• Resources Recycling
• /
• v.13 no.6
• /
• pp.31-36
• /
• 2004

This experiment was carried out to examine the effects of morphology on properties of La-Co substituted SrM ferrite. The magnetic properties of calcined and sintered materials were varried with the substitutional amount of La and Co elements in Sr-ferrite. In the substituted SrM ferrite, the atomic fraction x of La is directly related to the mole ratio n of iron oxide and the atomic fraction y of Co by equation x=2ny. The Hcj values of the calcined powder were about 270 kA/m and 240 kA/m with x=0.3 and x=0.2, respectively at stoichiometry, n=6.0. Crystallites of the sintered material were grown with a plate shape, and their size decreased with increasing mole ratios. Such a shape was caused by the initial state of crystallite formed after calcination. In case of x=0.3 and n=6.0, Br was 415 mT and Hcj was 355 kA/m, and in x=0.2 and n=6.0, Br was 410 mT and Hcj was 370 kA/m. The squareness in 2nd quarter of BH curve with x=0.2 was smoothly improved to compared with x=0.3.

• Journal of Advanced Marine Engineering and Technology
• /
• v.36 no.2
• /
• pp.276-285
• /
• 2012

The objective of this research is to develop the coating technique by a porous self-fluxing alloy for improving the mechanical properties of run-out table roller surface with the hot rolling. To enhance the durability of run-out table roller with the hot rolling, the high hardness of roller surface should be maintained at high temperatures, and the improvement of wear resistance, corrosion resistance, heat resistance, burn resistance and adhesion resistance should be maintained. In order to be able to transport reliably a hot rolled steel sheet, also, the appropriate friction coefficient on the roller surface should be maintained and the slip between roller and steel should not occur. In this study, the wear resistance of roller increases after the self-fluxing alloy is changed to a cermet by adding the tungsten carbide(WC), and the coefficient of friction increases and the ability of grip is improved because the porosities are made by coating with fine iron powder on the roller surface. As a result, it is found that the ability of grip between the steel and the roller coated by a porous self-fluxing alloy contained to 5 ~ 10 wt% of Fe in the coating layer is improved compared to the roller coated by Ni-Cr. This is because the porosities are made after Fe contained in the roller is partially alloyed by heating with a furnace in the fusing process and the rest is eliminated by oxidation and dissolution.

• Korean Journal of Food Science and Technology
• /
• v.25 no.6
• /
• pp.769-774
• /
• 1993

Defatted rice bran was microparticulated using fluidized bed opposed jet mill and air-classified at different air classifying wheel speed (ACWS) in Turboplex classifier. The median particle size and the standard deviation decreased, and concomitantly the specific surface area increased generally with increasing ACWS. The protein, fat and ash contents of the recovered rice bran increased with ACWS. The contents of minerals; magnesium, zinc, iron and manganese; increased positively with ACWS. The phytic acid content, however, was slightly higher at middle ACWS. The dietary fiber content was highest in the ACWS 15,000 rpm fraction showing 31.47%. Higher ACWS resulted in lighter colored powder. The water holding capacity (WHC) showed the maximum value at ACWS 12,000 rpm and decreased with increasing ACWS, while the oil holding capacity (OHC) increased with ACWS. The rheological property of the microparticulated rice bran/water suspension fitted to the linear model. The yield stress and viscosity of the suspension increased with ACWS. The shape of microparticulated rice bran at ACWS 21,000 rpm was spherical, and the median particle size was $3.7{\mu}m$. When cake was prepared with substitution of microparticulated rice bran at 5%, the cake height and volume increased remarkably.

• Journal of the Korean Chemical Society
• /
• v.37 no.11
• /
• pp.923-928
• /
• 1993

