• 한국가구학회지
• /
• 제21권4호
• /
• pp.284-292
• /
• 2010

This research was carried out to examine the properties of fancy cherry veneer overlaid on the PF resin bonded Meranti plywood floor, which 2.5% green tea leaf powder was applied in the UV varnishes and the adhesives for scavenging the volatile organic compounds. The results were as follows: 1. The various properties of the treated samples, such as density, moisture content, thickness swelling, bending strength(MOR), adhesion shear strength, surface abrasion, curling, cyclic delamination test with boiling water, boiling property, cold-resistance and heat resistance, acid resistance and alkali resistance, and anti-contamination property showed no significant difference between the properties of the control samples. 2.5% green tea leaf powder treated floor gave a little better results than the control for surface scratch test. 2. In case of QUV and weathering test, no difference between the treated sample and control was found. 3. The floor was discolored by adding 10% green tea leaf powder to UV coating, and the floor was also discolored to light green during by the soaking test. The color of floor was not changed up to 5% addition level.

• Journal of the Korean Wood Science and Technology
• /
• 제19권4호
• /
• pp.52-61
• /
• 1991

In this paper, the difference of the property of absorption and desorption for five species in semi-steady state are studied. The species used are listed in Table 1 and the dimension of specimen was $8\times8{\times}T$(Tangential direction)cm and tested in various conditions. A change of average moisture content with time were measured in each cycles. The results obtained are summarized as follows. When the relative humidity in air was maximum or minimum, the distribution of moisture In wood of all specimens were illustrated by exponential curves of decrease or increased from lace 10 center of wood. From the consideration of coefficient of decrease(C), the amount of moisture change of spruce was larger than the others. The pheonomenon was considered no relation to the specific gravity in air dry, but the wood structures. The velocity of the absorption and desorption for species decreased in the order spruce(Picea sitchensis) neodobam(Fagus crenata), solsong(Tsuga heterophylla), meranti(Shorea sp.) and kaesoo(Cercidiphyllum japoicum). In case of constant temperature and water vapor pressure is changed. the amount of absorbed moisture was larger than that of constant water vapor pressure and temperature vaned. In this fact, it is considered that the property of sorption of wood is strongly influenced by vapor pressure gradient than temperature gradient.

• Journal of Forest and Environmental Science
• /
• 제29권2호
• /
• pp.131-137
• /
• 2013

This study attempts to classify forest species using hyperspectral data for supporting resources management. The primary dataset used was AISA sensor. The sensor was mounted onboard the NOMAD GAF-27 aircraft at 2,000 m altitude creating a 2 m spatial resolution on the ground. Pre-processing was carried out with CALIGEO software, which automatically corrects for both geometric and radiometric distortions of the raw image data. The radiance data set was then converted to at-sensor reflectance derived from the FODIS sensor. Spectral Angle Mapper (SAM) technique was used for image classification. The spectra libraries for tree species were established after confirming the appropriate match between field spectra and pixel spectra. Results showed that the highest spectral signature in NIR range were Kembang Semangkok (Scaphium macropodum), followed by Meranti Sarang Punai (Shorea parvifolia) and Chengal (Neobalanocarpus hemii). Meanwhile, the lowest spectral response were Kasai (Pometia pinnata), Kelat (Eugenia spp.) and Merawan (Hopea beccariana), respectively. The overall accuracy obtained was 79%. Although the accuracy of SAM techniques is below the expectation level, SAM classifier was able to classify tropical tree species. In future it is believe that the most effective way of ground data collection is to use the ground object that has the strongest response to sensor for more significant tree signatures.

