• Title/Summary/Keyword: phenol-formaldehyde resin (PF resin)

Search Result 34, Processing Time 0.026 seconds

Synthesis of Resol Type Phenol Resins and Their Reaction Properties (Resol형 페놀수지의 합성과 반응특성)

  • Kim, Dong-Kwon;Joe, Ji-Eun;Kim, Jung-Hun;Park, In Jun;Lee, Soo-Bok
    • Applied Chemistry for Engineering
    • /
    • v.16 no.2
    • /
    • pp.288-291
    • /
    • 2005
  • Resol type phenol-formaldehyde (PF) resin was synthesized by addition reaction of formaldehyde (F) and phenol (P). And the PF resin was synthesized by condensation reaction in which water was removed. In this work, we studied the influence of experimental parameters in the addition reaction, such as F/P mole ratio, amount of catalyst, reaction temperature, reaction time, and so on. Also, we studied the influence of molecular weight and viscosity of PE resin as a function of condensation time. As a result, in addition reaction, the reaction time decreased remarkably as the catalyst concentration increased, and the time decreased with increasing reaction temperature at a constant catalyst concentration. Also, in condensation reaction, the viscosity of resol type PF resin increased from 1500 to 9000 cps as a function of condensation time; molecular weight showed from 500 to 1100 g/mol.

Properties and Curing Behavior of Urea-Modified Phenolic Resins

  • Lee, Sang-Min;Park, Sang-Bum;Park, Jong-Young
    • Journal of the Korean Applied Science and Technology
    • /
    • v.24 no.4
    • /
    • pp.339-346
    • /
    • 2007
  • The influence of adding urea to phenol-formaldehyde (PF) resins as a co-polymer component were investigated aiming at synthesizing useful phenol-urea-formaldehyde resins. Urea was added at 10% by total resin weight. Several methods for the addition of urea to the PF resins during synthesizing resins to see the co-polymerization occurs between urea and PF resins. The urea was added at the beginning, at three different middle stages, and at the end of PF resin synthesis. The copolymerized methylene bridges between phenol and urea molecules were not observed by $^{13}C-NMR;$ no signal around 50ppm. The curing of urea-modified PF resins, evaluated by dynamic mechanical analysis(DMA), showed some differences among the resins. DMA gel times ranged from 2.75 min to 3.25 min and the resins made with earlier urea additions showed slightly shorter gel times. The longest cure time and gelation time was observed for the resin PFU. Catalyst effects on the DMA cure time values of resins were not significant with different amounts of catalyst or different types of catalyst for all resins tested. Gel times of urea-modified PF resins shortened the most by triacetin catalyst.

Resin Impregnation of Sawdust Board for Making Woodceramics (I) - Effect of Impregnation Method and Time on Physical and Mechanical Properties -

  • Oh, Seung-Won
    • Journal of the Korean Wood Science and Technology
    • /
    • v.32 no.3
    • /
    • pp.25-32
    • /
    • 2004
  • This research work explored physical and mechanical properties of impregnated sawdust boards from three softwood species (P, densifora, L. kaemferi, and P. koraiensis) with phenol-formaldehyde (PF) resin by various vacuum treatment methods of combining pressure, vacuum, and ultrasonic waves. Simultaneous vacuum and ultrasonic wave treatments with no pressure resulted in the greatest increase in resin content, density, dimensional changes (thickness and length), bending strength, and hardness of impregnated board. This result seemed to be attributed to the ultrasonic wave treatment.

Effect of Phenol Formaldehyde Impregnation on The Physical and Mechanical Properties of Soft-Inner Part of Oil Palm Trunk

  • Hartono, Rudi;Hidayat, Wahyu;Wahyudi, Imam;Febrianto, Fauzi;Dwianto, Wahyu;Jang, Jae-Hyuk;Kim, Nam-Hun
    • Journal of the Korean Wood Science and Technology
    • /
    • v.44 no.6
    • /
    • pp.842-851
    • /
    • 2016
  • The objective of this study was to improve physical and mechanical properties of soft-inner part of oil palm trunk (S-OPT) after impregnation with phenol formaldehyde (PF) resin and densification by close system compression (CSC) method. Effect of different methods of PF resin impregnation (i.e., no vacuum-pressure, vacuum, and vacuum-pressure) was evaluated. The results showed that PF resin impregnation and CSC significantly improved the physical and mechanical properties of S-OPT up to: (1) 176% in density; (2) 309% in modulus of rupture (MOR); (3) 287% modulus of elasticity (MOE); and (4) 191% in the compressive strength. Physical and mechanical properties of S-OPT showed their best performances when PF resin impregnated with vacuum-pressure method as shown by higher weight gain, density, MOR, MOE, compressive strength, and lower recovery of set due to better penetration of PF resin into S-OPT. Combining PF resin impregnation and densification by CSC method could be a good method to improve physical and mechanical properties of S-OPT.

