• Journal of Powder Materials
• /
• v.13 no.3 s.56
• /
• pp.187-191
• /
• 2006

Al-Cu alloy nano powders were produced by the electrical explosion of Cu-plated Al wires. The composition and phase of the alloy could be controlled by varying the thickness of Cu deposit on Al wire. When the Cu layer was thin, Al solid solution and $CuAl_2$ were the major phases. As the Cu layer becomes thicker, Al diminished while $Al_4Cu_9$ phase prevailed instead. The average particle size of Al-Cu nano powders became slightly smaller from 63 nm to 44 nm as Cu layer becomes thicker. The oxygen content of Al-Cu powder decreased linearly with Cu content. It is well demonstrated that the electrodeposition combined with wire explosion could be simple and economical means to prepare variety of alloy and intermetallic nano powders.

• Proceedings of the KIEE Conference
• /
• 2009.04a
• /
• pp.30-32
• /
• 2009

In this study, $CuInS_2$ powders have been synthesized using polyol process of a mixture of copper nitrate, indium nitrate, and thiourea with various stoichiometric molar ratios in ethylene glycol at 196$^{\circ}C$. As boiling time goes by, the color of metal ion mixed solutions were changed transparent green to dark green and finally fumed to black by reduction of $OH^-$ radicals. The prepared powders were fully characterized by SEM, XRD and UV-Vis. The particle shape of black colored powders showed sphere with about 30 nm in particle size compared to those with dark green colored powders showed irregular shape with about 1 ${\mu}m$ in particle size. The XRD results showed highly crystallized $CuInS_2$. The UV-Vis spectra showed broad shoulder at 430 and 780 nm corresponding to 2.78 and 1.58 eV for the dark green colored one and black colored one, respectively.

• Journal of Powder Materials
• /
• v.21 no.3
• /
• pp.196-201
• /
• 2014

In this study, nanocrystalline Cu-Ni bulk materials with various compositions were cold compacted by a shock compaction method using a single-stage gas gun system. Since the oxide layers on powder surface disturbs bonding between powder particles during the shock compaction process, each nanopowder was hydrogen-reduced to remove the oxide layers. X-ray peak analysis shows that hydrogen reduction successfully removed the oxide layers from the nano powders. For the shock compaction process, mixed powder samples with various compositions were prepared using a roller mixer. After the shock compaction process, the density of specimens increased up to 95% of the relative density. Longitudinal cross-sections of the shock compacted specimen demonstrates that a boundary between two powders are clearly distinguished and agglomerated powder particles remained in the compacted bulk. Internal crack tended to decrease with an increase in volumetric ratio of nano Cu powders in compacted bulk, showing that nano Cu powders has a higher coherency than nano Ni powders. On the other hand, hardness results are dominated by volume fraction of the nano Ni powder. The crystalline size of the shock compacted bulk materials was greatly reduced from the initial powder crystalline size since the shock wave severely deformed the powders.

• Journal of the Korean Ceramic Society
• /
• v.39 no.4
• /
• pp.336-340
• /
• 2002

Pure and nano-sized $TiO_2$ and $CaTiO_3$ powders were fabricated by a polymeric steric entrapment route and planetary milling process. An ethylene glycol was used as a polymeric carrier for the preparation of organic-inorganic precursors. Titanium isopropoxide and calcium nitrate were dissolved in liquid-type ethylene glycol without any precipitation. At the optimum amount of the polymer, the metal cations were dispersed in solution and a homogeneous polymeric network was formed. The dried precursor ceramic gels were turned to porous powders through calcination process. The porous powders were crystallized at low temperatures and the crystalline powders were planetary milled to nano size.

• Korean Journal of Materials Research
• /
• v.11 no.11
• /
• pp.936-940
• /
• 2001

Spray pyrolysis is a favorable technique to form complex mixed-metal oxide powders with high purity in high temperature region. Manganese oxide powders were prepared by spray pyrolysis from an aqueous solution of $Mn(NO_3)_2$. Powders were formed in the temperature range of 500~$700^{\circ}C$ under the constant pressure of 300torr. All the powders have hydrous forms. When the temperature was increased, the size and the surface area of the particles decreased. An electrochemical capacitors were made with manganese oxide electrodes and KOH electrolyte. With the temperature decreased, capacitors showed high capacitance. Capacitor which was prepared with powders formed in the temperature $500^{\circ}C$ demonstrated specific capacitances as high as 83F/g.

