• Tribology and Lubricants
• /
• 제34권3호
• /
• pp.84-92
• /
• 2018

Bearings are essential for reducing vibration and wear, in order to achieve high durability and increase longevity. White metal treatment of tilting pads via centrifugal casting method has the possibility of increasing durability. However, this manufacturing method has drawbacks such as long processing time, high defect rate, and harmful health effects. Laser cladding deposition technique is a powerful method that can address these issues by decreasing the processing time and providing good adhesion. In this study, we suggest optimum conditions for laser cladding deposition that can be used in industrial applications. We deposited a soft white metal layer on SCM440 that is primarily used in shafts to minimize wear of bearing pads. During the laser deposition process, we controlled factors such as laser power, powder feed rate, and laser head speed to determine the optimum conditions. In addition, we measured the hardness using micro Vickers, and performed field emission scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, and friction tests to investigate the mechanical properties and surface characteristics for different parameters. Based on the experimental results, we suggest that laser power, powder feed rate, and laser head speed of 1.3 kW, 2.5 rpm, and 10 mm/s, respectively, constitute the optimum conditions for producing white metals using laser cladding.

• 한국재료학회지
• /
• 제8권10호
• /
• pp.918-924
• /
• 1998

본 연구는 티타늄과 활성탄소 원료분말을 반응밀링법에 의해 합성시, 밀링시간에 따른 Ti-TiC 복합재료의 미세조직과 기계적 성질에 미치는 TiC vol.% 및 열간압축성형온도의 영향에 관해 조사하였다. 티타늄과 활성 탄소 원료분말을 300시간 밀링 후 $5\mu\textrm{m}$이하의 미세한 구형의 Ti-TiC복합분말을 생성시킬 수 있었다. 반응밀링된 분말을 $1000^{\circ}C$이상에서 1시간동안 진공열간압축성형한 경우 이론밀도의 98%에 가까운 우수한 성형체를 얻었으며, TiC입자가 티타늄 기지 전반에 걸쳐 고르게 분산되어 Ti-TiC 복합재료의 기계적 특성을 향상시켰다. Ti-TiC복합재료의 고온안정성을 고찰하기 위해 $600^{\circ}C$등온열처리한 결과 80시간까지는 경도의 큰 변화없이 열적으로 안정하였다. Ti-20vol%TiC 복합재료를 $700^{\circ}C$에서 고온압축시험을 한 경우 330MPa의 높은 항복강도값을 나타내었다.

• 한국재료학회지
• /
• 제11권2호
• /
• pp.104-114
• /
• 2001

Zr-Sn-Nb 합금의 재결정에 미치는 Nb과 Sn의 첨가영향을 연구하기 위해 냉간압연한 시편을 $300^{\circ}C$~75$0^{\circ}C$의 온도구간에서 열처리한 후에 미소경도와 TEP (Thermoelectric Power)를 측정하여 재결정 거동을 조사하였으며 광학현미경, 주사전자 현미경 (SEM), 투과전자현미경 (TEM)으로 미세조직을 관찰하였다 미소경도 및 미세조직의 분석 결과에 따르면, Nb과 Sn의 첨가에 의해 재결정 활성화 에너지가 증가하여 재결정이 지연되었으며, 재결정 완료 이후의 결정립 성장도 억제되었음을 관찰하였다. Zr내의 고용도가 매우 낮은 Nb의 첨가는 석출물을 쉽게 형성하는 반면에 고용도가 비교적 큰 Sn은 기지상 내에 대부분 고용되어 석출물의 양이 매우 작았으나, Sn 첨가에 의한 재결정의 지연 효과가 더욱 컸다. Nb보다 Sn의 첨가가 Zr 합금의 재결정 거동을 효과적으로 지연시킨 것은 고용도가 높은 SR에 의한 치환형 고용체 형성과정에서 발생된 응력장이 전위의 이동을 효과적으로 억제했기 때문으로 생각된다. 한편, 회복과 재결정이 진행됨에 따라 전자 산란인자의 감소로 TEP는 증가하였으며, 재결정이 완료되면 TEP의 포화가 발생하였다. 석출물의 형성은 석출물 주변의 용질농도 감소로 인한 전자 산란인자의 감소에 기인하여 TEP의 증가를 가져왔다

