• 한국결정성장학회지
• /
• 제10권1호
• /
• pp.48-54
• /
• 2000

kaolin과 수산화알루미늄을 이용하여 mullite를 합성하는데 있어서 출발원료의 조성을 silica rich, stoichiometric, alumina rich 조성으로 준비하여 각각의 원료로부터 mullite를 합성할 때 mullite-seed가 미치는 영향을 연구하였다. 그 결과 silica rich 조성과 stoichiometric 조성에서는 mullite-seed의 첨가량이 증가할수록 꺾임강도값이 증가하며, alumina rich 조성에서는 mullite-seed의 첨가량이 증가할수록 꺾임강도값은 감소하는 경향을 보였다. 같은 양의 mullite-seed를 첨가했을 때 미세구조는 alumina 첨가 함량이 증가할수록 치밀도가 감소하고, aspect ratio는 증가하는 경향을 나타내었다. 순도면에서는 mullite정량결과 모든 조성에서 mullite-seed의 첨가량이 많을수록 합성된 mullite 결정상의 함량이 증가하는 경향을 보였다.

• 한국분말재료학회지
• /
• 제4권1호
• /
• pp.9-17
• /
• 1997

The mullite-zirconia composites were prepared by the pressureless sintering with addition of 10~20 vol% ZrO$_2$(TZ3Y) in the fused mullite and sol-gel mullite matrix. The densification rate of sol-gel mullite was higher than that of fused mullite, and the addition of ZrO$_2$(TZ3Y) was effective on the densification of fused mullite. The enhancement of densification and anisotropic growth of mullite in ZrO$_2$added specimen can be explained by the solid solution effect of $Zr^{+4}$ ion in mullite. Both mechanical strength and fracture toughness of mullite-zirconia composite were enhanced compared to those of mullite. The enhancement of mechanical properties is attributed to the hinderance of grain growth and the combined toughening effects of tetra-mono phase transformation and crack deflection due to the residual stress between mullite/ZrO$_2$.

• 한국세라믹학회지
• /
• 제35권8호
• /
• pp.878-884
• /
• 1998

Synthesis of high purity mullite from korean resourceful kaolin and water-soluble aluminium salts was in-vestigated by addition of mullite seed. Single phase of mullite was formed at 1350$^{\circ}C$ however its mullite con-tent was 31-33% Maximum content of mullite synthesized from kaoin aluminium nitrate and 8wt% mul-lite seed was 98% at 1600$^{\circ}C$ for 4 hours.

• 한국세라믹학회지
• /
• 제38권2호
• /
• pp.238-238
• /
• 2001

본 연구에서는 kaolin을 이용하여 반기상법, gel coating법, seed 첨가법으로 mullite를 합성하였으며 mullite 15 wt%를 고 알루미나질 내화물 원료에 첨가하여 내화물 시편을 제조하였다. 제조된 시편의 물성을 분석한 결과 seed 첨가법으로 제조된 mullite를 첨가한 시편의 물성이 338.60 MPa의 꺾임강도와 9,427 kgf/㎠의 압축강도값을 나타내었다. 제조된 시편의 내화도 및 잔존선팽창수축률을 측정한 결과 나머지 두가지 방법으로 합성한 mullite나 일반적인 고 알루미나질 내화물에 비하여 좋은 특성을 나타내었다.

• 한국세라믹학회지
• /
• 제38권3호
• /
• pp.238-244
• /
• 2001

본 연구에서는 Seed 첨가법에 의하여 제조된 mullite(Syn M)와 외국산 mullite 2종류(sintered mullite : SM, fused mullite : FM)를 고알루미나질 내화물 원료에 적용하여 내화물 시편을 제조하였으며 mullite에 따른 결정상, 미세구조, 부피비중, 강도를 조사하였다. SM, FM, Syn M의 mullite 함유량은 93.17%, 86.79%, 97.57%이었으며 mullite를 15 wt% 첨가하여 제조한 시편의 물성을 조사한 결과 Syn M을 함유한 시편이 꺾임강도 338.60 MPa, 압축강도 9,427kgf/$\textrm{cm}^2$을 나타내었다. 외국산 mullite를 첨가한 시편의 강도는 Syn M을 첨가한 것보다 약 5~10% 정도 낮은 강도를 보였다.

