• Journal of Powder Materials
• /
• v.11 no.6 s.47
• /
• pp.493-502
• /
• 2004

In this study, nano-sized indium oxide powder with the average particle size below 100 nm is fab-ricated from the indium chloride solution by the spray pyrolysis process. The effects of the reaction temperature, the concentration of raw material solution and the inlet speed of solution on the properties of powder were studied. As the reaction temperature increased from 850 to $1000^{\circ}C$, the average particle size of produced powder increased from 30 to 100 nm, and microstructure became more solid, the particle size distribution was more irregular, the intensity of a XRD peak increased and specific surface area decreased. As the indium concentration of the raw material solution increased from 40 to 350 g/l, the average particle size of the powder gradually increased from 20 to 60 nm, yet the particle size distribution appeared more irregular, the intensity of a XRD peak increased and spe-cific surface area decreased. As the inlet speed of solution increased from 2 to 5 cc/min., the average particle size of the powder decreased and the particle size distribution became more homogeneous. In case of the inlet speed of 10 cc/min, the average particle size was larger and the particle size distribution was much irregular compared with the inlet speed of 5 cc/min. As the inlet speed of solution was 50 cc/min, the average particle size was smaller and microstructure of the powder was less solid compared with the inlet speed of 10 cc/min. The intensity of a XRD peak and the variation of specific area of the powder had the same tendency with the variation of the average par-ticle size.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.503-504
• /
• 2006

The MIM technology is an alternative process for fabricating near net shape components that usually uses gas atomised powders with small size $(<\;20\;{\mu}m)$ and spherical shape. In this work, the possibility of changing partially or totally spherical powder by an irregular and/or coarse one that is cheaper than the former was investigated. In this way, different bronze 90/10 components were fabricated by mixing three different types of powder, gas and water atomised with different particle sizes, in order to evaluate how the particle shape and size affect the MIM process.

• Journal of Powder Materials
• /
• v.19 no.5
• /
• pp.348-355
• /
• 2012

Cold spray deposition using Titanium powder was carried out to investigate the effects of powder morphology and powder preheating on the coating properties such as porosity and hardness. The in-flight particle velocity of Ti powder in cold spray process was directly measured using the PIV (particle image velocimetry) equipment. Two types of powders (spherical and irregular ones) were used to manufacture cold sprayed coating layer. The results showed that the irregular morphology particle appeared higher in-flight particle velocity than that of the spherical one under the same process condition. The coating layer using irregular morphology powder represented lower porosity level and higher hardness. Two different preheating conditions (no preheating and preheating at $500^{\circ}C$) were used in the process of cold spraying. The porosity decreased and the hardness increased by conducting preheating at $500^{\circ}C$. It was found that the coating properties using different preheating conditions were dependent not on the particle velocity but on the deformation temperature of particle. The deposition mechanism of particles in cold spray process was also discussed based on the experimental results of in flight-particle velocity.

• Korean Journal of Food Science and Technology
• /
• v.16 no.3
• /
• pp.279-284
• /
• 1984

Microstructure of milk powder and cheese made from milk powder were observed by electron microscope. Freeze dried milk powder showed apple-like appearance. The cheese made from freeze dried milk powder had relatively flat surface and homogenous deposit in compare with classical processed cheese. Imported milk powder also indicated similar surface as well as freeze dried milk powder, however, the cheese made from imported milk powder had somewhat coarse surface structures with the spaces between casein matrix and deposit. Commericial milk powder showed irregular shape in size and coagulum which were possibly denatured in the course of drying. The cheese made from commercial powder indicted irregular and small deposit and porous structure. The porousity of the cheese seemed to be influenced by the degree of heat treatment. Denatured protein would be less dispersive than native in presence of polyphosphates. Fat globule and protein micelle of cheese made from skim milk powder get very adjacent to each other and showed compactness of micelles. It is thought that melting mechanism of skim milk powder was different from the melting of typical processed cheese.

• Journal of Powder Materials
• /
• v.7 no.4
• /
• pp.228-236
• /
• 2000

An investigation was carried out on the possibility whether the ball-milling process of low energy could successfully improve the packing density and flowability for MIM application in W-20wt%Cu system. In this study, W-20wt%Cu powder mixture was prepared by ball-milling. W powder was not fractured by low mechanical impact energy used in the present work during the critical ball-milling time, but the ductile Cu powder was easily deformed to the 3 dimensional equiaxed shape, having the particle size similar to that of W powder. The ball-milled mixture of W-20wt%Cu powder had the more homogeneous distribution of each component and the higher amount of powder loading for molding than the simple mixture of W-Cu powder with an irregular shape and a different size. Accordingly, the MIM W(1.75)-20wt%Cu powder compacts were able to be sintered to the relative density of 99% by sintering at $1400^{\circ}C$ for one hour.

