• Journal of Magnetics
• /
• v.9 no.2
• /
• pp.52-59
• /
• 2004

As deposited and annealed MTJs with the structure of $Ta(5 nm)/Cu(10 nm)/Ta(5 nm)/Ni_{80}Fe_{20}(2 nm)/Cu(5 nm)/ Ir_{25}Mn_{75}(10 nm)/Co_{70}Fe_{30}(2.5 nm)/Al-O/Co_{70}Fe_{30}(2.5nm)/Ni_{80}Fe_{20}(t)/Ta(5nm)/Ni_{80}Fe_{20}(t)/Ta(5 nm)$, where t=10, 30, 60 and 100 nm were characterized by XRD and magnetic hysteresis loops measurements. The XRD measurements were done in grazing incidence $(GID scan-2{\theta})$ and ${\theta}-2{\theta}$ geometry, by rocking curve $(scan-{\omega})$ and pole figures in order to establish correlation between texture and crystallites size and magnetic parameters of exchange biased and interlayer coupling. The variations of shifting and coercivity field of free and pinned layers after annealing in $300^{\circ}C$ correlate with the improvement of ［111］ texture and grains size of $Ni_{80}Fe_{20}$ and $Ir_{25}Mn_{75}$ respectively. The exchange biased and the coercivity fields of the pinned layer linearly increased with increasing grain size of $Ir_{25}Mn_{75}$, The reciprocal proportionality between interlayer coupling and coercivity fields of the free layer and grain size of $Ni_{80}Fe_{20}$ was found. The enhancement of interlayer coupling between pinned and free layers, after annealing treatment, indicates on the correlated in-phase roughness of dipolar interacting interfaces due to increase of crystallites size of $Ni_{80}Fe_{20}$.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.229-229
• /
• 2003

Enhancement of the exchange bias and optimization of the structure have been the focus that many researchers studied, recently [1]. In this report, magnetic properties of MTJs with structure of Si/Ta (5)/Cu (10)/ Ta (5)/ Ni$\sub$80/Fe$\sub$20/ Cu (5)/ Mn$\sub$75Ir$\sub$25/ (10)/ Co$\sub$70/Fe$\sub$30/ (2.5)/ Al-O (1.5)/ Co$\sub$70/Fe$\sub$30/ (2.5)/ Ni$\sub$80/Fe$\sub$20/ (t)/ Ta (5) (t=0,10, 30, 60 and 100 nm, respectively) were investigated. The relationship between the structure and magnetic parameters of interfacial exchange coupling and interlayer coupling in as-deposited and annealed junctions was studied. The temperature dependence of exchange coupling was considered.

• Journal of the Korean Magnetics Society
• /
• v.10 no.2
• /
• pp.62-66
• /
• 2000

Annealing cycle number and nonmagnetic layer thickness dependences of interlayer coupling field ( $H_{inf}$ ) and coercivity ( $H_{cf}$ ) of free magnetic layer on NiMn alloy-spin valve films (SVF) were investigated. The SVF is Glass (7059)/N $i_{81}$F $e_{l9}$(70 $\AA$)/Co(10 $\AA$)/Cu(t $\AA$)/Co(15 $\AA$)N $i_{81}$$Fe_{19}$(35 $\AA$)/N $i_{25}$M $n_{75}$(250 $\AA$)Ta(50 $\AA$) films, it were fabricated using the dc sputtering method at different pinning layer thickness and nonmagnetic spacer thickness (Cu thickness; 30 $\AA$, 35 $\AA$, 40 $\AA$) of NiMn alloy with 25 at.%. Ni In case that Cu thickness of SVF is 35 $\AA$ and peak exchange coupling field ( $H_{ex}$) was 620 Oe, while coercivity $H_{c}$ = 280 Oe and MR ratio showed 2.5%. As for $H_{inf}$ and $H_{cf}$ , every SVF increased up to the stabilized values with the increase of annealing cycle number 15, which were $H_{inf}$ of 120 Oe and $H_{cf}$ of 75 Oe. The increase of $H_{cf}$ with the annealing cycle number seems to be caused by the effective reduction of Cu layer thickness due to the increase of interfacial mixing of Cu layer and Co layer. In addition, the $H_{inf}$ and $H_{cf}$ dependences of free NiFe layer by the interfacial mixing effect were appeared the different aspects when Cu layer becomes more thinner and thicker than Cu layer thickness of 35 $\AA$, respectively.ively....