• The Journal of Korean Academy of Prosthodontics
• /
• v.55 no.3
• /
• pp.264-271
• /
• 2017

Purpose: The purpose of this study is to investigate the differences in bond strength of four different indirect composites to the gold alloy and Ni-Cr alloy according to type of metal surface treatment after water storage. Materials and methods: Type IV gold alloy and Ni-Cr alloy were used for casting alloy while four types of indirect composite resins (Gradia, Tescera Sinfony and in;joy) were used in this study. Metal specimens were produced by casting and total of 240 specimens (60 specimens per one indirect composite group) were prepared. After bonding indirect composite resin and undergoing 24 hours of polymerization, customized jig was attached to the metal specimen and shear bond strength were measured using universal testing machine. Also, differences in shear bond strength before and after water storage for 240 hours were also measured. Results: In the measurement of shear bond strength according to the metal surface treatments, bead group showed high strength followed by loop and flatting group (P<.05). After being stored in water bath for 240 hours, Gradia showed statistically significant high bond strength compared to other indirect composite resins in all groups (P<.05). Conclusion: Shearbond strength was found to be different according to type of metal surface treatment and type of metal used after storage in water. Further studies need to be developed for clinical practices as three are still problems of microleakage, stain or wear.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.42 no.4
• /
• pp.281-290
• /
• 2015

The aim of this study was to evaluate shear bond strength (SBS) of bulk-fill resin composites (RCs) to dentin and their micro-leakage. One high-viscosity bulk-fill RC and 2 low-viscosity bulk-fill RCs were compared with 1 conventional RC. 7thgenerationbondingagentswereused. In order to evaluate SBS values, 40 permanent molars were selected and divided into 4 groups. The bulk-fill RCs were applied in 4 mm thickness, whereas the conventional RC was applied in 2 mm thickness. In order to evaluate micro-leakage, class I cavities ($5{\times}2{\times}4mm$) were prepared in 32 permanent molars. The teeth were divided into 4 groups and restored with resin composites in an increment of 4 mm for the bulk-fill RC and in 2 horizontal increments of 2 mm for the conventional RC. The mean SBS value of conventional RC showed no statistically significant difference when compared with those of low-viscosity bulk-fill RCs. However, the mean SBS value of high-viscosity bulk-fill RC was significantly lower than that of conventional RC (p < 0.05). There were no statistically significant differences in micro-leakage between the 4 groups. For SBS and micro-leakage, the use of low-viscosity bulk-fill RCs might help clinicians simplify the procedure.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.36 no.1
• /
• pp.53-61
• /
• 2009

The property of pit and fissure sealant has been improved and many studies on the bond strength, penetration, microleakage have been published. But there are few studies on the using status and perception of pit and fissure sealant within the country. Therefore, this study made a survey on it. Pedodontists and non-pedodontists were surveyed by interview. The Results were as follows; 1. On caries prevention effect, 96.7% of the pedodontists replied that sealants were effective on both permanent teeth and primary teeth. On the other hand, 13.5% of the non-pedodontists replied that sealants weren't effective on both. 2. All of the pedodontists and 27% of the non-pedodontists used rubber dams. 83.3% of the pedodontists and 40.5% of the non-pedodontists used bonding agents. 3. Non-pedodontists used enameloplasty more frequently than Pedodontists but the pattern was not significantly different. 4. The causes of sealant failures included salivary contamination, caries under sealant, low strength, low flowability, overfilling. 5. In the pedodontists, 90% replied that PRR application was desirable and PRR applications were more frequent than sealant application.

• Restorative Dentistry and Endodontics
• /
• v.21 no.1
• /
• pp.187-201
• /
• 1996

