Carbonation Mechanism of Hydrated Cement Paste by Supercritical Carbon Dioxide (초임계 이산화탄소에 의한 시멘트 페이스트의 중성화 반응 메커니즘)

  • Park, Jeong-Won;Kim, Ji-Hyun;Lee, Min-Hee;Chung, Chul-Woo
    • Journal of the Korea Institute of Building Construction
    • /
    • v.18 no.5
    • /
    • pp.403-412
    • /
    • 2018
  • Recently, needs for utilization of recycled aggregate have been increasing. However, its utilization has been limited due to its high alkalinity, which mostly came from the unremoved cement paste particles that were attached at the surface of recycled aggregate. Various efforts has been made to reduce its alkalinity by using $CO_2$, but currently available methods that uses $CO_2$ generate the problem with pH recovery. Considering the fact that supercritical $CO_2$ ($scCO_2$) can provide more rapid carbonation of cement paste than by normal $CO_2$, $scCO_2$ was utilized in this work. The reaction between $scCO_2$ and hydrated cement paste has been systematically evaluated. According to the results, it was found that powder type showed higher carbonation compared to that of cube specimens. It seems the carbonation by $scCO_2$ has occurred only at the surface of the specimen, and therefore still showed some amount of $Ca(OH)_2$ calcium aluminates after reaction with $scCO_2$. With powder type specimen, all $Ca(OH)_2$ was converted into $CaCO_3$. Moreover, additional calcium that came from both calcium aluminate hydrates and calcium silicate hydrates reacted with $scCO_2$ to form $CaCO_3$. After carbonation with $scCO_2$, the powder type specimen did not show pH recovery, but cube specimens did show due to the presence of portlandite.

Addition of Polymeric Materials to Binders for Solidification of Heavy Metal Contaminated Mine Tailings (폴리머 물질 첨가를 통한 중금속 오염 광미의 고형화 처리)

  • Kim, Tae-Poong;Min, Kyoung-Won;Lee, Hyun-Cheol;Seo, Eui-Young;Lee, Won-Sup
    • Journal of Industrial Technology
    • /
    • v.30 no.A
    • /
    • pp.37-43
    • /
    • 2010
  • Polymeric materials in addition to Portland cement and hydrated limes were used to solidify heavy metal contaminated tailings from five abandoned metal mines in Korea. Mine tailings were mixed separately with Portland cement and hydrated lime at a concentration of 20-30 wt% and 6-9 wt%, respectively and Ethylene Vinyl Acetate(EVA) powder was added to each specimen at a ratio of 2.5 and 5.0 wt% to binders. Polymer-added and polymer-free solidified forms were evaluated for their appropriateness in accordance with the suggested test methods. Regardless of addition of polymeric materials, all solidified forms satisfy the uniaxial compressive strength(UCS) requirements(0.35MPa) for land reclamation and show remarkably reduced leaching concentrations of heavy metals such as As, Cd, Cu, Pb and Zn less than the toxicity criteria of Korean standard leaching test(KSLT). The addition of polymeric materials increased the UCS of solidified forms to improve a long-term stability of solidified mine tailings.

  • PDF

Recycling Technology Trend of Waste Concrete Powder for Carbon Neutrality in the Cement Industry (시멘트 산업 탄소중립을 위한 폐콘크리트 미분말의 재활용 기술 동향)

  • Sang-Chul, Shin;Jin-Man, Kim;Geon-Woo, Kim;In-Gyu, Kang
    • Journal of the Korean Recycled Construction Resources Institute
    • /
    • v.10 no.4
    • /
    • pp.465-474
    • /
    • 2022
  • Research on the recycling of waste concrete has been conducted mainly focusing on the production of high-quality recycled ag g reg ate, and as a result, standards and specifications for recycled ag g reg ate have been established. However, in the case of waste concrete powder, although a lot of research on its utilization has been conducted in Korea, an innovative technology leading to commercialization has not yet been announced. Recently, research on technology using waste concrete powder as a raw material for clinker or cement has been actively conducted in major overseas advanced countries. This study investigated the overseas cases with regard to high value-added recycling technology and commercialization trend of waste concrete powder for carbon neutrality in cement and concrete industries. A number of studies have reported that it is essential to completely separate the aggregate and hydrated cement paste fraction for recycling of waste concrete powder. Also in major foreig n countries such as EU and USA, commercialization and standardization of using waste concrete powder as a raw material for clinker or a additive for cement are now in progress beyond the R&D stage. Therefore, Research and standardization for recycling of waste concrete powder should be urgently carried out from the perspective of carbon neutrality in Korea.

