• The Research Journal of the Costume Culture
• /
• v.20 no.4
• /
• pp.463-474
• /
• 2012

The purpose of this research was to find the suitable dyeing method for dyeing cotton fabric into indigo blue color using the raw indigo powder dyes sold in the Korean market. The research focused primarily on the comparison of the non-reduced dyeing method and the reduced dyeing method. The dyeing effects using different dyeing temperatures ($2{\sim}80^{\circ}C$) and different concentrations of reducing agent and alkali were also investigated. It was found that the reduced dyeing method must be used for dyeing cotton into indigo blue color using the commercial raw indigo powder dyes. The best result was obtained by $20^{\circ}C$ dyeing with the $40^{\circ}C$ dyeing giving a comparable result. The intensity of the blue color could be enhanced by increasing the alkali concentration. The non-reduced dyeing could not dye cotton fabric into indigo blue color at any given dyeing temperatures ($2{\sim}80^{\circ}C$). The reduce-dyed cotton fabrics showed a gradual color change upon repeated washing and extended sunlight exposure, the most color change occurring after the first two washing cycles and the first 5 hours of sunlight exposure. The standard tests of colorfastness showed that the reduce-dyed cotton fabrics had good to excellent colorfastness whereas the colorfastness of the non-reduce-dyed cotton fabrics were mostly poor.

• The Research Journal of the Costume Culture
• /
• v.11 no.3
• /
• pp.431-440
• /
• 2003

The purpose of this study is to investigate the feasibility of applying the chitosan for a natural mordant. The chitosan, a natural chelate macromolecule, is acquired from the crustacean. Investigation was focused on the change of the dyeability according to the chitosan treatment based on the Caesalpinia sappan and the color change of the dyed fabric according to the application of heavy metal mordant. The change of air permeability of the fabric with the dyeing condition was also investigated systematically. The effect of dyeing with/without mordant on the air permeability of the fabric after the chitosan treatment. It seems that the increase in the dye-uptake is attributable to the fact that chitosan forms a complex with the Caesalpinia sappan and Al during mordant dyeing of cotton fabric. For nylon fabric, the darkest color was achieved on the occasion of non-mordant dyeing of the fabric. The mordant treatment or chitosan treatment, however, reduced the dyeability. While the dyed nylon fabric could maintain the same air permeability as the grey nylon fabric, the cotton fabric lowered the air permeability after dyeing.

• The Research Journal of the Costume Culture
• /
• v.24 no.6
• /
• pp.817-824
• /
• 2016

The introduction of natural dyes into modern dye houses is very promising green chemistry concept that should be popularized more to reduce the dependency of leather dyeing on some toxic and non-biodegradable synthetic dyes. In this study, the properties of dyeing of cochineal on cow leather were evaluated. The proper dyeing conditions were identified with dye uptake (K/S values) depending on the colorant concentration, dyeing duration, dyeing temperature, and dye bath pH. For the proper mordanting conditions, color changes for different mordants were observed as $La^{*}b^{*}$ and H V/C values. Color fastness (light, rubbing, and dry cleaning) was also examined. Additionally, antibacterial properties and UV protection were examined. The results were as follows: The optimized dyeing conditions were 300% o.w.f., $40^{\circ}C$, 40 min., and pH 5. The cow leather color was red in the absence of mordanting, while it was red purple after being mordanted with Al and Cu, and purple mordanted with Fe. The K/S value of cow leathers increased in the order of the dyeing using $AlK(SO_4)_2$ > $CuSO_4$ > $FeSO_4$. The colorfastness to light and rubbing were reduced compared to original (untreated) cow leather. However dry cleaning fastness was very satisfactory, with a 4~5 rating. The dyed and pre-mordanting dyed cow leather showed excellent antibacterial properties.

• Journal of the Korean Society of Costume
• /
• v.27
• /
• pp.121-132
• /
• 1996

This study showed the proper pigment extract in the Phe. Dyeing which is the basic dye of the natural plants dyeing,. Also it compared and examined the K/S the promotion of the color fastness and the effect of color difference change were attended by mordants and method of mordanting. 1. The most absorbance of Phellodendron. sol-ution is 330nm berberine is 430nm. 2. The best and proper temperature to extrat Phe,. was 80 and dyeing solution for 24 hours. 3. The pH effect was stable in the absorbances and color differences change. 4. Mordanted group increased the absorbances compared to non-mordanted sample. In case depth the most absorbance of Al. Sn. K. Cu and C. A solution were in 3% Fe and Cr were in 5%. In the color difference change they became dark reduced greenish and increased yellowish when their absorbances were in 3% 5. K./S was recoginzed by tainnin and fe, K/S was more increased pre-mordants than post-mordants. 6. Fe is the unchangable mordant in the color difference change and pre-mordants is more stable than post-mordants in the difference color. 7. Generally light C. F indicated more than grade 2 and light C. F, was much improved in post-mordanted by alumium potassium potass-ium dichromate. Washing C.F was improved in mordanted by tainnin and ferrous suulfate mordanted group was better than non-mordanted sample. Perspir-ation C,F was more stable in acid than alkali. Dry cleaning C.F indicated more than grade. 4.