The purpose of this study was to evaluate the sealing ability of a calcium hydroxide plug treated with a bonding agent. Ninety extracted human anterior teeth and premolars with single canal were used in this study. Crowns were removed. the canal's were instrumented. and the roots were randomly divided into three groups of 30 each. In control group. a single apical seat was prepared with #60 K file 1mm short of the apex and the root canal was obturated with Gutta-percha and Sealapex by the lateral condensation method. In experimental group 1 and group 2. to prepare an apical isthmus of 1mm in length. the first apical seat was prepared with a #45 K file 1mm short of the anatomical apex and with a #60 K file 2mm short for the second apical seat. Dry calcium hydroxide powders were packed in the apical isthmus with a hand plugger and #60 K file and then. the root canal was obturated with Gutta-percha and Seal apex by the lateral condensation method. In experimental group 2. following an application of the bonding agent to the plug. the root canal was obturated in the same way. The teeth of each group were immersed in a 2% methylene blue dye solution. for 1, 2, and 4 weeks. The distance from the tip of the cone to the deepest penetration was measured using the Tool maker's microscope. The results were as follows : 1. The teeth having the calcium hydroxide plug treated with the dentin bonding agent (experimental group 2) showed the lowest leakage with 1.4705mm and the control group without apical plug(no apical isthmus) showed the highest leakage with 3.1735mm. 2. The control group without apical plug showed higher leakage than experimental group 1 having the calcium hydroxide plug treated without the dentin bonding agent(p>0.05). 3. The control group without apical plug and experimental group 1, having the calcium hydroxide plug treated without the dentin bonding agent. showed higher leakage than experimental group 2. having the calcium hydroxide plug treated with the dentin bonding agent(p<0.001). 4. The immersion time had no significant effect on the degree of leakage. In conclusion, the results showed that the calcium hydroxide plug treated with the dentin bonding agent could decrease the microleakage from the root apex effectively.

• Restorative Dentistry and Endodontics
• /
• v.21 no.1
• /
• pp.174-186
• /
• 1996

The purpose of this study was to evaluate the adaptability to tooth structure of composite resin and glass ionomer cement according to filling methods. In this study. two class V cavities were prepared on the buccal and lingual surface of each tooth of forty extracted human premolars. and they were randomly assigned into 4 groups with 10 teeth. The cavities of each group were filled with the CLEARFIL FII self curing resin(Control Group), Z-100 light curing resin (Group 1). $Vitremer^{TM}$ light curing glass ionomer cement(Group 2) and Z-100 light curing resin over the $Vitremer^{TM}$ liner(Group 3). The specimens underwent temperature changed from $5^{\circ}C$ to $55^{\circ}C$ five hundred times. After thermocycling. specimens were immersed in 2% methylene blue solution and stored in 100% relative humidity at $37^{\circ}C$ for 24 hours. And then. the specimens sectioned buccolingually. Degree of dye penetration at tooth-restoration interfaces were examined by Tool maker's microscope(x 200) and Image analyzer. The results were as follows : 1. On the occlusal margin. among the experimental groups. the group 2 showed the highest dye penetration($2.40{\pm}0.68$) and the group 3 showed the lowest dye penetration($1.15{\pm}0.37$). There was significant difference among the experimental groups(p<0.001). 2. On the gingival margin, among the experimental groups, the group 1 showed the highest dye penetration($3.30{\pm}0.57$) and the group 2 showed the lowest dye penetration($1.65{\pm}0.49$). There was significant difference among the experimental groups(p>0.001). 3. About total degree of dye penetration, the group 1 showed the highest dye penetration($2.25{\pm}1.17$) and the group 3 showed the lowest dye penetration ($1.43{\pm}0.55$). There was significant difference among the experimental groups(p<0.001). 4. The sum of dye penetration at occlusal margin was less than gingival margin. There was significant difference between occlusal margin and gingival margin (p<0.001). The results showed that differences were more pronounced at the gingival margin. Composite restorations inserted over the glass-ionomer liner demonstrated significantly less leakage than single restoration that used composite resin or glass-ionomer cement.

• Restorative Dentistry and Endodontics
• /
• v.24 no.1
• /
• pp.67-75
• /
• 1999

The use of composite restorative materials is established due to continuing improvements in the materials and restorative techniques. Composite resins are widely used for the restoration of cervical lesions because of esthetics, good physical properties and working time. There are several types of cavity design for class V composite resin filling, but inappropriate cavity form may affect bonding failure, microleakage and fracture during mastication. Cavity preparations for composite materials should be as conservative as possible. The extent of the preparation is usually determined by the size, shape, and location of the defect. The design of the cavity preparation to receive a composite restoration may vary depending on several factors. In this study, 5 types of class V cavity were prepared on each maxillary central incisor. The types are; 1) V-shape, 2) round(U) shape, 3) box form, 4) box form with incisal bevel and 5) box form with incisal bevel and grooves for axial line angles. After restoration, in order to observe the concentration of stress at bonding surfaces of teeth and restorations, developing a 2-dimensional finite element model of labiopalatal section in tooth, surrounding bone, periodontal ligament and gingiva, based on the measurements by Wheeler, loading force from direction of 45 degrees from lingual side near the incisal edge was applied. This study analysed Von Mises stress with SuperSap finite element analysis program(Algor Interactive System, Inc.). The results were as follows : 1. Stress concentration was prevalent at tooth-resin bonding surface of cervical side on each model. 2. In model 2 without line angle, stress was distributed evenly. 3. Preparing bevel eliminated stress concentration much or less at line angle. 4. Model with round-shape distributed stress concentration more evenly than box-type model with sharp line angle, therefore decreased possibility of fracture. 5. Adding grooves to line angles had no effect of decreasing stress concentration to the area.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.30 no.1
• /
• pp.143-152
• /
• 2003

