• Journal of the Korean Magnetics Society
• /
• v.7 no.6
• /
• pp.314-320
• /
• 1997

We have observed the orientation behavior of acicular iron oxides in magnetic layer of the particular magnetic tape after magnetic paint was coated on polyester film. As results of the static orientation, orientation of iron oxides come to the maximum at the front and the back of orientation magnets, but it was a litter lower at the back than at the front, and it slowly decreases and come to the constant level after passing through the orientation magnets. In case of edge portion to be futher away from center in the coated film, the orientation of iron oxides in magnetic layer come to worse than that of the center. We think it is owing to the shape and the magnetic magnitude of orientation magnets. The results of the dynamic orientation are as follows. As the orientation of iron oxides in the particulated magnetic tape is higher, the output properties of tape come to better than ever. And the orientation of iron oxides can be changed by drying condition, as result, the output properties of tape can be also. Therefore we think the considrations of the design of orientation magnets and the control of drying condition are needed to improve output properties of the particulated magnetic tape.

• Korean Institute of Interior Design Journal
• /
• v.25 no.2
• /
• pp.59-69
• /
• 2016

This study aimed to understand the importance of applying finishing materials into interior space, and to add meaning to the creation of functional space, associated interior finishing materials with brain science. To achieve this purpose, brainwave(EEG) experiment was conducted. The brainwave appearing when sensing the surface of interior finishing materials with hands was measured. The locations of the electrode were FP1, FP2, F3, F4, C3, C4, P3, P4, O1, O2, F7, F8, T3, T4, T5, T6, CZ, FZ, and PZ and in addition to these, AFZ was added. Eight(8) kinds of finishing materials: metallic material, film paper, lumbar, stone, glass, silk wallpaper, fabric, and paint were used to measure '${\alpha}$-wave against ${\beta}$ wave.' As a result, it was found that the most activated finishing material in term of relaxation was film paper, followed by metallic, glass, paint, fabric, stone, lumbar, and silk wallpaper. To explain in light of this, (1) '${\alpha}$-wave against ${\beta}$ wave' was the most activated at ch1-FP1 and ch2-FP2, and at ch17-AFZ and ch19-FZ, which indicated that metopic-prefrontal lobe showed the highest activation in relaxation. Film paper, among the finishing materials, showed the highest increase in relaxation. (2) In general, '${\alpha}$-wave against ${\beta}$ wave' relaxation was inhibited at ch13-T3 and ch14-T4, and at ch15-T5 and ch16-T6 and the arousal in the temporal lobe was prominent. Silk wallpaper, among the finishing materials, showed the highest arounsal effect. As a result of measuring the superficial touch on the silk wallpaper, which was regarded as the most rough material among the eight finishing materials, the arousal effect of ${\alpha}$-wave against ${\beta}$-wave, among the brainwave characteristics, was found to be the highest. (3) to judge from the scope of this experiment regarding the tactile sensation over the finishing materials, it is considered that the brainwave reaction sometimes appeared contrastive depending on whether the surface was smooth or rough and there also appeared a difference in relaxation and arousal reaction of the brainwave depending on whether the surface was hot or cold, but the sensation on the surface texture was often evaluated differently depending on who you were. For this reason, this study has some limitations.

• Journal of the Society of Naval Architects of Korea
• /
• v.50 no.6
• /
• pp.399-406
• /
• 2013

In the present study, the flat plate model test method is developed to evaluate the skin friction of the marine coating in the cavitation tunnel. Six-component force balance is used to measure the profile drag of the flat plate and strut. LDV(laser Doppler velocimetry) technique is also employed to evaluate the drag and to figure out the reason of the drag reduction. The flow velocities above the surface can be used to assess the skin friction, combined with direct force measurement. Since the vortical structure in the coherent turbulence structure influences on the skin friction in the high Reynolds number regime, the interaction between the turbulence structure and the surface wall is paying more attention. This sort of thing is important in the passive control of the turbulent boundary layer because the skin friction can't be determined only by wall condition. As complicated flow phenomena exist around a paint film, systematic measurement and analysis are necessary to evaluate the skin friction appropriately.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.4
• /
• pp.281-288
• /
• 2001

Phosphating treatments have been performed to improve paint adhesion and corrosion resistance of zinc and zinc alloy coated steels for a long time. In this work, the effects of the addition of chelate compound were studied to improve the stability of surface conditioning solution and properties of zinc phosphate films. The coalescence of colloidal Ti-compound and extraneous charged particles (alkaliearth metal cation such as $Mg^{2+}$ , $Ca^{2+}$ ) were suppressed by using a surface conditioning solution with chelate compound. Therefore, after surface conditioning solution containing chelate compound was left standing for one week at room temperature, the formation of a white sediment was decreased comparing to surface conditioning solution without chelate compound. The crystal size of phosphate film was fine and the whiteness value of phosphated zinc coated steel sheets was also high without the decrease of corrosion resistance and anti-patina. It was very effective to use chelate compound improving the stability of surface conditioning solution.

