Ultra-fine zirconium carbide (ZrC) powder with nano-sized primary particles was synthesized by the carbothermal reduction method by using nano-sized $ZrO_2$ and nano-sized graphite powders mixture. The synthesized ZrC powder was well dispersed after simple milling process. After heat-treatment at $1500^{\circ}C$ for 2 h under vacuum, ultra-fine ZrC powder agglomerates (average size, $4.2{\mu}m$) were facilely obtained with rounded particle shape and particle size of ~200 nm. Ultra-fine ZrC powder with an average particle size of 316 nm was obtained after ball milling process in a planetary mill for 30 minutes from the agglomerated ZrC powder.

• Journal of Applied Reliability
• /
• v.14 no.1
• /
• pp.11-19
• /
• 2014

A colloidal silica slurry has been manufactured by mixing nano silica powders having different grain size to improve the reliability of Sapphire wafer CMP process. The main reliability problem of CMP process such as the breaking of wafer can be prevented by reducing the size of particles in a slurry. While existing commercial colloidal silica slurries are usually made of single grain size silica powder of about 120nm, in the present study 40nm and 100nm silica powders are mixed to achieve a similar removal rate. The new colloidal silica slurry showed wafer removal rate of $3.04{\mu}m/120min$ while that of a commercial colloidal silica slurry was $3.03{\mu}m/120min$. The roughness was less than $4{\AA}$ and scratch was 0. It is also expected that the reduction of the size of nano silica particles can improve the dispersion stability and prolong the useful life of the slurry.

• Journal of Powder Materials
• /
• v.10 no.6
• /
• pp.430-435
• /
• 2003

The phenomenon of electrical explosion of conductors is considered in the context of the changes in the energy and structural states of the metal at the stages of energy delivery and relaxation of the primary products of EEC. It is shown that these changes are related to the forced interaction of an intense energy flux with matter and to the subsequent spontaneous relaxation processes. The characteristics of nano-sized metal powders are also discussed. The preferential gas media during EEC is Ar+$H_2$. An increase in $e/e_s$ (in the range of values studied) leads to a reduction in the metal content. For reactive powders obtained with high metal content, it is necessary to separate the SFAP fractions, which settled on the negative electrode of the electric filter.

• Journal of Powder Materials
• /
• v.15 no.1
• /
• pp.31-36
• /
• 2008

In this study, the bottom-up powder metallurgy and the top-down severe plastic deformation (SPD) techniques for manufacturing bulk nanomaterials were combined in order to achieve both full density and grain refinement without grain growth of rapidly solidified Al-20 wt% Si alloy powders during consolidation processing. Continuous equal channel multi-angular processing (C-ECMAP) was proposed to improve low productivity of conventional ECAP, one of the most promising method in SPD. As a powder consolidation method, C-ECMAP was employed. A wide range of experimental studies were carried out for characterizing mechanical properties and microstructures of the ECMAP processed materials. It was found that effective properties of high strength and full density maintaining nanoscale microstructure are achieved. The proposed SPD processing of powder materials can be a good method to achieve fully density and nanostructured materials.

• Korean Journal of Materials Research
• /
• v.11 no.10
• /
• pp.846-850
• /
• 2001

In the present study, nano-size powders of ternary ferrites, $Ni_{0.5}Zn_{0.5}Fe_2O_4$, as the potential catalysts of $CO_2$decomposition, were prepared by the wet processing of hydrothermal synthesis and coprecipitation method, and the catalyzing effects of impregnation of the noble metals, Pt and Pd, onto $Ni_{0.5}Zn_{0.5}Fe_2O_4$for the $CO_2$decomposition were investigated. XRD results of the synthesized ferrites showed a typical spinel structure of ferrite and the particle size was very small as about 6~10 nm. BET surface area of the ternary ferrites was not affected by the impregnation of Pt and Pd. The reactivity of the $CO_2$decomposition to carbon was improved by the impregnation of the noble metals of Pd and Pt. The effect of Pd-impregnation on the $CO_2$decomposition rate was higher than Pt-impregnation.

• Korean Journal of Materials Research
• /
• v.12 no.3
• /
• pp.169-175
• /
• 2002

Semiconductive nano $(Ba_{1-x}Sb_x)TiO_3$ powders were synthesized by the hydrothermal process and Sb was simultaneously doped in the hydrothermal condition. $(Ba_{1-x}Sb_x)TiO_3$ powders obtained from optimum condition(at 20$0^{\circ}C$ for 3hr) exhibited spherical shape, high purity and nano size. The PTCR characteristics was observed when 0.1 and 0.2 mole% Sb were added and sintered at over 130$0^{\circ}C$ for 1 hour, respectively. And The ceramics exhibit the PTCR characteristics with a resistively jump $ratio($\rho$_{max}/$\rho$_{min})$ of about $10^4$. Also we found that PTCR characteristics were dependent on the microstructure.