• 한국세라믹학회지
• /
• 제31권3호
• /
• pp.275-281
• /
• 1994

Mullite ceramics have recently been utilized as ceramic gas filters for high-temperature treatment of solid wastes due to their low thermal expansion coefficient and high refractoriness under load. In this experiment, mechanical, thermal and microstructural properties of porous mullite ceramics, which were used as carriers and high-temperature gas filters in food industry, were investigated as a function of starting raw materials. Porous mullite ceramics showed different microstructures depending on their starting materials. The specimen M2 had excellent resistance to thermal spalling and high mechanical strength. The average pore size varied from 0.3 ${\mu}{\textrm}{m}$ to 16.6 ${\mu}{\textrm}{m}$, and porous mullite ceramics fabricated by thermal decomposition of Al(OH)3 had very large pores and broad distribution of pore size.

• The Korean Journal of Ceramics
• /
• 제5권2호
• /
• pp.137-141
• /
• 1999

To increase the strength of high-purity porous mullite ceramics, ultra fine mullite precursor powders of about 10nm in diameter were deposited at point of contact between primary coarse mullite particles of about 60$\mu\textrm{m}$. The deposited and hetero coagulated structures of ultra fine mullite precursor powders were controlled by pH. The optimum pH condition to form a uniform deposition of mullite powders between coarse mullite particles was in the range from 7 to 8. Deposition of the ultra fine powders did not form at pH < 7 and pH > 10 irregular deposition was observed from pH 8 to 9.

• 한국세라믹학회지
• /
• 제42권11호
• /
• pp.753-757
• /
• 2005

In this study, we attempted to recycle the fly ash as a mullite whisker with addition of $Al_{2}O_{3}$ to obtain the high yield of mullite whisker. During the reaction process, mullite whisker was formed with the reaction of amorphous $\alpha$-Cristobalite and Anorthite above $1350^{\circ}C$. With increasing the heat treatment temperature and time, the mean length and aspect ratio of mullite whiskers was gradually increased.

• 한국결정성장학회지
• /
• 제30권1호
• /
• pp.27-32
• /
• 2020

점토, 규석, 장석을 사용하여 만든 전통생활도자기는 주 결정상이 mullite와 cristobalite이다. Mullite 결정은 제품의 강도를 좋게 하지만 열팽창계수가 5.3 × 10^-6/℃로 비교적 커서 내열 도자기로는 사용할 수 없다. 본 연구에서는 산청토와 장수곱돌 sludge를 사용하여 도자기 내에 mullite 결정 대신 열팽창 계수가 2.6 × 10^-6/℃인 cordierite 결정이 생성되게 함으로써 가벼운 내열 도자기를 개발하고자 하였다. 그 결과 산청토 80 wt%, 장수곱돌 sludge 20 wt%를 사용하여 만든 도자기가 내열성이 좋고 강도와 하중연화도 우수하였으며, 부피비중도 1.7 8로 기존의 분청사기보다 가벼웠다.

• The Korean Journal of Ceramics
• /
• 제2권4호
• /
• pp.231-237
• /
• 1996

Mullite ceramics can be sintered by rf plasma sintering to densities as high as 97% compared to the theoretical density of the mullite, while SiC whisker-reinforced mullite matrix ceramic composites were not sintered by plasma sintering. Decomposition of mullite occurs in a superficial regins at the outside surface of the specimen by volatilization of SiO at elevated temperature by plasma. SiC whiskers were destroyed, and the matrix was converted to alumina from SiC-whisker reinforced mullite matrix ceramic composites during the plasma sintering. Accelerated volatilization from the SiC whisker in the mullite prevents sintering. The volatile species are mainly SiC and CO gas species. The effects of plasma on mullite and SiC-whisker reinforced mullite matrix composites are interpreted by thermodynamic simulation of the volatile species in the plasma environment. The thermodynamic results show that the decomposition will not occur during hot pressing.

