• Journal of Welding and Joining
• /
• v.31 no.6
• /
• pp.90-95
• /
• 2013

Pipe inside clad welding is mainly used to the flow pipe of sub-sea or chemical plant. For the inside clad welding to the medium pipe with the diameter of about 12", TIG welding is frequently applied with filler metal. In this case, the clad welding has the very broad weld area over $10m^2$. And, the non-destructive test (NDT) such as ultrasonic test (UT) or radiographic testing (RT) should be conducted on the broad weld area, and it costs very high due to the time-consuming work. Therefore, the present study investigated the variation of arc voltage to develop the in-line quality monitoring system for the pipe inside TIG cladding. The 4 experimental parameters (current, arc length, wire feed position, and shield gas flow rate) varied to observe the change of arc voltage and to establish the model for the monitoring. The arc voltage was decreased when the wire was fed to the backward eccentric position(over 2mm), and the shield gas flow rate was insufficient under 10L/min. In the case of the backward eccentric position over 2mm, the bead appearance was not good and the dilution ratio was increased due to deep penetration. When the shield gas flow rate was lower than 10L/min, the bead surface was oxidized.

• Journal of Welding and Joining
• /
• v.30 no.6
• /
• pp.42-48
• /
• 2012

Due to increase in demand of stable and long pipelines in natural gas industry, wide range of researches are being performed on automation welding to improved welding quality with respect to weld process parameters in real time measurement. In particular, the coupling between the pipe manufacturing process and location of the weld seam, the measured size of the gap that exists in the weld position and the weld angle depending on whether the movement of molten weld. This is due to absence of controlling welding penetration position, depending on the required size of the angle of the setting. In addition, the optimum welding conditions must be considered while selecting, the correlation between these variables and the systematic correlation has not yet been identified. Therefore, in most welded pipe root-pass weld solely depends on the experience of workers in relation to secure a stable weld quality. In this study, automation welding system is implemented to select a suitable root-pass STT (Surface Tension Transfer) welding method using the optimal welding conditions. To successfully accomplish this objective, there were various welding conditions used for welding experiment to confirm that the assessment required for construction through the pipe and automatic welding process is proposed to optimize this plan.

• Journal of Welding and Joining
• /
• v.27 no.1
• /
• pp.71-78
• /
• 2009

In the circumferential welding of pipe, welding phenomenon changes with the position of pipe. Especially in the overhead position, back bead of vertical-up position would be sunk. To investigate the size of back bead and keyhole with the change of the flow rate of pilot and shield gas at each position, bead-on plate welds were conducted on 6mm thickness SS400 with inclined-up position. When the rest of welding conditions remained constant, the width of back bead was increased as the flow rate of pilot gas was increased. And back bead tended to convex as the flow rate of shield gas was increased.

• Journal of Korean Society of Steel Construction
• /
• v.13 no.4
• /
• pp.327-335
• /
• 2001

The characteristics and production mechanism of residual stress generated by multi-pass welding of the steel pipe were elucidated from the results of three-dimensional thermal elastic-plastic FEM analysis. When the steel pipe was jointed by multi-pass welding, the stress components of circumferential direction and radial direction near welded joints on the inner surface and the outer surface of the pope were tensile. The stress component of axial direction on the inner surface was tensile and on the outer surface was compressive. On the other hands, the production mechanism of residual stress generated by multi-pass welding of the steel pipe was investigated. Residual stress generated by welding of the steel pipe was investigated not only by the thermal history but also by geometrical shape. Then, the generality of the production mechanism of residual stress generated by multi-pass welding was confirmed.

• Journal of Welding and Joining
• /
• v.26 no.2
• /
• pp.55-61
• /
• 2008

Various research to reduce weight of a car is achieving. This research is tendencious to manufacture solid piston rod of shock absorber as hollow piston rod using friction welding. This study deals with the friction welding of SM45C to SM45C-Pipe that is used in car shock absorber, The friction time was variable conditions under the conditions of spindle revolution of 2,000rpm, friction pressure of 55MPa, upset pressure of 75MPa, and upset time of 2.0seconds. Under these conditions, the microstructure of weld interface, tensile fracture surface and mechanical tests were studied of friction weld, and so the results were as follows. 1. In tensile strength, the hole processing is better than non-hole processing. 2. When the friction time was 1.5seconds under the conditions, the maximum tensile strength of the friction weld happened to be 869MPa, which is 103% of SM45C's tensile strength and 91% of SM45C's Pipe. 3. When the friction time was 2.0seconds under the conditions, the maximum bending strength of the friction weld happened to be 1599MPa, which is 80% of SM45C's bending strength and 118% of SM45C's Pipe.

• Journal of Energy Engineering
• /
• v.24 no.4
• /
• pp.55-62
• /
• 2015

It is expected that the size of welding defect affects the mechanical performance of welded medium density polyethylene (MDPE) pipe joints. In this study, butt fusion welded MDPE pipe joints with a single spherical or planar defect of various sizes were studied using experimental crush testing and also by finite element method. The crush test showed that the mechanical performance of crush was not affected by the size and geometry of a single welding defect when the defect size was increased to 45% of the pipe's wall thickness. The simulation results indicated that the effect of the single welding defect on the Von Mises stress distribution near the defect explained the reason of the test results.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.05a
• /
• pp.458-461
• /
• 2008

We carry out non-steady state finite element simulation of a porthole extrusion process for manufacturing a radiation pipe under isothermal assumption. It is assumed that welding takes place at the moment that the material contacts the plane of symmetry. Welding phenomena are revealed by observing the contacting mechanism of the material passed through the portholes. It is emphasized that mesh density control and intelligent remeshing during welding process govern the solution accuracy and the program applicability. AFDEX 3D is employed.

• Proceedings of the KWS Conference
• /
• 2005.06a
• /
• pp.161-163
• /
• 2005

• Journal of Welding and Joining
• /
• v.21 no.1
• /
• pp.60-65
• /
• 2003

At present. welding of most pipes with large diameter is carried out by the manual process. Automation of the welding process is necessary f3r the sake of consistent weld quality and improvement in productivity. In this study, two vision sensors, based on the optical triangulation, were used to obtain the information for seam tracking and detecting the weld defects. Through utilization of the vision sensors, noises were removed, images and 3D information obtained and positions of the feature points detected. The aforementioned process provided the seam and leg position data, calculated the magnitude of the gap, fillet area and leg length and judged the weld defects by ISO 5817. Noises in the images were removed by using the gradient values of the laser stripe's coordinates and various feature points were detected by using an algorithm based on the iterative polygon approximation method. Since the process time is very important, all the aforementioned processes should be conducted during welding.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.17 no.5
• /
• pp.36-43
• /
• 2008

This research is tendencious to manufacture solid piston-rod of shock absorber as hollow piston-rod using friction welding. The SM45C has been welded to the SM45C-pipe in order to investigate the effect of upset pressure on friction weldability. The friction time and upset pressure was variable conditions under the conditions of spindle revolution of 2,000rpm, friction pressure of 55MPa, and upset time of 2.0seconds. Under these conditions, the microstructure of weld interface, tensile fracture surface and mechanical tests were studied of friction weld, and so the results were as follows. When the upset pressure is sufficient, gets the high tensile strength. The optimal welding conditions were n=2,000rpm, $P_1$=55MPa, $P_2$=95MPa, $t_1$=1.5sec, $t_2$=2.0sec when the total upset length is 4.5mm.