The boron-nitrogen-containing phenol-formaldehyde resin (BNPFR)/$SiO_2$ nanocomposites (BNPFR/$SiO_2$) were synthesized in-situ, and structure of BNPFR/$SiO_2$ nanocomposites was characterized by FTIR, XRD and TEM. The loss modulus peak temperature $T_p$ of BNPFR/$SiO_2$ nanocomposites cured with different nano-$SiO_2$ content are determined by torsional braid analysis (TBA). The thermal degradation kinetics was investigated by thermogravimetric analysis (TGA). The results show that nano-$SiO_2$ particulate with about 50 nm diameter has a more uniformly distribution in the samples. The loss modulus peak temperature $T_p$ of BNPFR/$SiO_2$ nanocomposite is $214^{\circ}C$ when nano-$SiO_2$ content is 6 wt%. The start thermal degradation temperature $T_{di}$ is higher about $30^{\circ}C$ than pure BNPFR. The residual rate (%) of nanocomposites at $800^{\circ}C$ is above 40 % when nano-$SiO_2$ content is 9 %. The thermal degradation process is multistage decomposition and following first order.

• 연구논문집
• /
• 통권26호
• /
• pp.103-112
• /
• 1996

$Al_2O_3/SiC$ Hybrid-Composite이 일반적인 분말공정에 의하여 제조되었다. 소결시 $\gamma-Al_2O_3에서 $\alpha-Al_2O_3$로의 전이에 seed역할을 하는 $\alpha-Al_2O_3의 첨가는 균일한 미세구조를 발달시켜 강도의 증진을 가져왔다. nano size의 SiC의 첨가는 $Al_2O_3$의 소결성과 입성장에 영향을 미쳐 파괴강도의 증진을 가져왔다. $Al_2O_3/SiC$ nano-Composite에 SiC plates의 첨가는 파괴강도의 감소를 가져왔지만, 상대적으로 파괴인성은 증진되었다. SiC plates에 nitride (BN, $Si_3N_4$ 코팅을 할 경우 crack deflection을 더욱 유발하여 파괴인성이 증진되었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 추계학술대회 논문집
• /
• pp.225-225
• /
• 2009

In this study, Nano and micro-filler mixture composites were fabricated by fixed value of $SiO_2$ nano-filler 0.4 [wt%] according to increase of $SiO_2$ micro-filler [wt%] from 1 to 10. Composites with a good dispersion of mixed $SiO_2$ Nano and micro-particles in the epoxy resins were prepared and experiments were performed to measure the dielectric breakdown strength properties with various temperature and thickness. The dielectric strength properties are compared and analyzed with respect to nano/micro-composites filled with $SiO_2$ fillers less than properties obtained for nanocomposites.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2007년도 추계학술대회 논문집
• /
• pp.118-119
• /
• 2007

Phase stability and morphological investigation on the $Si/SiO_2/HfO_2$ and $Si/SiO_2/ZrO_2$ stack are presented. Thermal stability of $HfO_2$ and $ZrO_2$ determines the quality of interface and subsequently the performance of device. The stacks have been fabricated and annealed at $1000^{\circ}C$ for various time. In evolution of crystalline phase and morphology (electrical and geometrical) of high-k materials, annealing time and process are observed to be crucial factors. The crystallization of some phase has been observed in the case of $Si/SiO_2/HfO_2$. The chemical environment around Zr and Hf in respective samples is observed to be different.

• 한국자기학회지
• /
• 제18권1호
• /
• pp.43-47
• /
• 2008

[ $ZnO-Bi_2O_3-Al_2O_3-B_2O_3-SiO_2$ ] nano-glass를 sol-gel 법으로 제조 하였다. 평균 입자 크기는 60.3 nm였으며 매우 균일한 입도 분포를 가졌다. Nano-glass를 NiZnCu ferrite의 저온소성용 소결조제로 사용하였으며 NiZnCu ferrite에 nano-glass를 첨가한 후 $840{\sim}900^{\circ}C$에서 2시간 소결을 진행하였다. 소결성 및 자기적 특성에 대해 연구하였으며 밀도, 수축율, 초투자율, 품질계수, 및 포 화자화값을 측정하였다. nano-glass를 0.5 wt% 첨가하여 $900^{\circ}C$에서 소결한 토로이달 core 시편의 초투자율은 1 MHz에서 측정 시 193.3의 값을 가졌다. 초투자율과 포화자화값은 소결온도가 증가함에 따라 증가하는 경향을 나타내었다. sol-gel 법에 의해 제조된 $ZnO-Bi_2O_3-Al_2O_3-B_2O_3-SiO_2$ nano-glass를 칩인덕터용 NiZnCu ferrite의 저온 소결조제로 사용 가능함을 알 수 있었다.

• 대한기계학회논문집A
• /
• 제33권11호
• /
• pp.1233-1238
• /
• 2009

This study analyzed the characterization of high temperature strength of $Si_3N_4$ composite ceramics additive based on variations in the amount of nano colloidal $SiO_2$ added. Semi-elliptical cracks about 100 ${\mu}m$ length were obtained from a Vickers indenter using a load of 24.5 N. The results showed that the heat-treated smooth specimens with $SiO_2$ nano colloidal coating exhibited the highest bending strength at 0.0 wt% $SiO_2$ nano colloidal added, which is amounted to a 187 % increase over that of smooth specimen. Limiting temperature for bending strength of crack-healed zone for bending strength was about 1273 K. However, the bending strength of SSTS-3 and SSTS-4 was considerably increased while that of SSTS-1 and SSTS-2 was decreased at a temperature of 1,573K.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2003년도 추계총회 및 연구발표회 초록집
• /
• pp.82.2-82
• /
• 2003

• 한국재료학회지
• /
• 제19권1호
• /
• pp.50-53
• /
• 2009

Multi-walled carbon nanotubes (MWNTs) were synthesized on different substrates (bare Si and $SiO_2$/Si substrate) to investigate dye-sensitized solar cell (DSSC) applications as counter electrode materials. The synthesis of MWNTs samples used identical conditions of a Fe catalyst created by thermal chemical vapor deposition at $900^{\circ}C$. It was found that the diameter of the MWNTs on the Si substrate sample is approximately $5{\sim}10nm$ larger than that of a $SiO_2$/Si substrate sample. Moreover, MWNTs on a Si substrate sample were well-crystallized in terms of their Raman spectrum. In addition, the MWNTs on Si substrate sample show an enhanced redox reaction, as observed through a smaller interface resistance and faster reaction rates in the EIS spectrum. The results show that DSSCs with a MWNT counter electrode on a bare Si substrate sample demonstrate energy conversion efficiency in excess of 1.4 %.

• 한국세라믹학회지
• /
• 제34권4호
• /
• pp.406-412
• /
• 1997

Al2O3/SiC hybrid-composite has been fabricated by the conventional powder process. The addition of $\alpha$-Al2O3 as seed particles in the transformation of ${\gamma}$-Al2O3 to $\alpha$-Al2O3 provided a homogeneity of the microstructure. The grain growth of Al2O3 are significantly surpressed by the addition of nano-size SiC particles. Dislocation were produced due to the difference of thermal expansion coefficient between Al2O3 and SiC and piled up on SiC particles in Al2O3 matrix, resulting in transgranular fracture. The high fracture strength of the composite was contributed to the grain refinement and the transgranular fracture mode. The addition of SiC platelets to Al2O3/SiC nano-composite decreased the fracture strength, but increased the fracture toughness. Coated SiC platelets with nitrides such as BN and Si3N4 enhanced fracture toughness much more than non-coated SiC platelets by enhancing crack deflection.