To synthesize a new positive photosensitive polyimide precursor, parts of carboxylic acid groups in poly (amic acid) were esterified with 4,5-dimethoxy-2-nitrobenzyl bromide in the presence of K$_2$CO$_3$/HMPA followed by the chemical imidization of residual carboxylic acid units. The chemical structure of resulting polymer was characterized by $^1$H-NMR, UV/vis and FT-IR spectroscopic methods, and its thermal properties were examined by DSC and TGA. Upon UV irradiation, 4,5-dimethoxy-2-nitrobenzyl moiety underwent the photodegradation. As a result, the polymer became soluble in alkaline developer due to the formation of carboxylic acid moiety, which was used to make a micron-sized positive pattern. Sensitivity curves were obtained from the gel fraction experiments with respect to the various 4,5-dimethoxy-2-nitrobenzyl ester contents. From those curves, the sensitivity was ranged iron 4000 to 6000 mJ/㎠, and the contrast was measured to be from 3.1 to 4.9.

• Polymer(Korea)
• /
• v.38 no.5
• /
• pp.632-639
• /
• 2014

2,7-Dihydroxynaphthalene bis(trimellitate anhydride) (2,7-TA) was synthesized from trimellitic anhydride chloride and 2,7-dihydroxynaphthalene. Copolyimides (Co-PI) containing ester group were synthesized from 2,7-TA, pxylylenediamine, and 2,2'-bis(trifluoromethyl)benzidine (TFB). The Co-PI films were obtained from poly(amic acid) by solution casting through thermal imidization on a glass plate. The thermal property, gas permeation, and optical transparency of the Co-PI films with various TFB monomer contents were investigated. These Co-PIs could be solution-cast into a flexible and tough film. The cast Co-PI films exhibited high optical transparency with a cut-off wavelength of 370~395 nm in UV-vis. absorption and a low yellow index value of 3.55~7.63. The thermal property of Co-PI films increased linearly with increasing TFB content. However, the oxygen permeation and optical transparency of the Co-PI films was found to worsen with increasing TFB content.