Development of heat resistant body using Sanchung Kaolin and Jangsu gobdol sludge

The main cystal phases of traditional ceramics made of clay, quartz, and feldspar are mullite and cristobalite. Although mullite can provide strength to the ceramic body, it cannot be used for the heat resistant ceramics because the thermal expansion coefficient of it is relatively high as 5.3 × 10^-6/℃. In this study, development of lightweight heat resistant ceramics was tried by producing cordierite phase, of which the thermal expansion coefficient is 2.6 × 10^-6/℃, instead of forming mullite phase in the ceramic body by using Sanchung Kaolin and Jangsu gobdol sludge. It was concluded that ceramics having good heat resistant, bending strength, and refractoriness under load could be fabricated when 80 wt% of Sanchung Kaolin and 20 wt% of Jangsu gobdol sludge were used as raw materials. Also, the bulk specific gravity is 1.78, which is lighter than the existing Buncheong ware.

산청고령토와 장수곱돌 슬러지를 사용한 내열소지 개발

점토, 규석, 장석을 사용하여 만든 전통생활도자기는 주 결정상이 mullite와 cristobalite이다. Mullite 결정은 제품의 강도를 좋게 하지만 열팽창계수가 5.3 × 10^-6/℃로 비교적 커서 내열 도자기로는 사용할 수 없다. 본 연구에서는 산청토와 장수곱돌 sludge를 사용하여 도자기 내에 mullite 결정 대신 열팽창 계수가 2.6 × 10^-6/℃인 cordierite 결정이 생성되게 함으로써 가벼운 내열 도자기를 개발하고자 하였다. 그 결과 산청토 80 wt%, 장수곱돌 sludge 20 wt%를 사용하여 만든 도자기가 내열성이 좋고 강도와 하중연화도 우수하였으며, 부피비중도 1.7 8로 기존의 분청사기보다 가벼웠다.