• Korean Journal of Materials Research
• /
• v.9 no.12
• /
• pp.1181-1187
• /
• 1999

PZT(53/47) precursor 1M sols were prepared using a diol based Sol-Gel process, and thin films were deposited by spin coating onto Pt/Ti/$SiO_2$/Si substrates. With a single coating, final film thickness of aproximately 0.9${\mu}m $ was achieved from diol-based PZT sol. Since PZT crystallized in a ferroelectric perovskite phase from an intermediate nonferroelectric pyrochlore phase, the effects of the presence of perovskite PZT seeds on the phase transformation of PZT were investigated. Seeded PZT films were prepared from the seeded PZT 1M sols in which seeds with less than 0.2${\mu}m $ in size and 1wt% were dispersed in n-propanol before mixing with the PZT stock solution. The seeding effects were confirmed by the fact that the formation temperature of perovskite phase decreased by 50$^{\circ}C$ with less than 1wt% seeds.

• Journal of Powder Materials
• /
• v.29 no.6
• /
• pp.468-476
• /
• 2022

Yttria-stabilized zirconia (YSZ) has a low thermal conductivity, high thermal expansion coefficient, and excellent mechanical properties; thus, it is used as a thermal barrier coating material for gas turbines. However, during long-time exposure of YSZ to temperatures of 1200℃ or higher, a phase transformation accompanied by a volume change occurs, causing the YSZ coating layer to peel off. To solve this problem, YSZ has been doped with trivalent and tetravalent oxides to obtain coating materials with low thermal conductivity and suppressed phase transformation of zirconia. In this study, YSZ is doped with trivalent oxides, Nd₂O₃, Yb₂O₃, Al₂O₃, and tetravalent oxide, TiO₂, and the thermal conductivity of the obtained materials is analyzed according to the composition; furthermore, the relative density change, microstructure change, and m-phase formation behavior are analyzed during long-time heat treatment at high temperatures.

• Journal of the Korean Ceramic Society
• /
• v.32 no.2
• /
• pp.248-256
• /
• 1995

The electrical conducton in the sintered 3Bi2O3.WO3 solid electrolyte was investigated by measuring the conductivity and ionic transport number. The electrical conductivity was about three to ten times higher than that of YSZ at temperatures between 300 and 80$0^{\circ}C$. D.C. polarization method confirmed that 3Bi2O3.WO3 was predominantly an ionic conductor. Unlike the instability of high conductive fcc phase in the rare-earth oxide-Bi2O3 or Y2O3-Bi2O3 systems at temperature below $700^{\circ}C$, fcc phase in the 3Bi2O3.WO3 exhibited no transformation even after annealing over 900 hrs at 600 and $650^{\circ}C$. Two samples which had different grain sizes showed almost the same conductivity. This result suggests that the electrical properties of grain and grain boundry were very similar.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.111-111
• /
• 2003

The peroxo titanic acid solution was successfully prepared using titanium trichloride as a precursor. The basic properties of the TiO2 film prepared by the solution were investigated in view of phase change, bandgap energy, crystalline size etc. The film displayed amorphous TiO$_2$ at room temperature, anatase above 281$^{\circ}C$ and a mixture of anatase and rutile at 99$0^{\circ}C$, The crystalline size increases with annealing temperatures, while the bandgap energies decrease due to the quantum size effect and the formation of rutile phase which has low bandgap energy. As a result of TG-DTA, it was found that annealing treatment at 99$0^{\circ}C$ for 2h formed a mixtures of anatase and rutile through three steps: (1) the removal of physically adsorbed water (2) the decomposition of peroxo group (3) amorphous-anatase or anatase-rutile phase transformation.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.211-214
• /
• 2001

The undesirable phase transformation of zirconium dioxide at high temperatures can be eliminated by stabilization of the cubic phase with an addition of a selected alkaline earth or rare-earth oxide. In this paper the ionic conductivity of cubic solid solutions in the stabilized ZrO$_2$ by CaO-Y$_2$O$_3$ system was examined. The higher ionic conductivity appears to be related to lower activation energy rather than to the number of oxygen vacancies dictated by composition. Those compositions of highest conductivity lie close to the cubic-monoclinic solid-solution phase boundary. Conductivity temperature data are presented that indicate a reversible order-disorder transition for Zr$_2$2-Y$_2$O$_3$cubic solid solutions containing 20 and 25 mole % $Y_2$O$_3$.

