• Journal of the Korean Ceramic Society
• /
• v.41 no.10 s.269
• /
• pp.735-741
• /
• 2004

$LiMn_{1.92}Co_{0.08}O_4$ and $LiNi_{0.7}Co_{0.3}O_2$ synthesized by a simplified combustion method had good electrochemical properties. Mixtures $LiMn_{1.92}Co_{0.08}O_4$-x wt$\%$ $LiNi_{0.7}Co_{0.3}O_2$ (x=9, 23, 33, 41, and 47) were prepared by milling for 30 min and their electrochemical properties were investigated. The electrode with x=9 had a relatively large first discharge capacity (109.9 mAh/g at 0.1 C) and good cycling performance. The decrease in the discharge capacity of the mixture electrodes with cycling is considered to result mainly from the degradation of $LiNi_{0.7}Co_{0.3}O_2$, caused by coating of $LiNi_{0.7}Co_{0.3}O_2$ with Mn dissolved from $LiMn_{1.92}Co_{0.08}O_4$.

• Transactions of the Korean hydrogen and new energy society
• /
• v.15 no.1
• /
• pp.62-71
• /
• 2004

$LiMn_{1.92}Co_{0.08}O_4-x\;wt.%LiNi_{0.7}Co_{0.3}O_2$를 단순화한 연소법에 의하여 합성하고, 그것들의 전기화학적 특성을 조사하였다. 또한 30분동안 밀링하여 준비한 $LiMn_{1.92}Co_{0.08}O_4-x\;wt.%LiNi_{0.7}Co_{0.3}O_2$ (x=9, 23, 33, 41 and 47) 혼합물 전극의 전기화학적 특성을 조사하였다. x=33 조성의 전극이 가장 큰 초기방전용량(132.0mAh/g at 0.1C)을 나타내었다. x=9조성의 전극은 비교적 큰 초기방전용량(109.9mAh/g at 0.1C)과 우수한 싸이클 특성을 나타내었다. 싸이클링에 따른 혼합물 전극의 방전용량의 감소는 주로 $LiNi_{0.7}Co_{0.3}O_2$의 퇴화에 기인한다고 생각된다. 그런데 $LiNi_{0.7}Co_{0.3}O_2$의 퇴화는 $LiMn_{1.92}Co_{0.08}O_4$로부터 용해된 Mn이 $LiNi_{0.7}Co_{0.3}O_2$를 둘러쌈(coating)으로써 야기되는 것으로 생각된다.