Manufacture of Wood Veneer-Bamboo Zephyr Composite Board: II. Effect of Manufacturing Conditions on Properties of Composite Board (목재 단판-대나무 제퍼 복합보드 제조: II. 복합보드의 성능에 미치는 제조조건의 영향)

  • Roh, Jeang Kwan
    • Journal of the Korean Wood Science and Technology
    • /
    • v.35 no.6
    • /
    • pp.108-117
    • /
    • 2007
  • This research was performed to investigate the feasibility of bamboo as a raw material for the manufacture of plywood. Wood veneer-bamboo zephyr composite boards (WBCB) were manufactured using keruing (Dipterocarpus sp.) veneers and hachiku bamboo (Phyllostacbys nigra var. henonis Stapf) using various adhesives, and the effect of the method and amount of resin spread on the mechanical properties of the composites were investigated. The WBCB manufactured using polymeric isocyanate (PMDI) showed the best mechanical properties, followed by phenol-formaldehyde resin (PF), phenol-melamine-formaldehyde resin, urea-melamine-formaldehyde resin, and urea-formaldehyde resin. However, considering the operation feasibility as well as mechanical properties, PF resin proved to be the appropriate adhesive for the practical purpose. As the amount of resin spread increased, the mechanical properties of 5-ply WBCB with 12 mm thicknesses manufactured using PF resin tended to increase, and more failure occurred at the interface between veneer and bamboo zephyr than at the interface among bamboo zephyrs. This result suggests that penetration of resin into bamboo zephyr could be the important factor. In this research, the appropriate amount of resin amount was $320g/m^2$. 5-ply WBCBs were manufactured using various methods of resin spread but the effect of the methods on the mechanical properties showed no little difference, which meant that the method of resin spread could be chosen considering the manufacturing conditions and operation feasibility.

Adding Effect of TCA-Precipitated Blood Powder to the Phenol Formaldehyde Resin for Plywood (합판용 페놀수지 접착제에 대한 TCA침전 혈액분말의 첨가효과)

  • Lee, Hwa-Hyoung;Lee, Jong-Shin;Jang, Sang-Sik
    • Journal of the Korean Wood Science and Technology
    • /
    • v.24 no.2
    • /
    • pp.15-19
    • /
    • 1996
  • To utilize the waste materials and develope wood adhesive from isolated bloods of slaughtered cow and pig and also to prevent water pollution, simple and rapid method of isolation and purification of plasma proteins from pig bloods with trichloroacetic acid(TCA) treatment was developed. Adding of TCA-precipitated blood powder to the phenol formaldehyde resin(PF) improved dry and wet strength of plywood and resulted in fast hot pressing times.

  • PDF

Quality Enhancement of Falcataria-Wood through Impregnation

  • SUMARDI, Ihak;DARWIS, Atmawi;SAAD, Sahriyanti;ROFII, Muhammad Navis
    • Journal of the Korean Wood Science and Technology
    • /
    • v.48 no.5
    • /
    • pp.722-731
    • /
    • 2020
  • The purpose of this research is to determine the efficiency of impregnation using phenol formaldehyde resin to enhance Falcataria wood's stability and better mechanical properties. Impregnation process was carried out after moisture content stabilized at 12% on samples with a dimension of 20 mm × 20 mm × 300 mm at various concentrations and pressure time. Dimensional stability was evaluated by thickness swelling (TS) and anti-swelling efficiency (ASE) and the young's modulus was conducted according to BS 573. The mechanical properties and dimensional stability of impregnated wood were evaluated. Dimensional stability and mechanical properties of Falcataria wood were successfully increased after impregnation. PF impregnation can improve the mechanical properties and the density from 0.26 g/㎤ to 0.30 g/㎤ even with only 10% of weight percent grain. Dimensional stability increases with increasing resin concentration and time pressure. The highest increase in mechanical properties was found at a higher concentration of PF. The penetration of PF into the wood's cell darkens the color of impregnated wood.

