• Journal of the Korean Wood Science and Technology
• /
• 제42권5호
• /
• pp.555-562
• /
• 2014

Characteristics of carbonized fiberboard such as chemical materials absorption, electromagnetic shielding, and electrical and mechanical performance were determined in previous studies. The carbonized board therefore confirmed that having excellent abilities of these characteristics. In this study, the effect of density on physical properties and sound absorption properties of carbonized fiberboards at $800^{\circ}C$ were investigated for the potential use of carbonized fiberboards as a replacement of conventional sound absorbing material. The thickness of fiberboards after carbonization was reduced 49.9%, 40.7%, and 43.3% in low density fiberboard (LDF), medium density fiberboard (MDF), and high density fiberboard (HDF), respectively. Based on SEM images, porosity of carbonized fiberboard increased by carbonization due to removing adhesives. Moreover, carbonization did not destroy structure of wood fiber based on SEM results. Carbonization process influenced contraction of fiberboard. The sound absorption coefficient of carbonized low density fiberboard (c-LDF) was higher than those of carbonized medium density fiberboard (c-MDF) and carbonized high density fiberboard (c-HDF). This result was similar with original fiberboards, which indicated sound absorbing ability was not significantly changed by carbonization compared to that of original fiberboards. Therefore, the sound absorbing coefficient may depend on source, texture, and density of fiberboard rather than carbonization.

• Journal of the Korean Wood Science and Technology
• /
• 제17권4호
• /
• pp.77-82
• /
• 1989

In this study the oxygen index method was used to compare the duration of flaming and the rate of weight loss at the level of 6 and 9mm panel thicknesses among solid wood, plywood, particleboard, and medium density fiberboard. The obtained results were as follows: 1. In 9mm-thick panels, the combustibility was the largest in lauan solid wood followed by medium density fiberboard. particleboard. and plywood. 2. Medium density fiberboard was burned more easily than plywood in 6mm-thick panels and the higher oxygen concentration was needed as the panel thickness increased. 3. The oxygen indices of 9mm-thick panels were 29.0 in lauan solid wood, 31.4 in medium density fiberboard, 33.0 in particleboard, and 33.4 in plywood and those of 6mm-thick panels were 28.3 in medium density fiberboard and 29.7 in plywood. 4. The rate of weight loss was the largest in lauan solid wood followed by medium density fiberboard, plywood, and particleboard.

• Journal of the Korean Wood Science and Technology
• /
• 제19권4호
• /
• pp.43-51
• /
• 1991

This study was carried out to determine the withdrawal strength of various screws according to root diameter of screw and embeded length on the face and edge of domestic particleboard and medium density fiberboard. The obtained results were as follows: 1. The withdrawal strength of screw in domestic particleboard and medium density fiberboard was closely related to embeded length of the screw but less dependent on root diameter of the screw. 2. The withdrawal strength on the face and edge of domestic particleboard could be predicted by means of the following expression: $F_{Pf}=4.60{\times}D^{0.24}{\times}L^{1.14}(R^2=0.87)$ $F_{Pe}=0.54{\times}D^{0.43}{\times}L^{1.73}(R^2=0.84)$ Where: $F_{Pf}$ : withdrawal strength on the face of particleboard(kgf) $F_{Pe}$=withdrawal strength on the edge of particleboard(kgf) D=diameter of the screw(mm) L=embeded length(mm) 3. The withdrawal strength on the face and edge of domestic medium density fiberboard could he predicted by means of the following expression: $FM_f=1.53{\times}D^{0.53}{\times}L^{1.39}(R^2=0.93)$ $F_{Me}=1.14{\times}D^{0.66}{\times}L^{1.36}(R^2=0.87)$ where: $F_{Mf}$ = withdrawal strength on the face of medium density fiberboard(kgf) $F_{Mf}$=withdrawal strength on the edge of medium density fiberboard(kgf).

• Journal of the Korean Wood Science and Technology
• /
• 제19권3호
• /
• pp.27-34
• /
• 1991

Screw withdrawal test was carried out on the face and edge of domestic particleboard and medium density fiberboard in order to evaluate optimum pilot hole diameter. The obtained results were as follows: 1. Maximum withdrawal strengths on the face and edge of particleboard were obtained with pilot hole diameters at about 50% of root diameters of screw. 2. Maximum withdrawal strength on the face and edge of medium density fiberboard were obtained with pilot hole diameters that were about 60% and 50% of root diameters of screw, respectively. 3. Withdrawal strength showed about 91% of maximum withdrawal strength when pilot holes were not pre bored at particleboard. but when pilot holes at 90% of root diameter of screw withdrawal strength showed about as 51.3% of maximum withdrawal strength. 4. Withdrawal strength showed about 88% of maximum strength when pilot holes were not used, but withdrawal strength indicated 55.4% of maximum strength in case of 90% of root diameters of screw. 5. Maximum withdrawal strength on the face of particleboard was about 70.5% higher than that of the edge, and however medium density fiberboard was about 19.6% higher than that of the edge.

