• Journal of the Microelectronics and Packaging Society
• /
• v.26 no.4
• /
• pp.133-140
• /
• 2019

The effects of thermal cycle conditions on the bonding strength and crack propagation behaviors in electroplated Cr/electroplated Ni-P coatings were systematically evaluated. 1^st heat treatment was performed at 500℃ for 3 hours after electroplating Ni-P, and then, 2^nd heat treatment was performed at 750℃ for 6 hours after electroplating Cr. The measured bonding strength by ASTM C633 were around 25.6 MPa before thermal cycling, while it increased to 47.6 MPa, after 1,000 cycles. Increasing thermal cycles led to dominant fail mode with cohesive failure inside adhesive, which seemed to be closely related to the increasing bonding strength possibly not only due to higher Cr surface roughness, but also to penetrated channeling crack density. Also, increasing density of penetrated channeling cracks in electroplating Cr layer led to slightly stronger bonding strength due to mechanical interlocking effects of adhesive inside channeling cracks.