The series of solid solutions in the $Sr_{1+x}Ho_{1-x}FeO_{4-y}$ (x = 0.00, 0.25, 0.50, 0.75 and 1.00) systems with $K_2NiF_4$ type structure have been prepared at 1550$^{\circ}$C under an atmospheric air pressure. The X-ray powder diffraction spectra of these samples assign that the crystallographic phases are tetragonal system over the whole x range. The lattice volume was increased with increasing the substitution amount of the $Sr^{2+}$ ion. The mole ratio of the $Fe^{4+}$ ion to total iron ions or ${\tau}$ value has been determined by Mohr salt titration of the sample and then the y value was calculated from x and ${\tau}$ values. The ${\tau}$ and y values have been increased with x values. The nonstoichiometric chemical formula are formulated from the general formula of $Sr_{1+x}Ho_{1-x}Fe^3_{1-}\;^+_{\tau}Fe_{\tau}^{4+}O_{4-y}$ replaced by x,${\tau}$ and y values. Mossbauer spectra show the mixed valence state and coordination state of $Fe^{3+}\;and\;Fe^{4+}$ ions. It is found out that the magnetic property of the samples is paramagnetic at room temperature. Electrical conductivity varied within the semiconductivity range of 1.0 to 1 ${\times}\;10^{-9}{\Omega}^{-1}cm^{-1}$. Activation energy of the electrical conductivity was decreased with the $\tau$ value. The conduction mechanism should be explained by the hopping model of the conduction electrons between the valence states of $Fe^{3+}\;and\;Fe^{4+}$ ions.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2004.12a
• /
• pp.27-34
• /
• 2004

This experiment was carried out to examine the effects of morphology on properties of La-Co substituted SrM ferrite. The magnetic properties of calcined and sintered materials varied with the substitutional amount of La and Co elements in Sr-ferrite. In the substituted SrM ferrite, the atomic fraction x of La is directly related to the mole ratio n of iron oxide and the atomic fraction y of Co by equation x=2ny. The HcJ values of the calcined powder were about 270 kA/m and 240 kA/m with x=0.3 and K=0.2, respectively at stoichiometriy, n=6.0. Crystallites of the sintered material were grown with a plate shape, and their size decreased with increasing mole ratios. Such a shape was caused by the initial state of crystallite formed after calcination. In case of x=0.3 and n=6.0, Br was 415 mT and HcJ was 355 kA/m, and in x=0.2 and n=6.0, Br was 410 mT and HcJ was 370kA/m. The squareness in 2nd quarter of BH curve with x=0.2 was smoothly improved compared with x=0.3

• Economic and Environmental Geology
• /
• v.33 no.5
• /
• pp.391-404
• /
• 2000

This study investigated the geochemical characteristics of mine drainage discharged from an abandoned coal mine in the Hwasoon area. Surface water samples were collected from 23 locations along the Hancheon creek. The concentration of Zn and Cu in stream waters was highest at low pH (3.53), whereas the content of TDS and TDI was highest at high pH (7.78) due to the concentration of Ca, $HCO_3$ and $SO_4$. At the upstream site, the Ba, Fe, Mn, Zn, and $SO_4$ contents were relatively high but decreased significantly with the distance from the coal mine. On the contrary, the Na and $NO_3$ contents were low at the upstream site but increased downstream. Yellow precipitate material collected in the Hancheon consisted mainly of iron and LOI. This yellow precipitate was heated from 100 to $900^{\circ}C$ for 1 hour. With increasing temperature, the intensity of hematite peaks were sharply produced in X-ray pattern and the absorption band Fe-O of hematite increased in IR due to dehydration and melting. The yellow to brown precipitate and evaporite materials were collected by a air-dry from the acid mine water at the laboratory. After drying, the concentration of ions in the acid water samples increased progressively in oversaturation with respect to either gypsum, ferrohexahydrite or quenstedetite. The X-ray powder diffraction studies identified that the precipitated and evaporated materials after drying were well crystallized gypsum, ferrohexahydrite and quenstedetite. Diagnostic peaks used for identification of gypsum were the 7.65, 4.28, 3.03, 2.87 and 2.48$\AA$ peaks and those for ferrohexahydrite were the 5.46, 5.12, 4.89, 4.44, 4.05, 3.62, 3.46, 3.40, 3.20, 3.03, 2.94, 2.53, 2.28, 2.07, 1.88 and 1.86${\AA} peaks. The IR spectra with OH-stretching, deformation of $H_2O$and ${SO_4}^{2-}$stretching vibration include the existence of gypsum, ferrohexahydrite and quenstedetite in the precipitated and evaporite materials. In the SEM and EDS analysis for the evaporite material, gypsum with well-crystallized, acicular, and columnar form was distinctly observed.

