• Journal of the Korean Magnetics Society
• /
• v.18 no.4
• /
• pp.142-146
• /
• 2008

The angular dependence of the exchange bias($H_{ex}$) and coercivity($H_c$) in multilayer $[Pt/Co]_N-IrMn$ with applied measuring field rotated toward in-plane at angle $\theta$ from perpendicular-to-plane, has been measured. Multilayer films consisting of $Si/SiO_2/Ta(50)/Pt(4)/[Pt(15)/Co(t_{Co})]_N/IrMn(50)/Ta(50)(in\;{\AA})$ were prepared by magnetron sputtering under typical base pressure below $2{\times}10^{-8}$ Torr at room temperature. Magnetization measurements were performed on a vibrating sample magnetometer and extraordinary Hall voltage measurement systems after cooling from 550 K under a field of 2 kOe applied along the perpendicular to film direction. The hysteresis loop shifts from the origin not only along the field axis but also along the magnetization axis. $H_{ex}$ and $H_c$ show a $1/cos{\theta}$ and $1/|cos{\theta}|$ dependence on the angle($\theta$) between the applied measuring field and the perpendicular-film direction, respectively. This $1/cos{\theta}$ dependence can be accounted for by considering the angular dependence of strong out-of-plane magnetic anisotropy introduced during the field cooling.

• Journal of the Korean Magnetics Society
• /
• v.13 no.2
• /
• pp.53-58
• /
• 2003

Annealing effects of exchange bias fields ($H_{2ex}$(top), $H_{lex}$ (bottom)) on composite type NiFe/[FeMn/Mn]$_{80}$/NiFe multilayers have been studied. Three samples with ultra-thin Mn inserted layers on glass/Ta(50 $\AA$)/NiFe(150 $\AA$)/[F $e_{53}$M $n_{47}$(1.25 $\AA$)/Mn(0 $\AA$, 0.11 $\AA$, 0.3 $\AA$)]$_{80}$/NiFe(90 $\AA$)/Ta(50 $\AA$) were prepared by ion beam sputtering. The average x-ray diffraction peak ratios NiFe(111) of FeMn (111) fcc textures for the Mn inserted total thicknesses of 0 $\AA$, 9 $\AA$, and 24 $\AA$ were about 0.65, 0.90, and 1.5, respectively. For the sample without Mn inserted layer, the $H_{2ex}$ of 260 Oe up to 300 $^{\circ}C$ disappeared at 350 $^{\circ}C$. For two multilayer samples with ultra-thin Mn layers of 0.11 $\AA$ and 0.3 $\AA$, the $H_{2exs}$ of 310 Oe and 180 Oe up to 300 $^{\circ}C$ endured of 215 Oe and 180 Oe at 350 $^{\circ}C$, respectively. The $H_{ex}$ (bottom)s of three samples decreased from 100 Oe to 70 Oe up to 250 $^{\circ}C$, while these values increased beyond 300 $^{\circ}C$. This observation can be attributed to less diffusive path of Mn atoms in bottom NiFe than top NiFe layer. The top and bottom coercive fields slightly varied about 5 Oe∼10 Oe. From these results, we could obtain the enhancement of exchange coupling intensity and thermal stability by an ultra-thin Mn inserted layer on NiFe/[FeMn/Mn]$_{80}$/NiFe Multilayers.

• Journal of the Korean Magnetics Society
• /
• v.7 no.2
• /
• pp.90-96
• /
• 1997

