• 한국재료학회지
• /
• 제32권4호
• /
• pp.193-199
• /
• 2022

In this study, lenses are fabricated using various nanomaterials as additives to a silicone polymer made with an optimum mixing ratio and short polymerization time. In addition, PVP is added at a ratio of 1 % to investigate the physical properties according to the degree of dispersion, and the compatibility with hydrophobic silicone and the possibility of application as a functional lens material are confirmed. The main materials are SIU as a silicone monomer, DMA, a hydrophilic copolymer, EGDMA as a crosslinking agent, and 2H2M as a photoinitiator. Holmium (III) oxide, Europium (III) oxide, aluminum oxide, and PVP are used. When Holmium (III) oxide and Europium (III) oxide are added based on the Ref sample, the characteristics of the lens tend to be similar overall, and the aluminum oxide shows a tendency slightly different from the previous two oxides. This material can be used as a silicone lens material with various nano oxides and polyvinylpyrrolidone (PVP) acting as a dispersant.

• 한국안광학회지
• /
• 제16권4호
• /
• pp.383-390
• /
• 2011

목적: 본 연구에서는 소프트콘택트렌즈를 착용하였을 때 렌즈에 부착되는 누액 단백질에 의하여 굴절력의 변화가 유발되는 지를 알아보고자 하였다. 방법: -1.00 D, -3.00 D, -5.00 D 및 -7.00 D의 굴절력을 가지는 etafilcon A, hilafilcon A 및 comfilcon A 재질 렌즈를 인공누액에 각각 1일, 3일, 5일, 7일 및 14일 동안 배양시킨 후 자동렌즈미터를 이용하여 wet cell 방법으로 굴절력을 측정하였으며, 렌즈에 침착된 단백질 양을 Lowry 방법으로 정량하였다. 결과: 세 종류의 렌즈 가운데 이온성인 etafilcon A 재질 렌즈에서 가장 많은 단백질이 침착되어 굴절력의 변화 가 크게 나타남을 확인하였다. 즉, 인공누액에 1일 동안 배양시킨 후에는 모든 디옵터의 렌즈에서 굴절력이 크게 감소하였으나, 배양 기간이 증가할수록 굴절력이 다시 점차적으로 증가하였다. 모든 디옵터의 etafilcon A 렌즈에서 관찰된 굴절력 변화는 소프트콘택트렌즈의 기준오차범위를 벗어나는 큰 변화였으며 이러한 변화는 저굴절력 렌즈에서의 더 크게 나타났다. 반면, 비이온성의 hilafilcon A 렌즈는 etafilcon A 재질 렌즈의 약 20%에 해당하는 단백질 이 침착되었으며, 인공누액에서의 배양기간이 증가할수록 지속적으로 유의한 굴절력의 증가를 보였다. Hilafilcon A 재질 렌즈의 굴절력 역시 인공누액에 배양하게 되면 기준오차범위를 벗어나는 변화가 나타났으며 저굴절력 렌즈에서 더 큰 굴절력의 변화가 나타났다. 실리콘 하이드로겔 재질인 comfilcon A 렌즈의 경우는 침착되는 단백질의 양이 가장 적어 etafilcon A 렌즈의 약 10%에도 미치지 못하였으며, 이에 따른 굴절력 변화도 적어 모든 디옵터에서 기준 오차범위 내의 변화를 보였다. 결론: 본 연구에서는 렌즈에 침착된 누액 단백질에 의해 렌즈 재질에 따라서는 기준오차범위를 벗어날 정도의 큰 굴절력 변화가 나타남을 밝혔다. 이로써 소프트콘택트렌즈의 긴 착용 시간으로 유발되는 시야흐림 현상의 원인 중의 하나가 누액 단백질 침착에 의한 것임을 알 수 있었으며, 많은 침착 단백질 양을 가지는 콘택트렌즈 착용자의 경우 적절한 재질의 렌즈 선택이 필요하다는 것을 알 수 있었다.

