• Journal of the Korean Magnetics Society
• /
• v.12 no.3
• /
• pp.103-108
• /
• 2002

We investigated magnetoresistance(MR) and exchange bias properties by annealing in top and bosom type spin valves (SV) with nano-oxide layers (NOL). In top SVs with NOL, MR ratio of 9.2% is obtained after postdeposition annealing at 250$\^{C}$. In bottom SVs with NOL, MR ratio of 10.1 % is obtained after postdeposition annealing at 250$\^{C}$. Therefore, specular reflection of the NOL in bottom SVs is higher than that of the NOL in top SVs. Exchange biasing of bottom SVs with NOL is 28% higher than that of bottom SVs without NOL after annealing. This enhancement of exchange biasing is thought to be due to the reduced magnetic moment of the pinned layer with NOL and enhanced (111) FeMn texture.

• Journal of the Korean Magnetics Society
• /
• v.13 no.5
• /
• pp.187-192
• /
• 2003

The magnetic and thermal properties of NiFe/[IrMn-Mn]/CoFe with Mn additions have been studied. As-deposited CoFe pinned layers with [IrMn-Mn]layer had dominantly larger exchange biasing field ( $H_{ex}$) and blocking temperature ( $T_{b}$) than those with pure I $r_{22}$M $n_{78}$ used. The $H_{ex}$ and $T_{b}$ improved with 76.8-78.1 vol% Mn, but those of the NiFe/IrMn/CoFe dropped considerably with more addition of 0.6 vol % Mn. The average x-ray diffraction peak ratios of fcc [(111)CoFe, NiFe]/(111)IrM $n_3$ textures for the Mn inserted total vol of 75.5, 77.5, and 79.3% were about 1.4, 0.8, and 0.6, respectively. For the sample without Mn inserted layer, the $H_{ex}$ between IrMn and CoFe layers was almost zero, but it increased to 100 Oe after annealing of 250 $^{\circ}C$. For as-grown two multilayers samples with ultra-thin Mn layers of 77.5 and 78.7 vol %, the $H_{ex}$s were 259 and 150 Oe, respectively. In case of IrMn with 77.5 vol% Mn, the $H_{ex}$ was increased up to 475 Oe at 350 $^{\circ}C$ but decreased to 200 Oe at 450 $^{\circ}C$, respectively. The magnetic properties and thermal stabilities of NiFe/[IrMn-Mn]/CoFe multilayer were enhanced with Mn additions. In applications where higher $H_{ex}$ and $T_{b}$ are required, proper contents of Mn can be used. be used. used.