• Transactions of the Korean hydrogen and new energy society
• /
• v.22 no.4
• /
• pp.504-511
• /
• 2011

Nano-sized Sn powder was prepared by pulsed wire evaporation method. The Sn powder and carbon black were charged in jar and ball milled. The milling time was varied with 10 min., 1h, 2h, and 4h, respectively. The milled powders were dried and the shape and size were observed by FE-SEM. Nano-sized Sn powders were plastic-deformed and agglomerated by impact force of balls and heat generated during the SPEX milling. The agglomerated Sn powder also consisted of many nano-sized particles. Initial discharge capacities of milled Sn electrode powders with carbon powder were milled for 10 min., 1h, 2h, and 4h were 787, 829, 827, and 816 mAh/g, respectively. After 5 cycle, discharge capacities of Sn electrode powders with carbon powder milled for 10 min., 1h, 2h, and 4h decreased as 271, 331, 351, and 287 mAh/g, respectively. Because Sn electrode powders milled for 2h constist of uniform and fine size, the cyclability of coin cell made of this powders is better than others.

• Journal of Powder Materials
• /
• v.17 no.2
• /
• pp.123-129
• /
• 2010

The fabrication of interconnect from titanium powders and $TiN_x$ powders is investigated. Corrosion-resistant titanium and $TiN_x$ are used as reinforcement in order to reveal high heat and corrosion resistance at the elevated temperature. We fabricated the plates for interconnect reinforced with $TiN_x$ by mixing titanium powders with 10 wt.% of nano-sized $TiN_x$. Spark Plasma Sintering (SPS) was chosen for the sintering of these composites. The plate made of titanium powders and $TiN_x$ powders demonstrates higher corrosion resistance than that of the plate of titanium powders alone. The physical properties of specimens were analyzed by performing hardness test and biaxial strength test. The electrochemical properties, such as corrosion resistance and hydrogen permeability at high temperature, were also investigated. The microstructures of the specimens were investigated by FESEM and profiles of chemical compositions were analyzed by EDX.

• Korean Journal of Materials Research
• /
• v.27 no.10
• /
• pp.513-517
• /
• 2017

An optimum route to fabricate a hybrid-structured W powder composed of nano and micro size powders was investigated. The mixture of nano and micro W powders was prepared by a ball milling and hydrogen reduction process for $WO_3$ and W powders. Microstructural observation for the ball-milled powder mixtures revealed that the nano-sized $WO_3$ particles were homogeneously distributed on the surface of large W powders. The reduction behavior of $WO_3$ powder was analyzed by a temperature programmed reduction method with different heating rates in Ar-10% $H_2$ atmosphere. The activation energies for the reduction of $WO_3$, estimated by the slope of the Kissinger plot from the amount of reaction peak shift with heating rates, were measured as 117.4 kJ/mol and 94.6 kJ/mol depending on reduction steps from $WO_3$ to $WO_2$ and from $WO_2$ to W, respectively. SEM and XRD analysis for the hydrogen-reduced powder mixture showed that the nano-sized W particles were well distributed on the surface of the micro-sized W powders.

• Nuclear Engineering and Technology
• /
• v.44 no.1
• /
• pp.9-20
• /
• 2012

A brief review on the thermal plasma synthesis of nano-sized powders is presented according to the application materials, such as, metals, ceramics, glasses, carbonaceous materials and other functional composites, such as, supported metal catalyst and core-shell structured nano materials. As widely adopted plasma sources available for thermal plasma synthesis of nanosized powders, three kinds of plasma torches, such as transferred and non-transferred DC and RF plasma torches, are introduced with the main features of each torch system. In the basis of the described torch features and the properties of suggested materials, application results including synthesis mechanism are reviewed in this paper.

• Transactions of Materials Processing
• /
• v.16 no.3 s.93
• /
• pp.210-214
• /
• 2007

Manufacturing bulk nanostructured materials with least grain growth from initial powders is challenging because of the bottle neck of bottom-up methods using the conventional powder metallurgy via compaction and sintering. In the study, densification behavior of nano Cu powders during pressureless sintering was investigated using an in-situ optical dilatometer technique. The initial heating and steady temperature stages during the sintering of nano Cu powder compacts were observed. At the initial heating stage, the powder compact has many porosities and full densification needs high temperature and/or high pressure sintering. In the experimental analysis, changes in geometry and density were measured and discussed for optimal consolidation and densification by the in-situ optical dilatometer.