• KSBB Journal
• /
• 제11권5호
• /
• pp.557-564
• /
• 1996

Contact lens 재료물질로 사용되어지는 poly(2 h hydroxyethylmethacrylate), poly (HEMA) 는 물을 약 45퍼센트 포함하여 수화젤(hydrogel)을 만들 수 있는 고분자 물질이다. Poly(HEMA)와 단백질의 구성물질인 수용성 아미노산(alanine, argmme, glycine, lysine, methionine, proline, serine)과의 상호작용력과 작용위치에 대한 실험을 FT - IR과 R Raman 분광법을 사용하여 행한 결과 Arg과 Lys 이 가장 크게 작용하였고, 작용크기는 각 pH에 따라 존재하는 이온종과 양에 관계되며, 작용위치는 주로 poly(HEMA) 내에 존재하는 히드록시기에서 일어났다.

• 한국안광학회지
• /
• 제19권3호
• /
• pp.323-329
• /
• 2014

목적: 본 연구는 최근 4년간 대한민국의 안경원에서 판매된 콘택트렌즈를 조사하여 처방되는 추세를 알아보고자 하였다. 방법: 매년 100개의 설문지를 무작위로 전국 안경원에 우편 발송하였다. 각 설문지의 작성은 안경원에서 설문지를 받은 후에 판매된 처음 10건의 콘택트렌즈에 대한 정보를 기재하도록 하였고, 우편이나 이메일로 반송하도록 요청하였다. 결과: 총 400개의 설문지 중에 209개의 설문지가 반송되었고, 훼손이 없고 분석에 적합한 처방건수가 1937건이었다. 콘택트렌즈를 처방 받은 고객들의 평균 나이는 2010년에는 $26.2{\pm}7.0$세, 2011년에는 $26.1{\pm}7.6$세, 2012년에는 $24.7{\pm}.6$세, 2013년에는 $24.8{\pm}7.2$세로 나타났으며, 착용자의 대부분은 여성이었다(75%). 소프트콘택트 렌즈 중에서 실리콘 하이드로겔 렌즈의 비율은 평균 18%를 차지하였고, 디자인별로 분류했을 때, 토릭렌즈의 비율은 평균 17%였으며, 이 비율은 4년간 꾸준히 증가하였다(2010년:10%, 2011년:18%, 2012년:16%, 2013년:22%). 미용렌즈는 29%의 비율을 나타내었다. 일회용 렌즈의 비율은 29%이고, 3~6개월 교체용이 가장 많은 40%로 조사되었다. 결론: 콘택트렌즈 착용자의 대부분이 여성이었으며, 평균나이는 4년간 적은 비율로 차츰 감소하였다. 나이가 어린 여성 착용자가 증가한 것은 미용렌즈의 처방이 갈수록 증가한 것과 연관된다. 또한 미용렌즈의 처방 비율(29%)은 전세계의 미용렌즈 처방 평균(7%)보다 훨씬 높게 나타났다. 이러한 미용렌즈의 성장은 한국의 미용관련 시장의 상승세와 관련 있는 것으로 생각된다.

• 한국안광학회지
• /
• 제18권3호
• /
• pp.271-277
• /
• 2013

목적: 본 연구는 역방향(Everted) 실리콘 하이드로겔 렌즈 착용 후 각막 굴절력의 변화에 대하여 연구하였다. 방법: 각막 굴절력의 변화를 알아보기 위해 corneal topographer(CT-1000, Shin-nippon Co., Japan)를 이용하여 주경선 굴절력과 각막난시를 측정하였고, 굴절이상도 변화는 자동굴절검사기(Natural vision-K 5001, Shin-nippon Co., Japan)를 이용하여 타각적 굴절검사를 실시하였다. 렌즈 착용 전과 착용 1주일 후의 변화를 알아보았다. 결과: 각막 굴절력의 변화를 본 결과 경도 근시에서 보다 효과적으로 각막 굴절력을 교정할 수 있었고, 각막의 강주경선의 굴절력이 클수록, 각막난시가 많을수록 각막 눌림이 많았다. 대상자의 73%가 1 D이하의 타각적 굴절이상도 감소를 보였고, 17%가 굴절이상도가 증가하는 역효과가 나타났다. 타각적 굴절이상도의 감소는 각막 굴절력이 크고 각막난시가 많을 때 효과적이었다. 결론: 역방향 하이드로겔 렌즈에 의해 각막눌림이 야기될 수 있고, 이는 각막 굴절력과 각막난시, 타각적 굴절이상도에 따라 정도의 차이가 발생하였다. 렌즈의 파라미터를 변경하기 힘든 점을 고려하여 적정한 대상자의 선정이 중요할 것으로 사료된다.

