• Polymer(Korea)
• /
• v.39 no.1
• /
• pp.99-106
• /
• 2015

The surface of nano-kenaf containing cellulose fibers was treated with alkali (NaOH) and their effects on the physical properties of the polypropylene (PP) composite were investigated. The treatment of alkali on the fibers increased the melt flow index (M.I.), elongation%, and impact strength, while it decreased the tensile strength, flexural modulus and heat deflection temperature (HDT) of the compound compared to the untreated one. It seemed the alkali treatment on the nano-kenaf fiber changed the character of the fiber due to removal of impurities and chemicals on the surface and resulted in decreased interfacial adhesion between the nano-fiber surface and the PP matrix and changed the character of the PP.

• Fibers and Polymers
• /
• v.3 no.1
• /
• pp.38-42
• /
• 2002

Polypropylene filaments were spun from a mixture of PP chips of two different Melt Flow Index (MFI) (3 MFI and 35 MFI). A significant difference was observed in the melting characteristics of the resultant filaments from either of the individual components as observed from the DSC. The main difference being in the degree of melting achieved at any temperature in the initial stages of the melting range, which was found to be higher in case of the filaments spun from the b]end. These filaments were then thermally bonded using silicon oil bath and heated roller method. Subsequently the bond strength of the filaments was measured on the Instron Tensile Tester using the loop technique. The values of the world strengths obtained from the blend were compared with those made from the individual component. It was found that the bond strength of the bonds obtained from the blended filament at a given temperature was higher than that of the bonds made from the filaments of either of the individual components, which is also suggested by the DSC curves. The difference in the bond strength was found to be as high as 25% in case of the blend with 60:40 composition ratios of the 3 MFI and 35 MFI components respectively.

• Elastomers and Composites
• /
• v.46 no.2
• /
• pp.125-131
• /
• 2011

The effects of chopped kenaf fiber concentration on mechanical property of polypropylene (PP) composite are investigated. The addition of kenaf increased the tensile strength, flexural modulus, impact strength, specific gravity, and HDT, while decreased the elongation%, flexural strength, and melt flow index. The increase of mechanical properties is due to increased surface area contacting between fiber and polymer matrix and fiber-fiber interaction. Volatile extractives in the kenaf seemed to decrease the interfacial adhesion between kenaf surface and PP.

• Polymer(Korea)
• /
• v.39 no.2
• /
• pp.200-209
• /
• 2015

In this study, the influence of dilauroyl peroxide on mechanical and thermal properties of different polypropylene (PP) matrices was investigated. Polypropylene matrices, different molecular weight isotactic PP containing 0.01, 0.02, 0.04, 0.06, 0.08, and 0.1 wt% of dilauroyl peroxide (DLP) were prepared by using a single-screw extruder. The effect of the visbreaking agent (DLP) on mechanical, physical, thermal and morphological properties of different molecular weight PP had been studied. Mechanical properties (tensile strength at break point, at yield and elongation at break point), melt flow index (MFI), scanning electron microscope (SEM) and differential scanning calorimetric (DSC) analyses of these matrices were examined. Melting ($T_m$) and crystallization ($T_c$) temperatures, crystallinity ratio (%) and enthalpies were determined. The microstructure of isotactic polypropylene matrix was investigated by scanning electron microscopy (SEM). From SEM analysis, it was observed that the surface disorder increased by the increasing amount of DLP. As a result of DSC analyses, the crystallinity ratio of the PP matrices has varied between 1.64-7.27%. Mechanical properties of the matrices have been improved. Particularly, the mechanical tests of PP have given interesting results when compounded with 0.06-0.08 wt% dilauroyl peroxide (DLP). Mechanical properties and thermal decomposition processes were all changed by increasing the amount of DLP in the matrix structure.

• Polymer(Korea)
• /
• v.37 no.5
• /
• pp.613-617
• /
• 2013

The effects of nano size kenaf cellulose fiber on mechanical property of polypropylene (PP) composite were investigated. The addition of nano-kenaf in place of natural kenaf showed higher tensile strength, flexural strength, impact strength, and heat deflection temperature compared to the natural kenaf filled PP composite, while it shows lower melt flow index, elongation%, and flexural modulus. These seemed to be due to the increased surface area of nano-kenaf fiber contacting PP matrix and reduced impurities such as volatile extractives on the fiber surface.

• Elastomers and Composites
• /
• v.38 no.3
• /
• pp.262-272
• /
• 2003

Maleic anhydride-grafted-polypropylene(PP-g-MA) were used as a blend component and a compatibilizer, respectively, for two reactive blends of polyamide 66(PA 66)PP-g-MA binary blends and PA 66/polypropylene(PP)/PP-g-MA ternary blends. The goal of this work was to investigate the property differences between binary and ternary blends. Tensile strength, flexural modulus, heat deflection temperature, impact strength, melt flow index, and the dependence of melt viscosity on the shear rate were examined. The impact strengths of binary blends were higher than those of ternary blends at all compositions, since the in situ synthesis of PP-g-PA 66 copolymer through the imide formation between the amine end group of PA 66 and the anhydride group of PP-g-MA gave the increase of molecular weight and was more popular in binary blends than in ternary blends. In case of ternary blends, most of the properties were superior to those of binary blends, owing to the better properties of PP compared with PP-g-MA. The toughened binary blends with 70/30(PA 66/PP-g-MA) and 80/20 ratios were not commercially applicable due to their poor processibility. So, the ternary blends which showed lower melt viscosities were recommended for the commercial applications.

