• Applied Chemistry for Engineering
• /
• v.7 no.3
• /
• pp.424-432
• /
• 1996

The fiber reinforced thermoplastic composites(FRTP) were prepared with polypropylene fiber(PPF) as matrix and vinylon(VF), Aramid(KF) or nylon fiber(PAF) as reinforcing materials using the integrated fiber mixing apparatus. The composite sheets were prepared by compression molding and their impact and morphological properties were characterized. VF/PP system showed the maximum value in Izod impact strength, while KF/PP system showed the maximum value in high rate impact properties. Ductility Index(DI) order was VF/PP>KF/PP>PAF/PP. A maximum DI for VF/PP, 2.43, was obtained when the weight fraction of VF was 20%. The optimum amount of the reinforcing organic fiber was found to be 20~30%. As a result, it is concluded that VF/PP system has better interfacial adhesion properties than either KF/PP or PAF/PP.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.3
• /
• pp.160-166
• /
• 2014

In this research, as a measure of reducing energy lost through external wall, we used Glass Hollow Micro Sphere (HMS) to improve insulation performance to structural concrete. The following is a result of experimenting concrete using HMS. As usage of HMS, decrease in slump arose and it is judged as a need of using superplasticizer. Replacement ratio increasing more and more, amount of air showed tendency to decrease and compressive strength decreased for interfacial adhesion had not been formed. as replacement ratio and unit volume decreased. It appears that thermal conductivity decreased about 30.0~46.5 percent as compared with normal weight concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.1
• /
• pp.15-22
• /
• 2017

This study focuses on the investigation of bond strength of magnesium potassium phosphate cement mortar(MKPC) according to moisture condition of substrate. Tensile bond test, shear bond test and interfacial bond test are adopted for evaluating the adhesion characteristics of MKPC to conventional cement mortar substrate. The main experimental variables are test methods and moisture levels of substrate. Because the moisture condition of the substrate may be critical to achieving bond, optimum moisture condition for a conventional concrete substrate has evaluated in this study. The results are as follows ; The effects of moisture condition at substrate into the bonding of MKPC are less different than polymer cement mortar and epoxy mortar. But the saturated and surface dry condition is the most appropriate moisture level among the considered, followed by saturated condition and wet condition. Thus, an adequate moisture level of substrate for MKPC is essential for good bond strength.

• Elastomers and Composites
• /
• v.51 no.2
• /
• pp.113-121
• /
• 2016

Magneto-rheological elastomer (MRE) is a material which shows reversible and various modulus under magnetic field. Comparing to conventional rubber vibration isolator, MREs are able to absorb broader frequency range of vibration. These characteristic phenomena result from the orientation of magnetic particle (i.e., chain-like formation) in rubber matrix. In this study, silicone rubber was used as a matrix of MREs. Carbonyl iron particle (CIP) was used to give magnetic field reactive modulus of MRE. The surface of the CIP was modified with chemical reactants such as silane coupling agent and poly(glycidyl methacrylate), to improve interfacial adhesion between matrix and CIP. The mechanical properties of MREs were measured without the application of magnetic field. The results showed that the tensile strength was decreased while the hardness was increased with the addition of CIP. Also, surface modification of CIP resulted in the improvement of physical properties of MRE, but the degree of orientation of CIP became decreased. The analysis of MR effect was carried out using electromagnetic equipment with various magnetic flux. As the addition of CIP and magnetic flux increased, increment of MR effect was observed. Even though the surface modification of CIP gave positive effect on the mechanical properties of MRE, MR effect was decreased with the surface modification of CIP due to decrease of CIP orientation. Throughout this study, it was found that the loading amounts of CIP affected the mechanical properties of MRE, and surface property of CIP was an important factor on MR effect of MRE.

• Korean Journal of Materials Research
• /
• v.22 no.11
• /
• pp.626-630
• /
• 2012

The properties of SOFC unit cells manufactured using the decalcomania method were investigated. SOFC unit cell manufacturing using the decalcomania method is a very simple process. In order to minimize the ohmic loss of flattened tube type anode supports of solid oxide fuel cells(SOFC), the cells were fabricated by producing an anode function layer, YSZ electrolyte, LSM electrode, etc., on the supports and laminating them. The influence of these materials on the power output characteristics was studied when laminating the components and laminating the anode function layer between the anode and the electrolyte to improve the output characteristics. Regarding the performance of the SOFC unit cell, the output was 246 $mW/cm^2$ at a temperature of $800^{\circ}C$ in the case of not laminating the anode function layer; however, this value was improved by a factor of two to 574 $mW/cm^2$ due to the decrease of the ohmic resistance and polarization resistance of the cell in the case of laminating the anode function layer. The outputs appeared to be as high as 574 and 246 $mW/cm^2$ at a temperature of $800^{\circ}C$ in the case of using decalcomania paper when laminating the electrolyte layer using the in dip-coating method; however, the reason for this is that interfacial adhesion was improved due to the dense structure, which leads to a thin thickness of the electrolyte layer.