• 한국세라믹학회지
• /
• 제52권6호
• /
• pp.423-428
• /
• 2015

The machinability of materials is an important factor in engineering applications. Many ceramic components that have complex shapes require machining, typically using diamond tools, which leads to high production cost. Machinable ceramics containing h-BN have recently been developed, but these materials are very expensive because of high cost of raw materials and machining. Therefore the development of low-cost machinable ceramics is desirable. In this study, mullite-$ZrO_2$ ceramics were prepared additions of $Al_2TiO_5$. $ZrSiO_4$, $Al_2O_3$, and $Al_2TiO_5$ powders mixed at various molar ratios with sintering at 1400, 1500, and $1600^{\circ}C$ for 1 hr. Phase formation and microstructure of the sintered ceramics were observed by XRD and SEM, respectively. The machinability of each specimen was tested using the micro-hole machining method. The machinability results show that the ceramics sintered at temperatures over $1500^{\circ}C$ can be used as good low-cost machinable mullite-$ZrO_2-Al_2TiO_5$ ceramics.

• 한국세라믹학회지
• /
• 제47권6호
• /
• pp.509-514
• /
• 2010

Porous mullite-bonded SiC (MBSC) ceramics were fabricated at temperatures ranging from 1400 to $1500^{\circ}C$ for 2 h using silicon carbide (SiC), alumina ($Al_2O_3$), strontium oxide (SrO), and poly (methyl methacrylate-coethylene glycol dimethacrylate) (PMMA) microbeads. The effect of template content on porosity, pore morphology, and flexural strength were investigated. The porosity increased with increasing the template content at the same sintering temperature. The flexural strength showed maximum after sintering at $1450^{\circ}C$/2 h for all specimens due to small pores and dense strut. By controlling the template content and sintering temperature, it was possible to produce porous MBSC ceramics with porosities ranging from 30% to 54%. A maximum flexural strength of ~51MPa was obtained at 30% porosity when no template were used and specimens sintered at $1450^{\circ}C$/2 h.

• 한국세라믹학회지
• /
• 제36권6호
• /
• pp.671-678
• /
• 1999

Porous ceramics were fabricated from pressureless powder packing forming method using mullite and cordierite powders granulate by spray drying. The bending strength and shrinkage of porous ceramics were increased and their porosity were decreased with increasing temperature. It showed homogeneous distribution of 2$\mu\textrm{m}$ intergranular pores of mullite at 1400$^{\circ}C$, 2.5$\mu\textrm{m}$ intergranular pores of cordierite at 1300$^{\circ}C$ respedtively. Above that temperature intragranular particles were sintered and sintering by intergranular necking was extremely proceeded. In the test of thermal shock resistance sudden decrease of bending strength to $\Delta$T was not shown because intergranular large pore prevented sudden crack propagation.

• 동력기계공학회지
• /
• 제6권1호
• /
• pp.88-95
• /
• 2002

본 연구에서는 균열 치유 거동을 가지는 소결된 Mullite/SiC의 모재, 열처리재, 균열재, 치유 균열재의 기계적 특성이 논의되었다. 반타원형 균열의 치수는 $100{\mu}m$ 과 $200{\mu}m$이다. 얻어진 결과는 다음과 같다. (a) Mullite/SiC 복합 세라믹스는 균열 치유 능력이 있었다. (b) 최적의 균열 치유 열처리 조건은 $1300^{\circ}C$, 1시간이었다. (c) 치유 가능한 최대 균열 길이는 직경 $100{\mu}m$의 반타원 균열이다. (d) 균열 치유부는 $1200^{\circ}C$이상에서 충분한 강도를 가졌고, 대부분의 시험편은 균열 치유부 이외의 영역에서 파단 하였다. (e) 공기중에서 예열처리는 본 재료의 피로강도 향상에 유용하였다.

• 한국재료학회지
• /
• 제26권2호
• /
• pp.61-66
• /
• 2016

In order to fabricate porous mullite ceramics with controlled pore structure and improved mechanical strength, a freeze casting route has been processed using camphene mixed with tertiary-butyl alcohol (TBA) and coal fly ash/alumina as the solvent and the ceramic material, respectively. After sintering, the solidification characteristics of camphene and TBA solvent were evident in the pore morphology, i.e., dendritic and straight pore channels formed along the solidification directions of camphene and TBA ice, respectively, after sublimation. Also, the presence of microcracks was observed in the bodies sintered at $1500^{\circ}C$, mainly due to the difference in solidification volume change between camphene and TBA. The compressive strength of the sintered bodies was found generally to be dependent, in an inverse manner, on the porosity, which was mainly determined by the processing conditions. After sintering at $1300{\sim}1500^{\circ}C$ with 30~50 wt% solid loading, the resulting mullite ceramics showed porosity and compressive strength values in ranges of 83.8~43.1% and 3.7~206.8 MPa, respectively.