Preparation of Needle like Aragonite Precipitated Calcium Carbonate (PCC) from Dolomite by Carbonation Method

  • Ramakrishna, Chilakala;Thenepalli, Thriveni;Huh, Jae-Hoon;Ahn, Ji Whan
    • Journal of the Korean Ceramic Society
    • /
    • v.53 no.1
    • /
    • pp.7-12
    • /
    • 2016
  • In this paper, we have developed a simple, new and economical carbonation method to synthesize a pure form of aragonite needles using dolomite raw materials. The obtained aragonite Precipitated Calcium Carbonate (PCC) was characterized by XRD and SEM, for the measurement of morphology, particle size, and aspect ratio (ratio of length to diameter of the particles). The synthesis of aragonite PCC involves two steps. At first, after calcinated dolomite fine powder was dissolved in water for hydration, the hydrated solution was mixed with aqueous solution of magnesium chloride at $80^{\circ}C$, and then $CO_2$ was bubbled into the suspension for 3 h to produce aragonite PCC. Finally, aragonite type precipitated calcium carbonate can be synthesized from natural dolomite via a simple carbonation process, yielding product with average particle size of $30-40{\mu}m$.

A Study on the Alkali Application of Recycled Aggregates as a Solution to Reduced Intial Intensity of Blast Furnace Slags (고로슬래그의 초기강도 저하 해결방안으로써 순환 잔골재의 알칼리 활용가치에 대한 연구)

  • Kwak, Yong-Jin;Zhao, Yang;Jung, sang-woon;Heo, Young-sun;Han, Min-Cheol;Han, Cheon-Goo
    • Proceedings of the Korean Institute of Building Construction Conference
    • /
    • 2013.05a
    • /
    • pp.85-86
    • /
    • 2013
  • Weakness of fine powder of blast furnace slags includes the decrease of initial intensity and delay of setting time. To solve this problem, there has been research on the alkali activation to induce hardening using alkaline chemical. However, the use of chemicals is dangerous and not cost effective, which can be solved by using recycled aggregates, one of construction wastes. The role of alkali activator can be substituted by alkali of non-hydrated cement included in recycled aggregates. In this study, the alkaline value of recycled aggregates will be evaluated through the comparison of molarity of sodium hydroxide (NaOH).

  • PDF

Utilizability of Waste Concrete Powder as a Material for Soil Pavement (흙도로포장용 재료로서 폐콘크리트 미분말의 활용성 연구)

  • Kim, Yong-Jic;Choi, Yun-Wang;Kim, Young-Jin
    • Journal of the Korean Recycled Construction Resources Institute
    • /
    • v.3 no.3
    • /
    • pp.277-282
    • /
    • 2015
  • This study is conducted to utilize waste concrete powder (WCP) made as a by-product manufacturing high quality recycled aggregate. The blaine fineness of the used waste concrete powder was $928cm^2/g$. As the main characteristic of waste concrete powder, it showed an angular type similar to cement, but hydrated products were attached on the surface of particles. In addition, the size of the particles of waste concrete powder was larger than OPC and in terms of chemical components it had higher $SiO_2$ contents. For using WCP in soil cement-based pavement, the qualities, physical and chemical properties, of WCP should be researched. In the first step, the specified compressive strength of mortar for two types of clay sand soil and clay soil respectively was experimented to be 15 MPa and then optimum mixing ratio of chemical solidification agent were decided in the range of 1.5 - 3.0% in the replacement with cement weight content. In the second step, based on the prior experimental results, recycling possibility of WCP in soil cement-based pavement was studied. In the result of experiment the mixing ratio of WCP were 5, 10, 15 and 20% in the replacement with soil weight and the compressive strength of mortar was somewhat decreased according to the increase of the mixing ratio of WCP.

