• Journal of the Korean Wood Science and Technology
• /
• v.42 no.5
• /
• pp.605-614
• /
• 2014

This study investigated microstructural changes of cured urea-formaldehyde (UF) resins mixed with aqueous rubber latex emulsion after intentional acid etching. Transmission electron microscopy (TEM) was used in order to better understand a hydrolytic degradation process of cured UF resins responsible for the formaldehyde emission from wood-based composite panels. A liquid UF resin with a formaldehyde to urea (F/U) molar ratio 1.0 was mixed with a rubber latex emulsion at three different mixing mass ratios (UF resin to latex = 30:70, 50:50, and 70:30). The rate of curing of the liquid modified UF resins decreased with an increase of the rubber latex proportion as determined by differential scanning calorimetry (DSC) measurement. Ultrathin sections of modified and cured UF resin films were exposed to hydrochloric acid etching in order to mimic a certain hydrolytic degradation. TEM observation showed spherical particles and various cavities in the cured UF resins after the acid etching, indicating that the acid etching had hydrolytically degraded some part of the cured UF resin by acid hydrolysis, also showing spherical particles of cured UF resin dispersed in the latex matrix. These results suggested that spherical structures of cured UF resin might play an important role in hindering the hydrolysis degradation of cured UF resin.

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.5
• /
• pp.11-23
• /
• 2008

The mechanical and physical properties of zinc borate (ZB)-modified oriented strandboard (OSB) from southern wood species were investigated in this study. OSB panels treated with ZB were not significantly weaker than the untreated samples in terms of specific modulus of elasticity (SMOE) and specific modulus of rupture (SMOR). ZB showed the negative effect on specific internal bond (SIB) strength, since some of ZB would persist as a powder state on the flake surfaces, thereby reducing the bonding efficiency of the adhesive. The ZB level did not show significant effect on thickness swelling (TS). ZB-modified OSB showed the suitable mechanical and physical properties for the structural wood composites.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.3
• /
• pp.315-325
• /
• 2020

Boron compound had many advantages as wood preservative, but it was prone to leaching. Improving boron preservation was required to extend the service life of fast growing and low durability red jabon (Antochephalus macrophyllus) hardwood. This study aimed to evaluate the dimensional stability, color change and durability of modified red jabon wood by double impregnation with boron and methyl methacrylate (MMA) and heat treatment. Impregnation I used boric acid or borax, and impregnation II used MMA, while heat treatment used temperatures of 90 ℃ or 180 ℃ for 4 hours. The dimensional stability, leachability, water absorption, color change and decay resistance of modified red jabon wood were tested. The results showed that MMA impregnation increased the dimensional stability of red jabon wood, while the leaching and water absorption in the wood significantly reduced. Heating at 180 ℃ caused less water absorption and higher dimensional stability of the wood than that of heating at 90 ℃. Impregnation with boric acid and MMA followed by heating at 90 ℃ resulted in the highest wood ASE, 89.9%. The color change (∆E^*) of wood increased significantly after MMA impregnation and heating at 180 ℃. Boric acid impregnation caused more resistant wood than borax impregnation against decay fungi and termites. Impregnation with boric acid and MMA followed with heating at 180 ℃ increased significantly the wood resistance against decay fungi and termites.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.2
• /
• pp.204-217
• /
• 2016

Modified poplar has emerged as a potential raw material for furniture production. Lack of specific modified poplar strength information; however, restricts applications in the furniture industry especially as related to strength in corner-joints. Optimization of strength in L-shaped corner dowel modified poplar joints under compression loads utilizing finite element analysis (FEA) by Taguchi method with the focus of this study. Four experiment factors (i.e., Structure Style, Tenon Length, Tenon Diameter, and Tenon Gap), each at three levels, were conducted by adopting a $L_9-3^4$ Taguchi orthodoxy array (OA) to determine the optimal combination of factors and levels for the von Mises stress utilizing ANSYS software. Results of Signal-to-Noise ratio (S/N) analysis and the analysis of variance (ANOVA) revealed the optimal L-shaped corner dowel joint in modified poplar is $45^{\circ}$ Bevel Butt in structure style, 24 mm in tenon length, 6 mm in tenon diameter, and 20 mm in tenon gap. Tenon length and tenon gap are determined to be significant design factors for affecting von Mises Stress. Confirmation tests with optimal levels and experimental test indicated the predicted optimal condition is comparable to the actual experimental optimal condition.

• Applied Chemistry for Engineering
• /
• v.10 no.1
• /
• pp.46-50
• /
• 1999

Effects of $(NH_4)_2HPO_4$ and boron compounds ($Na_2B_4O_7:H_3BO_3=5:1\;ratio$) on the flame retarding characteristics of the surface modified wood powder-filled polypropylene composites were studied experimentally. The mechanical properties of m-phenylene dimaleimide(PDMI)-modified polypropylene composite were also compared with those of unmodified one. The flame retardance of $(NH_4)_2HPO_4$-modified wood powder composites was more improved than that of boron compounds-modified one. The impact strength of composites increased and the tensile strength of those decreased progressively with an increase of wood powder loading. The mechanical properties of modified polypropylene composites are more improved than those of unmodified one. The tensile strength also increased marginally with increasing the concentration of flame retardants, yielding a maximum when the concentration of flame retardant is 25.0 wt %. And the tensile strength of the composite was increased up to 16 wt % with increasing concentration of PDMI.

