• 구강회복응용과학지
• /
• 제22권3호
• /
• pp.203-210
• /
• 2006

Although porcelain fused to metal crowns made from non-precious metal have good mechanical properties, they also have disadvantages such as the poor biological acceptability and the low corrosional resistance. Titanium is used as the alternative metal for porcelain fused to metal crowns, in spite of difficulties in casting. For that reason non-precious alloy including titanium which is easy to cast is currently used. This study evaluated the bond strength between non-precious alloy including titanium and Ni-Cr alloy. $Tilite^{(R)}V$ as non-precious alloy including titanium, $Rexilium^{(R)}V$ as Ni-Cr alloy and $Omega900^{(R)}$ and $Vintage(Regular)^{(R)}$ as porcelain powders were used. The results were as follows. 1. In comparison with the kind of alloy, the bond strength of $Tilite^{(R)}V$ was lower than that of $Rexilium^{(R)}V$. There was no significant difference between two groups. 2. In comparison with the kind of porcelain powder, the bond strength of $Omega900^{(R)}$ was higher than that of $Vintage(Regular)^{(R)}$ in $Tilite^{(R)}V$. There was significant difference between two groups(p < 0.05).

• 한국표면공학회지
• /
• 제29권5호
• /
• pp.478-481
• /
• 1996

Disproportionation reaction is very important and interesting reaction to be applied to such surface treatment as metal, alloy, compound coating, a surface etching and so on. In gaseous system, the reaction of Al chloride is applied to Al and Al alloy coating, and the similar reaction of Ti chloride is also used for Ti, Ti alloy and Ti compound coating. As for aqueous system, this reaction is utilized to such metal coat as Sn etc. and metal etching such as Cu, Fe and so on. Also in molten salts system, this reaction has many application for surface treatment like metal, alloy and compound coatings for corrosion, wear, heat resistance and so forth. For instance, carbide film, nitride film, boride film, alloy film, quite new different film from the components of substrate material are coated in single and multiple component film system by the disproportionation reaction.

• Journal of Welding and Joining
• /
• 제19권5호
• /
• pp.534-539
• /
• 2001

The formation mechanism of microconstituents in brazed joints of duplex stainless steel and Cr-Cu alloy which is an essential process of rocket engine manufacturing was investigated using Cu base insert metal. $SUS329J_3L$ and C18200 were used for base metal and AMS 4764 was used for insert metal. The brazing was carried out under various conditions. There were various phases in the joints, because of reaction between liquid insert metal and base metals. Since liquid insert metal reacts with duplex stainless steel, liquid Cu from insert metal infiltrated into the $\alpha/\beta$ interface of duplex stainless steel. Through the process of Cu infiltration, isolated stainless steel pieces come into the liquid insert metal. Since liquid insert metal reacts with Cr-Cu alloy. Cr precipitates from C18200 come into the liquid insert metal. With increment of bonding temperature and holding time, amounts and sizes of phases increased. but Cr-Mn compounds decreased at 1303k for 1.2ks and Mn-rich phases disappeared Fe-Cr compounds formed.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.771-772
• /
• 2006

Mechanical properties of metal injection molded titanium and titanium alloy parts were investigated in this study. Material powders with low oxygen content and spherical shape were obtained by electrode induction-melting gas atomization which could melt and atomize titanium and titanium alloy bars with no touch on crucible or tundish. Tensile specimens were fabricated from obtained powders by metal injection molding process. Tensile strength of the specimens increases with increasing oxygen content. This result corresponds to a tendency of wrought metal.

• Journal of Welding and Joining
• /
• 제18권6호
• /
• pp.62-67
• /
• 2000

Metallurgical characteristics of bonded region and high temperature mechanical properties of heat resistant alloy, Fe-35Ni-26Cr during liquid phase diffusion bonding were investigated employing AM17 insert metal. The insert metal for bonding, AM17 was newly developed Ni-base metal using interpolation method. Bonding of specimens were carried out at 1,403~1,463K for 600s in vacuum. The microconstituents in the bonded interlayer disappeared in the bonding temperature over 1,423K. The microstructures, alloying elements and hardness distribution in the base metal. The tensile strength and elongation of the joints at elevated temperatures were the same level as one of the base metal in the bonding temperature over 1,423K. The creep rupture strength and rupture lives of joints were almost identical to those of base metal.

• 대한치과기공학회지
• /
• 제35권4호
• /
• pp.353-358
• /
• 2013

Purpose: This study was observation shear bonding strength by compositional change and firing step of a Ni-Cr alloy for porcelain fused metal crown. The aim of study was to suggest the material for firing step of Ni71-Cr14 alloy to development of alloy for porcelain fused to metal crown. Methods: The test was on the two kinds of Ni-Cr alloy specimens. The surfaces of two alloys were analyzed by EDX in order to observe oxide characteristic. And the shear test was performed by MTS. Results: The surface property and oxide characteristic analysis of oxide layer, weight percentage of Element O within $Ni_{71}Cr_{14}$ alloy measured 23.32wt%, and $Ni_{59}Cr_{24}$ alloy was measured 23.03wt%. And the maximum shear bonding strength was measured 58.02MPa between $Ni_{59}Cr_{24}$ alloy and vintage halo(H4 group). Conclusion: The surface property and oxide characteristic three kind of Ni-Cr alloy was similar. and shear bonding strength showed the highest bonding strength in H4 specimens.

