• Corrosion Science and Technology
• /
• 제19권6호
• /
• pp.296-301
• /
• 2020

Failure analysis on the welded type 304 pipe used for cooling water piping in the district heating primary side was conducted. Inorganic elements and bacteria in the cooling water and in corrosion products were analyzed, and the weldment was inspected by microscopy and a sensitization test. Corrosion damages were observed in the heat-affected zone, on weld defects such as incomplete fusion or excessive penetration caused by improper welding, or/and at the 6 o'clock position along the pipe axial direction. However, the level of concentration of chloride in the cooling water as low as 80 ppm has been reported to be not enough for even a sensitized type 304 steel, meaning that the additional corrosive factor was required for these corrosion damages. The factor leading to these corrosion damages was drawn to be the metabolisms of the types of bacteria, which is proved by the detection of proton, sulfur containing species, biofilms, and both bacteria and corrosion product analyses.

• 대한토목학회논문집
• /
• 제28권5A호
• /
• pp.665-672
• /
• 2008

본 연구에서는 교량이나 선박 등의 강구조물에서 널리 사용되고 있는 하중 전달형 십자형 필렛용접 시험편에 대해 피로시험을 실시하여, 용접 후처리 조건에 따른 피로강도를 분석하였다. 용접 후처리 방법으로는 Toe Grinding, TIG Dressing 및 Weld Profiling을 적용하였으며, 피로시험은 일정진폭 반복하중 하에서 실시하였다. 피로시험 결과 하중 전달형 십자형 필렛용접 시험편은 용접 후처리를 실시한 경우와 실시하지 않은 경우 모두에서 BS 피로설계기준의 F등급을 만족하는 결과를 나타내었다. 또한 용접 후처리 방법에 따른 피로강도의 향상 효과는 Toe Grinding, TIG Dressing, Weld Profiling 순서로 증가하는 것을 알 수 있었다.

• Journal of Advanced Marine Engineering and Technology
• /
• 제11권2호
• /
• pp.71-81
• /
• 1987

Nowadays, the high development of industrial technique demands the optimal design of marine structures to be welded under the water, because the underwater welding of the ship hull and marine structures can decrease manpower and cost of production. However there is not available at present any report on fatigue behavior about underwater welded joints. In this paper under tention- tension repeated fatigue stress with frequency of 10 cycles per second by local controlled system, the fatigue strength properties of underwater welded joints of SM41A-2 Plate-to-Plate of 10 mm thickness were experimentally examined. The results obtained were as follows : 1) The fatigue strength of underwater welded joints of SM41A-2 was peaked at the heat input of about 1, 400 joule/mm(180 A, 36 V), while, at the heat input of more than about 1, 100 joule/mm (160 A, 33 V) that of the underwater welds at the higher than cycle of life rather than the lower cycle was higher than that of the base metal but lower than that of the atmosphere welds on account of both cooling and notch effects. 2) The fatigue limit of underwater welds increased with an increase of heat input resulting in a peak of that at the heat input of about 1, 400 joule/mm and then decreased gradually. 3) The fatigue strength at N cycles was peaked between the heat input of about 1, 400 and 1, 700 joule/mm where the strain was rapidly increased. 4) It was confirmed that the optimal zone of heat input condition for obtaining the underwater welds fatigue strength higher than that of the base metal exists, and if out of this zone, the fatigue strength of the underwater welds was lower than that of the base metal because of lack weld penetration, inclusion of slag, voids, etc. 5) By the fatigue test, the underwater welds fractured brittly without visual deformation, so the strain was remarkably less than of the atmosphere welds. 6) The fatigue life factor was peaked at the heat input of about 1, 600 joule/mm (200 A, 36 V) at which the mean strain is a little higher than that of the base metal but quite lower than those of the atmosphere welds, resulting in good underwater welds because both fatigue strength and ductility of the underwater welds are higher than those of the base metal at such heat input.

• 대한기계학회논문집A
• /
• 제37권3호
• /
• pp.387-395
• /
• 2013

최근 국외의 원자로 상부헤드 CRDM 관통노즐에 일차수 응력부식균열로 인한 냉각수 누출사고가 발생하였다. 일차수응력부식균열은 부식에 민감한 재료, 인장 잔류 응력 및 부식 환경 등의 3 가지 요인의 상호작용에 의해 발생하는 것으로 알려져 있기 때문에 응력 부식 균열 발생 및 균열 진전을 억제하기 위해서는 용접에 의한 잔류응력에 대한 정확한 예측이 선행되어야 한다. 본 논문에서는 국내 Westinghouse 형 원자로 상부 헤드 관통노즐(CRDM)을 대상으로 노즐의 두께 및 형상 비($r_o/t$)에 따른 노즐 잔류응력 분포 특성에 대해 연구를 수행하였다. 국내에 현존하는 원자로 상부헤드 관통노즐의 실제크기($r_o$=51.6, t=16.9 mm)를 기준으로 노즐의 두께 및 형상 비($r_o/t$=2, 3, 4)의 변수를 정립하였으며 정중앙 및 최외곽에 위치한 노즐을 대상으로 연구를 수행하였다.

• 대한기계학회논문집A
• /
• 제35권10호
• /
• pp.1337-1345
• /
• 2011

가압경수로형 원자로의 원자로압력용기 상부헤드에는 많은 제어봉구동장치(CRDM) 노즐이 분포한다. 최근 10 여 년 동안 제어봉구동장치 alloy 600 CRDM 노즐에서 균열 발생 사례가 증가하고 있으며, 이는 용접과 연관성이 매우 깊은 것으로 알려져 있다. CRDM 노즐에서 발생하는 축 및 원주방향 균열은 유럽과 미국의 원자력 발전소에서 발견되었으며, 사고의 원인은 용접 잔류응력 및 작용하중에 기인하는 일차수응력부식균열(PWSCC)임이 확인되었다. 이러한 이유로 본 연구에서는 유한요소해석을 통해 한국형 원자로의 CRDM 관통 노즐 용접부를 대상으로 용접 잔류응력을 예측하였으며, 특히, 관통노즐의 위치와 형상, 용접부 필렛 형상 및 인접노즐 용접에 의한 영향을 분석하였다.