• Journal of the Korean Ceramic Society
• /
• v.43 no.6 s.289
• /
• pp.333-337
• /
• 2006

In this study, the $Sr_{1-x}Ba_{x}Al_{2}O_{4}:Eu^{2+},Dy^{3+}$ phosphor were prepared by the solid-state reaction method and its photoluminescence properties were investigated. Starting powders of $SrCO_3,\;BaCO_3,\;and\;Al_{2}O_3$ were mixed with $Eu_{2}O_3$ as activator, $Dy_{2}O_3$ as co-activator and $B_{2}O_3$ as flux. Then, the mixed powders were heated at the temperature of $1100{\sim}1400^{\circ}C$ for 3 h under the reducing ambient atmosphere of $95%Ar+5%H_2$. The effect of Ba addition from 0.0 to 1.0 mol on photoluminescence was investigated. As the amount of Ba increased, the intensity of emission increased and the optimum long phosphorescence occurred at the amount of 0.1 mol Ba. The optimum sintering condition for long phosphorescent phosphor of $Sr_{1-x}Ba_{x}Al_{2}O_{4}:Eu^{2+},Dy^{3+}$($x=0{\sim}1.0mol$) was found at $1400^{\circ}C$. The excitation spectra showed a broad band of $250{\sim}450nm$ with maximum peak at 360 nm. The maximum peak intensity of emission spectra occurred at the range of $480{\sim}520nm$, depending on Ba content.

• Journal of the Korean Ceramic Society
• /
• v.45 no.3
• /
• pp.146-149
• /
• 2008

Strontium-substituted $Sr_{1-x}Ba_xAl_2O_4:Eu^{2+},\;Dy^{3+}$ compositions were prepared by the solid state synthesis method. These compositions were characterized for their phase, crystallinity and morphology using powder x-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques. Photoluminescence properties were investigated by measuring excitation spectra, emission spectra and decay time for varying Ba/Sr concentrations. Photoluminescence results show higher luminescence and long decay time for $Sr_{1-x}Ba_xAl_2O_4:Eu^{2+},\;Dy^{3+}$(x=0). This is probably due to the influence of the 5d electron states of $Eu^{2+}$ in the crystal field. Long persistence was observed for these compositions due to $Dy^{3+}$ co-doping.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.145.2-145
• /
• 2003

• Journal of the Korean Applied Science and Technology
• /
• v.19 no.3
• /
• pp.174-180
• /
• 2002

In recent days, the study of a new phosphorescent phosphor has been performed in order to overcome the defect of sulfide phosphor and increase the brightness and long after-glow characteristic of phosphorescent phosphor. Particularly, sulfide phosphor usually used is so chemically unstable that the study of oxide phosphors are processing. $Eu^{2+}$, $Nd^{3+}$ doped Ba-Al-O phosphors sintered at $600{\sim}1500^{\circ}C$ for 2hours had the PL emission spectrum and after-glow over $1200^{\circ}C$. In this system, as the mole concentration of alumina increases, emission bands of phosphors moved from 500nm to 380nm. The optimum concentration of flux was 5wt% and after-glow characteristics of phosphors were found at the host material molar ratio ($BaCO_{3}:Al_{2}O_{3}$), 1:1 and 1:3.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.54-54
• /
• 2008

$Eu^{2+}$, $Nd^{3+}$ co-doped $BaAl_2O_4$ are known as a long afterglow phosphor. We found that $Eu^{2+}$-doped $BaAl_2O_4$ showed ptotoconductivity in the range of UV and visual light. In this study, $BaAl_2O_4$:Eu thin film has been prepared by RF sputtering method and a sensing characteristics to UV and visual light was performed. Only $Eu^{2+}$ and $Nd^{3+}$ co-doped $BaAl_2O_4$ powders and targets for deposition were prepared by a convention solid state method, and the deposition was performed in a reducing $H_2$-Ar mixture gas on Si substrates. The observation of crystalline phase and morphology of the sputtered film were performed using XRD, EDX. The photoluminescence and photocurrent to UV and visual light were measured simultaneously using 300W-Xe solar simulator as a light source. It was confirmed that the photocurrent induced by irradiation of light showed a linear relationship to the light intensity.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2004.08a
• /
• pp.1083-1086
• /
• 2004

We applied the spray pyrolysis technique to prepare Mn-doped $BaMgAl_{10}O_{17}$ (BAM) particles with high photoluminescence, which could be used in the plasma display device as a green phosphor. Several preparation conditions were investigated in order to tail the vacuum ultraviolet (VUV) characteristics. Some portions of barium were replaced with strontium to improve the luminescent intensity of BAM:Mn particles under VUV excitation. The content of Mn and Sr was optimized to obtain high luminescent efficiency under VUV excitation. Finally, the optimized BAM:Mn green particles showed higher photoluminescence intensity than that of commercial $Zn_2SiO_4$ and comparable with commercial barium-aluminate phosphor.