• Journal of the Korean Wood Science and Technology
• /
• 제36권6호
• /
• pp.49-58
• /
• 2008

본 연구는 내구성이 우수하며 포름알데히드방출이 적은 페놀수지 사용 메란티합판을 마루판용 대판으로 사용하고 북미산 벚나무 단판을 표면재료로 사용한 마루판의 제조과정에서 접착제 및 도료에 녹차잎 분말을 첨가하였을 때 마루판으로부터 방출하는 총휘발성유기화합물(TVOC)과 포름알데히드의 감소효과와 녹차잎 분말의 적정 첨가량을 구명하였다. 1) 녹차잎 분말의 폴리페놀화합물량은 9.85%였다. 2) 녹차잎 분말은 FT-IR 결과 벤즈알데히드와 에틸헥사알콜과 반응하여 화학결합을 하는 것으로 나타났다. 3) 페놀수지메란티대판에 벚나무단판오버레이 마루판 제조를 위한 접착제와 UV도료에 전건중량기준으로 2.5%의 녹차잎 분말을 각각 첨가하는 것이 총휘발성유기화합물과 포름알데히드의 방산제거 효과가 매우 적절한 것으로 나타났다. 4) 20L 소형챔버법에 의한 녹차잎 분말 2.5%를 접착제와 도료에 각각 첨가한 온돌용 마루판의 7일째 TVOC는 $0.089mg/m^2hr$이고 포름알데히드는 $0.001mg/m^2hr$를 나타내 최우수등급으로 나타났다.

• Journal of the Korean Wood Science and Technology
• /
• 제13권4호
• /
• pp.3-57
• /
• 1985

본(本) 시험(試驗)에 있어서 파아티클보오드와 콤플라이보오드용(用)의 칩은 공(共)히 메란티 수종(樹種)(Shorea spp.)을 팔만칩퍼로 제조(製造)하였으며 콤플라이보오드의 표층단판(表層單板)의 수종(樹種)은 아피통(Dipterocarpus spp.)을 사용(使用)하였다. 칩의 크기는 6메쉬를 통과(通過)하고 25 메쉬위에 남는 것을 이용(利用)하였으며 콤플라이보오드의 단판(單板)두께는 0.9mm, 1.6mm 및 2.3mm의 것을 사용(使用)하였고 접착제(接着劑)로는 요소수지(尿素樹脂)를 파아티클의 전건조량(全乾燥量)에 대(對)해 10%첨가(添加)한 후 성형(成型)하여 파아티클보오드를 만들었고 표층용단판(表層用單板)의 접착(接着)에는 36g/(30.48cm)$^2$을 도포(塗布)하였다. 내화약제(耐火藥劑)로는 제2인산(第二燐酸)암모늄, 황산(黃酸)암모늄, 제1인산(第一燐酸)암모늄, 파이래소트, 미나리스의 5종(種)에 대(對)해 단판(單板)에는 20% 농도(濃度)로 파아티클에는 5, 10, 15, 20%의 농도(濃度)로 침지법(浸漬法)을 적용(適用)하여 처리(處理)하였다. 이런 조건(條件)으로 만든 내화(耐火)파아티클보오드와 콤플라이보오드의 물성(物性) 기계적(機械的) 성질(性質) 및 내화도(耐火度)를 조사(調査)하여 내화처리(耐火處理)파아티클 및 콤플라이보오드 제조가능성(製造可能性)을 구명(究明)하고져 하였다. 본(本) 연구(硏究)에서 얻은 결론(結論)을 요약(要約)하면 다음과 같다. 1. 파아티클보오드와 콤플라이보오드의 5종(種)의 약제보유량중(藥劑保有量中) 5% 황산(黃酸)암모늄처리(處理)가 1.34kg/(30.48cm)$^3$로 가장 적었으나 모두가 최저보유량(最低保有量) 1,125kg/(30.48cm)$^3$ 보다도 높은 것을 나타내었다. 2. 파아티클보오드와 콤플라이보오드의 파괴계수(破壞係數), 탄성계수(彈性係數), 박리강도(剝離强度) 및 나사못 유지력(維持力)은 제2인산(第二燐酸)암모늄처리(處理)가 다른 약제처리(藥劑處理)보다 우수(優秀)하였다. 3. 내화처리(耐火處理)콤플라이보오드의 파괴계수(破壞係數) 및 탄성계수(彈性係數)는 내화처리(耐火處理)파아티클보오드보다 더 양호(良好)한 결과(結果)를 나타내었다. 4. 내화처리(耐火處理)콤플라이보오드의 두께 팽창율(膨脹率)은 내화처리(耐火處理)파아티클보오드의 것보다 훨씬 적었다. 5. 파이레소트와 미나리스처리(處理)는 파아티클보오드와 콤플라이보오드의 함수율(含水率)을 증가(增加)시켰으나 제1인산(第一燐酸)암모늄처리(處理)는 오히려 함수율(含水率)을 감소(減少)시켰다. 6. 내화처리(耐火處理)콤플라이보오드는 착화(着火)가 되지 않았고 내화처리(耐火處理)콤플라이보오드는 착화(着火)는 되었지만 대조구(對照區)에 비(比)해 착화시간(着火時間)이 훨씬 지연(遲延)되었다. 또한 단판(單板)만 내화처리(耐火處理)한 콤플라이보오드는 착화(着火)되어 잔염(殘炎)은 있으나 대조구(對照區)에 비(比)해 그 잔염시간(殘炎時間)이 훨씬 짧았다. 단판(單板)과 중층(中層)파아티클보오드에 처리(處理)한 콤플라이보오드는 착화(着火)는 되었으나 잔염(殘炎)은 없었다. 7. 불꽃의 길이, 탄화면적(炭化面積) 및 중량감소율(重量減少率)은 대조구(對照區)에 비(比)해서 훨씬 적었으나 약제간(藥劑間)에 차이(差異)는 없었다. 8. 시험(試驗)한 5종(種)의 약제(藥劑)에서 내화처리(耐火處理)파아티클보오드의 이면온도(裏面溫度)는 처리농도(處理濃度)가 증가(增加)함에 따라서 감소(減少)하는 경향(傾向)을 나타내고 있다. 9. 내화처리(耐火處理)파아티클보오드의 이면온도(裏面溫度)가 가장 높은 약제(藥劑)는 파이레소트처리(處理)이고 가장 낮은 약제(藥劑)는 미나리스처리(處理)였다. 10. 내화처리(耐火處理)콤플라이보오드의 이면온도(裏面溫度)는 대조구(對照區)에 비(比)해서 현저히 낮았다.

