• Structural Engineering and Mechanics
• /
• 제5권6호
• /
• pp.817-837
• /
• 1997

In the present contribution an interface crack model is introduced which is capable of modelling crack initialisation and growth in aluminium as well as in Fibre Metal Laminates. Interface elements are inserted in a finite element mesh with a yield function which bounds all states of stress in the interface. Hardening occurs after a state of stress exceeds the yield stress of the material. The hardening branch is bounded by the ultimate stress of the material. Thereafter, the state of stress is reduced to zero while the inelastic deformations grow. The energy dissipated by the inelastic deformations in this process equals the fracture energy of the material. The model is applied to calculate the onset and growth of cracking in centre cracked plates made of aluminium and GLARE$^{(R)}$. The impact of the model parameters on the performance of the crack model is studied by comparisons of the numerical results with experimental data.

• Journal of Welding and Joining
• /
• 제16권3호
• /
• pp.111-120
• /
• 1998

To predict and evaluate metallurgical and mechanical behavior of th welds, it is essential to understand solidification behavior and microstructural evolution experienced in the welds, neither of which follows the equilibrium phase diagram because of rapid heating and cooling conditions. Metallurgical phenomena in austenitic stainless steel fusion welds, types 304, 309S, 316L, 321 and 304N, were investigated in this study. Autogenous GTA welding was performed on weld coupons, and primary solidification mode and phase distribution were investigated from the welds. Varestraint test was employed to evaluate solidification cracking susceptibilities of the alloys. GTA weld fusion zones in type 304, 321 and 304N stainless steels experienced primary ferrite solidification while those in type 309S primary austenite solidification. Type 316L exhibited a mixed type of primary ferrite and primary austenite solidification. The primary solidification mode strongly depended on $Cr_{eq}/Ni_{eq}$ ratio. In terms of solidification cracking susceptibility, type 309S that solidified as primary austenite exhibited high cracking susceptibility while the alloys experienced primary ferrite solidification showed low cracking susceptibility. The relative ranking in solidification cracking susceptibility was type 304=type 304N < type 321 < type 316L < type 309S.

• 한국도로학회논문집
• /
• 제7권4호
• /
• pp.9-20
• /
• 2005

본 연구는 아스팔트 덧씌우기 포장에 나타나는 반사균열을 제어하기 위하여 노후된 시멘트 콘크리트 포장과 아스팔트 덧씌우기 포장 경계면에 보강재의 효과적인 부착 방법을 찾기 위하여 수행하였다. 이를 위한 부착재로는 RSC-4 유화아스팔트, 컴파운드, 불포화 폴리에스터 수지 (UPR) 등 3종류를 사용하였다. 또한 아스팔트 혼합물은 3종류의 밀입도 혼합물(AC 60-80, RLDPE 8%, PG 76-22)을 사용하였다. 보강 재료로서 유리섬유 그리드 하부에 직포가 부착된 것을 사용하였다. 복합모드 파괴(mode II)의 모사를 위한 촉진시험은 휠트랙킹 장비를 이용하여 수행하였다. 반사균열의 진전은 피로수명으로서 하중 사이클 수에 따라 측정하였고, 공시체의 변위는 각각 시험 공시체에 대하여 demec 게이지를 이용하여 측정하였다. 본 연구 결과, UPR 부착이 가장 효과적이었으며 다음은 RSC-4의 순이었다. 그러나 현장 적용성을 고려할 때 , RSC-4 유제가 보강 재료의 부착을 위해 적절한 선택으로 판단된다.

