• Journal of Ocean Engineering and Technology
• /
• v.14 no.1
• /
• pp.29-36
• /
• 2000

Surface micro-crack grows along intergranular or transgranular region of crystal grains. But if it meets the barrier such as sessile dislocation and precipitates it loses straightness and deflects. Investigators had many difficulties in estimating fatigue life of smooth specimen because of the random distribution growth and coalescence of surface micro-cracks. The path of surface micro-crack has irregularity due to nonhomogeneous microstructure. Euclidian geometry can't quantify the shape of surface micro-crack but fractal geometry can. Therefore in this paper fractal dimension is measured at various stage of cycle ratio and estimated cycle ratio in 2024-T3 aluminium, alloy.

• Journal of Welding and Joining
• /
• v.8 no.4
• /
• pp.27-34
• /
• 1990

Integranular corrosion behaviors of KAL (Knife Line Attack) and mechanical properties such as tensile and creep rupture were investigated for the tube material used for nearly 20 years under the condition of 463.deg. C and 28 $kg/cm^2$. Based and weld metal were austenitic stainless steel AISI 321 containing Ti, AISI 347 containing Nb, respectively. KLA is a kind of the intergranular corrosion which often occurs just near the HAZ (heat affected zone) of AISI 321 and AISI 347 stainless steel due to the grain boundary sensitization. In KLA zone, intergranular corrosion crack has propagated outwards from the inner surface and carbides of white and narrow band type assuming as (Cr, Fe) carbide were confirmed. All the delta-ferrite formed in the weld metal during weld solidification has been transformed into sigma-phase since delta-ferrte was exposed for 20 years at 463.deg. C. Elongation was very low at the range from room temperature to 600.deg. C and it was confirmed that creep-rupture properties were not consideralbly affected.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2000.04a
• /
• pp.373-378
• /
• 2000

The heat resistant material, in service, may experience static loading, cyclic loading, or a combination of two. An experimental study of crack growth behavior of STS 316L austenitic stainless steel under fatigue, and creep-fatigue loading conditions were carried out on compact tension specimens at various tensile hold times. In the crack growth experiments under hold times. In the crack growth experiments under hold time loading conditions, tensile hold times were ranged from 5 seconds to 100 seconds and its behavior was characterized using the $\Delta$K parameter. The crack growth rates generally increase with increasing hold times. However in this material, the trend of crack growth rates decreases with increasing hold times for short hold time range relatively. It is attributed to a decline in the cyclic crack growth rate as a result of blunting at the crack tip by creep deformation. The effect of grain size on the creep behavior of STS 316L was investigated. Specimens with grain size of 30, 65 and 125${\mu}{\textrm}{m}$ were prepared through various heat treatments and they were tested under various test conditions. The fracture mode of 316L changed from transgranular to intergranular with increasing grain size.

• Journal of Power System Engineering
• /
• v.18 no.2
• /
• pp.62-69
• /
• 2014

In this paper, in order to investigate the effects of marco and microscopic observations of fatigue crack growth in friction stir welded (FSWed) 7075-T651 aluminum alloy plates, fatigue crack growth tests were performed under constant amplitude loading condition at room temperature with three different pre-cack locations, namely base metal (BM-CL) and two kinds of pre-crack locations in welded joints, weld metal (WM-CL) and heat affected zone (HAZ-CL) specimens. The fatigue crack growth behavior of FSWed 7075-T651 aluminum alloy plates were discussed based on the marco and microscopic fractographic observations. The marcoscopic aspects of surface crack growth path for BM-CL and HAZ-CL specimens indicate relatively straight lines, however, the crack growth paths of WM-CL specimens grow first straight and by followed toward the TMAZ and HAZ. The microscopic aspects of fatigue fracture for BM-CL and HAZ-CL specimens indicate typical fatigue striation, but WM-CL showed intergranular fracture pattern by micro structural changes of FSW process.

• Journal of the Korean Ceramic Society
• /
• v.36 no.6
• /
• pp.662-670
• /
• 1999

Porous alumina was fabricated from pressureless powder packing forming method using powders granulated by spray drying. It was investigated the pore size distribution of fabricated porous alumina. The results of microstructural observation showed that intraganular pore size and intragranular pore size. At 1700$^{\circ}C$ there were no intragranular pores but it showed homogeneous distribution of intergranular pore size. The bending strength and shrinkage increased as porosity decreased. In case of thermal shock resistance sudden decrease of bending strength to $\Delta$T was not shown because intergranular large pore prevented sudden crack propagation.