• 한국산림과학회지
• /
• 제64권1호
• /
• pp.26-32
• /
• 1984

본(本) 연구(硏究)는 COMPLY의 core에 사용(使用)되는 파티클보오드를 내수처리(耐火處理)파티클보오드로 사용(使用)하였을 때 COMPLY의 강도적(強度的) 성질(性質)에 미치는 영향(影響)을 규명하고져 실시(實施)하였다. Ammonium sulfate의 경우 COMPLY의 MOR은 약액농도(藥液濃度)가 증가(增加)함에 따라 약액농도(藥液濃度)가 10%까지는 증가(增加)하나 그 이후(以後)는 감소(減少)하는 경향(傾向)을 나타내고 있으며 Minalith의 경우는 ammonium sulfate의 경우와는 반대경향(反對傾向)을 나타내고 있다. COMPLY의 MOE는 약액농도(藥液濃度)가 증가(增加)함에 따라 감소(減少)하는 경향(傾向)을 나타내고 있지만 약액농도간(藥液濃度間)에 유의적(有意的)인 차이(差異)는 나타내고 있지 않다. COMPLY의 전단강도(剪斷強度)는 약제(藥劑)의 처리농도증가(處理濃度增加)에 따라 증가(增加)하는 경향(傾向)을 나타내고 있으나 유의적(有意的)인 차이(差異)는 없으며 ammonium sulfate보다는 Minalith가 더 양호(良好)한 결과(結果)를 나타내고 있다. COMPLY의 목피율(木破率)은 15%농도(濃度)까지는 증가(增加)하는 경향(傾向)을 보이고 있으나 그 이후(以後)는 감소현상(減少現象)을 나타내고 있다. 평행(平行) 및 교호적층재(交互的層材)의 결과(結果)는 COMPLY 결과(結果)보다 대체로 좋은 결과(結果)를 나타내고 있으나 무처리(無處理)파티클보오드의 결과(結果)는 저조(低調)한 결과(結果)를 나타내고 있다. 약제처리(藥劑處理) COMPLY의 MOR, MOE는 무처리(無處理) 파티클보오드의 결과(結果)보다 136%, 170%로 각각(各各) 증가(增加)하였다. 따라서 내수처리(耐火處理)로 인(因)한 파티클보오드의 강도감소현상(強度減少現像)은 COMPLY를 제조(製造)함으로서 강도적(強度的) 특성(性質)을 개선(改善)시킬 수 있다.

