• Applied Chemistry for Engineering
• /
• v.7 no.1
• /
• pp.136-144
• /
• 1996

Polyacrylic super absorbent polymer(SAP) containing sorbitol was synthesized by inverse-suspension polymerization method. Sodium acrylate and acrylic acid were used as a monomer, ethylene glycol dimethacrylate(EGDMA) and glycerol polyglycidyl ether(GPGE) were used as a crosslinking agent, potassium persulfate(PPS) was used as an initiator, and cyclohexane was used as a solvent. Content of sorbitol was from 10mol% to 50mol% according to the mol ratio of acrylic acid monomer. The size distribution of the round shaped polymeric particle was $177{\sim}707{\mu}m$. Absorption amount of the polymer containing sorbitol was 785 to 1086 times of the polymer weight in distilled water, was 50 to 83 times in 0.9 % NaCl solution. Absorption and retention amount of the polymer were decreased with increasing the amount of sorbitol, but the polymer has an endothermic property which is +5 cal/g SAP.

• Textile Coloration and Finishing
• /
• v.29 no.3
• /
• pp.122-130
• /
• 2017

In the direct digital textile printing process, the pre-treatment process is an essential condition for products by forming a clear pattern by sticking and penetration of DTP dye without spreading on the fabric. Recently, pre-treatment agent is changing from high viscosity to low viscosity in order to reduce defects of fabric during pre-treatment process. In this study, pre-treatment agent of acrylic polymer with low viscosity(less than 50cps) was prepared according to the solid content of the polymer, pre-treated on the cotton fabric, and direct DTP printing was performed to compare the color and sharpness. As a result, it showed high color at a viscosity of 50cps or less. When the solid content of the polyacrylic acid having a high molecular weight(A1) was 2.5wt%, when the solid content of the polyacrylic acid having a low molecular weight(A2) was 1 - 1.5wt%, the color was the best. And when the solid content of A1 and A2 was 1.5wt%, the degree of spreading was small and A1 was superior to A2 at the sharpness.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.25 no.1
• /
• pp.76-92
• /
• 1998

The purpose of this study was to evaluate the possible efficacy of Nd-YAG laser as a dentin conditioner by observing the laser irradiation dentin surface under scanning electron micrograph and measuring shear bond strength of restored light-cured glass ionomer mold. Fifty intact premolars were prepared for shear bond strength tests. The teeth were randomly divided into five groups as follows; Group I. no treatment Group II. 10% poly acrylic acid, 20 sec Group III. laser treatment 2 w, 20 Hz, 2 sec Group IV. laser treatment 2 w, 20 Hz, 5 sec Group V. laser treatment 2 w, 20 Hz, 10 sec Samples of each group were restored with light-cured glass ionomer cement after dentin conditioning and then measuring the shear bond strength of each specimen were measured using universal testing machine. Additional ten premolars were prepared for SEM analysis The result from the this study can be summarized as follows. 1. Shear bond strength of polyacrylic acid-treated group (II) was significantly higher than other groups (p<0.05). 2. No statistically significant difference could be found between three laser-treated groups (III, IV, V) in shear bond strength(p>0.05) 3. According to the result of observation under SEM, Polyacrylic acid was shown to have removed the smear layer effectively and opened the dentinal tubules, whereas the laser has produced the irregular surface mainly composed of melted and fused structure. The microcracks found in laser-treated groups increased in number with irradiation time and formed the regular mesh-type in 10 sec-irradiation group. 4. The ultrastructural change of dentin surface created by laser irradiation was found to the improper for bonding of the glass ionomer restorative materials. And the lower shear bond strength of laser irradiated group might have been due to the failure to form the suit able dentin surface for the glass ionomer to penetrated into and form the proper micromechanical retention.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.24 no.3
• /
• pp.311-316
• /
• 2008

Calcium phosphate cement (CPC) has been used as bone substitute successfully due to good biocompatibility and osteoconductivity. One of the important mechanical characteristics of CPC is flowablility, which can be evaluated by measuring rheological parameters. However, there have been few studies that measured rheological properties of CPC. The purpose of this study was to evaluate the rheological properties of CPC paste mixed with 2 kinds of setting solutions, 2% hydroxyprophyl methylcellulose (HPMC) and 35% polyacrylic acid (PAA). The CPC used was dicalcium phosphate dihydrate (DCPD). Rheological properties of CPC paste were measured using rheometer. The statistical analysis was carried out with Mann-whitney test with Bonferronis collection. CPC with both setting solutions showed shear thinning behavior. CPC with 2% HPMC showed signigicantly higher complex viscosity than CPC with 35% PAA(p<0.05).