• Korean Journal of Materials Research
• /
• v.14 no.11
• /
• pp.802-806
• /
• 2004

Skutterudite $CoSb_3$ powders were produced by mechanical alloying (MA) of elemental powders using a nominal stoichiometric composition. Annealing of MA powders under specific condition led to a complete phase transformation to a semiconducting ${\delta}-CoSb_3$. Single phase $CoSb_3$ was successfully produced by vacuum hot pressing using MA powders without subsequent annealing. Phase transformations during mechanical alloying and hot pressing were systematically investigated using XRD and SEM. Thermoelectric properties as a function of temperature were evaluated for the hot pressed specimens and compared with results of analogous studies.

• Journal of the Korean Ceramic Society
• /
• v.32 no.10
• /
• pp.1162-1168
• /
• 1995

Systematic studies of the effects of additives and processing variables on the sintered density and the effect of crystalline forms of starting powders on the microstructure of pressureless sintered silicon carbide are described. Oxide additives were effective for the densification of SiC up to 96% of theoretical density at temperature as low as 185$0^{\circ}C$. Use of embedding powder increased the sintered density, up to 98% of theoretical density, by decreasing the weight loss during sintering. Composite type duplex microstructure has been developed due to the $\beta$longrightarrow$\alpha$ phase transformation of SiC by sintering at 185$0^{\circ}C$ and heat treatment at 195$0^{\circ}C$ for 1h.

• Transactions of Materials Processing
• /
• v.25 no.4
• /
• pp.248-253
• /
• 2016

Induction hardening process of tubular drive shaft for automobile is simulated by combining the thermal, mechanical, electro-magnetic and metallurgical analysis models. Various material properties for each analysis model are obtained in a consistent way via material properties calculation software, JMatPro^®. To consider the scanning process of induction heating, boundary element method is adopted for electro-magnetic field calculation. The distribution of temperature, stress and phase volume fraction are tracked out through the whole process and the effect of scanning velocity is reviewed. The analysis result shows that the critical principal stress is developed at the phase boundary where martensite is formed.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.27 no.1
• /
• pp.81-90
• /
• 1990

In this study, ion beam deposited tungsten thin film for gate material of GaAs SAGFET(Self Aligned Gate FET) was annealed from 800\ulcorner to 900\ulcorner using RTA and detailed investigations of structural and electrical characteristics of this film were carried out using four-point probe, XRD, SEM, AES and current-voltage measurement. Investigated results showed phase of as deposited tungsten film was fine grain \ulcornerphase and phase tdransformation of this film into \ulcornerphase occured at annealing condition of 900\ulcorner, 6sec. But regardless of phase transformation, electrical characteristics of tungsten film were very stable to 900\ulcorner and in case of 900\ulcorner, 4sec annealing condition Schottky barrier height obtained from 10 diodes measurements was 0.66 + 0.003 eV.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.10a
• /
• pp.203-206
• /
• 2008

Transformation of austenite to martensite during cold rolling has been widely used to strengthen metastable austenitic stainless steel grades. Aging treatment of cold worked metastable austenitic stainless steels, including ${\alpha}'$-martensite phase, results in the further increase of strength, when aging is performed in $200^{\circ}C$ to $450^{\circ}C$ temperature range. The purpose of the present study was to evaluate the effect of time and temperature on the stress-strain behavior of cold worked austenitic stainless steels. The amount of ${\alpha}'$-martensite during cold working and aging was examined by ferrite scope and X-ray diffraction (XRD). During aging at $450^{\circ}C$ for 1hr, tensile strength dramatically increased by 150MPa. Deformed metastable austenitic steels containing the "body-centered" ${\alpha}'$-martensite are strengthened by the diffusion of interstitial solute atoms during aging at low temperature.