• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2003년도 학술.기술논문 발표회
• /
• pp.43-48
• /
• 2003

This paper investigate that the effect of the concrete containing mineral admixtures(pozzolanic materials such as fly-ash, ground granulated blast-furnace slag, silica fume and meta kaolin) on the resistance properties to chloride ion invasion. The purposed testing procedure was applied to the concrete added mineral admixtures for 3~4 replacement ratios under W/B ratios ranged from 0.40 to 0.55. For the electrical migration test, Tang and Nilsson's method was used to estimate the migration coefficient of chloride ion. As a results, the W/B ratios, kinds of admixture and replacement ratios, water curing periods had a great effect on the migration coefficient of chloride ion, and the optimal replacement ratios of admixture had a limitation for each admixtures. Also, the addition of mineral admixtures by mass(replacement of OPC) enhanced the resistance of the mixture to chloride penetration compared with the plain concrete. The amount of acid soluble chloride ions and water soluble chloride ions were varied with the kinds of mineral admixtures. The compressive strength was shown related to the migration coefficient of chloride ion, the compressive strength increased with the decreasing migration coefficient of chloride ion. Below the 50MPa, the variation of migration coefficient of concrete added mineral admixtures was bigger than plain concrete.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2003년도 학술.기술논문발표회
• /
• pp.43-48
• /
• 2003

This paper investigate that the effect of the concrete containing mineral admixtures(pozzaolanic materials such as fly-ash, ground granulated blast-furnace slag, silica fume and meta kaolin) on the resistance properties to chloride ion invasion. The purposed testing procedure was applied to the concrete added mineral admixtures for 3∼4 replacement ratios under W/B ratios ranged from 0.40 to 0.55. For the electrical migration test, Tang and Nilsson's method was used to estimate the migration coefficient of chloride ion. As a results, the W/B ratios, kinds of admixture and replacement ratios, water curing periods had a great effect on the migration coefficient of chloride ion, and the optimal replacement ratios of admixture had a limitation for each admixtures. Also, the addition of mineral admixtures by mass(replacement of OPC) enhanced the resistance of the mixture to chloride penetration compared with the plain concrete. The amount of acid soluble chloride ions and water soluble chloride ions were varied with the kinds of mineral admixtures. The compressive strength was shown related to the migration coefficient of chloride ion, the compressive strength increased with the decreasing migration coefficient of chloride ion. Below the 50MPa, the variation of migration coefficient of concrete added mineral admixtures was bigger than plain concrete.

• Geomechanics and Engineering
• /
• 제36권6호
• /
• pp.619-629
• /
• 2024

To improve the utilization rate of phosphate tailings (PTs) and widen the sources of subgrade filler, the PTs is employed to modify clay, forming a PTs modified clay, applied in the subgrade. Accordingly, the environmental friendliness of PTs was investigated. Subsequently, an optimal proportion was determined through compaction and California Bearing Ratio (CBR) experiments. Afterward, the stability of mixture with the optimal proportion was further evaluated through the water stability and dry-wet stability experiments. Finally, via the gradation and microstructure experiments, the strength mechanism of PTs modified clay was analyzed. The results show that the PTs were classified in the non-hazardous solid wastes, belonging to Class A building materials. With the increase of PTs content and the decrease of clay content, the optimum water content and the swelling degree gradually decrease, while the maximum dry density and CBR first increase and then decrease, reaching their peak value at 50% PTs content, which is the optimal proportion. The resilient modulus of PTs modified clay at the optimal proportion reaches 110.2 MPa. The water stability coefficient becomes stable after soaking for 4 days, while the dry-wet stability coefficient decreases with the increase of cycles and tends to be stable after 8 cycles. Under the long-term action, the dry-wet change has a greater adverse impact than continuous soaking. The analysis demonstrates that the better strength mainly comes from the skeleton role of PTs and the cementation of clay. The systematic laboratory test results and economic analysis collectively provide data evidence for the advantages of PTs modified clay as a subgrade filler.

• 한국구조물진단유지관리공학회 논문집
• /
• 제18권1호
• /
• pp.93-100
• /
• 2014

해수중 환경에서 콘크리트 구조물 내에 매립된 철근은 용존산소의 부족으로 부식이 잘 발생하지 않는다. 이 때문에 해수중 환경의 부식촉진시험은 전기화학적인 방법으로 실시되어, 실제 부식 메커니즘과 맞지 않고 장기거동과의 상관성 도출도 어려운 실정이다. 본 연구에서는 해수중 환경에서의 부식촉진시험법을 정립하기 위해 온도와 염화물농도를 주된 변수로 부식촉진시험을 실시하였다. 부식의 발생 유무는 갈바닉 전위측정법과 반전지전위법을 통한 철근부식모니터링 결과로 판단하였다. 부식촉진시험 결과 온도의 영향이 가장 지배적이라고 평가되었다. 염화물량은 시험 시편의 깊이별 염화물 농도를 측정하였다. 동일한 조건으로 FEM 내구성 해석 프로그램인 DuCOM을 통해 염화물침투 해석을 실시하여 입증하였다. 또한, 인공해수 침지 조건에 따른 용존 산소량은 실험을 통해 구했으며 이를 통해 부식촉진시험 결과의 타당성을 검증하였다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.793-796
• /
• 2004

In domestic, various repair materials and method systems to keep up with these reinforced concrete deteriorated due to salt damage, carbonation. chemical decay et. being developed and applied. However, present polymer cement mortar applied to section restoration system cause the problem of long-term working and economica] efficiency. because that is divided into two process of liquid corrosion prevention agent and polymer cement mortar. In this background, accelerated test with due regard to $3\%$ NaCl soaking and autoclave cure was performed to confirm steel bar corrosion prevention properties of polymer cement mortar mixed with corrosion prevention agent of powdered type. In conclusion. we confirmed application possibility and excellency of steel bar corrosion prevention properties of polymer cement mortar mixed with corrosion prevention agent of powdered type comparing general polymer cement mortar applied to section restoration system of present study.