• 한국주조공학회지
• /
• 제39권2호
• /
• pp.26-31
• /
• 2019

In this study, the mechanical characteristics and microstructure of hypereutectic Al-17Si-5Fe extruded alloys prepared by a rapid solidification process (RSP) were investigated. The hypereutectic Al alloy was fabricated by means of RSP and permanent casting. For RSP, the Al alloy melted at $920^{\circ}C$, cooling the specimens at a rate of $10^6^{\circ}C/s$ when the RSP was used, thus allowing the refining of primary Si particles more than when using permanent casting, at a rate of about 91%. We tested an extrusion RSP billet and a permanent-cast billet. Before the hot-extrusion process, heating to $450^{\circ}C$ took place for one hour. The samples were then hotextruded with a condition of extrusion ratio of 27 and a ram speed of 0.5 mm/s. Microstructural analyses of the extruded RSP method and the permanent casting method were carried out with OM and SEM-EDS mapping. The mechanical properties in both cases were evaluated by Vickers micro-hardness, wear resistance and tensile tests. It was found that when hypereutectic Al-17Si-5Fe alloys were fabricated by a rapid solidification method, it becomes possible to refine Si and intermetallic compounds. During the preparation of the hypereutectic Al-17Si-5Fe alloy by the rapid solidification method, the pressure of the melting crucible was low, and at faster drum speeds, smaller grain alloy flakes could be produced. Hot extrusion of the hypereutectic Al-17Si-5Fe alloy during the rapid solidification method required higher pressure levels than hot extrusion of the permanent mold-casted alloy. However, it was possible to produce an extruded material with a better surface than that of the hot extruded material processed by permanent mold casting.

• 한국주조공학회지
• /
• 제41권2호
• /
• pp.127-131
• /
• 2021

고온 환경에 대한 우수한 특성을 바탕으로 산업 장비의 고온 재료에 Ti-48Al-2Cr-2Nb 합금이 사용된다. 본 연구에서는 Ti-48Al-2Cr-2Nb 합금 터보 차저 터빈 휠을 진공 원심 주조 방법으로 제작했다. 알루미나 몰드를 이용한 원심 주조시 터보 차저 터빈 휠 블레이드의 미스런 불량을 방지하기 위한 조건을 조사하였다. 진공 원심 주조로 제조된 합금의 미세 구조는 광학 현미경 (OM), 마이크로 비커스 경도 분석기 (HV), X- 선 회절 (XRD) 및 SEM-EDS로 연구하였다. 주조된 Ti-48Al-2Cr-2Nb 합금의 경도 및 SEM-EDS 결과는 산화층 (α- 케이스)의 두께가 일반적으로 50㎛ 미만임을 보여주었다. 예열 온도 1,100oC, RPM 260, 게이트 크기가 큰 알루미나 몰드의 경우 미스런 불량이 거의 없었다. 따라서 높은 예열 온도, 중간 RPM, 큰 게이트 크기 및 알파 케이스 형성 억제를 위한 알루미나 몰드를 통해 미스런이 적은 Ti-48Al-2Cr-2Nb 합금 터보 차저 터빈 휠을 얻을 수 있음을 확인했다.

• 치위생과학회지
• /
• 제11권2호
• /
• pp.69-76
• /
• 2011

본 연구는 전문가불소도포로 사용되고 있는 1.23% APF겔과 2% NaF 용액의 적용 횟수와 방법을 달리하여 적용시 치아 경조직의 내산성에 영향을 줄 수 있을지 비교분석하였으며, 다음과 같은 결과를 얻었다. 1. 불소도포를 실시한 모든 그룹에서 표면미세경도가 증가하였고(p<0.05), 불소도포의 횟수를 달리하는 경우 2% NaF 용액을 4회 이온 도포한 그룹에서 표면 미세경도값이 가장 높았다. 2. pH-cycling model 적용 후의 표면미세경도의 변화 비교는 모든 Group에서 불소도포 후에 비해 감소하였지만 불소 적용을 하지 않은 Control group은 가장 낮은 표면미세경도값을 나타내었으며, Control group과 전문가불소도포를 한 Group간에 표면미세경도값은 유의한 차이를 나타내었다(p<0.05). 3. 불소도포 하기 전 Baseline에 비해 pH-cycling model 적용 후 표면미세경도 값은 Control group에서 가장 많은 소실 값을 나타내었고, NaF 용액을 이용하여 4회 이온도포한 Group이 가장 적은 표면미세경도 소실값을 나타내었으며, 유의한 차이를 보였다(p<0.05). 4. Control group에 비해 1회씩 불소 도포한 Group에서 법랑질의 탈회가 적게 관찰되었고, 4회 불소 도포한 Group의 표면은 Control group과 1회씩 불소 도포한 Group에 비해 규칙적인 표면 양상을 보였다. 이상의 실험결과를 종합해보면 법랑질 산부식증 유발환경에서 2% NaF 용액을 4회 이온도포하는 전문가불소도포법이 법랑질 탈회를 최소화할 수 있는 방법으로 나타났다.