• The Journal of Advanced Prosthodontics
• /
• 제7권5호
• /
• pp.392-399
• /
• 2015

PURPOSE. The aim of this study was to evaluate the effect of metal primers on the bonding of dental alloys and veneer resin. Polyvinylpyrrolidone solution's tarnish effect on bonding strength was also investigated. MATERIALS AND METHODS. Disk-shape metal specimens (diameter 8 mm, thickness 1.5 mm) were made from 3 kinds of alloy (Co-Cr, Ti and Au-Ag-Pd alloy) and divided into 4 groups per each alloy. Half specimens (n=12 per group) in tarnished group were immersed into polyvinylpyrrolidone solution for 24 hours. In Co-Cr and Ti-alloy, Alloy Primer (MDP + VBATDT) and MAC-Bond II (MAC-10) were applied, while Alloy Primer and V-Primer (VBATDT) were applied to Au-Ag-Pd alloys. After surface treatment, veneering composite resin were applied and shear bond strength test were conducted. RESULTS. Alloy Primer showed higher shear bond strength than MAC-Bond II in Co-Cr alloys and Au-Ag-Pd alloy (P<.05). However, in Ti alloy, there was no significant difference between Alloy Primer and MAC-Bond II. Tarnished Co-Cr and Au-Ag-Pd alloy surfaces presented significantly decreased shear bond strength. CONCLUSION. Combined use of MDP and VBATDT were effective in bonding of the resin to Co-Cr and Au-Ag-Pd alloy. Tarnish using polyvinylpyrrolidone solution negatively affected on the bonding of veneer resin to Co-Cr and Au-Ag-Pd alloys.

• 대한치과보철학회지
• /
• 제32권1호
• /
• pp.9-22
• /
• 1994

Porcelain and resin are widely used in esthetic dentistry. In the field of esthetic dentistry, the color and color stability of prosthetic materials are very important in esthetics. In this study, porcelain and resin with the same color were used to veneer on the 3 different metal alloys. Color was evaluated by the CIE $L^*a^*b^*$ system. The purpose of this study was evaluated the cole, difference and cole, stability of the specimens, according to the veneered materials and types of metal alloys. Specimens were divided into 6 groups as follows ; Group 1; Porcelain on the precious metal alloy Group 2; Porcelain on the semiprecious metal alloy Group 3; Porcelain on the nonprecious metal alloy Group 4; Resin on the precious metal alloy Group 5; Resin on the semiprecious metal alloy Group 6; Resin on the nonprecious metal alloy The results obtained were as follows; 1. In porcelain specimens, $L^*$ values showed no significant difference and $a^*$ value of group 2 was lower than that of groups 1, 3 and $b^*$ value of group 2 was higher than that of groups 1, 3. The ${\Delta}E^*ab$ values between group 1-2, group 2-3 were higher than 1.5. 2. In resin specimens. $L^*$ value of group 6 was lower than that of groups 4, 5, $a^*$ value of group 4 was higher than that of group 6, $b^*$ value of group 4 was higher than that of groups 5, 6. The ${\Delta}E^*ab$ values between group 4-5, group 5-6 were higher than 1.5, and between group 4-6 was higher than 3.0. 3. Comparing with veneered materials, $L^*$ flues of porcelain were higher than that of resin. 3. Comparing with veneered materials, $L^*$ values of porcelain were higher than that of resin. In semiprecious metal alloy, $a^*$ values of porcelain were lower than that of resin. In semiprecious and nonprecious metal alloy, $b^*$ values of porcelain were higher than that of resin. The ${\Delta}E^*ab values were higher than 6.0. 4. The color stability of resin specimen was relatively inferior to porcelain specimen.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2007년도 춘계학술대회B
• /
• pp.2050-2054
• /
• 2007

This study numerically and experimentally investigated on thermal strain analysis of aluminum alloy casting mold using metal foundry. To predict the numerical result of thermal strain in Al alloy casting mold during the cooling process, it is performed the investigation of temperature distribution, stress and displacement based on the physical properties of Al alloy. In results of this study, Al alloy casting mold represented rapidly cooling graph during initial 20minutes after beginning cooling process, therefore value of stress and displacement is rapidly changed during initial 20minutes after beginning cooling process. In addition to, temperature distribution obtained by experiment confirmed corresponding pattern then compared numerical analysis with experiment. These results are distribute to make the effective and the high precision casting mold.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제53권4호
• /
• pp.208-212
• /
• 2004

In this paper, the characteristics of co-sputtered Ru-Zr metal alloy as gate electrode of MOS capacitors have been investigated. The atomic compositions of alloy were varied by using the combinations of relative sputtering power of Ru and .Zr. C-V and I-Vcharacteristics of MOS capacitors were measured to find the effective oxide thickness and work function. The alloy made of about 50% of Ru and 50% of Zr exhibited an adequate work function for nMOS. C-V and I-V measurements after 600 and $700^{\circ}C$ rapid thermal annealing were performed to prove the thermal and chemical stability of the Ru-Zr alloy film. Negligible changes in the accumulated capacitance and work function before and after annealing were observed. Sheet resistance of Ru-Zr alloy was lower than that of poly-silicon. It can be concluded that the Ru-Zr alloy can be a possible substitute for the poly-silicon used as a gate of nMOS.