THE CANAL SEALING EFFECT OF WARM LATERAL CONDENSATION OF GUTTA-PERCHA

가온 측방가압 근관충전법의 폐쇄효과

The purpose of this study was to evaluate the sealing effect of warm lateral condensation technique by Endotec spreader, comparing with other canal filling techniques. One hundred and forty extracted human teeth with single canal were instrumented and randomly divided into four groups according to canal filling techniques including lateral condensation with sealer, warm lateral condensation with sealer, warm lateral condensation without sealer, and injection-molded thermoplasticized gutta-percha without sealer. Obturated canals were exposed to 2 % methylene blue solution at $37^{\circ}C$ for 24 hours and measurement of the degree of microleakage was done linearly and volumetrically with stereozoom microscope and UV-spectrophotometer respectively. The results were as follows ; When sealer was used, the canals obturated by warm lateral condensation showed less leakage linearly and volumetrically than the canals obturated by standard lateral condensation with no statistically significant difference. The obturated canals by warm lateral condensation with sealer showed less leakage linearly and volumetrically than the canals obturated by warm lateral condensation without sealer and by injection-molded thermoplasticized gutta-percha without sealer with statistical significance (p<0.05). No statistical difference revealed that the group filled with the use of the Endotec had significantly less leakage than any of the other groups. There was a significant correlation between the linear measurement and volumetric measurement(r=0.4459, p<0.05).

이 연구의 목적은 spreader를 전기적으로 가열, 냉각시킬 수 있는 Endotec을 이용하여 가온 측방가압 근관충전한 근관에서 근단공을 통한 누출의 정도를 정선적 및 정량적으로 측정하여 근관폐쇄효과를 평가하는데 있다. 발거된 단근치 140개를 4개군으로 나누어 45번 file 크기까지 근관형성하고, sealer를 사용한 측방가압법 및 가온 측방가압법, sealer를 사용 않은 가온 측방가압법 및 고온 용융 gutta-percha 주입법으로 근관충전하고 2% methylene blue 용액에 24시간 경과시킨 다음 색소침투 정도를 정선적 및 정량적으로 측정하였다. Sealer를 사용한 가온 측방가압 충전법은 sealer를 사용한 측방가압법 보다 정선적 및 정량적 측정 모두에서 색소침투는 적게 나타났으나 통계학적 유의성은 없었다. Sealer를 사용한 가온 측방가압 충전법은 sealer를 사용 않은 가온 측방가압 충전법 및 고온용융 gutta-percha 주입 충전법 보다 정선적 및 정량적 측정 모두에서 유의성 있게 적은 색소침투를 보였다 (p<0.05). 가온 측방가압 근관충전법의 근관폐쇄효과가 우수하였다는 증거는 통계학적으로 검증되지 않았다. 정선적 측정치와 정량적 측정치 사이에는 유의한 상관관계가 있었다(r=0.4459, p<0.05).