• Journal of the Korean Wood Science and Technology
• /
• 제15권3호
• /
• pp.56-67
• /
• 1987

Plywoods used for construction as a decorative interior material are inflammable and can make fire accidents, causing destruction of human life and property. Therefore, it is indeed required to make fire-retardant treated plywood. In this study, 3.7mm yellow meranti plywoods were soaked in 18% boric acid solutions and tap water by hot-cold bath for 1/2, 2/2, 4/2, 6/2 hours and redrying of treated plywoods was carried out by press drying at the platen temperature of 110, 130, 160, $180^{\circ}C$ and then it was conducted to investigate solution absorption, drying rates, dynamic young's modulus. specific gravity and fire-retardant factors such as burning point, flame spread length. flame exhausted time, back side carbonized area and weight loss by treating time, treating solutions and platen temperature. The results are as follows; 1. When plywood was impregnated with the hot bath temperature of $70^{\circ}C$ for 1. 2, 4, 6 hours and the cold bath temperature of $15^{\circ}C$ for 2 hours respectively, retentions of boric acid were 1.565, l.597, 1.643, 1.709kg/$(30cm)^3$ and all of them exceeded the minimum retention [1.125kg/$(30cm)^3$] even in the shortest treatment. 2. In hot-cold bath method for 1/2 hours, the drying rates of treated plywood remarkably increased with the extension of platen temperature of 110, 130, 160, $180^{\circ}C$ and the values of boric acid treated plywood were 5.900, 10.196, 45.42, 54.958m.c%/min and the values of water treated plywood were 6.014, 12.373, 46.520, 55.730m.c%/min and drying rates of water treated plywood were faster than those of boric acid treated plywood. 3. The values of boric acid treated plywoods in dynamic young's modulus were widely higher than those of water treated plywoods. And it can be observed that there were highly significant differences for treating time between dynamic young's modulus, and the values of boric acid plywoods increased with the extension of treating time but on the contrary water treated plywoods were decreased values with prolonged time 4. It was observed that there were highly significant differences for platen temperature between dynamic young's modulus. When the values of water treated plywoods in dyna nic young's modulus were abruptly decreased according to the rise of platen temperature. boric acid treated plywoods showed rather increased values at $160^{\circ}C$ of platen temperature. And in 2- way interactions, there were also highly significant for dynamic young's modulus between treating time x treating solutions and platen temperature x treating solutions. 5. Correlation coefficients of fire-retardant factors were shown in table 5. It could be recognized that there were close correlations between the treating solutions and burning point, flame spread length, back side carbonized area, flame exhausted time and weight loss, but there was no correlation between fire-retardant factors and treating time and platen temperature. 6. From table 6, it can be observed that there were highly significant differences for burning point, flame spread length, flame exhausted time, back side carbonized area, weight loss between treating solutions. And in 2-way interactions, there were highly significant for burning point, flame spread length, weight loss between treating time $\times$ treating solutions.

• Journal of the Korean Wood Science and Technology
• /
• 제12권4호
• /
• pp.12-18
• /
• 1984