We have studied crystallographic and magnetic properties of $NdFe_{10.7}Ti_ {1.2}Mo_{0.1}$ by Mossbauer spectroscopy, X-ray diffraction and vibrating sample magnetometer (VSM). The alloys were prepared by arc-melting under an argon atmosphere. The $NdFe_{10.7}Ti_{1.2}Mo_{0.1}$ has pure a single phase, whereas $NdFe_{10.7}Ti_{1.3}$ contains some $\alpha$-Fe, conformed with X-ray diffractometry and Mossbauer measurements. The $NdFe_{10.7}Ti_ {1.2}Mo_{0.1}$ has a $ThMn_{12}-type$ tetragonal structure with $a_0=8.637{\AA}$ and $c_0=4.807{\AA}$. The Curie temperature ($T_c$) is 600 K from the result of Mossbauer measurement performed at various temperatures ranging from 13 to 800 K. Each spectrum of below $T_c$ is fitted with five subspectra of Fe sites in the structure ($8i_1, 8i_2, 8j_2, 8j_1, 8f$). The area fractions of the subspectra at room temperature are 12.3%, 14.0%, 21.0% 11.8%, 40.9%, respectively. Magnetic hyperfine fields for the Fe sites decrease in the order, $H_{hf}(8i)>H_{hf}(8j)>H_{hf}(8f)$. The abrupt changes in the magnetic hyperfine field, an magnetic moment observed at about 160 K in $NdFe_ {10.7} Ti_{1.2}Mo_{0.1}$ are attributed to spin reorientations. The average hyperfine field of the $NdFe_{10.7}Ti_{1.2}Mo_{0.1}$ shows a temperature dependence of $[H_{hf}(T)-H_{hf}(0)]/H_{hf}(0)=-0.34(T/T_C)^{3/2}-0.14(T/T_C)^{5/2}$ for $T/T_c<0.7$, indicative of spin wave excitation. The Debye temperatures of $NdFe_{10.7}Ti_{1.2}Mo_{0.1}$ is found to be Θ=340$\pm$5 K.

• Journal of the Korean Magnetics Society
• /
• v.15 no.2
• /
• pp.100-105
• /
• 2005

$Ni_{0.9}Zn_{0.1}Fe_2O_4$ nanoparticles have been prepared by a sol-gel method. The structural and magnetic properties have been investigated by DTA/TGA, XRD, SEM, and $M\ddot{o}ssbauer$ spectroscopy, VSM. $Ni_{0.9}Zn_{0.1}Fe_2O_4$ powder that was annealed at $300^{\circ}C$ has spinel structure and behaved superparamagnetically. The estimated size of superparammagnetic Ni-Zn ferrite nanoparticle is around 10 nm. The hyperfine fields at 13 K for the A and B patterns were found to be 533 and 507 kOe, respectively. The blocking temperature ($T_B$) of superparammagnetic $Ni_{0.9}Zn_{0.1}Fe_2O_4$ nanoparticle is about 250 K. The magnetic anisotropy constant and relaxation time constant of $Ni_{0.9}Zn_{0.1}Fe_2O_4$ nanoparticle were calculated to be $1.6\times10^6\;ergs/cm^3$ and ${\tau}_0=5.0{\times}10^{-13}$ s, respectively. Also, Temperature increased up to $43^{\circ}C$ within 10 minutes under AC magnetic field of 7 MHz. It is considered that $Ni_{0.9}Zn_{0.1}Fe_2O_4$ powder that was annealed at $300^{\circ}C$ is available for biomedicine application such as hyperthermia, drug delivery system and contrast agents in MRI.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.864-873
• /
• 1995

Amorphous $Fe_{73.5}Cu_{1}Nb_{3}Si_{16.5}B_{6}$ ribbons were annealed for different time at $500^{\circ}C$ and $552^{\circ}C$, just before and after the exothermic reaction in DSC curve. The development of nanocrystalline phase was investigated by means of $M\"{o}ssbsuer$ spectroscopy. The crystalline phase consists mainly of $DO_{3}Fe-Si$. Though slight in amount (5%), another ferromagnetic phase which could be presumed $t-Fe_{3}B$ was detected Si content of $DO_{3}Fe-Si$, Si/(Fe+Si), was 0.218 under the heat treatment at $500^{\circ}C$ for 60 min and 0.222 at $552^{\circ}C$ for 10 min. Since then both of those values decreased with time until 120 min and finally these two values remained constant at 0.210. The variation in Si content with annealing time results in the variation in the hyperfine field and the isomer shift. The increase in the mean hyperfine fields and the decrease in the mean isomer shifts of Fe-Si are caused by the increase in Si content. The volume fractions of residual amorphous phase rapidly decrease during the early stage of annealing and come nearer to saturation after 120 min both at $500^{\circ}C$ and $552^{\circ}C$. The decrease in the mean hyperfine field of residual amorphous. in spite of slight changes in the volume fractions of Fe-Si and of residual amorphous after 120 min. is caused by the increase in the content of Nb and B in residual amorphous phase. The saturated volume fraction of the crystalline phase was 81% for $500^{\circ}C$ (180 min) and 77% for $552^{\circ}C$ (960 min), different from expectation.