• Polymer(Korea)
• /
• v.30 no.4
• /
• pp.305-310
• /
• 2006

The hybrid cation exchange fibers using graft copolymer of styrene onto PE/PP with PET trunk polymers were synthesized by electron beam preirradiation. The degree of grafting showed 123% value at 80% concentration of styrene. And also, amount of sulfonyl group in the ion exchanger was showed 3.3 mmol/g at 70% concentration of styrene and their values were constant after 70%. The tensile strength for fibers was lower than trunk fibers, and their value of ion exchange fibers were also below than copolymer. It was $0.206kgf/mm^2$ value. The breakthrough time for Ca and Mg ions of hybrid cation exchange fibers were increased with the increase in the pH and temperature. The breakthrough of Mg was slower the mixture than single Mg solution. Adsorption rate constant for Ca, Mg ions and maximum ion exchange capacity were 0.012, 0.011 L/mg.h and 47.06, 42.83 mg/g, and also, activation energies were 2169 and 1534 J/mol, respectively.

• Polymer(Korea)
• /
• v.30 no.6
• /
• pp.525-531
• /
• 2006

In this study, Sulfonated PONF-g-styrene ion exchange fibers were synthesized by radiation induced graft copolymerization. And also, hybride ion exchange fibers, which was combined sulfonated PONF-g-styrene fibers and cationic ion exchange resin, were fabricated by hot melt adhesion method and then their adsorption properties were investigated. ion exchange capacity and water content of hybrid ion exchange fibers increased as compared with those of bead and ion exchange fiber. Their maximum values were 4.76 meq/g and 23.5%, respectively. Adsorption breakthrough time for mercury of hybrid ion exchange fiber was slower than those of bead resin and fibrous ion exchanger. It's value was 130 minutes. Their breakthrough time become short as increasing of pH, and concentration. The initial breakthrough time was observed before and after 10 minutes as increasing of concentration. The adsorption of hybrid ion exchange fibers for $Hg^{2+}\;Pb^{2+},\;Cd^{2+}$ among heavy metals in the mixed solution was observed before 20 min. And also, The adsorption for $Hg^{2+}$ among the heavy metals by hybride ion exchange fibers was observed.

• Polymer(Korea)
• /
• v.31 no.6
• /
• pp.479-484
• /
• 2007

In this study, the hybrid ion exchange fibers (HIEF) were prepared by using web spraying muthod with hot melt adhesive. Characteristics of HIEF and their adsorption properties for ammonia gas were investigated. The ion exchange capacity (IEC) of HIEF was increased with increasing the resin contents and their values were higher than those of pure resin and ion exchange fabrics. The removal efficiency for ammonia gas increased with an increase in packing density of hybrid ion exchange fabrics in the column. The adsorption breakthrough time was 270 min, which was slower than those of the resin and fibers. The maximum value of adsorption for ammonia gas was 94%. The breakthrough time was also increased with increasing the concentration and flow rate of ammonia gas. The reaction constant(k) for ammonia gas was increased with increasing the concentration and flow rate of the gas, while it was decreased an the mass was increased.