• Journal of the Korean Wood Science and Technology
• /
• 제31권5호
• /
• pp.15-22
• /
• 2003

국산 간벌재 3수종을 이용하여 밀도 및 수지첨가량을 달리해서 톱밥보드를 제조한 후 감압 후 상압, 감압·초음파 병행 후 상압으로 20분씩 3반복 함침하여 밀도 및 수지첨가량에 따른 함침 보드의 물성을 측정하고, 함침 시 초음파처리 효과를 조사하였다. 밀도 및 수지첨가량이 증가함에 따라 함침 보드의 밀도, 휨강도 및 브리넬 경도는 증가하였으나, 수지 함침율은 감소하였다. 감압·초음파 병행 후 상압 함침에 의한 함침보드의 밀도, 수지함침율, 휨강도 및 브리넬 경도가 감압 후 상압에 의한 함침 보드 보다 컸다. 보드 함침 시 초음파처리를 병행함으로써 수지 함침율이 증가되어 함침 보드의 물성에 영향을 미치는 것으로 판단된다.

• Journal of the Korean Wood Science and Technology
• /
• 제32권3호
• /
• pp.25-32
• /
• 2004

This research work explored physical and mechanical properties of impregnated sawdust boards from three softwood species (P, densifora, L. kaemferi, and P. koraiensis) with phenol-formaldehyde (PF) resin by various vacuum treatment methods of combining pressure, vacuum, and ultrasonic waves. Simultaneous vacuum and ultrasonic wave treatments with no pressure resulted in the greatest increase in resin content, density, dimensional changes (thickness and length), bending strength, and hardness of impregnated board. This result seemed to be attributed to the ultrasonic wave treatment.

• Journal of the Korean Wood Science and Technology
• /
• 제30권2호
• /
• pp.158-164
• /
• 2002

우드세라믹의 성질에 영향을 미치는 보드의 수지 함침율과 밀도경사의 특성을 알아보기 위하여 증기 처리를 하지 않은 보드와 증기 처리를 1, 5, 10분 실시한 보드를 석탄산수지로 함침한 후 증기분사 시간의 영향을 조사하였다. 증기처리를 하지 않은 보드의 중층과 표층의 밀도 비가 가장 컸으며, 수지 함침율, 길이 및 두께 증가율은 밀도가 증가함에 따라 감소하였다. 또한 등기처리를 10분 실시한 보드의 수지 함침율, 길이 및 두께 증가율이 가장 컸다.

• Journal of the Korean Wood Science and Technology
• /
• 제28권4호
• /
• pp.56-60
• /
• 2000

A new porous carbon material "woodceramics" was developed by carbonizing wood or woody materials impregnated with thermosetting resin. Steamed board and non-steamed board were made from thinned small log of Aomori Hiba (Thujopsis dolabrata S. et. Z. var. hondae M.). They were impregnated with phenol resin and sintered in a vacuum furnace at $650^{\circ}C$. In this paper, the manufacturing method of woodceramics and changes of dimension, weight and compressive strength were investigated. The changes of dimension, weight and compressive strength depend on the types of board and density.

• Journal of the Korean Wood Science and Technology
• /
• 제30권2호
• /
• pp.115-120
• /
• 2002

MDF를 페놀수지에 함침한 후 500, 650, 800, 1,000℃에서 소성하여 우드세라믹을 제조한 후 함침재 및 우드세라믹의 치수 변화와 휨강도를 측정하였다. 수지 함침율이 증가할수록 함침재의 치수 증가율 및 휨강도는 증가하였다. 소성온도에 따른 중량, 길이 및 두께감소율은 각각 소성온도 500℃일 때 59.9%, 19.4%, 26.3%이었으며, 소성온도 1,000℃일 때 65.3%, 22.5%, 31.6%로 소성온도가 증가함에 따라 증가하였으며, 휨강도 또한 함침율 40%일 때 소성온도 500℃에서 50.3 kgf/cm³, 800℃에서 0.79 g/cm³로 증가하였으나, 1,000℃에서는 0.75 g/cm³로 약간 감소하였다. 이상의 결과로 함침재 및 우드세라믹의 성질은 수지 함침율 및 소성온도의 영향을 받음을 알 수 있었다.