The aims of the present study was to observe resin tag of the resin/enamel, dentin interface produced by self-etching adhesive systems and evaluate effect of additional acid etching on resin tag formation. Three self-etching primer(SE bond, AQ bond and L Pop) and an one bottle adhesive(Single bond) were used. Flat occlusal enamel and dentin disks were obtained from extracted human molars. A total of 20 surfaces were collected and divided into four groups of 5 samples. One-half of each specimen in each group was etched with 35% phosphoric acid prior to the application of each adhesive system, with the second half being kept unetched. Subsequently, resin composite was placed and polymerized. The samples were sliced and immersed into HCl and NaOCl solutions, followed by drying and sputter coating for examination with a SEM. The results were as follows; 1. Additional etching side of dentin displayed longer and thicker resin tag than unetched side in all self-etching adhesive groups. 2. In enamel, additional etching side displayed deeper and more distinct etching pattern than unetched side except L Pop. There is no difference between etched and unetched enamel in L Pop. The results obtained suggest the self-etching adhesive did not etch enamel and penetrate into dentinal tubule as deeply as did additional etching. Further research should include the evaluation of the relationship of boding strength, microleakage and resin tag morphology.

• Restorative Dentistry and Endodontics
• /
• v.19 no.2
• /
• pp.429-446
• /
• 1994

The purpose of this study was to evaluate the sealing effect of warm lateral condensation technique by Endotec spreader, comparing with other canal filling techniques. One hundred and forty extracted human teeth with single canal were instrumented and randomly divided into four groups according to canal filling techniques including lateral condensation with sealer, warm lateral condensation with sealer, warm lateral condensation without sealer, and injection-molded thermoplasticized gutta-percha without sealer. Obturated canals were exposed to 2 % methylene blue solution at $37^{\circ}C$ for 24 hours and measurement of the degree of microleakage was done linearly and volumetrically with stereozoom microscope and UV-spectrophotometer respectively. The results were as follows ; When sealer was used, the canals obturated by warm lateral condensation showed less leakage linearly and volumetrically than the canals obturated by standard lateral condensation with no statistically significant difference. The obturated canals by warm lateral condensation with sealer showed less leakage linearly and volumetrically than the canals obturated by warm lateral condensation without sealer and by injection-molded thermoplasticized gutta-percha without sealer with statistical significance (p<0.05). No statistical difference revealed that the group filled with the use of the Endotec had significantly less leakage than any of the other groups. There was a significant correlation between the linear measurement and volumetric measurement(r=0.4459, p<0.05).

• Restorative Dentistry and Endodontics
• /
• v.27 no.5
• /
• pp.479-487
• /
• 2002