• The Korean Journal of Community Living Science
• /
• v.28 no.1
• /
• pp.143-154
• /
• 2017

This study was conducted to develop fabrics using non-toxic and eco-friendly natural dyes made from curcuma and coffee extract. The natural dyes were applied to non-printed cotton fabrics using the dip dyeing method, and the pattern was hand-printed onto the dyed fabrics to make dyed printed-fabrics. The four types of developed fabric samples were compared to analyze the effects of the dyeing materials and printing on the hygienic properties of curcuma- and coffee-dyed fabrics. The findings were as follows. First, air permeability of both curcuma- and coffee-dyed fabrics was greatly affected by the presence of patterns, although the type of dye did not seem to have an effect. Printing greatly reduced air permeability of the fabric, and coffee-dyed fabric showed greater reduction of dyeing method than curcuma-dyed fabric. Moisture regain also tended to decrease with printing, but the change was much smaller compared to air permeability. Second, increased UV blockage was observed in curcuma- and coffee-dyed fabrics with patterns compared to non-printed fabrics, showing that printing enhanced UV blocking. Third, deodorization rate tended to increase sharply for both curcuma- and coffee-dyed fabrics until 30 minutes and gradually increased thereafter to yield 30% for curcuma and 50% for coffee at 120 minutes, demonstrating higher deodorization of coffee dye. Coffee-dyed fabric showed an antibacterial rate about twice as high as that of curcuma-dyed fabric, and the observed data suggest that curcuma-dyed fabric had an insignificant level of antibiosis. Fourth, printing significantly enhanced wash, sunlight, and compound colorfastness of the two types of dyed fabrics. The effect of printing was most dramatic on sunlight and compound colorfastness, which are aspects in which natural dyed fabrics perform poorly in general. Eventually, the development and application of biologically- and environmentally-friendly fabrics with natural dyes correspond with increased interest towards the wellness and healthy attitudes of modern society.

• Journal of Korea Society of Waste Management
• /
• v.35 no.7
• /
• pp.653-659
• /
• 2018

In the industrial wastewater that occupies a large proportion of river pollution, the wastewater generated in textile, leather, and plating industries is hardly decomposable. Though dyeing wastewater has generally been treated using chemical and biological methods, its characteristics cause treatment efficiencies such as chemical oxygen demand (COD) and suspended solids (SS) to be reduced only in the activated sludge method. Currently, advanced oxidation technology for the treatment of dyeing wastewater is being developed worldwide. Electro-coagulation is highly adapted to industrial wastewater treatment because it has a high removal efficiency and a short processing time regardless of the biodegradable nature of the contaminant. In this study, the effects of the current density and the electrolyte condition on the COD removal efficiency in dyeing wastewater treatment by using electro-coagulation were tested with an aluminum anode and a stainless steel cathode. The results are as follows: (1) When the current density was adjusted to $20A/m^2$, $40A/m^2$, and $60A/m^2$ under the condition without electrolyte, the COD removal efficiency at 60 min was 62.3%, 72.3%, and 81.0%, respectively. (2) The removal efficiency with NaCl addition was 7.9% higher on average than that with non-addition at all current densities. (3) The removal efficiency with $Na_2SO_4$ addition was 4.7% higher on average than that with non-addition at all current densities.

• Korean Journal of Materials Research
• /
• v.34 no.5
• /
• pp.254-260
• /
• 2024

This study is to manufacture a titanium dioxide (TiO₂) photocatalyst by recycling sludge generated using titanium tetrachloride (TiCl₄) as a coagulant. Compared to general sewage, a TiCl₄ coagulant was applied to dyeing wastewater containing a large amount of non-degradable organic compounds to evaluate its performance. Then the generated sludge was dried and fired to prepare a photocatalyst (TFS). Scanning electron microscope-energy dispersive X-ray spectroscopy (SEM-EDX), X-ray diffraction (XRD), and nitrogen oxide reduction experiments were conducted to analyze the surface properties and evaluate the photoactive ability of the prepared TFS. After using titanium tetrachloride (TiCl₄) as a coagulant in the dyeing wastewater, the water quality characteristics were measured at 84 mg/L of chemical oxygen demand (COD), 10 mg/L of T-N, and 0.9 mg/L of T-P to satisfy the discharge water quality standards. The surface properties of the TFS were investigated and the anatase crystal structure was observed. It was confirmed that the ratio of Ti and O, the main components of TiO₂, accounted for more than 90 %. As a result of the nitric oxide (NO) reduction experiment, 1.56 uMol of NO was reduced to confirm a removal rate of 20.60 %. This is judged to be a photocatalytic performance similar to that of the existing P-25. Therefore, by applying TiCl₄ to the dyeing wastewater, it is possible to solve the problems of the existing coagulant and to reduce the amount of carbon dioxide generated, using an eco-friendly sludge treatment method. In addition, it is believed that environmental and economic advantages can be obtained by manufacturing TiO₂ at an eco-friendly and lower cost than before.

• Journal of Korean Society of Water and Wastewater
• /
• v.20 no.1
• /
• pp.128-137
• /
• 2006

This study aims at developing the practical technology in the treatment of box-mill wastewater using the aerobic co-metabolism principle. The conventional activated sludge method exhibited the removal efficiency of $TBOD_5$ and $TCOD_{Mn}$ as 30~50% and 40~50%, respectively. Color was rather increased by 30~130% because the conventional treatment under the aerobic condition did not induce the conversion of molecular structure of dyeing agents. Meanwhile, when the aerobic co-metabolism principle was applied to the same wastewater, the removal efficiency of $TBOD_5$ and $TCOD_{Mn}$ were obtained as 92~97% and 90~94%, respectively. In particular, color was significantly reduced down to 65~85%. The enhancement of treatment efficiency was ascribed to occur not only that the non-degradables were converted to the second substrates, but also that the enzyme activity was increased as MLVSS was kept 3000mg/l or more with the first substrates injected.