• Macromolecular Research
• /
• v.11 no.5
• /
• pp.317-321
• /
• 2003

In order to prepare a prodrug, poly(polyethylene glycol methacrylate-co-methacryloyloxymethyl-5-fluorouracil) (poly(PEGM-co-MAOFU)) prodrug particles were prepared by precipitation polymerization of MAOFU and PEGM in polyacrylic acid solution. The size of prodrug particles were 0.2-0.35 ${\mu}{\textrm}{m}$. The antitumor activity of prodrugs against sarcoma-l80 tumor cell in mice was demonstrated and the polymer particles themselves showed low toxicity and good biocompatibility when they were administrated into mice.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.281-281
• /
• 2010

Very low refractive index (<1.4) materials have been proved to be the key factor improving the performance of various optical components, such as reflectors, filters, photonic crystals, LEDs, and solar cell. Highly porous SiO2 are logically designed for ultralow refractive index materials because of the direct relation between porosity and index of refraction. Among them, ordered macroporous SiO2 is of potential material since their theoretically low refractive index ~1.10. However, in the conventional synthesis of ordered macroporous SiO2, the time required for the crystallization of organic nanoparticles, such as polystyrene (PS), from colloidal solution into well ordered template is typical long (several days for 1 cm substrate) due to the low interaction between particles and particle - substrate. In this study, polystyrene - polyacrylic acid (PS-AA) nanoparticles synthesized by miniemulsion polymerization method have hydrophilic polyacrylic acid tails on the surface of particles which increase the interaction between particle and with substrate giving rise to the formation of PS-AA film by simply spin - coating method. Less ordered with controlled thickness films of PS-AA on silicon wafer were successfully fabricated by changing the spinning speed or concentration of colloidal solution, as confirmed by FE-SEM. Based on these template films, a series of macroporous SiO2 films whose thicknesses varied from 300nm to ~1000nm were fabricated either by conventional sol - gel infiltration or gas phase deposition followed by thermal removal of organic template. Formations of SiO2 films consist of interconnected air balls with size ~100 nm were confirmed by FE-SEM and TEM. These highly porous SiO2 show very low refractive indices (<1.18) over a wide range of wavelength (from 200 to 1000nm) as shown by SE measurement. Refraction indices of SiO2 films at 633nm reported here are of ~1.10 which, to our best knowledge, are among the lowest values having been announced.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.118-119
• /
• 2014

원전 운전 중 2차계통 구성재료가 부식되어 철 산화물이 증기발생기 내부로 유입된다. 유입된 철산화물은 고온고압의 환경에서 침적되어 슬러지가 된다. 침적된 슬러지는 증기발생기 전열관 재료에 응력부식균열(SCC)을 일으키는 주원인으로 원전에서는 철 산화물의 유입을 최소화하기 위해 기동전 2차계통을 순환 세정하고 있다. 해외 원전에서는 고분자 아크릴산(Polyacrylic Acid)을 순환세정시 주입함으로써 2차계통 철 산화물 제거 효율을 높인 사례가 있었다. 이에 우리 원전에서도 기동전 순환세정시 고분자 아크릴산을 주입 적용하였다. 고분자 아크릴산 주입 전 필수적으로 이뤄져야할 연구는 고분자 아크릴산이 재료에 미치는 영향평가이다. 본 연구에서는 고분자 아크릴산 농도(1, 10, 100 ppm)에 따라 2차계통 구성재료인 SA106 Gr.B와 Alloy 690의 건전성에 미치는 영향를 수행하였다. 평가방법으로는 전기화학 분극실험, 시편을 침지시켜 실험 전, 후 무게 감량을 이용한 부식률 측정, 표면 상태분석등을 이용하여 종합적으로 평가하였다. 전기화학 분극실험과 부식률 측정결과, 고분자 아크릴산 농도가 높을수록 부식은 증가하였고 고분자 아크릴산 농도 100 ppm일 때 최대 부식률이 0.037 mils로 계산되었다. 이는 부식허용 기준치(5.8 mils)보다는 100배이상 낮았으며 표면분석 결과 고분자 아크릴산으로 인한 pitting 부식은 발생하지 않았다. 이와 같은 결과로 기동시 환경에서 고분자 아크릴산 농도 100 ppm까지는 재료 건전성에 미치는 영향은 거의 없는 것으로 판단된다.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.12
• /
• pp.3593-3599
• /
• 2010

