for nanometer precision thin film patterning. Single-shot ablation craters on films of various thicknesses have been examined by atomic force microscopy, and beam spot diameters and ablation threshold fluences have been determined by square diameter-regression technique. The ablation thresholds of polymer film are about 1.5 times smaller than that of quartz substrate, which results in patterning crater arrays without damaging the substrate. In particular, at a $1/e^2$ laser spot diameter of $0.86{\mu}m$, the smallest craters of 150-nm diameter are fabricated on 15-nm thick film. The ablation thresholds are not influenced by the film thickness, but diameters of the ablated crater are bigger on thicker films than on thinner films. The ablation efficiency is also influenced by the laser beam spot size, following a $w_{0q}{^{-0.45}}$ dependence.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.34 no.1
• /
• pp.16-20
• /
• 2021

In this study, we tried finding new materials to improve the stain resistance properties of polymer insulating materials. Using the filtered vacuum arc source (FVAS) with a graphite target source, DLC thin films were deposited on silicon and polymer insulator substrates depending on their thickness to confirm the surface properties, physical properties, and structural properties of the thin films. Subsequently, the possibility of using a DLC thin film as a protective coating material for polymer insulators was confirmed. DLC thin films manufactured in accordance with the thickness of various thin films exhibited a very smooth and uniform surface. As the thin film thickness increased, the surface roughness value decreased and the contact angle value increased. In addition, the elastic modulus and hardness of the DLC thin film slightly increased, and the maximum values of elastic modulus and hardness were 214.5 GPa and 19.8 GPa, respectively. In addition, the DLC thin film showed a very low leakage current value, thereby exhibiting electrical insulation properties.

• Journal of the Korean Ceramic Society
• /
• v.45 no.11
• /
• pp.744-749
• /
• 2008

The properties of the polymer-modified mortars are influenced by the polymer film, cement hydrates and the combined structure between the organic and inorganic phases. Also, this quality of polymer modified cement strongly depend on weather condition and polymer cement ratio. To overcome this problem, polymer-modified cement were prepared by varying polymer/cement mass ratio (P/C) with $0{\sim}20%$ and constant water/cement mass ratio of 0.5. The effect of polymer on the hydration of this polymer cement is studied on different polymer cement ratio. The results showed that the polymer cement paste have increased the viscosity in addition the amount of polymer dosage and the polymers is completed resulting in a reduced degree of hydration caused by different ion elution amount. Also we know that the reactants is calcium acetate as a results of chemical reaction between acetate group in EVA which is hydrolysis in water and $Ca^{2+}$ ion during hydration of cement.

• Biomedical Science Letters
• /
• v.28 no.1
• /
• pp.50-57
• /
• 2022

In this study, we tried to examine the possibility of developing a dental product such as tooth decay prevention and oral hygiene by manufacturing a natural polymer film for oral use. Natural polymer films were prepared from shark byproduct extract (SBE) and gellan gum (GG). As an antibacterial substance, the antibacterial activity of green tea extract against tooth decay-causing bacteria was measured. An film was prepared by adding green tea extract to the composition of SBE and GG. The mechanical, solubility, moisture content and antibacterial function of the prepared film were investigated in detail. Also, the incorporation of GTE into the SBE/GG film improved the physical performance of the film. Increasing the content of GTE improved the antioxidant and antibacterial properties of the film. Formulation of antimicrobial SBE/GG film containing green tea extract was established and these results evidently showed potential for cavity prevention products application.