• Bulletin of the Korean Chemical Society
• /
• 제32권12호
• /
• pp.4239-4243
• /
• 2011

Biocompatible hydrogels from 2-hydroxyethyl methacrylate (HEMA) monomer containing various amount of alginate in the presence and absence of hydrophilic methacrylic acid (MAA) were synthesized in order for biomedical application. The antimicrobial effect and interaction with proteins for hydrogels were investigated in this study. MAA was introduced because it was expected to increase the amount of water content in the polymer which is an important factor for biocompatibility, and alginate was expected to enhance the antimicrobial activity. The antimicrobial effect against S. aureus and E. coli increased for all hydrogels as the amount of alginate and MAA contained. Presence of MAA further enhances the antimicrobial effect. Amount of adsorption of bovine serum albumin (BSA) increased with increasing concentration of alginate whether MAA was present or not. Contrarily, the amount of lysozyme was not affected with increasing alginate concentration in the absence of MAA, while it decreased in the presence of MAA.

• 대한화학회지
• /
• 제40권6호
• /
• pp.385-393
• /
• 1996

Poly(2-hydroxyethylmethacrylate, HEMA)는 contact lens 재료물질로 사용되고, 물을 약 45퍼센트 포함하여 수화겔(hydrogel)을 만들 수 있는 고분자이다. Poly(HEMA)와 아미노산(alanine, arginine, methionine, proline, glycine, serine, lysine)과의 상호작용력을 DSC와 TGA 열분석법으로 측정한 결과 lysine, arginine, alanine의 결합성이 큼을 알 수 있었다.

• 한국안광학회지
• /
• 제19권1호
• /
• pp.69-77
• /
• 2014

목적: 본 연구는 플루오로로 치환된 아닐린 (2,4-difluoroaniline, 2,6-difluoroaniline, 3,4-difluoroaniline)을 첨가제로 사용한 기능성 콘택트렌즈를 제조한 후 각각의 물리 광학적 특성을 알아보았다. 방법: 친수성 하이드로젤 콘택트렌즈를 제조하기 위해 HEMA(2-hydroxyethylmethacrylate), NVP(N-vinyl pyrrolidone), MA(methacrylic acid), 교차결합제인 EGDMA(ethylene glycol dimethacrylate), 그리고 개시제인 AIBN(azobisisobutyronitrile)을 기본배합으로 한후, 불소로 치환된 aniline을 첨가하였다. 콘택트렌즈 제조방법은 cast mould법을 사용하여 공중합 하였으며, 제조된 콘택트렌즈는 0.9% NaCl normal saline에 완전히 침지시켜 24시간 수화 후 콘택트렌즈의 물리 광학적 특성을 측정하였다. 결과: 2,4-, 2,6- 및 3,4-difluoroaniline을 비율별로 첨가한 sample의 함수율을 측정한 결과, 첨가제의 비율이 증가할수록 함수율이 감소하는 경향을 나타내었으며, 굴절률의 경우 첨가제의 비율이 증가할수록 함수율과 반비례 하여 굴절률은 증가하는 경향을 나타내었다. 제조된 고분자에 대한 자외선 영역의 광투과율을 측정한 결과, 2,4-difluoroaniline를 첨가제로 사용한 경우, UV-B(9.8~51.4%), UV-A(58.8~79.2%) 그리고 visible transmittance(87.0~90.4%)의 투과율을 나타내었고, 2,6-difluoroaniline를 첨가제로 사용한 sample 렌즈는, UV-B(80.2~83.2%), UV-A(85.8~86.4%), 그리고 visible transmittance(90.8~91.4%)의 투과율을 나타내었다. 또한, 3,4-difluoroaniline를 첨가제로 사용한 고분자 렌즈는, UV-B(3.8~30.4%), UV-A(47.8%~74.4%) 그리고 visible transmittance(86.2~91.0%)의 투과율을 각각 나타내었다. 결론: 본 연구 결과를 통해, 2,4-difluoroaniline 그리고 3,4-difluoroaniline은 자외선 차단성을 지닌 착색 안의료용 렌즈 재료로 유용하게 사용될 수 있을 것으로 판단된다.