• Applied Microscopy
• /
• v.42 no.2
• /
• pp.87-93
• /
• 2012

In this study, fine structures of silica, titanium dioxide, talc and kaolin used in decorative cosmetics and the mixture extracted from BB cream cosmetics were observed by scanning electron microscopy. Kaolin had plate like shape structures of polygon with smooth surface and edge of kaolin had a relatively smooth appearance in comparison with talc. Also, thickness of each layer was estimated to about $0.1{\mu}M$ in the lump formed in stratum of several layers. Talc was observed by lumps shape phase of layering very thin flake. Boundary of thin flake was sharp or angular phase and thickness of flake was approximately 600 nm in diameter. When comparing the thickness of kaolin and talc, we was confirmed that kaolin was thicker than talc. Diameter of titanium dioxide was estimated to 0.2~0.3 ${\mu}M$ and surface of particle was a soft cubic form. Silica was confirmed that variety of size from 200 nm to $15{\mu}M$ of globular shape was measured. From the observation of inorganic pigments, silica was homogeneous dispersed in the BB cream cosmetics and among each other was filled with relatively small size like talc, kaolin, titanium dioxide and iron oxide. In conclusion, we suggest that silica at decorative cosmetics were formed in cosmetic coat at the skin as the minimum thickness.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.3
• /
• pp.255-262
• /
• 2020

Blended cement with fly ash and bottom ash from Circulating Fluidized Bed Combustor boiler(CFBC) burned at a low temperature, can be high heat of hydration and abnormal setting caused by higher volumn contents of Fe₂O₃, free-CaO, SO₃. In this study, the ground CFBC bottom ash powder mixed with blast furnace slag was used as substitute activator of gypsum and recycled iron slag was produced from mix and pulverized by ball mill to increase the recycling rate. The effect on compressive strength of cements with the mixture of original and hydrated bottom ash mixtures with BFS with small water, respectively, was analyzed, and it was found that the hydrated bottom ash activator was more effective in initial strength development. To improve the initial strength of blended cement, an activator mixed with a blast furnace slag and bottom ash mixing ratio of 5:95 and 10:90, respectively, the slag cement by about 6%, and it was analyzed to develop an initial strength similar to gypsum as a conventional activator.

• Resources Recycling
• /
• v.30 no.6
• /
• pp.53-60
• /
• 2021

In EAF steelmaking industries, MgO content in slag increases due to the addition of dolomite flux to protect refractory lines of furnaces and improve the desulfurization capability of slag. In addition, coal powder is injected in the molten steel bath to increase the energy efficiency of the process. In this regard, the utilization of waste MgO-C refractory material as a flux was examined because it has high amounts of MgO (>70%) and graphite carbon (>10%). A series of experiments were carried out using industrial EAF slag with added light burnt dolomite and waste MgO refractory material from a Korean steel company. The results for the addition of the two fluxes were similar in terms of slag basicity; therefore, it is expected that waste MgO-C refractory material can successfully replace dolomite flux. In addition, when the waste MgO-C refractory material was added as flux, slag foaming phenomenon was demonstrated because of the reaction between the graphite from the refractory material and iron oxides in the slag.

• Applied Chemistry for Engineering
• /
• v.29 no.6
• /
• pp.696-702
• /
• 2018

Recently, the current thermal battery technology needs new materials for electrodes in the power and energy density to meet various space and defense requirements. In this paper, to replace the pellet type Li(Si) anode having limitations of the formability and capacity, electrochemical properties of the lithium anode with high density for thermal batteries were investigated. The lithium anode (Li 17, 15, 13 wt%) was fabricated by mixing the molten lithium and iron powder used as a binder to hold the molten lithium at $500^{\circ}C$. The single cell with 13 wt% lithium showed a stable performance. The 2.06 V (OCV) of the lithium anode was significantly improved compared to 1.93 V (OCV) of the Li(Si) anode. Specific capacities during the first phase of the lithium anode and Li(Si) were 1,632 and $1,181As{\cdot}g^{-1}$, respectively. As a result of the thermal battery performance test at both room and high temperatures, the voltage and operating time of lithium anode thermal batteries were superior to those of using Li(Si) anode thermal batteries. The power and energy densities of Li anode thermal batteries were also remarkably improved.