• Journal of the Korean Society for Railway
• /
• v.3 no.2
• /
• pp.77-83
• /
• 2000

This study proposes the integrity evaluation of the bogie frame using ultrasonic fractography analysis. Analysis objectives in this study are to investigate fracture planes of damaged zone by the A-scan method. The surface condition of fracture planes shows degree of degradation by the stress concentration. The detection of the natural defects in the bogie frame is performed using the characteristics of echodynamic pattern in ultrasonic signal. Results of ultrasonic testing agree fairly well with those of actual fracture plane. In quantitative fractography analysis, microstructures of actual fracture plane turned out to be intergranular and transgranular fracture. Proposed ultrasonic fractography analysis in this study can be used for the integrity evaluation of the bogie frame.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.3 s.174
• /
• pp.603-612
• /
• 2000

Corrosion characteristics on the 12Cr alloy steel of turbine blade was electro-chemically investigated in 3.5wt% NaCI and 12.7wt% Na2S04 solution, respectively. Electro-chemical polarization test, Huey test and Oxalic acid etching test were previously conducted to estimate corrosion susceptibility of the material. And, using the horizontal corrosion fatigue tester, corrosion fatigue characteristics of 12Cr alloy steel in distilled water, 3.5wt% NaCI solution, and 12.7wt%(1M) Na2S04 solution were also fracture-mechanically estimated and compared their results. Parameter considered was room temperature, 60'C and 90'C. Corrosion fatigue crack length was measured by DC potential difference method.Obtained results are as follows,1) 12Cr alloy steel showed high corrosion rate in 3.5wt% NaCI solution and Na2S04 solution at high tempratue.2) Intergranular corrosion sensitivity of 12 Cr alloy was smaller than austenitic stainless steel.3) Corrosion fatigue crack growth rate in 3.5wt% NaCI and 12.7wt%(IM) Na2S04 solution is entirely higher than in the distilled water, and also increased with the temperature increase.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1997.04a
• /
• pp.143-149
• /
• 1997

the horizontal corrosion fatigue tester has been developed for investigating environmental strength. Using this tester, we investigated about corrosion fatigue caracteristic for A106 GrB steel weldments in 3.5% synthetic seawater and room temperature. Considered parameter is only frequency of 1,3 and 5Hz. and Corrosion fatigue crack length was measured by DC potential difference method. From the results, we could find that the horizontal corrosion fatiued tester could be well applied to estimation of fatigue strength. and In case of 5Hz, corrosion fatigue crack growth path of A106 GrB steel weldment was transgranular, and of 1 and 3Hz showed that transgranular and intergranular was mixed. Also, Corrosion fatigue crack growth caracteristic values estimated in each frequency were C=9.33 x 10-9 and m=2.93 in 1Hz, C=9.77x10-10 and m=3.47 in 3Hz, C=1.02x10-10 and m=4.05 in 1Hz

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.78-83
• /
• 2004

Environmental fatigue crack propagation of CF8M and CF8A steels used in the domestic PWR were investigated on the simulated PWR condition(Temperature: $316^{\circ}C$, Pressure: 15MPa). The test equipment for environmental fatigue(high temperature-high pressure loop, autoclave, load frame, measurement system) were designed. As-received and 60-year aged specimens were used in the test. To compare with environmental fatigue test, another test was performed in the air condition. The fracture surface of specimens were difficult to verify the fracture modes such as striation, intergranular crack and cleavage and so on. As the ferrite content of CF8M is increased, more particles covered fracture surface were peeled.

• Journal of the Korean Ceramic Society
• /
• v.34 no.8
• /
• pp.877-885
• /
• 1997

The dependence of strength, crack growth, fracture mode and degree of domain rearrangement of PZT ceramics on poling strength were studied. The PZT [(Pb0.94Sr0.06)(Zr0.46Ti0.54)O3+Nb(trace)] specimens were poled at 0, 0.5, 1.0, 1.5, 2.0, 2.5, 3.0 kv/mm, and the strength of the specimens was measured by 3 point flexure system. The bending strength of the specimen decreased in different modes according to the bending directions; xz, zx and yz plane direction with x axis of the poling direction in Cartesian coordinate system. The strength differences between the directions increased as the poling strength increased. The fracture mode transferred to intergranular fracture mode from transgranular one as the poling strength increased. The mechanical breakdown occurred when the poling strength higher than 3 kV/mm was applied to the specimen. It was observed that the crack length increased in the normal direction to the poling direction, however, decreased in the parallel direction to the poling direction when the poled PZT specimen was indented by the Vickers indenter. However, the crack produced by indentation continuously was continuously increased little by little after indentation on the specimen. The domain rearrangement occurred as the poling strength increased and the domains were rearranged more effectively when the electric field was continuously increased little by little.