• 콘크리트학회논문집
• /
• 제12권2호
• /
• pp.63-69
• /
• 2000

This study investigates a new method of using a concrete disk to calculate stress intensity factor (SIF) for mixed mode cases. The results indicate that the disk method is more accurate than three point bending test (TPB) in obtaining correct SIF values for mixed mode fracture propagation. Stress intensity factors $K_{I}$ and $K_{II}$ are calculated using a center notched disk subjected to splitting load. The notch angle is calculated by finite element (FEM). Fracture toughness $K_\textsc{k}$ of the concrete is obtained from the load intensities at the initiation of crack propagation. According to the finite element analysis(FEA) and disk test, the results show that mode I and mixed mode cracks propagate toward the directions of crack face and loading point, respectively. The results from FEA with maximum stress theory compare well with the experimental date. Unlike TPB method where an accurate fracture toughness value is difficult to obtain due to the irregular shape of load deflection curve and delayed final crack propagation (following slow stable cracking). fracture toughness value is easily measured in the disk test from the crack initial load. Therefore, it is safe to conclude that disk method is more advantageous than TPB method in analyzing combined mode fracture problems.

• 한국안전학회지
• /
• 제29권6호
• /
• pp.9-14
• /
• 2014

Recently many efforts and researches have been done to cope with industrial facilities that require a low energy machines due to the gradual depletion of the natural resources. The fiber-reinforced composite materials in general have good properties and have the proper mechanical properties according to the change of the ply sequences and fiber distribution types. However, in the fiber-reinforced composite material, there are several problems, including fiber breaking, peeling, layer lamination, fiber cracking that can not be seen from the metallic material. Particularly, the fracture and delamination are likely to be affected by the thickness of the stacking laminates when the bi-material laminated structure is subjected to a load of the mixed mode. In this study, we investigated the effect of the thickness ratio of the difference in the CFRP/GFRP bi-material laminate composites by measuring the cracking behavior and the AE characteristics in a mixed mode loading, which may be generated in the actual structure. The results show that the thickness of the CFRP becomes more thick, the mode I energy release rate becomes a larger, and also the influence of mode I is greater than that of mode II. In addition, AE amplitude which shows the level of the damage in the structure was obtained the more damage in the CFRP with the thin thickness.

• Nuclear Engineering and Technology
• /
• 제51권1호
• /
• pp.228-237
• /
• 2019

The crack growth responses of as-received and as-welded Alloy 600/182 and Alloy 690/152 welds to constant loading were measured by a direct current potential drop method using compact tension specimens in primary water at $325^{\circ}C$ simulating the normal operating conditions of a nuclear power plant. The as-received Alloy 600 showed crack growth rates (CGRs) between $9.6{\times}10^{-9}mm/s$ and $3.8{\times}10^{-8}mm/s$, and the as-welded Alloy 182 had CGRs between $7.9{\times}10^{-8}mm/s$ and $7.5{\times}10^{-7}mm/s$ within the range of the applied loadings. These results indicate that Alloys 600 and 182 are susceptible to cracking. The average CGR of the as-welded Alloy 152 was found to be $2.8{\times}10^{-9}mm/s$. Therefore, Alloy 152 was proven to be highly resistant to cracking. The as-received Alloy 690 showed no crack growth even with an inhomogeneous banded microstructure. The cracking mode of Alloys 600 and 182 was an intergranular cracking; however, Alloy 152 was revealed to have a mixed (intergranular + transgranular) cracking mode. It appears that the Cr concentration and the microstructural features significantly affect the cracking resistance and the cracking behavior of Ni-base alloys in PWR primary water.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2000년도 가을 학술발표회논문집(I)
• /
• pp.733-738
• /
• 2000

It is difficult to obtain accurate fracture toughness values by RILEM committees proposed three point bend test(TPB) because the shape of load-deflection curve is irregular and final crack propagation occurs after some slow stable cracking. However, for disk test, fracture toughness is easily obtained from crack initial load. We examined the cracked high strength concrete disk and the experimental results were compared with the results by finite element analysis(FEA). Also we compared experimental fracture locus with theoretical fracture locus.