• Journal of the Korean Society for Heat Treatment
• /
• v.9 no.1
• /
• pp.62-68
• /
• 1996

In order to establish making process of water atomized iron powder for powder metallurgy, effect of heat treatment condition on change of powder properties and impurities was investigated at each tempeature of $850{\sim}950^{\circ}C$. The results are as follows. Particle morphology of iron powder changed slightly from sphercial type to irregular type and the amount of fine particle decreased more and more with increasing of heat treatment time at each temperature. The flow rate and apparent desity of iron powder also decreased due to particle coalescence in order of $850^{\circ}C$, $950^{\circ}C$, $900^{\circ}C$. Those powder Properties became to decrease particularly at $900^{\circ}C$ in alpha iron region. On the other hand, residual carbon and oxygen contents in iron powder decreased extremely with increasing of heat treatment temperature and time.

• Journal of Welding and Joining
• /
• v.15 no.1
• /
• pp.116-124
• /
• 1997

A scope of this study is to establish the optimum plasma spray conditions for fine ($5\mu\textrm{m}$) $Al_2O_3$ powder. However, the flowability of the $Al_2O_3$ powder is not so good because of irregular particle shape and fine particle size. Therefore, powder feeding system was modified by 1) change of powder feeding line material from polymer to copper 2) shorten the powder feeding tube length 3) heating the powder feeding system to $80^{\circ}C$4) vibrating the powder feeding line continuously, in order to feed the fine powder homogeneously. The homogeneous powder feeding conditions were obtained with the modified powder feeding system by controlling the powder carrier gas flow and the powder flow rate indicator. The best plasma spraying conditions for the fine $Al_2O_3$ powder were found out as 40kw gun power, 80 g/min. powder feed rate and 50 mm working distance after characterizing the microstructure, hardness and wear loss of the $Al_2O_3$ coating layer.

• Analytical Science and Technology
• /
• v.25 no.6
• /
• pp.345-349
• /
• 2012

Polysilane black powders were synthesized by sonochemical methods from silicon tetrachloride with sodium metal with 37.0% yield. Those black powder materials were found to have fibrous or irregular shapes with round surface. It was found that thermal behaviors of those polysilane black powders were similar to that of hydropolysilanes which was reported earlier. After thermal treatment, black polysilicon was obtained with 57.1% residue yield, and those fibrous or irregular shapes with round surface were intact but lots of small cavities were formed indicating porous structure, and found to be an amorphous state from XRD analysis.

• Journal of Powder Materials
• /
• v.9 no.1
• /
• pp.11-18
• /
• 2002

The 6061 Al alloy based composites reinforced with 10 vol% SiC whiskers were prepared by powder metallurgy with the powders having the different sizes, i.e. < $30{\mu}m$ and > $30{\mu}m$ The composites were subjected to equal channel angular pressing (ECAP) at various conditions and the microstructural changes during ECAP were examined In the composites SiC whiskers were clustered and randomly aligned. The clusters were relatively well distributed in the composite with the smaller initial powder size. After ECAP, the clusters were aligned parallel to flow direction and became smaller. In addition, the shape of clusters was changed from irregular to round. The microstructure of the ECAPed samples were compared with those of the conventionally hot-extruded composites. The uniform microstructure and enhanced microhardness could be obtained by using the powders having the smaller size, decreasing ECAP temperature and repeating ECAP.

• Journal of Powder Materials
• /
• v.27 no.5
• /
• pp.388-393
• /
• 2020

The enamel powders used traditionally in Korea are produced by a ball-milling process. Because of their irregular shapes, enamel powders exhibit poor flowability. Therefore, polygonal enamel powders are only used for handmade cloisonné crafts. In order to industrialize or automate the process of cloisonné crafts, it is essential to control the size and shape of the powder. In this study, the flowability of the enamel powders was improved using the spheroidization process, which employs the RF plasma treatment. In addition, a simple grid structure and logo were successfully produced using the additive manufacturing process (powder bed fusion), which utilizes spherical enamel powders. The additive manufacturing technology of spherical enamel powders is expected to be widely used in the field of cloisonné crafting in the future.