The Feasibility Study for Utilization of Blended Cement as a Activator of Bottom Ash from Circulating Fluidized Bed Combuster Boiler (순환유동층 보일러 바텀애시의 혼합시멘트 자극제 활용을 위한 타당성 연구)

  • Park, JongTak;Jung, Gwon Soo;Kang, Chang Ho;Oh, Hongseob
    • Journal of the Korean Recycled Construction Resources Institute
    • /
    • v.8 no.3
    • /
    • pp.255-262
    • /
    • 2020
  • Blended cement with fly ash and bottom ash from Circulating Fluidized Bed Combustor boiler(CFBC) burned at a low temperature, can be high heat of hydration and abnormal setting caused by higher volumn contents of Fe2O3, free-CaO, SO3. In this study, the ground CFBC bottom ash powder mixed with blast furnace slag was used as substitute activator of gypsum and recycled iron slag was produced from mix and pulverized by ball mill to increase the recycling rate. The effect on compressive strength of cements with the mixture of original and hydrated bottom ash mixtures with BFS with small water, respectively, was analyzed, and it was found that the hydrated bottom ash activator was more effective in initial strength development. To improve the initial strength of blended cement, an activator mixed with a blast furnace slag and bottom ash mixing ratio of 5:95 and 10:90, respectively, the slag cement by about 6%, and it was analyzed to develop an initial strength similar to gypsum as a conventional activator.

A study on the application of waste concrete powder as a material for construction (건설용 재료로써 폐콘크리트 미분말의 활용성 연구)

  • Kim, Yong-Jic;Choi, Yun-Wang;Kim, Sang-Chel;Kim, Young-Jin
    • Journal of the Korean Recycled Construction Resources Institute
    • /
    • v.7 no.4
    • /
    • pp.88-94
    • /
    • 2012
  • This study is conducted to utilize waste concrete powder made as a by-product manufacturing high quality recycled aggregate. The blaine fineness of the used waste concrete powder was 928 and $1,360cm^2/g$. As the main characteristic of waste concrete powder, it showed an angular type similar to cement, but hydrated products were attached on the surface of particles. In addition, the size of the particles of waste concrete powder was larger than OPC and in terms of chemical components it had higher $SiO_2$ contents. The viscosity of the paste that mixed waste concrete power decreased by 62% at the most, compared to the paste that only used OPC, and the final set time was delayed about two hours. As composition rates of waste concrete powder increased, the flow value decreased by 30% at the most according to the comparison with mortar that only used OPC, and sorptivity coefficients increased by 70%. The compressive strength of mortar decreased by 73% at the most as composition rates of waste concrete powder increased. According to the test results, it is desirable to use waste concrete powder by combining OPC appropriately(below 15%).

  • PDF

Formation Behavior of Microporous Ettringite Body by Hydration of Tricalciumaluminate Clinker and Gypsum (알루민산삼칼슘 클링커와 석고의 수화에 의한 에트린자이트 미세다공체 생성거동)

  • Na, Hyeon-Yeop;Song, Tae-Woong
    • Journal of the Korean Ceramic Society
    • /
    • v.45 no.11
    • /
    • pp.734-738
    • /
    • 2008
  • Ettringite$(3CaO{\cdot}Al_2O_3{\cdot}3CaSO_4{\cdot}32H_2O)$, one of the hydrated phase of Portland cement is usually formed in the early stage of hydration by the reaction of tricalciumaluminate$(C_3A)$ and gypsum. The rapid and strong crystal growth of separated rod-shaped ettringite have been utilized for the preparation of special cements of rapid setting, high strength and non-shrinking properties. The ettringite also has been noticed as a promising materials for the immobilization of various waste ions because of its unique crystal structure which has abundant channels and exchangeable ionic compounds. In this study, the formation and growth behavior of the ettringite was investigated in the system $C_3A-CaSO_4-H_2O$ using $C_3A$ clinker and gypsum to obtain a microporous body for waste ion immobilization. Ettringite was revealed to form by the dissolution-precipitation mechanism and the bulk body was by the entangled growth of rod-shaped ettringite crystals. The hardened body was composed of nearly pure rod-shaped ettringite interlocked each other with adequate mechanical strength. The homogeneity of structure, pore size, specific surface area and porosity of the hardened body were influenced by reaction temperature, water/powder ratio and the curing time. The hardened body prepared with water/powder ratio of 1 at $24^{\circ}C$ for one day showed excellent morphological properties for the purposed materials.