• Polymer(Korea)
• /
• v.32 no.1
• /
• pp.77-84
• /
• 2008

The thermal properties, morphology, mechanical properties and gas permeability of the blends of poly (amic acid) (PAA) and poly (o-hydroxyamides) (PHAs) having pendant group was investigated. The 5% weight loss and major weight loss of the b)ends occurred in the ranges of $348{\sim}407^{\circ}C$ and $589{\sim}615^{\circ}C$ upon a heating process. After a thermical annealing, the tensile strength and initial modulus of blends increased $3.7{\sim}52.9%$ and $34.4{\sim}70%$ from the value of pure PAA, respectively. Especially the tensile strength and modulus of the PAA/MP-PHA=9/1 showed the highest values (97.5 MPa and 2.67 GPa, respectively), which were 53 and 70% higher than those of pure PAA. The fine PHA domains were found to be uniformly dispersed. The interfacial adhesion between PAA and PHA was identified to be good. The gas permeabilities of PAA/M-PHA blend increased with M-PHA contents.

• Elastomers and Composites
• /
• v.51 no.1
• /
• pp.17-23
• /
• 2016

In this study, the reclaimed polypropylene (RPP) and waste ground rubber tire (WGRT) were used to simulate the thermoplastic vulcanizate (TPV) for cost reduction and resources recycling. Also, we examined the effects of dicumyl peroxide (DCP) and 2,5-dimethyl-2,5-di-(tert-butylperoxy)-hexane (DTBPH) as peroxide type cross-linking agents to enhance the properties of TPV's. The components of RPP and WGRT were fixed at 30 and 70 wt%, and DCP and DTBPH were added in the concentrations from 0.5 to 1.5 phr, respectively. RPP/WGRT composites with different contents of DCP and DTBPH were prepared by a modular intermeshing co-rotating twin screw extruder. The Young's modulus of composites were decreased with increasing peroxides contents. On the other hand, tensile strength, elongation at break, and impact strength of the composites were increased with peroxide contents. We also confirmed that interfacial adhesion between RPP and WGRT was considerably improved by adding the peroxides. Taken together, DTBPH added RPP/WGRT composites exhibited better mechanical properties rather than those of DCP added composites.

• Elastomers and Composites
• /
• v.49 no.3
• /
• pp.225-231
• /
• 2014

In this study, we used polypropylene grafted with itaconic acid (PP-g-IA) as a compatibilizer to prevent phase separation phenomenon which occurs upon blending polypropylene (PP) and ethylene-vinyl alcohol copolymer (EVOH). A compatibilizer was prepared using graft copolymerization of itaconic acid (IA) onto PP where input ratio of IA was 1, 2, 5, and 10 wt.%. To confirm the structure of PP-g-IA and the graft ratio of IA onto PP, we used $^1H$ NMR and FT-IR. We tested the compatibilizer which has highest graft ratio of 1% in immiscible PP/EVOH blends. The morphologies of PP/PP-g-IA/EVOH blends were analyzed by SEM. Thermal and mechanical properties of the blends were analyzed by DSC and UTM. PP-g-IA enhanced the interfacial adhesion of PP and EVOH copolymer.

• Elastomers and Composites
• /
• v.36 no.3
• /
• pp.177-187
• /
• 2001

Polypropylene(PP)/polyurethane(PU) blends with reactive compatibilizers were prepared by the compositional quenching process. Maleic anhydride grafted PP(MPP) and hydroxyethyl maleimide grafted PP(HPP) were introduced as reactive compatibilizers. The formation of HPP and the reactions of compatibilizers with the PU components were confirmed by FT-IR spectroscopy. The morphology, tensile properties, thermal stability, and surface property were studied. The blends prepared by the compositional quenching showed better dispersed domain morphology than the melt blends. The PU domain size became more uniform and reduced in size with increasing the amount of compatibilizers. The blends with HPP showed sightly smaller domain sire than the blends with MPP. The blends with compatibilizers all showed improved tensile properties, surface property. and thermal stability due to the interfacial adhesion effect. The blends with MPP showed higher surface energy than the blends with HPP, but the latter showed better thermal stability compared to the former.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.54 no.3
• /
• pp.114-119
• /
• 2005

We investigated compatibilizing effects of electrical properties such as charge distributions and electrical breakdown in blends of low density polyethylene (LDPE) / polystyrene (PS) with poly [styrene-b-(ethylene-co-butylene)-b-styrene] (SEBS), the triblock copolymer. The blends with $70\;wt\%$ of LDPE and $30\;wt\%$ of PS were prepared through a melt blending in a batch type kneader at a temperature of $220^{\circ}C$ when the SEBS content increased up to $10\;wt\%$. Scanning electron microscopy (SEM) was investigated for observation of morphology of LDPE / PS blends increasing SEBS contents. The morphological observation showed that addition of SEBS results in the domain size reduction of the dispersed PS phase and a better interfacial adhesion between LDPE and PS phases. Measurements of space charge distributions for blends was carried out with pulsed electroacoustic (PEA) method. It was possible to observe that the amount of charge storage in the LDPE / PS blends decreased wiか increasing of SEBS content. The location of SEBS at a domain interface enables charges to move from one phase to the other via domain interface and results in a indicative decrease in the amount of space charge for the LDPE / PS blends with SEBS. Electrical breakdown strength of these blends was observed. It was found that the maximum breakdown strength of the blend was 51.55 kV/mm. These results were better than 38.38 kV/mm of LDPE used electrical insulator for cables and were caused by crystalinity of blends. Because the crystalinity of blends were lower than LDPE, electrical breakdown strength of LDPE / PS blends is higher than that of LDPE. We evaluated the possibility of these blends for insulating material substituted LDPE.