• Korean Journal of Materials Research
• /
• v.21 no.12
• /
• pp.644-649
• /
• 2011

[ $A_{3-2x/3}Al_{1-z}In_{z}O_4F:Eu_x^{3+}$ ](A = Ca, Sr, Ba, x = -0.15, z = 0, 0.1) oxyfluoride phosphors were simply prepared by the solid-state method at $1050^{\circ}C$ in air. The phosphors had the bright red photoluminescence (PL) spectra of an $A_{3-2x/3}Al_{1-z}In_{z}O_4F$ for $Eu^{3+}$ activator. X-ray diffraction (XRD) patterns of the obtained red phosphors were exhibited for indexing peak positions and calculating unit-cell parameters. Dynamic excitation and emission spectra of $Eu^{3+}$ activated red oxyfluoride phosphors were clearly monitored. Red and blue shifts gradually occurred in the emission spectra of $Eu^{3+}$ activated $A_3AlO_4F$ oxyfluoride phosphors when $Sr^{2+}$ by $Ca^{2+}$ and $Ba^{2+}$ ions were substituted, respectively. The concentration quenching as a function of $Eu^{3+}$ contents in $A_{3-2x/3}AlO_4F:Eu^{3+}$ (A = Ca, Sr, Ba) was measured. The interesting behaviors of defect-induced $A_{3-2x/3}Al_{1-z}In_{z}O_{4-{\alpha}}F_{1-{\delta}}$ phosphors with $Eu^{3+}$ activator are discussed based on PL spectra and CIE coordinates. Substituting $In^{3+}$ into the $Al^{3+}$ position in the $A_{3-2x/3}AlO_4F:Eu^{3+}$ oxyfluorides resulted in the relative intensity of the red emitted phosphors noticeably increasing by seven times.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.1
• /
• pp.67-74
• /
• 2002

A phosphor for Plasma Display Panel, BaMgAl$_{10}$ O$_{17}$ :Eu$^{2+}$, showing a blue emission band at about 450nm was prepared by a solid-state reaction using BaCO$_3$, $Al_2$O$_3$, MgO, Eu$_2$O$_3$ as starting materials wish flux AlF$_3$. The study of the behaviour of Eu in BAM phosphor was carried out by the photoluminescence spectra and the Rietveld method with X-ray and neutron powder diffraction data to refine the structural parameters such as lattice constants, the valence state of Eu, the preferential site of Mg atom and the site fraction of each atom. The phenomenon of the concentration quenching was abound 2.25~2.3wt% of Eu due to a decrease in the critical distance for energy transfer of inter-atomic Eu. Through the combined Rietveld refinement, R-factor, R$_{wp}$, was 8.11%, and the occupancy of Eu and Mg was 0.0882 and 0.526 at critical concentration. The critical distance of Eu$^{2+}$ in BAM was 18.8$\AA$ at 2.25% Eu of the concentration quenching. Furthermore, c/a ratio was decreased to 3.0wt% and no more change was observed over that concentration. The maximum entropy electron density was found that the modeling of $\beta$-alumina structure in BaMgAl$_{10}$ O$_{17}$ :Eu$^{2+}$correct coincided showing Ba, Eu, O atoms of z= 1/4 mirror plane.e.ane.e.

• Journal of the Korean Ceramic Society
• /
• v.41 no.5
• /
• pp.370-374
• /
• 2004

Sr$_{l-x}$Ba$_{x}$Al$_2$O$_4$:Eu (x = 0, 0.1, 0.2, and 0.3 mol) phosphor was synthesized by the hydrothermal method and its properties of photoluminescence and long-afterglow were investigated. The mixtures of Sr(NO$_3$)$_2$, Al(NO$_3$)$_3$9$H_2O$, and Eu(NO$_3$)$_3$$.$6$H_2O$ salts dissolved in distilled water, after controlling their pH by NH$_4$OH solution, put into an Autoclave reactor with high temperature and pressure to react. Such synthesized SrAl$_2$O$_4$:Eu powders showed homogeneous and ultra-fine particles of sub-micron size. In order to have the photoluminescence characteristic, powders were heat treated at 1100 -140$0^{\circ}C$ for 2 h in Ar/H$_2$ reduction atmosphere. Photoluminescence spectra showed a excitation along the wide wavelength of 250 ∼ 450 nm, and broaden emission with maxima peak at 520 nm. Also, it showed a good long afterglow with decaying over 1000 sec after excitation illumination for 10 min. In addition, the microstructure and crystal structure of SrAl$_2$O$_4$:Eu powders were investigated by an SEM and XRD, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.566-569
• /
• 1999

The blue emitting BAM Phosphor Particles with various compositions were Prepared by the spray Pyrolysis. The effect of composition on the morphology of BAM particles was Investigated. In the case of BaMgAl$_{10}$ /O$_{22}$ : Eu$^{2+}$, the morphology of particles with sphericity and non-aggregation characteristics disappeared after post-treatment at 1400 $^{\circ}C$ for 3 hrs. On the other hand, the ocher composition particles except BaMgAl$_{10}$ /O$_{22}$ : Eu$^{2+}$ maintained their original morphology after post-treatment, even if the particles were prepared at low temperatures in the spray pryrolysis. The BAM particles with MgAl$_{2}$/O$_4$as intermediate material at low post-treatment temperature had high thermal stability and maintained sphericity of particles after post-treatment. All the samples had main omission peak at 450 nm, which corresponds to blue emission. The optimum post-treatment temperature of BAM:Eu$^{2+}$ particles for the maximum PL(photoluminescence) intensity in the spray pylolysis was 1200 $^{\circ}C$ because of high crystallinity, Phase-Purity, and good morphology.ology.