• Journal of the Korean Institute of Landscape Architecture
• /
• v.26 no.2
• /
• pp.229-239
• /
• 1998

This study investigated ecological and growth characteristics of Sorbus alnifolia for usage of landscape woody plant. The results are obtained as follows: 1) The results of investigate the native Sorbus alnifolia vegetations in Seoul and Kyonggi-do are as follows. From the investigation of canopy and understory, Pinus densiflora, Pinus rigida, Quercus mongolica Quercus dentata and Quercus aliena grow well in natural habitat of Sorbus alnifolia. While Rhod. mucronulatum, Symplocos chinensis, Corylus hetrophylla and alnifolia. While Rhod. mucronulatum, Symplocos chinensis, Corylus hetrophylla and Lindera obtusiloba are commonly found from shrub structure in the habitat. These structure pattern of natural setting would be applied for ecological planting design. 2) The Mt. Rabong area, which locates near a heavy factory district and is considered as environmental dteriorated area has the lowest soil acidity range among three investigated area. Sorbus alnifolia grows in where contains low soil acidity and inorganic nutrient. It might concluded that Sorbus alnifolia be tolerates to air pollution. 3) From the investigation of good specimen tres, the oldest good specimen trees of Sorbus alnifolia have grown in Seoul and Kyonggi-Do for 130 years with 15m height and 12m width. Most of good specimen trees are over 50 years old with 10~15m height, 4.5-12m width. These growth shape and form could be recommend that Sorbus alnifolia would be used as street tree and landscape woody plant in urban park.

• Journal of the Korean Society for Heat Treatment
• /
• v.11 no.1
• /
• pp.62-72
• /
• 1998

High carbon steel is used for rails due to the excellent wear resistance, however the welding of high carbon steel is more difficult than that of mild steel owing to the high hardenability and sensitivity to cracking at the weldment. In this study, the impact toughness and cracking behavior of a rail weldment were evaluated as function of preheating temperatures. Impact toughness were more excellent in the specimen welded with preheating temperature above $250^{\circ}C$ than that below $100^{\circ}C$, and cracks were not detected in the specimen welded with preheating temperature above $250^{\circ}C$.

• Proceedings of the Plant Resources Society of Korea Conference
• /
• 2020.08a
• /
• pp.16-16
• /
• 2020

Systematic studies for genus Anaphalis in Koreaare relatively scarce. As a fundamental step to further taxonomic studies of this genus, we here propose lectotype for A. morii, endemic taxa in Korea with a brief re-evaluation of its taxonomic entity. During the examination of herbarium specimen for A. morii, we found nine sheets of five collections in three herbaria. Among the original materials, we selected a specimen in TI which was first cited by the author and include an additional annotation, matching with his own description. Also, we were able to determine the taxonomic relationships between A. morii and its relatives, A. yakusimensis. Based on our observation, we identified that several morphological characters are clearly differ from A. yakusimensis occurring only Isl. Yakushima in Japan.

• Korean Journal of Materials Research
• /
• v.29 no.6
• /
• pp.349-355
• /
• 2019

This study deals with the microstructure and tensile properties of 600 MPa-grade seismic reinforced steel bars fabricated by a pilot plant. The steel bar specimens are composed of a fully ferrite-pearlite structure because they were air-cooled after hot-rolling. The volume fraction and interlamellar spacing of the pearlite and the ferrite grain size decrease from the center region to the surface region because the surface region is more rapidly cooled than the center region. The A steel bar specimenwith a relatively high carbon content generally has a higher pearlite volume fraction and interlamellar spacing of pearlite and a finer ferrite grain size because increasing the carbon content promotes the formation of pearlite. As a result, the A steel bar specimen has a higher hardness than the B steel bar in all the regions. The hardness shows a tendency to decrease from the center region to the surface region due to the decreased pearlite volume fraction. On the other hand, the tensile-to-yield strength ratio and the tensile strength of the A steel bar specimen are higher than those of the B steel bar with a relatively low carbon content because a higher pearlite volume fraction enhances work hardening. In addition, the B steel bar specimen has higher uniform and total elongations because a lower pearlite volume fraction facilitates plastic deformation caused by dislocation slip.

• Journal of the Korean GEO-environmental Society
• /
• v.10 no.3
• /
• pp.5-12
• /
• 2009

This study presents static and dynamic strength of coal ashes collected from disposal site of power plant. Main compositions of coal ashes were bottom ashes. In order to evaluate static and dynamic characteristics of coal ash, NGI direct-simple shear tests, cyclic simple shear tests and direct shear tests were conducted. The strengths of coal ashes from those tests were compared to those of sands. Bottom ashes among coal ashes used for this study were classified as sand from the grain size distribution and show higher strength properties than the sands. For utilization of coal ashes in civil engineering project, mixing coal ashes with sandy soil using batch plant is inconvenient and the cost is higher than the spreading sand layer and coal layer alternately. In order to simulate both mixing type and layered type construction, sands and coal ashes were mixed with volume ratio 50:50 and prepared sand and coal ash layers alternately with the same volume ratio. From the tests mixed coal ashes-specimen shows slightly higher static and cyclic strength than the layered specimen at the same density. The higher strength seems due to the angular grain of bottom ashes. The cyclic stress ratio at liquefaction decreases rapidly as the number of cycle increases at mixed specimen than that of layered specimen.

