• 한국세라믹학회지
• /
• 제48권3호
• /
• pp.217-221
• /
• 2011

Glass-ceramic materials, which consist of glass matrix phase containing crystalline ${\beta}-Ca_3(PO_4)_2$ and ${\beta}-Ca_2P_2O_7$, have been prepared by heating at $750-900^{\circ}C$ of calcium phosphate invert glasses in the silica-free $CaO-P_2O_5-TiO_2-Na_2O$, system. With increasing heating temperature from 750 to $900^{\circ}C$, the crystallite size of precipitated ${\beta}-Ca_3(PO_4)_2$ in glass with $55CaO{\cdot}35P_2O_5{\cdot}3TiO_2{\cdot}7Na_2O$ (mol%) composition increased from 48 to 91 nm. With the extension of the immersion time in dilute acetic acid solution (pH = 5) to ${\geq}$200 min, the degree of dissolution of $Ca^{2+}$ and $P^{5+}$ ions in the glass-ceramics was linearly increased and the solution was constantly maintained at pH = ~7. Biomimetic nanostructured (62-88 nm in average dia.), sphere-shaped hydroxyapatite was homogeneously formed on the surface of the glass-ceramics when socked for 7-14 days in a Hanks' solution, indicating bioactivity of the prepared glass-ceramics.

• 한국세라믹학회지
• /
• 제40권11호
• /
• pp.1132-1137
• /
• 2003

환경친화적인 유리비료로서의 응용을 위해 인산염계 유리의 용출특성에 대한 연구를 진행하였다. 0.1K₂O-0.1SiO₂-0.6P₂O/sub 5/계 유리를 기본조성으로 하고, CaO와 MgO의 함량변화를 준 다양한 유리조성에 대한 유리 형성 조건을 확인하고자 하였다. 또한 CaO 및 MgO의 함량변화에 따른 열적특성 및 용출 특성 변화를 확인하였다. MgO 함량의 증가에 따라 유리 전이온도 및 연화온도는 증가하였으며, CaO 및 MgO의 함량변화에 따라 용출특성에 큰 영향을 미치는 것을 확인하였다.

• 한국세라믹학회지
• /
• 제48권1호
• /
• pp.26-33
• /
• 2011

The glass in the system of CaO-$SiO_2-P_2O_5$ and the corresponding glass-ceramics are prepared for bone cements and the behaviors of the hardening and hydroxyapatite formation were studied for the glass and glass-ceramic powders. The glass crystallized into apatite, $\alpha$-wollastonite and $\beta$-wollastonite depending on the glass composition when they were heat-treated at $950^{\circ}C$ for 4 h. A DCPD (dicalcium phosphate dihydrate : $CaHPO_4{\cdot}2H_2O$) was developed when the prepared glass and glass-ceramic powders were mixed with 3M-$H_3PO_4$ solution. The DCPD (Ca/P=1.0) transformed to HAp (Ca/P=1.67) when the bone cement was soaked in simulated body fluid (SBF), and this HAp formation strongly depended on the releasing capacity of $Ca^{2+}$ ions from the glass and glass-ceramic cements. The glass-ceramic bone cement containing $\alpha$-wollastonite crystals showed faster transformation of DCPD to HAp than other glass-ceramics containing $\alpha$- and $\beta$-wollastonite crystals. No hydroxyapatite was observed when the glass-ceramic bone cement containing apatite crystals (36P6C) was soaked in SBF even for 1 month, because no $Ca^{2+}$ ion can be released from the stable apatite crystals.

• 한국산학기술학회논문지
• /
• 제2권2호
• /
• pp.91-94
• /
• 2001

Glass ceramics composed of (5-X)$Li_2O$ㆍ$XAg_2O$ㆍ36CaOㆍ$20TiO_2$.27$P_2O_5$(X=1 to 5) were prepared by melting process and 2 step heat treatment for nucleation at$610^{\circ}C$ and crystallization at $730^{\circ}C$, Fabricated crystal phases were $LiTi_2(PO_4)_3$(LTP),$AgTi_2(PO_4)_3$(AgTP)와 $\beta-Ca_3(PO_4)$. Antibacterial effects and characterizations of the glass ceramics as $Ag_2$O content were investigated. Staphylococcus aureus and Salmonella typhi were used in this study. Staphylococcus aureus and Salmonella typhi bacteria were removed 5 hours added after glass ceramics.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2006년도 6th International Meeting on Information Display
• /
• pp.935-937
• /
• 2006

Phosphate glass system is expected to be useful as a lead-free material in many devices in plasma display panels (PDP). The present study is mainly focused on the evaluation of interface reaction between ceramic fillers and phosphate glass matrix for barrier ribs in PDP. The results suggest that properties of barrier rib depend on the crystallization behavior and interface reaction between the fillers and glass matrix.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2002년도 International Meeting on Information Display
• /
• pp.795-798
• /
• 2002