• Applied Chemistry for Engineering
• /
• v.5 no.4
• /
• pp.698-705
• /
• 1994

The basic medium oil modified alkyd resin was synthesized from linseed oil fatty acid(LOFA), phthalic anhydride(PAA), maleic anhydride(MA) and trimethylol propane(TMP) by condensation polymerization at $230^{\circ}C$. MA/TMPTA modified water-reducible alkyd resins were synthesized with TMPTA graft copolymerization onto the basic resin at $180^{\circ}C$. Acid value of the resin was controlled by the addition amount of MA and N,N-dimethylethanol amine(DMEA) was used as a neutralizing agent to prepare of the water-reducible alkyd resin. The effect of TMPTA on the graft copolymerization of the resin was studied by measuring molecular weight glass transition temperature(Tg), viscosity, graft efficiency, and gel contents of melanin cured film. Heat resistance, UV resistance and water resistance of cured film of MA/TMPTA modified resin was compared to those of TMA/TMPTA modified alkyd resin. The molecular weight, viscosity gel contents and graft efficiency of water reducible alkyd resin were increased according to the TMPTA graft copolymerization, but Tg was decreased. The viscosity was lower when the solid contents reached 40% than that of 30% content and also and also became lower with the extent of neutralization ratio, The heat resistance, UV resistance and water resistance of the MA/TMPTA modified alkyd resis were better than those of TMA/TMPTA modified alkyd resin but the storage stability of the TMA/TMPTA alkyd resis was better than that of MA/TMPTA modified alkyd resin.

• Journal of Adhesion and Interface
• /
• v.12 no.1
• /
• pp.34-42
• /
• 2011

The roll coating process is well-known for completely replacement coating system with an existing wet paint process for automotive which has low productivity and is not environment-friendly process. It is very important to evaluate the curing behavior, corrosion resistance and processing property as well as rheological behavior in order to realize a film flexibility and hardness simultaneously. In this study, we have synthesized the polyester resin modified with hydroxyl values and molecular weight to apply the pre-painted system, and then evaluated the curing behavior, deep drawing, tensile strength and rheological properties. It was observed that N-0375-40 of 40 (mg KOH/mol) hydroxyl values showed the most suitable for flexibility, film hardness, and curing behavior.

• Journal of Korea Multimedia Society
• /
• v.18 no.6
• /
• pp.734-741
• /
• 2015

Coating is a type of paint. It protects a product forming a film layer on the product and assigns various properties to the product. Coating is one of the fields which is being studied actively in the polymer industry. Importance of coating in various industries is more increased. However, mixing process has been performing in dependence on operator's experience. In this paper, we found the relationship between each data from coating formulation process. We propose a framework to analyze the coating formulation process as well. It can improve the coating formulation process. In particular, the suggested framework may reduce degradation and loss costs due to absence of standard data which is accurate formulation criteria. Also it suggests responses to errors which can be occurred in the future through the analysis of the error data generated in mixing step.

• Journal of the Korean Applied Science and Technology
• /
• v.19 no.4
• /
• pp.311-319
• /
• 2002

Environmental friendly acrylic/urea high-solid paint(MUHC) were prepared through the curing reaction of acrylics resin(EBHC) containing 70wt% of solids content and butylated urea curing agent. The synthesis of EBHC Was done at $150^{\circ}C$ for 6 hours, and the results were obtained as follows : $M_{n}=1830{\sim}2190$, $M_{w}$ $3290{\sim}4000$, $M_{w}/M_{n}$=1.80{\sim}1.83$ viscosity=$110{\sim}352$ cps, and conversion=$82{\sim}92$%. After the film was coated with MUHC, the various physical properties were measured. They showed that enhancement of the coating properties such as adhesion, flexibility, abrasion resistance, impact resistance, and water resistance could be expected through introdl1cing caprolactone acrylate component in acrylics resin for the high-solids content acrylics/urea coatings.

• Elastomers and Composites
• /
• v.48 no.2
• /
• pp.167-171
• /
• 2013

Weatherability was examined according to aluminum particle size and its orientation used in PCM(Paint Coated Metal). Substrate delamination was checked by different UV transmission rate with QUV$^{(R)}$ (Q-LAB) equipment that can make accelerated UV irradiation. Film was prepared using three different types of conflake aluminum pastes under a PCM coating process and clearcoat was sprayed. UV transmission test results showed low transmission rate when EKART #790 having the smallest particle size and horizontal orientation was used. From the gloss retention results, gloss retention was highest in EKART #790 and followed by #770, #750.

• Corrosion Science and Technology
• /
• v.5 no.1
• /
• pp.27-32
• /
• 2006

One of the critical issues in the coating specification is the allowable limit of surface contaminant(s) - such as soluble salt(s), grit dust, and rust - after grit blasting. Yet, there is no universally accepted data supporting the relationship between the long-term coating performance and the amount of various surface contaminants allowed after grit blasting. In this study, it was attempted to prepare epoxy coatings applied on grit-blasted steel substrate dosed with controlled amount of surface contaminants - such as soluble salt(s), grit dust, and rust. Then, coating samples were subjected to 4,200 hours of cyclic test(NORSOK M-501), which were then evaluated in terms of resistance to rust creepage, blistering, chalking, rusting, cracking and adhesion strength. Additional investigations on the possible damage at the paint/steel interface were carried out using an Electrochemical Impedance Spectroscopy(EIS) and observations of under-film-corrosion. Test results suggested that the current industrial specifications were well matched with the allowable degree of rust, whereas the allowable amount of soluble salt and grit dust after grit blasting showed a certain deviation from the specifications currently employed for fabrication of marine vessels and offshore facilities.