열판온도(熱板溫度)가 내화약제(耐火藥劑)로 처리(處理)된 합판(處理)의 재건조(再乾燥) 후(後) 곡강도(曲强度)에 미티는 영향(影響)을 조사(調査)하기 위해 두께 3.5mm 메란티합판(合板)을 황산(黃酸)암모늄, 제1(第一)인산암모늄, 제2인산(第二燐酸)암모늄 그리고 혼합약제(混合藥劑)인 붕사(硼砂) 붕산(硼酸) 및 미나리스 등(等) 5종(種)의 내화제(耐火劑)의 20% 수용액(水溶液)에 9시간(時間)동안 침지처리(浸漬處理)한 다음, 각각(各各) 열판온도(熱板溫度) $90^{\circ}C$, $120^{\circ}C$ 및 $150^{\circ}C$를 적용(適用)한 단계별(段階別) 건조방식(乾燥方式)으로 건조(乾燥)하여 곡강도시험(曲强度試驗)을 행(行)하였다. 비례한계(比例限界)에서의 응력(應力), 탄성계수(彈性係數), 파괴계수(破壞係數) 및 비례한계(比例限界)까지의 단위체적당(單位體積當) 일 등(等)을 조사(調査)한 바, 수분처리대조구(水分處理對照區)의 경우, 열판온도(熱板溫度) $120^{\circ}C$까지 유지(維持)되던 강도(强度)가 $150^{\circ}C$에 이르러서는 현저한 감소경향(減少傾向)을 나타내었으나, 내화약제처리합판(耐火藥劑處理合板)은 $150^{\circ}C$까지 열판온도(熱板溫度)가 상승(上昇)함에도 불구(不拘), 강도(强度)가 유지(維持)되었으며 일부 약제처리(藥劑處理)의 경우엔 오히려 증가(增加)하는 양상(樣相)도 보여주었다. 건조속도(乾燥速度)와 강도유지(强度維持)의 측면(側面)을 고려할 때, 바람직한 열판건조온도(熱板乾燥溫度)는 $150^{\circ}C$ 였으며 내화약제중(耐火藥劑中) 보강효과(補强效果)가 가장 좋은 약제(藥劑)는 붕사(硼砂) 붕산(硼酸)이었다.

• 한국산림과학회지
• /
• 제60권1호
• /
• pp.30-36
• /
• 1983

대표적(代表的)인 건축내장재료(建築內裝材料)인 합판(合板)은 가연성(可燃性)이 매우 커서 각종(各種) 대형화재(大型火災)의 요인(要因)이 되고 있다. 따라서 내화합판(耐火合板) 제조(製造)의 필요성(必要性)이 절실(絶實)히 요구(要求)되고 있으며, 이와 관련(關聯)하여 우선적(優先的)으로 해결(解決)해야 할 과제(課題)로서 DAP 처리합판(處理合板)의 재건조(再乾燥)에 관(關)한 연구(硏究)를 수행하였는 바 5.25mm두께의 Meranti합판(合板)을 제2인산(第二燐酸)암모늄(DAP) 20% 수용액(水溶液)에 온냉욕법(温冷浴法)으로, 즉 각각 3, 6, 9 및 12시간(時間) 온냉처리(温冷處理)한 다음 공(共)히 3시간(時間) 냉액침지처리(冷液浸漬處理)하였으며 그 때의 약액흡수량(藥液吸收量)과, 이들 처리합판(處理合板)을 130, 145, 160 및 $175^{\circ}C$의 열판온도(熱板温度)로 건조(乾燥)함으로써 건조곡선(乾燥曲線)과 건조속도(乾操速度)를 고찰(考察)하였다. 그 결과(結果), 온냉욕법(温冷浴法)에 의한 합판(合板)의 약액흡수량(藥液吸收量)은 침지시간(浸漬時間)이 증가(增加)함에 따라 꾸준히 증가(增加)하였고, 수분(水分)의 흡수량(吸收量)이 DAP의 흡수량(吸收量)보다 더 많았으며 DAP 약제보유량(藥劑保有量)은 최단침지처리시간(最短浸漬處理時間)의 경우에도 최저보유량(最低保有量)[$1.125kg/(30cm)^3$]을 상회(上廻)하였다. 한편 내화처리합판(耐火處理合板)의 건조곡선(乾操曲線)은 모든 처리시간(處理時間)에서 수분처리합판(水分處理合板)의 건조곡선(乾操曲線)이 DAP약제처리합판(藥劑處理合板)의 그것보다 경사가 급했으며 열판온도(熱板温度)가 상승(上昇)할수록 건조(乾操)가 급속(急速)히 진행(進行)되어 $160^{\circ}C$를 적용(適用)했을 때는 2.5~4분(分)에 건조(乾操)가 완료(完了)되었다. 건조속도(乾操速度)에 있어서도 대체(大體)로 열판온도(熱板温度)가 증가(增加)할수록 그 값이 증가(增加)하였으며 DAP처리(處理)의 경우는 $175^{\circ}C$ 적용시(適用時), 그리고 수분처리(水分處理)의 경우는 $160^{\circ}C$부터 10%/min 이상(以上)의 건조속도(乾操速度)를 나타내었다.