Replacing Pb-free glass composition for the dielectric materials is expected in PDP industry. In this study, phosphate glasses, $P_2O_5$- ZnO- SnO (PZS), $P_2O_5$-ZnO-BaO (PZB) were selected for a new transparent dielectric. Thermal properties (Tg, CTE) were measured with differential thermal analyzer and thermal mechanical analyzer. The glass transition of the glasses was ranged at $365{\sim}405^{\circ}C$ for the PZS system and $5.9{\sim}9.5{\times}\;10^{-6}$ of thermal expansion were found. The PZB system showed $445{\sim}470^{\circ}C$ of glass transition. Thus, the glass compositions would be a potential candidate for a transparent dielectric layer in plasma display panel.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1983년도 하계학술회의강연.논문초록집
• /
• pp.221-222
• /
• 1983

• 한국광학회:학술대회논문집
• /
• 한국광학회 1989년도 광학 및 양자전자학 워크샵
• /
• pp.44-50
• /
• 1989

1 tera watt (1012 watt)의 출력을 내는 phosphate glass 레이저를 개발하는 것이 최종목적이며, 1차적으로 완전한 계통도를 설계하였다.

• 대한치과보철학회지
• /
• 제25권1호
• /
• pp.227-242
• /
• 1987

This study was designed to investigate the pulpal effects of the glass ionomer cement. (Lining cement, G-C Co. Japan) For this purpose, 10 cats were selected, and Class V cavities were prepared on canines of the cats. One experimental group was filled with glass ionomer cement and the other group was filled with zinc phosphate cement . (G-C Co, Japan) The animals of the experimental and control group were sacrificed at 1,2,3,4,6, weeks after the experiment. For comparison of reparative dentin formation pattern in direction of the pulpal and fractured lateral surface, each of them was observed with scanning electron microscope. The findings led to the following conclusions; 1. Reparative dentin of the glass ionomer cement and zinc phosphate cement filling groups were formed on the internal surface of dentin as the shape of hemispherical and spherical with a rough surface. 2. Some of reparative dentin of the glass ionomer cement filling group was started to form at 1 week after experiment, and at 6 weeks after experiment, it had been increased gradually in number and size. 3. Reparative dentin of zinc phosphate cement filling group was formed vigorously, however, gradually was decreased in number and size, and disappeared at 6 weeks after experiment. 4. During the formation of reparative dentin, peritubular dentins were indistinguishable. 5. The diameter of dentinal tubules of reparative dentin has been decreased, during the reparative dentin formed, and it became very irregularly at 6 weeks after experiment.

• The Journal of Advanced Prosthodontics
• /
• 제4권3호
• /
• pp.127-133
• /
• 2012

PURPOSE. Many dentists use desensitizing agents to prevent hypersensitivity. This study compared and evaluated the effect of two desensitizing agents on the retention of cast crowns when cemented with various luting agents. MATERIALS AND METHODS. Ninety freshly extracted human molars were prepared with flat occlusal surface, 6 degree taper and approximately 4 mm axial length. The prepared specimens were divided into 3 groups and each group is further divided into 3 subgroups. Desensitizing agents used were GC Tooth Mousse and $GLUMA^{(R)}$ desensitizer. Cementing agents used were zinc phosphate, glass ionomer and resin modified glass ionomer cement. Individual crowns with loop were made from base metal alloy. Desensitizing agents were applied before cementation of crowns except for control group. Under tensional force the crowns were removed using an automated universal testing machine. Statistical analysis included one-way ANOVA followed by Turkey-Kramer post hoc test at a preset alpha of 0.05. RESULTS. Resin modified glass ionomer cement exhibited the highest retentive strength and all dentin treatments resulted in significantly different retentive values (In Kg.): GLUMA ($49.02{\pm}3.32$) > Control ($48.61{\pm}3.54$) > Tooth mousse ($48.34{\pm}2.94$). Retentive strength for glass ionomer cement were GLUMA ($41.14{\pm}2.42$) > Tooth mousse ($40.32{\pm}3.89$) > Control ($39.09{\pm}2.80$). For zinc phosphate cement the retentive strength were lowest GLUMA ($27.92{\pm}3.20$) > Control ($27.69{\pm}3.39$) > Tooth mousse ($25.27{\pm}4.60$). CONCLUSION. The use of $GLUMA^{(R)}$ desensitizer has no effect on crown retention. GC Tooth Mousse does not affect the retentive ability of glass ionomer and resin modified glass ionomer cement, but it decreases the retentive ability of zinc phosphate cement.