• 폴리머
• /
• 제33권2호
• /
• pp.169-174
• /
• 2009

Poly(ethylene glycol)(PEG)이 콘택트렌즈에 미치는 영향을 조사하기 위하여 PEG가 도입된 실리콘 수화젤 렌즈를 제조하고 특성을 평가하였다. 실리콘 수화젤 렌즈는 methacryloxypropyl tris(trimethylsiloxy) silane(TRIS), methyl methacrylate(MMA), N,N'-dimethyl acrylamide(DMA) 등과 PEG 함유 단량체인 poly(ethylene glycol) methyl ether methacrylate(PEG-MEM)를 공중합하여 제조하였다. 특성평가는 Fourier transform infrared spectroscopy(FT-IR), electron spectroscopy of chemical analysis(ESCA), scanning electron microscopy(SEM) 등과 물 흡수도, 물 접촉각, 광투과도, 인장강도 등을 평가하였고 단백질 흡착 실험을 행하였다. FT-IR 및 ESCA 분석결과 C-O 결합피크의 증가를 보여 PEG 도입을 확인하였고 SEM 분석결과 상분리 현상은 나타나지 않았다. 물흡수도는 PEG-MEM의 도입에 따라 1차적으로 증가하였고 물 접촉각 및 광투과도는 감소하는 현상을 나타내었다. 단백질흡착 실험결과, PEG의 도입에 따라 눈물 속에 있는 단백질인 albumin, lysozyme, $\gamma$-globulin 등의 흡착이 감소하는 현상을 나타내었다. 또한 PEG 분자량의 증가에 따라 흡착되는 단백질의 양이 감소하는 것을 확인할 수 있었다. 인공눈물을 사용한 단백질 흡착실험에서도 PEG의 도입에 따라 단백질 흡착이 감소하는 현상을 나타내었다.

• 한국안광학회지
• /
• 제15권1호
• /
• pp.39-46
• /
• 2010

목적: 자동렌즈미터를 이용한 소프트 콘택트렌즈의 굴절력 측정에서 dry blotting과 wet cell 방법에 따른 신뢰도를 평가하고자 하였다. 방법: 측정에 사용한 소프트렌즈는 현재 국내에서 유통되고 있는 렌즈 5종류, 4개의 굴절력(-1.50D, -3.00D, -6.00D, -9.00D)을 이용하였고, 두 검사자가 자동렌즈미터로 측정하여 반복성과 재현성을 평가하였다. 결과: Dry blotting방법으로 측정한 굴절력의 평균 차이는 0.03~0.18D였으며, 실리콘 하이드로겔 렌즈에서 0.10~0.18D, 하이드로겔 렌즈에서 0.03~0.08D로 나타났다. 두 검사 간의 평균 차이는 0.10D이하로 측정자 간의 재현성이 좋은 것으로 나타났다. Wet cell방법으로 측정한 굴절력의 평균 차이는 0.09~0.69D였으며, 두 검사자 간에 평균 차이는 0.02~0.59D로 나타났으며, 소재에 따른 측정의 신뢰도와 검사자 간의 재현성은 낮았다. 결론: 모든 재질에 대해 dry blotting 방법이 wet cell방법보다 신뢰도가 좋았으며, 두 방법 모두 실리콘 하이드로겔 렌즈에서는 낮은 신뢰도를 보였다. 자동렌즈미터를 이용하여 신속히 후면 정점굴절력을 확인할 필요가 있는 실무 현장에서 dry blotting방법이 효율적인 것으로 판단된다.