• Journal of the Korean Wood Science and Technology
• /
• 제16권2호
• /
• pp.1-41
• /
• 1988

톱밥을 보드에 활용(活用)하기 위한 방안(方案)으로서, 톱밥자체의 약(弱)한 결집력(結集力)과 치수불량성(不良性)을 개선(改善)하기 위하여 비(非) 목질계(木質系) 재료(材料)인 폴리프로필렌 사(絲)칩과 배향사(配向絲)를 혼합(混合) 결체(結締)함에 다른 보드의 기초성질(基礎性質)로서 물리적(物理的) 기계적(機械的) 성질(性質)을 고찰(考察)하였는 바, 현재(現在) 제재용(製材用)으로 많이 이용(利用)되고 있는 나왕재(羅王材)(white meranti)의 톱밥에 개질재료(改質材料)로서 비(非) 목질(木質) 계(系) 플라스틱 물질(物質)인 폴리프로필렌 사(絲)를 칩상(狀) 또는 배향사(配向絲)의 형태(形態)로 조제(調製)하여 일반(一般) 성형법(成型法)을 적용(適用)함으로써 톱밥과 결체(結締) 구성(構成)한 톱밥보드를 제조(製造)하였다. 12 및 15%로 하여 구성(構成)하였다. 배향사(配向絲)는 보드폭방향(幅方向)으로 0.5, 1.0 및 1.5cm의 일정(一定)한 간격(間隔)으로 배열(配列)하였다. 위의 조건(條件)에 의(依)해 단(單) 2 3층(層)으로 각기(各己) 구분(區分)제조된 사(絲)칩 또는 배향사(配向絲) 구성(構成) 톱밥보드의 물리적(物理的) 및 기계적(機械的) 성질(性質)을 구명(究明)하였는 바, 그 주요(主要)한 결론(結論)을 요약(要約)하면 다음과 같다. 1. 사(絲)칩 혼합(混合) 단층구성(單層構成)보드의 두께 팽창율(膨脹率)은 톱잡대조(對照)보드의 팽창율보다 모두 낮았다. 사(絲)칩 함량(含量)을 증가(增加) 시킴에 따라서 두께 팽창율은 점차(漸次) 감소(減少)하는 경향이 뚜렷하였다. 한편, 2층구성(層構成)보드는 단층(單層) 구성(構成)보드보다 높은 팽창율을 나타냈으나 대부분이 톱밥대조(對照)보드 보다 팽창율이 낮았다. 3층(層)으로 사(絲)칩구성(構成)한 보드는 톱밥대조(對照)보드보다도 모두 낮은 두께 팽창율을 나타냈다. 2. 사(絲)칩 배향사(配向絲) 구성(構成)보드의 두께 팽창율은 0.5cm 배향간격에서 사(絲)칩함량(含量) 12%와 15%의 길이 1.0cm와 1.5cm로 구성함으로써 단층(單層) 및 3층구성(層構成)보드의 최저치(最低値)보다 더 낮았다. 3. 단층구성(單層構成)보드의 휨강도는 비중(比重) 0.51 구성(構成)보드의 경우 사(絲)칩함량(含量) 3%에서 톱밥대조)對照)보드보다 높은 강도를 나타냈으나, KS F 3104 의 파티클보드 100타입 기준(基準) 값인 80 kgf/$cm^2$에 훨씬 못 미쳤다. 그러나 비중(比重) 0.63 구성(構成)보드에서 함량(含量) 6%의 길이 1.5cm 사(絲)칩 구성과 함량(含量)3% 의 모든 사(絲)칩 길이로 구성한 보드, 그리고 비중(比重) 0.72의 모든 사(絲)칩 구성보드는 KS F 기준값을 훨씬 상회(上廻) 하였다. 2층구성(層構成)보드의 휨강도는 톱밥대조(對照)보드보다도 사(絲)칩구성의 경우 모두 낮았으며 단층구성(單層構成)보드의 휨강도보다도 낮은 값을 나타냈다. 3층구성(層構成)보드의 휨강도는 사(絲)칩 함량(含量) 9% 이하(以下)의 길이 1.5cm 구성보드는 모두 톱밥대조(對照)보드보다 높은 값을 나타냈으며 KSF 기준값을 훨씬 상회(上廻) 하였다. 4. 