• 공업화학
• /
• 제24권6호
• /
• pp.672-675
• /
• 2013

Medium-density fiberboard의 최적 열분해 조건을 찾기 위해 유동층 반응기를 이용하여 다양한 실험조건에서 급속열분해 실험을 수행하였다. 열분해 온도를 $425^{\circ}C$와 $575^{\circ}C$ 사이에서 변화시켰을 때, $525^{\circ}C$에서 최대 바이오오일 수율 52 wt%를 얻을 수 있었다. 열분해 온도가 높을수록 생성되는 바이오오일의 품질이 좋은 것으로 나타났다. 높은 온도에서 열분해 반응을 수행할 경우, 상당한 양의 oxygenates 및 acids 물질들이 분해되고, 대신 aromatics와 phenolics 같은 고부가가치 물질들이 생성되었다. 기체상 생성물의 대부분은 CO와 $CO_2$였다. 열분해 온도가 높을수록 CO와 $C_1-C_4$ 탄화수소 생성량이 많았다.

• Journal of the Korean Wood Science and Technology
• /
• 제45권4호
• /
• pp.444-455
• /
• 2017

This study was conducted to evaluate the effect of panel density and resin content on properties of medium density fiberboard (MDF) to obtain some insights on MDF properties as a function of panel density and resin content. MDF panels with different panel densities such as 650, 700, 750 and $800kg/m^3$ were manufactured by adjusting the amount of wood fibers in the mat forming. MDF panels were also fabricated by spraying 8, 10, 12, and 14% of urea-formaldehyde (UF) resins onto wood fibers in a drum-type mechanical blender to fabricate MDF panels with a target density of $650kg/m^3$. As the panel density and resin content increased, the internal bonding (IB) strength of MDF panel consistently increased. Modulus of rupture (MOR), modulus of elasticity (MOE) and screw withdrawal resistance (SWR) had a similar trend to the IB strength. In physical properties, thickness swelling (TS) and water absorption (WA) decreased with an increase in both panel density and resin content. In addition, the formaldehyde emission (FE) which increased as the panel density and resin content became greater. In overall, the panel density of MDF had more significant effect than the resin content in all properties of MDF panels, indicating that it was better to adjust the panel density rather than the resin content for MDF manufacture.

• Journal of the Korean Wood Science and Technology
• /
• 제42권5호
• /
• pp.597-604
• /
• 2014

Laboratory-scale landfills (simulated landfills) were designed to determine the formaldehyde released into air and leachate from medium density fiberboard (MDF). Simulated landfills were constructed using cylindrical plastic containers containing alternating layers of soil and MDF for a total of five layers. The highest concentration of formaldehyde was found in the air and leachate from the MDF only treatment compared to treatments containing MDF and soil. At the end of the study (28 days), formaldehyde concentrations in air and leachate from treatments containing MDF and soil decreased by 70 percent and 99 percent, respectively, while the treatment containing MDF only still released formaldehyde into the air and leachate. Therefore, waste MDF after storing 4 weeks in water may be recycled as compost or mulch based on formaldehyde leaching. Also, these data indicate soil restricts formaldehyde release into air and leachate and provides new information about the fate of wood-based composite waste containing UF resin disposed in landfills.

• International Journal of Reliability and Applications
• /
• 제4권4호
• /
• pp.157-170
• /
• 2003

In this paper we apply statistical reliability tools to manage and seek improvements in the strengths of medium density fiberboard (MDF). As a part of the MDF manufacturing process, the product undergoes destructive testing at various intervals to determine compliance with customer′s specifications. Workers perform these tests over sampled cross sections of the MDF panel to measure the internal bond (IB) in pounds per square inches until failure. We explore both graphically and statistically this "pressure-to-failure" of MDF. Also, we briefly comment on reducing sources of variability in the IB of MDF.

• Journal of the Korean Wood Science and Technology
• /
• 제49권5호
• /
• pp.453-461
• /
• 2021

In wood-based composite panels, low-molar ratio (LMR) urea-formaldehyde (UF) resins usually result in reduced formaldehyde emission (FE) at the expense of poor adhesion. However, the FE and adhesion of medium-density fiberboard (MDF) bonded with LMR UF resins were both improved in this study. The modified LMR UF resins with transition metal ion-modified bentonite (TMI-BNT) nanoclay simultaneously improved the FE and adhesion of MDF panels. The modified LMR UF resins with 5% TMI-BNT resulted in a 37.1% FE reduction and 102.6% increase in the internal bonding (IB) strength of MDF panels. Furthermore, thickness swelling and water absorption also significantly decreased to 13.0% and 24.9%, respectively. These results imply that TMI-BNT modification of LMR UF resins could enhance the formation of a three-dimensional network rather than crystalline domains, resulting in improved cohesion.

• Journal of the Korean Wood Science and Technology
• /
• 제33권5호통권133호
• /
• pp.45-49
• /
• 2005

The sound absorption coefficients of three types commercial fiberboard were experimentally measured under a relatively low frequency range of 50 to 1600 Hz by the two microphone transfer function method. The sound absorption coefficient of 30 mm thick fiberboard was higher than that of 18 mm thick fiberboard at the frequency range of 50 to 1.2 KHz. The sound absorption coefficient of medium density fiberboard was a little higher than that of low density fiberboard.