• 한국세라믹학회지
• /
• 제27권2호
• /
• pp.201-210
• /
• 1990

The mullite-15v/o ZrO2 composites were prepared by dispersing ZrO2-3m/o Y2O3 powders into the mullite matrix in order to improve the mechanical properties of the mullite. The densification and retention of t-ZrO2 in the matrix of synthetic mullite were also investigated. From IR spectroscopic analysis, the obtained amorphous SiO2-Al2O3 powder was observed to have Si-O-Al chemical bond in its structure which might result in the homogeneous mullite composition. The lattice parameter of the mullite powder calcined above 130$0^{\circ}C$ (a0=7.5468$\AA$) is nearly close to the value of stoichiometric mullite (71.8wt% Al2O3, a0=7.5456$\AA$). The sintering behavior, microstructure, flexural strength and fracture toughness of the mullite and mullite-15v/o ZrO2 composites have been studied. The mullite-15v/o ZrO2(+3m/o Y2O3) ceramics with relative densities of 96% were obtained when sintered at 1$600^{\circ}C$. The flexural strength and fractrue toughness of the composites sintered at 1$600^{\circ}C$(calcination temperature of mullite powders ; 125$0^{\circ}C$) had maximum values of 307MPa and 2.50MPa.m1/2, respectively. The fracture toughness improvement in the mullite-ZrO2 cmoposite is assumed to be resulted from the combined effect of the stress-induced phase transformation of tetragonal ZrO2 and the crack deflection due to microcracking by the monoclinic ZrO2 formation.

• The Korean Journal of Ceramics
• /
• 제2권4호
• /
• pp.231-237
• /
• 1996

Mullite ceramics can be sintered by rf plasma sintering to densities as high as 97% compared to the theoretical density of the mullite, while SiC whisker-reinforced mullite matrix ceramic composites were not sintered by plasma sintering. Decomposition of mullite occurs in a superficial regins at the outside surface of the specimen by volatilization of SiO at elevated temperature by plasma. SiC whiskers were destroyed, and the matrix was converted to alumina from SiC-whisker reinforced mullite matrix ceramic composites during the plasma sintering. Accelerated volatilization from the SiC whisker in the mullite prevents sintering. The volatile species are mainly SiC and CO gas species. The effects of plasma on mullite and SiC-whisker reinforced mullite matrix composites are interpreted by thermodynamic simulation of the volatile species in the plasma environment. The thermodynamic results show that the decomposition will not occur during hot pressing.

• 한국세라믹학회지
• /
• 제41권9호
• /
• pp.663-669
• /
• 2004

Mullite와 cordierite는 우수한 열적, 화학적 특성을 나타내는 안정된 산화물로서 다양한 구조재료 및 전자재료에 사용되어지고 있으나, mullite의 경우 내열충격성이, cordierite의 경우 고온강도가 떨어지는 단점이 있다. 이와 같은 단점을 서로 보완하기 위한 mullite-cordierite 복합체에 대한 연구가 진행되고 있다 본 연구에서는 fused silica, aluminium nitrate, magnesium nitrate와 PVA의 혼합을 이용한 solution-polymerization 합성법에 의해, mullite-cordierite복합분말을 합성하고 생성상 및 결정성, 밀도 및 비표면적 등의 특성을 분석하였다 그 결과, 본 실험의 모든 조성에서 있어서 130$0^{\circ}C$로 열처리하였을 경우, mullite와 cordierite의 상이 공존하는 복합분말이 생성되는 것을 확인할 수 있었다. 이 mullite-cordierite복합 분말을 planetary milli로 1시간 분쇄하였을 때 비표면적은 약 20 $m^2$/g로서 미립의 분말이 확인되어졌고, 분쇄시간의 증가에 따라 4시간에서는 23$m^2$/g, 8시간에서는 24$m^2$/g로 비표면적이 증가하였다.

• 한국세라믹학회지
• /
• 제38권1호
• /
• pp.9-14
• /
• 2001

본 연구는 우리나라 하동지방에서 다량으로 산출되는 저급 Kaoline을 활용하여 Mullite를 합성하는데 목적이 있다. 저질 Kolin을 AlF$_3$와 충분히 혼합한 후 130$0^{\circ}C$에서 반응시키면 거의 순간적으로 Mullite의 합성이 가능하였으며 이때에 얻어진 Mullite는 X-ray 회절결과 순수한 Mullite 단일상으로 나타났으며 소결체의 특성에 보면 1$600^{\circ}C$ 3시간 소결 후 비중은 2.8g/$m^2$이며 굽힘강도는 170 MPa을 나타내었다.

• 한국세라믹학회지
• /
• 제38권2호
• /
• pp.128-136
• /
• 2001

본 연구에서는 kaolin을 이용하여 반기상법, gel coating법, seed 첨가법으로 mullite를 합성하였으며 mullite 15 wt%를 고 알루미나질 내화물 원료에 첨가하여 내화물 시편을 제조하였다. 제조된 시편의 물성을 분석한 결과 seed 첨가법으로 제조된 mullite를 첨가한 시편의 물성이 338.60 MPa의 꺾임강도와 9,427 kgf/$\textrm{cm}^2$의 압축강도값을 나타내었다. 제조된 시편의 내화도 및 잔존선팽창수축률을 측정한 결과 나머지 두가지 방법으로 합성한 mullite나 일반적인 고 알루미나질 내화물에 비하여 좋은 특성을 나타내었다.