• Journal of the Korean Wood Science and Technology
• /
• v.39 no.1
• /
• pp.21-27
• /
• 2011

This study was carried out to examine properties of water resistant plywood by using serum protein adhesive which is natural, environment-friendly and human-friendly. For the preparation of the serum protein adhesive, pig blood from slaughterhouse was centrifuged and serum was separated from corpuscles and concentrated to 30% by dry weight basis. This concentrated serum protein was modified with PF resin (50% NVC) with the ratio of 9 : 2.5. Plywood made by this modified serum protein gave 1.21 N/$mm^2$ of dry bonding strength, 0.80 N/$mm^2$ of wet boil bonding strength, 0% of cyclic delamination test value, and 0.025 ppm of HCHO emission, which met the excellent super $E_0$ grade and water resistant plywood.

• Journal of the Korean Wood Science and Technology
• /
• v.28 no.1
• /
• pp.36-41
• /
• 2000

This study was carried out to introduce functional groups onto wood by reacting with 2-methacryloyloxyethyl isocyanate(MOI). The effects of the catalyst and the reaction conditions(temperature and time) on the treatment were investigated. The evidence of bonding between wood and MOI were examined by infrared(IR) spectroscopy. The change in surface characteristics of MOI treated wood was examined by water contact angle measurement and X-ray photoelectron spectroscopy(XPS). Wood reacted quickly with MOI in the presence of di-n-butiltin dilaurate catalyst. Especially, the increase in weight percent gain(WPG) with increasing in reaction time was remarkable at the reaction temperature of over $50^{\circ}C$. The IR spectrum of wood reacted with MOI showed a strong urethane absorption(1715 $cm^{-1}$) but no isocyanate(2235 $cm^{-1}$) absorption. It also showed a sharp olefinic C=C double bond absorption at 1635 $cm^{-1}$. This means that an introduced methacrylate group becomes the starting point of further graft copolymerization with another vinyl monomers. The wood modified with MOI showed a gradual increase in contact angle with increasing in WPG, which means that the hydrophilic wood surface become quite hydrophobic. Also, it was cleared that most parts of the wood surface were modified with MOI by XPS analysis.

• Journal of the Korean Wood Science and Technology
• /
• v.39 no.5
• /
• pp.381-389
• /
• 2011

The effect of organoclays on the mechanical properties of cured phenol formaldehyde resin and oriented strand lumber made from Mountain Pine Beetle killed pine strands was analyzed. Three organoclays were used: a natural montmorillonite, hydrophobic organically modified 10 A, and hydrophilic organically modified 30 B. The oriented strand lumber samples were less creep deformation as well as improved internal bonding strength by adding organoclays in the order of 10 A 2% > MMT 2% > 30 B 2% > control. Furthermore, time-temperature superposition (TTS) analysis was proved to be able to predict the long-term creep behavior of MPB-OSL samples.

• Journal of the Korean Wood Science and Technology
• /
• v.39 no.4
• /
• pp.344-350
• /
• 2011

In this study, LVLs of radiata pine were fabricated with non-preservative treated veneers, CuAz treated veneers, and ACQ treated veneers, using aqueous vinyl urethane adhesive and phenol modified resorcinol resin adhesive. Then density gradient, bonding strength, bending properties and decay resistance of LVLs were evaluated. As results, the cone-shaped and higher density gradient pattern was found in layer close to glueline. After cyclic water boiled test, the LVL bonded with aqueous vinyl urethane resin adhesive was delaminated in all layers or partly delaminated including check, chasm in glueline layer. In the case of LVL bonded with phenol modified resorcinol resin adhesive, despite slight cupping due to great glueline stress and vertical check between glueline layers, it was observed that the bonding strength to delamination was higher, owing to most absence of delamination through overall glueline. On the other hand, in the decay test, mass loss by brown rot fungi was greater than white rot fungi in LVL bonded with aqueous vinyl urethane resin adhesive. However, in LVL bonded with phenol modified resorcinol resin adhesive, the mass loss by brown rot fungi was slight and non-preservative treated LVL was low. The mass loss of preservative-treated LVL was 0 (zero), showing the high decay resistance effect.

• Journal of the Korean Wood Science and Technology
• /
• v.49 no.2
• /
• pp.191-209
• /
• 2021

Australia has significant wood resources in its native forest, but the resource available for harvest becomes lesser due to the conversion of native forest to conservation reserves. The natural occurrences of bushfires, droughts, and cyclones are highly destructive, making the situation worse. The shortage of wood resources is having a significant negative impact on Australia because wood is so scarce that they cannot meet domestic demands, especially durable wood. Australia cleared approximately 100 million hectares of its land to establish forest plantations, and two million trees were planted. However, most of these plantations are for pulpwood production; however, their application for high-value products is limited due to their undesirable properties. Wood modification is a process of improving unfavorable wood properties to be utilized for a wide range of applications. Australia has not adopted any of these modification processes; it still depends on the less toxic wood preservative to treat wood. This study focuses on the recent advancement in industrial wood modification worldwide and how it may be used to modify Eucalyptus wood for high-value applications. The opportunities and suggestions for Eucalyptus wood modification in Australia will be discussed. Before the study concludes, the future of commercial wood modification for Eucalyptus plantation in Australia will also be presented.