• Journal of Plant Biology
• /
• v.37 no.2
• /
• pp.245-252
• /
• 1994

Pollens of 20 species of Sedum were investigated with a scanning electron microscope. The pollen morphology of Sedum was rather variable, within particular species or even within a single inflorescence. Differences occurred in the number and shape of apertures and surface sculpture. Besides 3-colporate, various aperture types including 2-syncolporate, 3-syncolporate, 40stephanocolporate, 5-stephanocolporate, zonate, and irregular types were found in a single specimen. Also, striate-rugulose and psilate sculpture were found in S. viviparum. No correlation was found between the pollen morphology and the floral formula. Pollen characters appeared to be not useful for infrageneric classification of Korean Sedum.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.8
• /
• pp.2033-2042
• /
• 1993

In conventional SCC susceptibility test, there are constant strain test, constant load test, slow strain rate test(SSRT) and K$_{ISCC}$ test. Among them, the SSRT method is much more aggressive in producing SCC than the other tests, so that the test time of it is considerably reduced. But this SSRT method has mostly been worked using the uniaxial tensile specimen untill now. Therefore, the SSRT method using the tensile specimen(Ten-SSRT) has much difficulty in SCC susceptibility evaluation of a localized region like weldment and the advantage material of high order. Recentely, the small punch(SP) test method using miniaturized small specimen is the very effective test method for fracture strength evaluation of a localized region like weldment and fusion reactor wall irradiated in the nuclear power plant. This paper investigated the possibility of SCC susceptibility evaluation by the SP-SSRT method using the miniaturized small specimen. Therefore, we obtained the result that the SP-SSRT had the possibility for the evaluations of SCC susceptibility for shorter time to corrosive environment compare to Ten-SSRT which was conventional method.

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 2011.04a
• /
• pp.415-418
• /
• 2011

Thermal fatigue is one of the life-limiting damage mechanisms in the nuclear power plant conditions. The turbulent mixing of fluids of different temperatures induces rapid temperature changes to the pipe wall. The successive thermal transients cause varying cyclic thermal stresses. These cyclic thermal stresses cause fatigue crack nucleation and growth similar to the cyclic mechanical stresses. The aim of this study was to fulfil the need by developing an real crack manufacturing method, which would produce realistic cracks. The test material was austenitic STS 304, which is used as pipelines in the reactor coolant system of a nuclear power plants. In order to fabricate thermal fatigue crack similar to realistic crack, successive thermal transients were applied to the specimen. Thermal transient cycles were combined with heating (60sec) and cooling cycle (30sec). And, In order to identify ultrasonic characteristic, it was performed the ultrasonic reflection measuring method for the fabricated specimen. From the results of ultrasonic reflection measuring testing, it was conformed that A-scan results(average 83% of real crack depth) for the TFC reference specimen was more enhanced NDT reliability than results(average 38% of real crack depth) for the EDM notch reference specimen.

• Korean Journal of Materials Research
• /
• v.29 no.8
• /
• pp.497-504
• /
• 2019

In this study, the correlation between microstructure and Charpy impact properties of FCAW(Flux cored arc welding) HAZ(Heat affected zone) of thick steel plates for offshore platforms was investigated. The 1/4 thickness(1/4t) location HAZ specimen had a higher volume fraction of bainite and finer grain size of acicular ferrite than those of the 1/2 thickness (1/2t) location HAZ specimen because of the post heat effect during the continuous FCAW process. The Charpy impact energy at $-20^{\circ}C$ of the 1/4t location HAZ specimen was lower than that of the 1/2t location HAZ specimen because of the high volume fraction of coarse bainite. The Charpy impact energy at -40 and $-60^{\circ}C$ of the 1/2t location HAZ specimen were higher than those of the 1/2t location HAZ specimen because the ductile fracture occurred in the fine acicular ferrite and martensite regions. In the ductile fracture mode, the deformed regions were observed in fine acicular ferrite and martensite regions. In the brittle fracture mode, long crack propagation path was observed in bainite regions.

• Korean journal of applied entomology
• /
• v.52 no.2
• /
• pp.125-127
• /
• 2013

Coleophora virgaureae Stainton of Coleophoridae is reported for the first time from Korea, with a description and illustrations of the adult and genitalia are presented based on a single female specimen collected from Mt. Suri, Gyeonggi-do.