• Journal of the Korean Wood Science and Technology
• /
• 제42권4호
• /
• pp.420-427
• /
• 2014

제재과정에서 발생되는 톱밥과 농업부산물인 왕겨의 활용방안을 찾고자 왕겨의 혼합비율에 따라 혼합보드를 제조하고 수지함침 및 탄화과정을 거쳐 혼합세라믹을 제조하여 왕겨의 혼합비율에 따라 물성을 조사하였다. 같은 수지함침율에서 왕겨혼합비율이 증가함에 따라 탄화 후 밀도 및 휨강도는 증가하였으나 중량감소율은 감소하였다. 또한 같은 탄화온도에서 밀도와 휨강도는 왕겨혼합비율이 40%일 때 가장 큰 것으로 나타났다.

• 한국가구학회지
• /
• 제11권1호
• /
• pp.31-36
• /
• 2000

Woodceramics are new porous carbon materials obtained by carbonization of wood or woody materials impregnated with thermosetting resin in a vacuum furnace. This study examined the electrical properties of woodceramics made from thinned logs of Cryptomeria japonica as a use for electric articles. The summarized results were as follows: 1. The volume resistivity of woodceramics decreased with increasing density of woodceramics made from 3 type board. And the volume resistivity of woodceramics made from non- steamed board was somewhat higher than steamed board. 2. The consumption of electric power of woodceramics decreased with increasing density of woodceramics and resin contents made from 3 type board. And the consumption of electric power of woodceramics made from non-steamed board was somewhat higher than steamed board. 3. When the woodceramics were coated by silicon, the consumption of electric power increased about 7%.

• 대한건축학회논문집:구조계
• /
• 제34권1호
• /
• pp.53-60
• /
• 2018

For test on flooring board laminated with PVC decoration materials in order to replace the current surface materials such as HPL in decoration wood-based flooring board. the Results of comparison and analysis are as follows: For thermal conductivity, flooring board decorated with PVC did not show huge differences when temperature was rising and lowering compared to the flooring materials laminated with the existing HPL surface materials. It seems the most meaningful results for using it as indoor flooring materials. That is, in Korea where there is the culture focusing on ondol heating, use amount of heat energy and efficiency of flooring materials are very important and sensitive issues, involving immediately with household economy of final consumers, and it might be a criteria to judge basic performances required as flooring materials. As a result of the analysis on mandatory durability test items such as abrasion resistance, absorption width expansion rate, impact resistance, surface hardness, and impact absorption for flooring materials, compared to flooring board laminated with general HPL surface decoration materials, decoration wood-based flooring board laminated with PVC surface decoration materials which is higher abrasion resistance with smaller transformation and has better durability and impact absorption of the surface, is available for actual application as indoor flooring board, and for replacing surface decoration materials impregnated with heat-hardened resion such as HPL.

• Journal of the Korean Wood Science and Technology
• /
• 제28권4호
• /
• pp.51-55
• /
• 2000

The woodceramics which are new porous carbon materials were obtained by carbonizing from thinned small log of Aomori HIBA (Thujopsis dolabrata S. et. Z. var. hondae M.) impregnated with phenol resin in a vacuum furnace. During the carbonization process, the resin changes into glassy carbon, which has superior property. The resin impregnation rate and bending strength depend on the types of board and density. In this paper, the manufacturing method of woodceramics made from thinned small logs of Aomori HIBA was introduced and some properties were examined.

• 한국화재소방학회논문지
• /
• 제30권2호
• /
• pp.7-18
• /
• 2016

본 연구는 주택이나 창고 등의 내부 마감재로 사용하는 합성 목재의 연소 독성평가에 관한 것으로 SEM, 콘 칼로리미터, FTIR를 활용해 집성판, MDF, 미송합판, 코어합판, 나왕 방부목 5종의 재료별 연소가스 독성을 실험 및 분석하였다. 각 재료별 독성특성 중 나왕 방부목에서 이산화탄소($CO_2$)의 치사농도인 100,000 ppm을 2.5배 초과하는 256,965 ppm, 이산화황($SO_2$)의 치사농도인 400 ppm의 3.6배를 초과하는 1,475 ppm이 검출되었다. 집성판은 이산화질소($NO_2$)가 1,569 ppm으로 치사농도인 250 ppm의 6배가 측정되었고, 암모니아($NH_3$)는 MDF에서 치사농도 값인 750 ppm 대비 795 ppm이 측정되었다. 따라서 대부분의 건축 재료에서 인체에 치명적인 가스가 발생되는 것을 확인하였고, 향후 건축 재료의 위해성을 평가하기 위한 기초데이터로 활용하고자 한다.