복합레진의 중합시 발생하는 수축과 응력은 와동의 형태에 의하여 영향을 받으며 이는 수복재는 물론 접착계면의 물성을 결정하는 요인이 된다. 본 연구는 다양한 C-factor를 갖는 와동에 상아질 접착제 Clearfil SE Bond(Kuraray)를 도포하고 혼합형 복합레진인 Clearfil AP-X(Kuraray)와 미세혼합형의 Esthet-X(Dentsply)를 충전하여 미세인장강도 및 변연누출을 측정 평가함으로써 중합수축이 수복물과 치아계면에 미치는 영향을 평가하고자 시행하였다. 98개의 Bovine 하악전치를 이용하여 표면의 상아질을 #600 SiC paper로 연마한 대조군 및 와동의 넓이를 조절하여 C-factor 2.3, 3.0, 3.7이 되도록 제작한 실험군 와동에 복합레진을 충전한 후 37의 증류수에 24시간 보관하였다. 저속 diamond saw(Buehler)를 이용하여 1mm 두께로 수직절단 후 고속 diamond point(#104 Shofu)를 이용하여 단면적 1mm$^2$가 되도록 hour-glass모양으로 형성하여 시편을 제작하였고, Universal testing machine(EZ-Test; Shimadzu, Japan)에 시편을 부착하고 cross head speed 1mm/min으로 인장력을 가하여 미세인장 결합강도를 측정하였다. 각 C-factor에 따른 변연누출실험을 위하여 복합레진이 수복된 치아를 37$^{\circ}C$의 증류수에 24시간 보관한 후 와동을 제외한 부위에 nail varnish를 도포하고 3mol/L silver nitrate용액에 24시간 암보관한 다음 수세하여 현상액에 24시간 경과시킨 후 치아의 장축에 따라 절단하여 침투된 색소의 정도를 광학현미경상에서 40배로 관찰하였다. 각각의 실험결과는 ANOVA/Tukey's test 및 Kruskal-Wallis non-parametric independent analysis와 Mann-Whitney U test에 의하여 통계 분석하여 다음과 같은 결론을 얻었다. 1. 대조군에 있어서 혼합형 복합레진의 미세인장 결합강도는 미세혼합형에 비하여 높았으며, 실험군 사이에는 유의차를 보이지 않았다. 2.모든 복합레진의 미세인장 결합강도는 와동의 C-factor증가에 따라 감소하는 경향을 나타내었고, 혼합형 복합레진의 실험군은 대조군에 비하여 낮게 나타났으며, 미세혼합형 복합레진에서는 유의차를 보이지 않았다. 3. 절단측 및 치은측 변연부의 미세누출정도는 혼합형 복합레진이 미세혼합형에 비하여 대체로 높게 나타났다. 4. 모든 실험군에서 미세누출은 C-factor증가에 따라 증가하였고 절단측에 비하여 치은측 변연이 높게 나타났으나 통계학적 유의차는 보이지 않았다. C-factor의 변화에 대하여 필러함량과 탄성계수가 높은 혼합형 복합레진이 미세혼합형에 비하여 더 민감한 결과를 보인다. 이는 복합레진 수복시 재료의 선택과 중합수축의 적절한 조절이 중요한 요소임을 시사한다.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.4
• /
• pp.706-718
• /
• 1997

Ceramometal crowns are common restorations in fixed prosthodontics because of their casting accuracy, the high strength properties of the metal, and the cosmetic appearance of porcelain. However, deterioration of the initial fit of the metal coping has been observed after the porcelain firing cycle. The distortion due to repeated firing makes it difficult to fit crown margin and elicits microleakage. The major causes of distortion are the residual stress that accumulate during wax-up, casting, cold work and the induced stress caused by the mismatch of porcelain-metal thermal contraction. This study examined the marginal fit changes of metal copings in relation to repeated firing and the effects of heat treatment that reduce the distortion resulted from residual stress. The marginal changes of the copings that were treated with conventional method and those treated with heat before repeated firing, were evaluated. The metal die which represented preparations of a maxillary central incisor was fabricated, and 45 wax patterns were cast with nonprecious metal alloys. The heat treatment of each group was performed as follows. Group 1(control) : Casting - Devesting - Cold work - Firing Group 2 : Casting - Heat treatment - Devesting - Cold work - Firing Group 3 : Casting - Devesting - Cold work - Reinvesting - Heat treatment - Devesting - Firing The copings were fired 3 times. After each firing, the marginal fit changes were measured with inverted metallurgical microscope at the 4 reference points located at labial, lingual, and both proximal surface. Measurements were compared, and statistically analyzed. The results were as follows ; 1. In all groups, the highest value of marginal fit changes of the copings studied were found after the first firing cycle. 2. When the distortion of each experimental group at the first firing cycle were compared, group 1 exhibited the greatest changes($20-27{\mu}m$), followed by group 2($9-13{\mu}m$), and group 3($8-10{\mu}m$). 3. The copings treated with heat before devesting(group 2) revealed significantly smaller marginal fit changes than the copings treated with conventional method(group 1). (p<0.01) 4. The copings treated with heat after reinvesting(group 3) revealed significantly smaller marginal fit changes than the copings treated with conventional method(group 1). (p<0.01) 5. No siginificant differences in marginal fit changes were found between the copings treated with heat before devesting(group 2) and the copings treated with heat after reinvesting(group 3). (p>0.01)