• Macromolecular Research
• /
• v.12 no.5
• /
• pp.459-465
• /
• 2004

We have synthesized poly(l,4-cyclohexylenedimethylene terephthalate-co-hexamethylene terephthalate) [P(CT-co-HT)] random copolymers having various comonomer contents, from 0 to 100 mol% HT, by melt-condensation and have investigated their crystallization behavior by using differential scanning calorimetry (DSC) and wide-angle X-ray diffraction (WAXD). We observed that P(CT-co-HT)s exhibit clear melting and crystallization peaks in their DSC thermograms and sharp diffraction peaks in their WAXD patterns for all of their copolymer compositions as a result of cocrystallization of the CT and HT units, even though the copolymers are statistically random copolymers. When we plotted the melting and crystallization temperatures of P(CT-co-HT)s and the d-spacings of all the reflections against the copolymer composition, we observed a eutectic point at ca. 80 mol% HT, which suggests that a crystal transition occured from a PCT-type crystal to a PHT-type crystal. Both the DSC and WAXD results support the notion that P(CT-co-HT) copolymers undergo an isodimorphic cocrystallization.

• Polymer(Korea)
• /
• v.30 no.3
• /
• pp.224-229
• /
• 2006

Quaternary ammonium salt terminated silane was prepared from aminopropyldimethylethoxysilane with methyliodide and ionized 7,7,8,8-tetracyanoquinodimethane $(Li^+TCNQ^-)$ was prepared from TCNQ with methyliodide and lithium iodide. Quaternary ammonium salt silane-TCNQ adduct (ST) was prepared by reacting quaternary ammonium salt terminated silane with $Li^+TCNQ^-$ solution. Poly (dimethylsiloxane)-ST adduct (PST) was prepared by condensation of $\alpha,\omega-hydroxyl$ group terminated poly (dimethylsiloxane) (PDMS) with ST. Maleated polyethylene modified with PDMS (PST-g-MPE) was prepared by melt polymerization of maleated PE and PST in internal mixer and PST-g-MPE/carbon black (CB) and MPE/CB composites were prepared by compounding PST with MPE and PST-g-MPE, respectively. The thermal and mechanical properties of the composites were measured and dispersion characteristics of CB in matrix rosins show that the dispersion of CB in PST-g-MPE/CB was better than that of MPE/CB composite.

• Polymer(Korea)
• /
• v.36 no.1
• /
• pp.9-15
• /
• 2012

We prepared a series of aromatic liquid crystals (LCs) based on wholly aromatic ester units with the reactive end group methyl maleimide by means of melt condensation method, and the resulting LCs were thermally crosslinked to produce liquid crystalline thermoset (LCT) films. The synthesized LCs and LCTs were characterized with Fourier transform infrared (FTIR) spectroscopy, wide angle X-ray diffraction (WAXD), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), thermomechanical analysis (TMA), and polarizing optical microscopy (POM) with a hot stage. The glass transition temperature ($T_g$) and coefficient of thermal expansion are strongly affected by the mesogen units in their main chain structures. The $p$-substituted biphenyl LC was found to have the highest thermal property value.

• Journal of the Korean Chemical Society
• /
• v.18 no.5
• /
• pp.381-388
• /
• 1974

When mixture of p-phenylenediamine (PPD) and m-aminophenol (MAP) were reacted with formaldehyde (F) varying their amounts under $N_2$ stream at the temperature of -5∼0$^{\circ}$, addition condensation reaction occurred and brown colored resins(in some cases orange colored) were formed immediately. All resins thus formed were insoluble in most ordinary organic solvents and did not melt up to 300$^{\circ}$. When the resins were treated with dilute(7 %) aqueous sodium hydroxide solution, the adsorptivity of methylene blue on them showed marked improvement reaching as much as 80 mg of methylene blue on 1 g of the resin. On the other hand, in the case of bromophenol blue, its amount of adsorption appeared 250 mg per 1 g of the resin. The TGA under $N_2$ atmosphere indicated that the resin formed in molar ratio of 1 : 3 : 8 (PPD : MAP : F) showed the best heat-resistant property among others. About 40 % weight loss was observed for this resin at 900$^{\circ}$ with heating rate of 2$^{\circ}$ per minute.