Physical Properties of Hybrid Poplar Flakeboard Bonded with Alkaline Phenolic Soy Adhesives

  • Yang, In;Kuo, Monlin;Myers, Deland J.
    • Journal of the Korean Wood Science and Technology
    • /
    • v.33 no.5 s.133
    • /
    • pp.66-75
    • /
    • 2005
  • Soybean-based adhesives have recently been reconsidered as alternatives to petroleum-based adhesives due to the uncertainty of availability of petrochemical products and the increased demand for wood adhesives. This study was conducted to investigate the adhesive properties of alkaline phenolic soy (APS) resin for hybrid poplar flakeboard. The APS resin was formulated by crosslinking an alkaline soy flour hydrolyzate with lab-prepared PF resin in the soy hydrolyzate to PF resin weight ratios of 70/30, 60/40, and 50/50. The APS resins were used to fabricate homogeneous hybrid poplar flakeboards with different resin solid levels (5%, 7%, and 9%), press temperatures (175 and $200^{\circ}C$), and press times of 8 and 10 minutes. The IB, wet MOR, and dimensional stability properties of board improved with increasing press time, press temperature, and PF level in APS resins. Increasing press time can be used to offset poor IB strength associated with a 9% resin solid level and the excessive moisture content in the mat. The following conditions were concluded to meet the requirements of the CSA standard for exterior-grade flakeboard: a 50% PF level, a 5% resin content, a $200^{\circ}C$ press temperature, and an 8 minute press time.

Phenol-Formaldehyde (PF) Resin Bonded Medium Density Fiberboard

  • Park, Byung-Dae;Riedl, Bernard;Park, Sang-Jin
    • Journal of the Korean Wood Science and Technology
    • /
    • v.27 no.1
    • /
    • pp.64-71
    • /
    • 1999
  • This study was conducted to manufacture MDF panels bonded with PF resins which provide excellent durability and dimensional stability with panels, and to identify benefits and weaknesses of using PF resins for MDF panels that have been manufactured with urea-formaldehyde (UF) resins for interior applications due to its low dimensional stability under moisture conditions. The results showed that the performance of PF-bonded MDF panels satisfied the performance requirement. A six-cycle aging test also revealed that PF-bonded MDF panels had high durability. Thickness swelling after 24 hours submersion in cold water was less than 2 percent, showing good dimentioanl stability. The identified weaknesses of using PF resins were relatively high resin content and long hot-pressing time. An acceptable resin content appeared to be 8 percent which can increase the production cost of PF-bonded MDF panels. The hot-pressing time (7 minutes) used in this study is relatively long compared to that of UF-bonded MDF panels. This result also indicates that hot-pressing process has to be optimized to control various pressing variables.

  • PDF

Thermal Curing Behavior and Tensile Properties of Resole Phenol-Formaldehyde Resin/Clay/Cellulose Nanocomposite

  • Park, Byung-Dae;Kadla, John F.
    • Journal of the Korean Wood Science and Technology
    • /
    • v.40 no.2
    • /
    • pp.110-122
    • /
    • 2012
  • This study investigated the effects of layered clay on the thermal curing behavior and tensile properties of resole phenol-formaldehyde (PF) resin/clay/cellulose nanocomposites. The thermal curing behavior of the nanocomposite was characterized using conventional differential scanning calorimetry (DSC) and temperature modulated (TMDSC). The addition of clay was found to accelerate resin curing, as measured by peak temperature ($T_p$) and heat of reaction (${\Delta}H$) of the nanocomposite’ curing reaction increasing clay addition decreased $T_p$ with a minimum at 3~5% clay. However, the reversing heat flow and heat capacity showed that the clay addition up to 3% delayed the vitrification process of the resole PF resin in the nanocomposite, indicating an inhibition effect of the clay on curing in the later stages of the reaction. Three different methods were employed to determineactivation energies for the curing reaction of the nanocomposite. Both the Ozawa and Kissinger methods showed the lowest activation energy (E) at 3% clay content. Using the isoconversional method, the activation energy ($E_{\alpha}$) as a function of the degree of conversion was measured and showed that as the degree of cure increased, the $E_{\alpha}$ showed a gradual decrease, and gave the lowest value at 3% nanoclay. The addition of clay improved the tensile strengths of the nanocomposites, although a slight decrease in the elongation at break was observed as the clay content increased. These results demonstrated that the addition of clay to resole PF resins accelerate the curing behavior of the nanocomposites with an optimum level of 3% clay based on the balance between the cure kinetics and tensile properties.