In an original effort, this lab attempted to employ polystyrene nanoparticles as a template for the synthesis of ordered and highly porous macroporous $SiO_2$ thin films, utilizing their high combustion temperature and narrow size distribution. However, polystyrene nanoparticle thin films were not obtained due to the low interaction between individual particles and between the particle and silicon substrate. However, polystyrene-polyacrylic acid (PS-AA) colloidal particles of a core-shell structure were synthesized by a one-pot miniemulsion polymerization approach, with hydrophilic polyacrylic acid tails on the particle surface that improved interaction between individual particles and between the particle and silicon substrate. The PS-AA thin films were spin-coated in the thickness ranges from monolayer to approximately $1.0\;{\mu}m$. Using the PS-AA thin films as sacrificial templates, macroporous $SiO_2$ thin films were successfully synthesized by vapor deposition or conventional solution sol-gel infiltration methods. Inspection with field emission scanning electron microscopy (FE-SEM) showed that the macroporous $SiO_2$ thin films consist of interconnected air balls (~100 nm). Typical macroporous $SiO_2$ thin films showed ultralow refractive indices ranging from 1.098 to 1.138 at 633 nm, according to the infiltration conditions, which were confirmed by spectroscopy ellipsometry (SE) measurements. This research shows how the synthetic control of the macromolecule such as hydrophilic polystyrene nanopaticles and silicate sol precursors innovates the optical properties and processabilities for actual applications.

• The korean journal of orthodontics
• /
• v.28 no.5 s.70
• /
• pp.689-698
• /
• 1998

The purpose of this study was to evaluate the shear bond strength of light cured glass ionomer cement to enamel surface which treated with $37\%$ phosphoric acid, $10\%$ polyacrylic acid, $1.23\%$ acidulated phosphate fluoride gel and no etching agent. To compare the shear bond strength of glass ionomer cement, light-cured composite resin and chemically-cured composite resin were empoloyed as controls. Eight experiments groups were composed. 10 specimens of each group were bonded by metal bracket by tested in universal testing machine for shear bond strength, in stereoscope for adhesive remnants index. The data were evaluated statistically by SPSS/PC+. The results were as follows. 1. Among the groups of $37\%$ phosphoric acid treated and dry and bonded with light cured glass ionomer, light cured composite resin, and chemically cured composite resin, the shear bond strength of glass ionomer group showed no significant difference to the others, but the shear bond strength of chemically cured resin showed statistically lower than that of light cured resin (p<0.05). 2. The shear bond strengths of glass ionomer cement to enamel treated group with $1.23\%$ acidulated phosphate fluoride gel and $10\%$ polyacrylic acid and $37\%$ phosphoric acid showed statistically higher than that of no etched enamel group(p<0.U). 3. In the groups of glass ionomer cement, the presence of moisture was not significantly effect to the shear bond strength (p<0.05). 4. After debonding, no etched enamel group showed less residual materials on the enamel surface than the group of enamel etched with $37\%$ Phosphoric acid.

• Textile Coloration and Finishing
• /
• v.11 no.4
• /
• pp.50-56
• /
• 1999

The adhesive properties of polyester cord in rubber matrix were investigated according to the surface modification. The polyester cord was oxidized in sodium hypochlorite solution, and graft-polymerized with acrylic acid under the irradiation with ultraviolet light, and then coated with resorcinol-formaldehyde latex (RFL). The modified surface was checked with scanning electron microscope. The adhesive properties were measured by the full-Out method, and evaluated with regard to the energy of adhesion and the maximum load. The polyester was not oxidized in sodium hypochlorite solution, so the surface was not able to etch to produce the coarse topology. As the concentration of acrylic acid and the reaction time were increased, the graft yields were also increased. It was considered that the acrylic acid would swell the polyester and diffuse easily to the inner side of substrate. The adhesive properties of polyeser to rubber matrix were affected by the surface condition. Namely, the maximum load was almost same, but the energy of adhesion was rather higher In the polyester grafted with acrylic acid than in control one. We concluded that the flexible aliphatic chains of polyacrylic acid situated in the interface of cord and rubber matrix were distributed well the stress and strain all over the filler resulting the high energy of adhesion.