배향사구성(配向絲構成) 톱밥보드의 경우(境遇), 배향간격(配向間隔)이 좁은 0.5cm에서 가장 높은 휨강도를 나타냈으며, 배향간격이 보다 넓은 1.0cm 와 1.5cm 구성(構成)에서는 휨 강도가 0.5cm 간격 보다 낮았다. 그러나 배향사구성(配向絲構成) 톱밥보드는 모두 톱밥대조(對照)보드 보다 높은 휨강도를 나타냈다. 5. 사(絲칩) 배향사(配向絲) 구성 보드의 휨강도는 거의 대부분(大部分)의 구성보드에서 톱밥대조(對照)보드보다 높은 값을 나타냈으며 KSF 기준값을 훨씬 상회(上廻) 하였다. 특(特)히 배향간격이 좁고, 길이가 긴 사(絲)칩으로 구성한 보드의 휨강도가 높은 값을 나타냈다. 그리고 사(絲)칩을 배향사(配向絲)와 혼합(混合) 구성(構成)할 때 배향사의 간격이 넓어짐에 따라 톱밥과 배향사(配向絲)만으로 구성한 보드보다도 휨 강도가 높아지는 현상(現象)이 나타났다. 6. 단층(單層), 2층(層) 및 3층(層) 구성(構成) 보드의 탄성계수는 대부분(大部分) 톱밥대조(對照)보드 보다 낮은 값을 나타냈다. 그러나 배향사(配向絲) 구성(構成) 톱밥보드에 있어서는, 배향 간격이 0.5, 1.0, 1.5crn로 됨에 따라서 톱밥대조(對照)보드보다도 각각(各各) 20%, 18%, 10% 탄성계수가 증가(增加)되었다. 7. 사(絲)칩 배향사(配向絲) 구성(構成) 보드의 탄성계수(彈性係數)는 배향간격 0.5crn, 1.0cm 및 1.5crn에서 거의 모두 톱밥대조(對照)보드보드보다도 훨씬 높은 값을 나타냈다. 그리고 함량(含量)9% 이하(以下)에서 사(絲)칩길이를 0.5cm이상(以上)으로 구성하였을 때 배향사(配向絲)만을 구성한 톱밥보드보다도 탄성계수가 높아지는 현상(現象)이 나타났는데, 배향(配向)간격이 좁은 경우 사(絲)칩결체(結締)에 의(依)한 탄성계수(彈性係數) 증가효과(增加效果)가 컸다. 8. 사(絲)칩 혼합(混合) 단층구성(單層構成) 보드의 박리저항(剝離抵抗)은 톱밥대조(對照)보드 보다 모두 낮았다. 그러나 비중(比重) 0.63의 사(絲)칩 구성보드는 KS F 3104의 100타입 기준 값인 1.5kgf/$cm^2$를 모두 상회(上廻) 하였고, 비중(比重) 0.72의 사(絲)칩 구성보드는 200타입의 기준값 3kgf/$cm^2$를 상회(上廻)하는 박리저항(剝離抵抗)을 나타냈다. 2층(層), 3층(層) 및 배향구성(配向構成)도 거의 모두 200타입의 기준값 3kgf/$cm^2$를 상회(上廻) 하였다. 9. 단층구성(單層構成)보드의 나사못유지력(維持力)은 사(絲)칩을 혼합 구성한 경우, 대체(大體)로 톱밥대조(對照)보드보다도 낮은 값을 나타냈다. 그러나, 2층(層) 및 3층구성(層構成)보드에서는 사(絲)칩 구성(構成)에 따른 감소경향(減少傾向)이 나타나지 않고 대체로 고른 나사못 유지력을 나타냈다. 또한, 사(絲)칩 배향사(配向絲) 구성(構成)보드에서는 사(絲)칩함량(含量) 9% 이하(以下)에서 거의 모두 톱밥대조(對照)보드 보다도 높은 나사못 유지력을 나타냈다.