• Applied Chemistry for Engineering
• /
• v.16 no.1
• /
• pp.144-149
• /
• 2005

Sulfonated poly(ether ether ketone) (SPEEK) was blended with poly(ether sulfone) (PES) at various compositions. To investigate the possibility of using the blend membranes as polymer electrolyte membranes for direct methanol fuel cell, the blend membranes were characterized in terms of methanol permeability, proton conductivity, ion exchange capacity, and water content. Both proton conductivity and methanol permeability of SPEEK were relatively high. As the amount of PES increased, methanol permeability decreased more rapidly compared to proton conductivity. The experimental results indicated that the blend membrane with 40 wt% PES was the best choice in terms of the ratio of proton conductivity to methanol permeability.

• Membrane Journal
• /
• v.15 no.1
• /
• pp.1-7
• /
• 2005

Polymer electrolyte membranes containing polysilsesquioxane (PSQ) spheres were prepared with the blend of sulfonated poly(ether ether ketone) (SPEEK) (60%) and poly(ether sulfone) (PES) (40%). The amount of PSQ spheres was fixed at 10 wt%. The prepared polymer electrolyte membranes were characterized in terms of methanol permeability, proton conductivity, and ion exchange capacity. In all cases, both methanol permeability and proton conductivity of the polymer electrolyte membranes containing PSQ spheres were lower than the values of Nafion 117 and higher than those of SPEEK/PES (6:4) blend without PSQ spheres. The experimental results indicated that the polymer electrolyte membranes containing MS64 and VTMOS spheres were the best choice in terms of the ratio of proton conductivity to methanol permeability.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.487-488
• /
• 2006

Novel bisphenol-based wholly aromatic poly(ether sulfone-ketone) copolymer containing pendant sulfonate groups were prepared by direct aromatic nucleophilic substitution polycondensation of 4,4-difluorobenzophenone, 2,2'-disodiumsulfonyl-4,4'-fluorophenylsulfone (40mole% of bisphenol A) and bisphenol A. Polymerization proceeded quantitatively to high molecular weight in N-methyl-2-pyrrolidinone at $180^{\circ}C$. Organic-inorganic composite membranes were obtained by mixing organic polymers with hydrophilic $SiO_2$ (ca. 20nm) obtained by sol-gel process. The polymer and a series of composite membranes were studied by FT-IR, $^1HNMR$, differential scanning calorimetry (DSC) and thermal stability. The proton conductivity as a function of temperature decreased as $SiO_2$ content increased, but methanol permeability decreased. The nano composite membranes were found to posse all requisite properties; Ion exchange capacity (1.2meq./g), glass transition temperatures $(164-183\;^{\circ}C)$, and low affinity towards methanol $(4.63-1.08{\times}10^{-7}\;cm^2/S)$.

• Korean Chemical Engineering Research
• /
• v.53 no.6
• /
• pp.690-694
• /
• 2015

Recently, direct formic acid fuel cells (DFAFC) among direct liquid fuel cells is studied actively. Economical hydrocarbon membranes alternative to fluorinated membranes for DFAFC's membrane are receiving attention. In this study, characteristics of sulfonated poly(ether ether ketone, sPEEK) and sulfonated poly(arylene ether sulfone, PAES) membranes were compared with Nafion membrane at DFAFC operation condition. Formic acid crossover current density of hydrocarbon membranes were lower than that of Nafion 211 fluorinated membrane. I-V performance of sPEEK MEA(Membrane and Electrode Assembly) was similar to that of Nafion 211 MEA due to similar membrane resistance each other. sPEEK MEA with low formic acid crossover showed higher stability compared with Nafion 211 MEA.

• Macromolecular Research
• /
• v.12 no.4
• /
• pp.413-421
• /
• 2004

Sulfonated poly(phthalazinone ether sulfone ketone) (SPPESK) membranes and sol-gel derived SPPESK/silica hybrid membranes have been investigated as potential polymer electrolyte membranes for direct methanol fuel cell (DMFC) applications. In comparison with the SPPESK membrane, the SPPESK/silica membranes exhibited higher water content, improved proton conductivity, and lower methanol permeability. Notably, the silica embedded in the membrane acted as a material for reducing the fraction of free water and as a barrier for methanol transport through the membrane. From the results of proton conductivity and methanol permeability studies, we suggest that the fractions of bound and free water should be optimized to obtain desirable proton conductivities and methanol permeabilities. The highly sulfonated PPESK hybrid membrane (HSP-Si) displayed higher proton conductivity (3.42 ${\times}$ 10$^2$ S/cm) and lower methanol permeability (4.15 ${\times}$ 10$\^$7/ $\textrm{cm}^2$/s) than those of Nafion 117 (2.54 ${\times}$ 10$^2$ S/cm; 2.36 ${\times}$ 10$\^$6/ $\textrm{cm}^2$/s, respectively) at 30$^{\circ}C$. This characteristic of the SPPESK/silica membranes is desirable for future applications related to DMFCs.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.489-490
• /
• 2006

Branched sulfonated poly(ether sulfone-ketone) copolymer was prepared with bisphenol A, 4,4-difluorobenzophenone, sulfonated chlorophenyl sulfone (40mole% of bisphenol A) and THPE (1,1,1-tris-p-hydroxyphenylethane). THPE was used 0.4 mol% of bisphenol A to synthesize branched copolymers. Organic-inorganic nano composite membranes were prepared with copolymer and a series of $SiO_2$ nanoparticles (20 nm, 4, 7 and 10 wt%). The composite membranes were cast from dimethylsulfoxide solutions. The films were converted from the salt to acid forms with dilute hydrochloric acid. The membranes were studied by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). Sorption experiments were conducted to observe the interaction of sulfonated polymers with water and methanol. Branched copolymer and nano composite membranes exhibit proton conductivities from $1.12{\times}10^{-3}$ to $6.04{\times}10^{-3}\;S/cm^2$, water uptake from 52.9 to 62.4%, IEC from 0.81 to 1.21 meq/g and methanol diffusion coefficients from $1.2{\times}10^{-7}$ to $1.5{\times}10^{-7}\;cm^2/S$.