• Polymer(Korea)
• /
• v.33 no.4
• /
• pp.358-363
• /
• 2009

Maleic anhydride-grafted polypropylene has been widely used to improve the interfacial interaction between the components in PP/polar polymer blends and PP/filler composites and to maximize the physical properties and thermal properties. In this paper. the maleic anhydride (MAH)-grafted polypropylene (co-PP) was fabricated through reactive extrusion process with di-cumyl peroxide (DCP) as an initiator. The grafting degree of MAH depending on the contents of DCP and MAH was investigated by FT-IR spectra and chemical titration. The grafting degree increased with increasing MAH concentration and also showed maximum value at 0.06 wt% of DCP concentration. Melt flow index (MFI) of the grafted copolymer was increased with increasing the contents of MAH. The DSC and TGA analysis data indicate the melting temperature and thermal degradation of PP depending on the grafting degree of MAH.

• Journal of the Korean Society of Safety
• /
• v.26 no.4
• /
• pp.47-58
• /
• 2011

Halogen free intumescent flame retardants(IFRS), such as the mixture of melamine phosphate(MP) and char forming agents(pentaerythritol(PER), di-pentaerythritol(DiPER), tris(2-hydroxyethyl) isocyanurate(THEIC)), were prepared and characterized. Polypropylene(PP)/$IFR_S$ composites were also prepared in the presence of ethylene diamine phosphate(EDAP) as a synergist and used into flame retardant PP powder coatings. Thermoplastic PP powder coatings at 20 wt% flame retardant loading were manufactured by extruded and then mechanical cryogenic crushed to bring them in fine powder form. These intumescent flame retardant powder coatings($IFRPC_S$) were applied on mild steel surface for the purpose of protection and decorative. It is a process in which a $IFRPC_S$ particles coming in contact with the preheated mild steel surface melt and form a thin coating layer. The obtained MP flame retardant was analyzed by utilizing FTIR, solid-state $^{31}P$ NMR, ICP, EA and PSA. The mechanical properties as tensile strength, melt flow index(MFI) and the thermal property as TGA/DTA and the fire safety characteristics as limiting oxygen index(LOI), UL94 test, SEM were used to investigate the effect of $IFRPC_S$. The experimental results show that the presence of $IFR_S$ considerably enhanced the fire retardant performances as evidenced by the increase of LOI values 17.3 vol% and 32.6 vol% for original PP and $IFRPC_S$-3(PP/MP-DiPER/EDAP), respectively, and a reduction in total flaming combustion time(under 15 sec) in UL94 test of $IFRPC_S$. The prepared $IFRPC_S$-3 have good comprehensive properties with fire retardancy 3.2 mm UL94 V-0 level, LOI value 32.6%, tensile strength $247.3kg/cm^2$, surface roughness Ra $0.78{\mu}m$, showing a better application prospect. Through $IFRPC_S$-2(PP/MP-PER/EDAP) and $IFRPC_S$-3 a better flame retardancy than that of the $IFRPC_S$-1(PP/MP/EDAP) was investigated which was responsible for the formed more dense and compact char layer, improved synergy effect of MP and PER/DiPER.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.5 no.4
• /
• pp.318-331
• /
• 1995

The c - axis oriented single crystal of $LiNbO_3$ and $LiNbO_3$ : 5mol%MgO was success-fully grown by Floating zone method using halogen lamp as a heat source. The effects of the sintering condition of the feed rod and the atmosphere gas during the crystal growth on the be havior of the feed rod/melt interface were studied for growing crystal with the high quality, and then, the optimum growth conditions were determined by studying the experimental param eters, such as gas flow rate, pulling rate, rotation speeds of the feed rod and the seed. The grown crystals were analyzed using the chemical etching to observe the tch pattern and the ICP (Inductively Coupled Plasma) to determine the composition uniformity and the impurity content of Fe. The effects of additive (5 mol % MgO) on the transmittance and refractive index was, also, analyzed. In order to compare the nonlinear optical oharacteristics of $LiNbO_3$ with those of the other optical materials, the nonlinear optical refractive index ($n_2$) was calcu l lated using the measured refractive index.

• Applied Chemistry for Engineering
• /
• v.24 no.1
• /
• pp.104-111
• /
• 2013

Poymer blends of two degradable aliphatic polyesters, relatively expensive material polylactic acid (PLA) and relatively inexpensive material poly(butylene adipate-co-terephthalate) (PBAT), were used in this study. Three different kinds of modifiers were used with various amounts. Diisocyanate type methylenediphenyl 4,4'-diisocyanate (MDI) and hexamethylene diisocyanate (HDI) were used as modifiers and epoxy type coupling agents also used. The melt flow index (MFI) and dynamic viscoelasticity of various compositions of PLA/PBAT blends were studied. The mechanical property and morphology with respect to the fracture surface of PLA/PBAT blends were also investigated using tensile test and field emission scanning electronic microscopy, respectively. These tests were also used to verify the compatibility of PLA/PBAT and the effect of mechanical properties due to the use of modifiers. Tensile properties of PLA/PBAT blends modified with HDI were improved remarkably.