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 1998년도 춘계학술발표회논문집(2)
• /
• pp.84-89
• /
• 1998

Alloy 600 및 alloy 690과 Ni-8Cr-lOFe 합금 등의 응력부식(stress corrosion cracking, SCC) 거동을 고온의 염기성 분위기에서 C-ring 시편을 사용하여 연구하였다. Alloy 600과 alloy 690을 여러 조건에서 열처리하여 etching한 후 탄화물의 분포와 입계 주변의 Cr고갈 정도 등의 미세조직을 광학현미경과 주사 전자현미경(SEM)으로 관찰하였다. 이들 재료에 대한 SCC 시험을 315$^{\circ}C$의 40% NaOH 수용액에서 일정한 부하전위(부식전위 + 200㎷)를 가하면서 수행하였으며, 동일 조건에서의 분극거동도 측정하였다. Alloy 600 MA(mill anneal) 및 TT(thermal treatment)의 SCC 저항성은 alloy 690 TT와 Ni-8Cr-10Fe SA(solution anneal)보다 낮았다. Alloy 600 TT 재료는 alloy 600 MA 및 SA 재료에 비해 SCC 저항성이 더 컸다. 고용 탄소농도는 alloy 600의 SCC 저항성에 큰 영향을 주지 못했다. 대부분의 Alloy 600은 균열전파 입계균열을 보였으나, 일부에서는 입계 및 입내 혼합양상(mixed mode cracking)을 보였다. 염기성 분위기에서 Ni기 합금의 SCC 거동을 미세조직, 분극거동의 관점에서 고찰하였다.

• 한국표면공학회지
• /
• 제32권6호
• /
• pp.647-657
• /
• 1999

Due to the inherently poor adhesion strength of Cu-based leadframe/EMC (Epoxy Molding Compound) interface, popcorn cracking of thin plastic packages frequently occurs during the solder reflow process. In the present work, in order to enhance the adhesion strength of Cu-based leadframe/EMC interface, black-oxide layer was formed on the leadframe surface by chemical oxidation of leadframe, and then oxidized leadframe sheets were molded with EMC and machined to form SDCB (Sandwiched Double-Cantilever Beam) and SBN (Sandwiched Brazil-Nut) specimens. SDCB and SBN specimens were designed to measure the adhesion strength between leadframe and EMC in terms of critical energy-release rate under quasi-Mode I ($G_{IC}$ ) and mixed Mode loading ($G_{C}$ /) conditions, respectively. Results showed that black-oxide treatment of Cu-based leadframe initially introduced pebble-like X$C_2$O crystals with smooth facets on its surface, and after the full growth of $Cu_2$O layer, acicular CuO crystals were formed atop of the $Cu_2$O layer. According to the result of SDCB test, $Cu_2$O crystals on the leadframe surface did not increase ($G_{IC}$), however, acicular CuO crystals on the $Cu_2$O layer enhanced $G_{IC}$ considerably. The main reason for the adhesion improvement seems to be associated with the adhesion of CuO to EMC by mechanical interlocking mechanism. On the other hand, as the Mode II component increased, $G_{C}$ was increased, and when the phase angle was -34$^{\circ}$, crack Kinking into EMC was occured.d.

• Corrosion Science and Technology
• /
• 제17권1호
• /
• pp.6-11
• /
• 2018

Outdoor exposure tests using of 7B04 aluminium alloy samples including plate, tensile and various SCC samples were carried out in Tuandao station, Shandong province (East of China) and Wanning station, Hainan province (South of China). Corrosion characteristics including weight loss, microstructure, tensile strength and SCC susceptibility were investigated. The corrosion rates in Tuandao and Wanning showed high to low and the corrosion rates changed to the following equation of $w=at^b$ (b<1). The corrosion of 7B04 aluminium alloy in Wanning was more serious than that in Tuandao. Pitting appeared at early stage of expose test, and it can be changed to general corrosion with test time extension. The 7B04 aluminium alloy of which specimen shapes are forging and thick plate also showed SCC (Stress corrosion cracking) in the marine atmosphere. The higher SCC sensitivity was observed in Wanning station than in Tuandao station. The 7B04 aluminium alloy with a high stress level was more sensitive to SCC. Intergranular and transgranular or a mixed mode of cracking can be observed in different marine exposure.