• Corrosion Science and Technology
• /
• 제22권6호
• /
• pp.429-434
• /
• 2023

This study investigated the localized corrosion behavior of a UNS G41400 steel surface treated with manganese phosphate. The phosphate coating, primarily composed of oxygen (O), phosphorus (P), and manganese (Mn) elements, had an approximate thickness of 6 ㎛. The particles comprising the coating varied in size by several micrometers; smaller particles were mainly composed of O, P, Mn, and iron (Fe) elements, indicating incomplete formation of the manganese phosphate film. Potentiodynamic polarization curves revealed a decrease in anodic current after surface treatment and a shift in corrosion potential toward the noble direction after treatment. After immersion in a 3.5 wt% NaCl solution for 96 hours, localized corrosion was observed, with some regions retaining residual phosphate film. Even though localized corrosion occurred on the treated surface, it was less severe than that on the untreated UNS G41400 steel surface. These findings suggest that manganese phosphate coating improved resistance to localized corrosion.

• 한국표면공학회지
• /
• 제44권3호
• /
• pp.82-88
• /
• 2011

A uniform chromium-free conversion coating treated with an alkaline phosphate- permanganate solution was formed on the AZ 31 magnesium alloy. The effect of acid pickling on the morphology and on the corrosion resistance of the alkaline phosphate-permanganate conversion coating was investigated. The chemical composition and phase structure of conversion coating layer were determined via optical microscopy, SEM, EDS, XPS and XRD. Results show that the conversion coatings are relatively uniform and continuous, with thickness 1.8 to $2.4\;{\mu}m$. The alkaline phosphate-permanganate conversion coating was mainly composed of elements Mg, O, P, Al and Mn. The conversion-coated layers were stable compounds of magnesium oxide and spinel ($MgAl_2O_4$). These compounds were excellent inhibitors to corrosion. The electrochemical corrosion behaviors of coatings in 3.5 wt.% NaCl solutions were evaluated by electrochemical impedance spectroscopy, potentiodynamic polarization technique. EIS results showed a polarization resistance of $0.1\;k{\Omega}$ for the untreated Mg and $16\;k{\Omega}$ for the alkaline phosphate-permanganate conversion treatment sample, giving an improvement of about 160 times. The results of the electrochemical measurements demonstrated that the corrosion resistance of the AZ 31 magnesium alloy was improved by the alkaline phosphate-permanganate conversion treatment.

• 한국산업융합학회 논문집
• /
• 제25권2_2호
• /
• pp.199-208
• /
• 2022

The steel wire or steel bar processing process applied to the manufacture of various bolts and power transmission shafts was improved by applying in-line phosphate film treatment technology. By applying a polymer lubricant for a non-reactive metal forming process and a non-reactive non-phosphorus lubricating coating agent, the film formation for each process time was comparatively analyzed and reviewed. Compared to the nine processes applied previously, the in-line phosphate film treatment technology applied with only two processes has been effectively improved in terms of reduction of treatment time, reduction of facility installation area, prevention of water pollution due to wastewater, and non-use of ozone-depleting substances. In addition, it was found that it can have an important effect on productivity improvement and price competitiveness from the simplification of quality control and process control as well as improvement of the working environment.

• 한국산학기술학회논문지
• /
• 제18권10호
• /
• pp.603-610
• /
• 2017

탄약을 포함한 다양한 산업 분야에서 사용되는 철강 재료는 부식에 취약하므로, 표면 그대로 사용하는 것은 바람직하지 않다. 따라서 도금, 도장, 화성처리와 같은 표면 처리 이후 사용하여야 하는데, 탄약 제조 과정에서는 주로 아연계 인산염 피막 처리가 사용되고 있다. 표면 처리 기법 중 하나인 아연계 인산염 피막은 금속 표면을 화학적으로 처리하여 안정성이 높은 화합물 층을 표면에 고착시키는 방법으로, 크게 도장 하지용 경인산염 피막과 부식 방지용 중인산염 피막으로 나뉘어지는데, 아연계 인산염 피막은 전산도, 철 함량과 같은 여러 가지 인자에 의해 피막의 품질과 내식성이 결정된다. 본 연구에서는 전산도 및 철 함량이 탄약 부식 방지 목적으로 사용되는 아연계 중인산염 피막의 중량 및 내식성에 미치는 영향에 대하여 알아보았다. 철 함량에 따라 피막의 구조가 치밀해지며, 내식성이 향상되는 결과를 확인할 수 있었으나, 전산도는 피막의 두께와 중량에만 영향을 주고 내식성에는 큰 영향을 주지 못하였다. 위 결과를 토대로 탄약 제조 과정에서 사용되는 인산염 피막 처리 공정의 최적 제어 수준을 제시하였다.

• Corrosion Science and Technology
• /
• 제17권1호
• /
• pp.30-36
• /
• 2018

The high rate of corrosion of magnesium alloys makes it limited for industrial applications. Therefore, surface treatment is required to enhance their corrosion resistance. In our study, a chemical conversion coating for protecting the corrosion of the magnesium alloy, AZ31B, was prepared by using a phosphate-permanganate solution. The chemical conversion coating had a limited protection ability due to defects arising from cracks and pores in the coating layer. The sol-gel coating was prepared by using trimethoxymethylsilane (MTMS) and 3-glycidoxypropyltrimethoxysilane (GPTMS) as precursors, and aluminum acetyl acetonate as a ring opening agent. The corrosion protection properties of sol-gel and conversion coatings in 0.35wt% NaCl solution were measured by the electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization test. The EIS results indicated that the resistance of the chemical conversion coating with the sol-gel coating was significantly improved through the sol-gel sealed phosphate-permanganate conversion coating. The results of the potentiodynamic polarization test revealed that the sol-gel coating decreased the corrosion current density ($I_{corr}$). The SEM image showed that the sol-gel coating sealed conversion coating and improved corrosion protection.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2022년도 가을 학술논문 발표대회
• /
• pp.81-82
• /
• 2022

Al and Zn are used to protect the steel structures from corrosion. In the present studies, 15Al-85Zn alloy wires has been used for the deposition of coating by arc thermal spray process. Moreover, this process of coating exhibited severe defects formation, therefore, this coating was post-treated with different concentrations i.e. 0.05, 0.1 and 0.5M sodium hexa meta phosphate (Na6[(PO3)6]: SHMP) to fill to defects of deposited coatings and assessed their corrosion resistance in 3.5 wt.% NaCl solution with exposure periods. After the treatment, the porosity of the coating reduced significantly by formation of composite oxide films onto the coating surface. Initially, 0.5 M SHMP treated coating exhibited highest in total impedance due to significant reduction of porosity but once the exposure periods are extended, the composite oxides are dissolved, thus, total impedance is decreased.

• 한국지반환경공학회 논문집
• /
• 제20권1호
• /
• pp.27-33
• /
• 2019

산성배수가 발생하는 비탈면에서 생태적 녹화를 위한 산성배수 중화기법을 알아보기 위한 연구를 진행하였다. 산성배수중화기법을 위한 4가지 유형의(무처리, 석회고토 처리, 인산염 처리, 석회고토 + 인산염 처리) 시험구를 조성하였다. 실험결과 산도(pH), 피복율(%), 고사율(%), 식물뿌리상태 등에서 중화기법에 따른 유의차가 발생하는 것을 알 수 있었다. 중화기법에 따른 연구결과 (첫 번째 : 석회고토 + 인산염 처리, 두 번째 : 인산염 처리, 세 번째 : 석회고토 처리, 네 번째 : 무처리) 순서로 산도 중화 및 식물생장에 효과적이었다. 산성배수 비탈면에서 석회고토 처리와 인산염 처리는 토양산도 중화와 식물생장에 효과적이었으나, 석회고토 처리에 비해 인산염 처리가 더 효과적이었으며, 인산염 처리가 황화광물의 코팅 효과 때문에 토양산도 중화와 식물 생장에 더 효과적이라는 것을 알 수 있었다.

• 한국신뢰성학회지:신뢰성응용연구
• /
• 제1권2호
• /
• pp.95-108
• /
• 2001

To enhance the corrosion resistance of a bolt by surface treatment, dacrotization was considered as a substitute for phosphate coating which is widely used for general applications. In this study, comparisons were made among 5 different kinds of surface treatments including dacrotization and phosphate coating with respect to corrosion resistance, adhesion property with painting, and preload when tightened. The result shows that the dacrotized and surface-stabilized bolt is much superior in every aspects studied herein to others. An excellent corrosion resistance and a fairly good adhesion property with painting were achieved in the dacrotized and surface-stabilized bolt. When tightened at the same torque, the amount of preload and its deviation of dacrotized and surface-stabilized bolt were comparable with those of phosphate coated bolt.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2007년도 춘계학술대회 논문집
• /
• pp.149-154
• /
• 2007

The zinc prosphate film treatments used to lubricating treatment of mostly cold forging processes. But there are several problems happened to lubricating treatment process such as happening harmful environment on person, complex lubrication processing occurring in energy and time consumption, eco-destructive and chemical by-product generation, the needs of waste disposal etc. As a result, a water-soluble lubricant was developed to replace the perfect or some of the zinc prosphate film in the world. In order to solve these problems, this study evaluated the performance of the typical water-soluble. In this study, for these requirement inquiry of two part. First, about possibility of replace zinc phosphate lubricant, quantitatively evaluation developed of water-soluble lubricant for cold forging vs zinc phosphate lubricant. Second, About optimization of coating Process use to equipment with practicable automatic coating Process. The performance evaluation of these lubricants was conducted using the double cup extrusion test and spike forging test. With the use of the commercial FE code DEFORM, friction factor calibration curves, i.e. cup height ratio vs. punch stroke and spike height vs. punch stroke, were established for different friction factor values. By matching the cup height ratio and the punch stroke and spike height vs. punch stroke from experiment to that obtained from FE simulations, the friction factor of the lubricants was determined. Survey of comparative analysis use to SEM that sprayed lubricant surface structure of grain shape and characteristic of lubricant performance based on grain shape and deformed lubricant surface expansion. As a result, developed lubricant were found to perform comparable to or better than zinc phosphate. And thought this result, innovatively cope with generated problem of existing lubrication process.

• 한국표면공학회지
• /
• 제43권2호
• /
• pp.73-79
• /
• 2010

A chromium-free conversion coating for AZ31 magnesium alloy has been obtained by using a permanganatephosphate solution, which has been developed with acid pickling. Examination have been carried out on the conversion coatings for morphology, composition and corrosion resistance. The morphology of the conversion-coated layer was observed using optical microscope and SEM. It was shown that the conversion coatings are relatively uniform and continuous, with thickness 1.8 to 2.7 ${\mu}m$. The chemical composition of conversion coating was mainly consisted of Mg, O, P, K, Al and Mn by EDS analysis. It was found that the corrosion resistance of the AZ31 magnesium alloy has been improved by the permanganate-phosphate conversion treatment from electrochemical polarization.